Synthesis of binary complex perovskite solid solution by application of both precursor method and wet-dry combination method

A binary complex perovskite solid solution, Sr(Cu,Zn)_1/2W_1/2O₃ (SCZW), was synthesized using a precursor of (Cu,Zn)WO₄ (CZW) prepared by a combination of wet and dry methods. Compositional fluctuations in the resulting material were investigated. The new method includes three steps. The first step is a preparation of an oxide mixture of CuO and ZnO (CZ) by the decomposition of a coprecipitate of Cu²⁺ and Zn²⁺ (wet process). The second step is a solid-state reaction between CZ and WO₃ (dry process) to form a precursor, CZW. The third step is a solid-state reaction between SrCO₃ and CZW to form SCZW. Powder X-ray diffraction analysis revealed that the SCZW was free from the compositional fluctuation which could not be eliminated by application of the precursor method alone.     

Formation of Infinite-Layered (Ca1-xSrx) CuO2 and NaCuO2-type (Ca1-yNay)0.85CuO2 in Tartrate Route

Both NaCuO₂-type Ca_0.85CuO₂ and infinite-layered (Ca_{1- x} Sr _x )CuO₂ could be prepared much more easily by firing the dried solids from mixed acetate aqueous solutions titrated with tartaric acid than by normal calcination. The presence of a narrow solid-solution composition range of 0.10 < x > 0.16 was confirmed in infinite-layered (Ca_{1- x} Sr _x )CuO₂ in the preparation using the tartrate route. The calcium could also be substituted by sodium in a range of y > 0.15 in NaCuO₂-type (Ca_{1- y} Na _y )_0.85CuO₂ using the same route. Further substitution of Ca²⁺ with Y³⁺ might also be possible in infinite-layered (Ca_{1- x} Sr _x )CuO₂, but resulted in the NaCuO2-type compound in the substitution with Na⁺.     

Structure and Microwave Dielectric Properties of Hexagonal Ba[Ti1−x(Ni1/2W1/2)x]O3 Ceramics

Microwave dielectric ceramics with the composition of Ba[Ti_{1− x} (Ni_1/2W_1/2) _x ]O₃ ( x =0.4–0.6) were prepared by a solid-state reaction method. The evolution of the crystalline phases was investigated by X-ray powder diffraction analysis. A cubic-to-hexagonal phase transition occurred between 1000° and 1300°C. The phase transition is irreversible; thus, the hexagonal phase remains stable at room temperature. The X-ray powder diffraction data for x =0.5 were refined using the Rietveld method. It was identified as a h -BaTiO₃-type hexagonal perovksite with the space group of P 6₃/ mmc . It also reveals that random occupancy of Ti⁴⁺ and W⁶⁺ ions occurs in the B-site substructures, whereas Ni²⁺ ions exclusively occupy the octahedral site in the corner-sharing octahedron. The dielectric properties of dense-sintered ceramics were characterized at microwave frequencies. With an increase in x from 0.4 to 0.6, the Q × f value increased from 26 700 to 42 000 GHz, whereas ɛ_r decreased from 29.8 to 20.0, and τ_f from +6.5 to −9.9 ppm/°C.     

Fast Li+ Ion Conduction in Li2O-Al2O3-TiO2-SiO2-P2O5 Glass-Ceramics

Fast lithium ion conducting glass-ceramics have been successfully prepared from the pseudobinary system 2[Li_{1+ x} Ti₂Si _x P_{3− x} O₁₂]-AlPO₄. The major phase present in the glass-ceramics was LiTi₂P₃O₁₂ in which Ti⁴⁺ ions and P⁵⁺ ions were partially replaced by Al³⁺ ions and Si⁴⁺ ions, respectively. Increasing x resulted in a considerable enhancement in conductivity, and in a wide composition range extremely high conductivity over 10⁻³ S/cm was obtained at room temperature.     

Porous Glass-Ceramics with a Skeleton of the Fast-Lithium-Conducting Crystal Li1+xTi2−xAlx(PO4)3

Porous glass-ceramics with a skeleton of the fast-lithium-conducting crystal Li_{1+ x} Ti_{2− x} Al _x (PO₄)₃ (where x = 0.3–0.5) were prepared by crystallization of glasses in the Li₂O─CaO─TiO₂─Al₂O₃–P₂O₅ system and subsequent acid leaching of the resulting dense glass-ceramics composed of the interlocking of Li_{1+ x} Ti_{2− x} Al _x (PO₄)₃ and β-Ca₃(PO₄)₂ phases. The median pore diameter and surface area of the resulting porous Li_{1+ x} Ti_{2− x} Al _x (PO₄)₃ glass-ceramics were approximately 0.2 μm and 50 m²/g, respectively. The electrical conductivity of the porous glass-ceramics after heating in LiNO₃ aqueous solution was 8 × 10⁻⁵ S/cm at 300 K or 2 × 10⁻² S/cm at 600 K.     

Formation and Structural Characterization of 1:1 Ordered Perovskites in the Ba(Zn1/3Ta2/3)O3–BaZrO3 System

The phase stabilities in the(1−x)Ba(Zn_1/3Ta_2/3)O₃ (BZT)-xBaZrO₃(BZ)system have been investigated using samples prepared by the mixed oxide method. The substitution of Zr⁴⁺destabilizes the 1:2 cation ordering in BZT and pro-motes the formation of a cubic, 1:1 ordered structure with a doubled perovskite repeat. The homogeneity range of the 1:1 phase extends from x = 0.04 to approximately x = 0.25; substitutions beyond this range stabilize a disordered perovskite. The limits of stability of the 1:1 ordering coin-cide with compositions previously found to exhibit anoma-lies in their dielectric loss. The range of homogeneity is consistent with a "random layer" model for the 1:1 ordered "Ba{β';_1/2β^1/2}O₃" structure. In this model the B× positions are assumed to be occupied exclusively by Ta⁵⁺, and the b× sites by a random distribution of Zn₂₊, Zr₄₊, and the remaining Ta 5+ cations. The validity of the model, where the ordered solid solutions can be represented by Ba{[Zn_{2− y /3}Ta_{(1−2 y )/3}Zr y ]_1/2[Ta]_1/2}O₃(y =2x)was con-firmed by Rietveld refinements conducted using data col-lected with a synchrotron X-ray source.     

Peculiar Dielectric Behaviors of (Na1/2Bi1/2)0.87Pb0.13TiO3 Thin Films

PbTiO₃-doped sodium bismuth titanate (Na_1/2Bi_1/2)_{1− x} Pb _x TiO₃ of perovskite structure is one of the best-known piezoelectrics/ferroelectrics. However, it has not been properly investigated in any thin-film forms. In this study, the dielectric properties of (Na_1/2Bi_1/2)_0.87Pb_0.13TiO₃ thin films synthesized via a sol–gel route were investigated. They exhibit a strong frequency dispersion of the dielectric permittivity at relatively high frequencies, which is shifted to lower frequencies with increasing temperature. The electrical behavior can be fitted using Jonscher's universal law for dielectric relaxation. The peculiar dielectric behaviors observed can be ascribed to the coexistence of two different dielectric phases in the films, which is believed to be associated with the growth of the local Pb²⁺TiO₃ nanoclusters upon substitution of Pb²⁺ for Na⁺/Bi³⁺ in the (Na_1/2Bi_1/2)_{1− x} Pb _x TiO₃ films.     

Structural and Dielectric Characteristics in a Ca(Mg1/3Nb2/3)O3–CaZrO3 System

This study investigates the effect of CaZrO₃ (CZ) substitution on the evolution of an ordered structure in a Ca(Mg_1/3Nb_2/3)O₃ (CMN) system using Raman spectroscopy, X-ray diffractometry, and transmission electron microscopy. It indicates that a (1− x ) CMN−( x )CZ solid solution has the 1:2 and 1:1 ordered structure distorted by the antiphase, the inphase tilting of oxygen octahedra, and the antiparallel shift of A-site cation. A distinct correlation is noted between the transition of the ordered structure and microwave dielectric properties. The differences in ɛ_r and τ_f are attributed exclusively to the differences in the type of cation arrangement. The structure with the 1:2 ordering exhibits a lower relative permittivity and a more negative τ_f than the structure with the 1:1 ordering. The increased fraction of compressed Nb–O bond in the 1:2 ordered structure associated with a large NbO₆ octahedral distortion is correlated with a decrease in relative permittivity and change of τ_f toward more negative values. Simultaneously, the substitution of the Zr⁴⁺ ion causes a linear increase in polarizability, and it also results in an increase in the relative permittivity.     

Microstructure and Properties of Co2+: ZnAl2O4/SiO2 Nanocomposite Glasses Prepared by Sol–Gel Method

Transparent bulk Co²⁺: ZnAl₂O₄/SiO₂ nanocomposites containing nanocrystalline Co²⁺: ZnAl₂O₄ dispersed in silica glass matrix were obtained by the sol–gel method. The gels of composition 89SiO₂–6Al₂O₃–5ZnO− x CoO ( x =0.2, 0.4, 0.6, 0.8, 1.0) (mol%) were prepared at room temperature by using two different aluminum salts, aluminum nitrate and aluminum alkoxide (aluminum-iso-propoxide, Al(OPrⁱ)₃), as starting materials. The transparent gels were converted to the crystalline phase of gahnite by heating above 900°C. The microstructural evolution of gels was characterized. The effect of Co²⁺ concentration on spectroscopic properties was also discussed. Co²⁺: ZnAl₂O₄ nanocrystals dispersed in the SiO₂-based glass are formed at lower heat-treatment temperature and shorter heating time by using Al(OPrⁱ)₃ as raw material.     

Hydrothermal Synthesis and Characterization of KxNa(1−x)NbO3 Powders

NaNbO₃, KNbO₃, and K _x Na_{(1− x )}NbO₃ powders were successfully prepared by the hydrothermal method. The phase of the products was identified to be orthorhombic structure by X-ray diffraction (XRD) technique, and the XRD results revealed that the x value of the K _x Na_{(1− x )}NbO₃ gradually increased with the increase in the ratio of K⁺ to Na⁺ in alkaline solution. The morphology and the microstructure were investigated by scanning electron microscopy, energy-dispersive spectroscopy, and transmission electron microscopy, and the results indicated that the ratio of K⁺ to Na⁺ in the solution had a great effect on the morphology and the size of products. Na_0.5K_0.5NbO₃ with morphotropic phase boundary composition could be synthesized when the molar ratio of K⁺ to Na⁺ was between 4:1 and 6:1 in the solution. A possible formation mechanism of the K _x Na_{(1− x )}NbO₃ crystal was also proposed based on the experimental results.     

Microwave Dielectric Properties of CaTiO3-CaAl1/2Nb1/2O3 Ceramics Doped with Li3NbO4

The microwave dielectric properties of CaTi_{1− x} (Al_1/2Nb_1/2) _x O₃ solid solutions (0.3 ≤ x ≤ 0.7) have been investigated. The sintered samples had perovskite structures similar to CaTiO₃. The substitution of Ti⁴⁺ by Al³⁺/Nb⁵⁺ improved the quality factor Q of the sintered specimens. A small addition of Li₃NbO₄ (about 1 wt%) was found to be very effective for lowering sintering temperature of ceramics from 1450–1500° to 1300°C. The composition with x = 0.5 sintered at 1300°C for 5 h revealed excellent dielectric properties, namely, a dielectric constant (ɛ_r) of 48, a Q × f value of 32 100 GHz, and a temperature coefficient of the resonant frequency (τ_f) of −2 ppm/K. Li₃NbO₄ as a sintering additive had no harmful influence on τ_f of ceramics.     

Photoluminescence Characteristics of Energy Transfer Between Eu3+and Bi3+in LiEu1−xBix (WO4)0.5(MoO4)1.5

A series of novel red phosphors LiEu_{1− x} Bi _x (WO₄)_0.5(MoO₄)_1.5 ( x =0, 0.05, 0.10, 0.15, 0.20, 0.30, 0.40, and 0.50) were synthesized by the conventional solid-state reaction method. The spectrum and the crystal structure of the phosphors were characterized by Fluorescence spectrophotometry and X-ray diffraction, respectively. The photoluminescent results show that all samples can be excited efficiently by UV (396 nm) and blue (467 nm) light and that they emit red light at 615 nm with line spectra, which are coupled well with the characteristic emissions from UVLED and blue light-emitting diode (LED), respectively. There is an efficient energy transfer from Bi³⁺ to Eu³⁺ ions, leading to the emission intensity of Eu³⁺ being enhanced by 1.5 times, and even more when Bi³⁺ ions are introduced into LiEu (WO₄)_0.5(MoO₄)_1.5. The introduction of Bi³⁺ ions broadened the excitation band of the phosphor, and the optimum doping concentration is found to be 10 mol% of Bi³⁺.     

Strong Green and Red Upconversion Emission in Er3+-Doped Na1/2Bi1/2TiO3 Ceramics

Upconversion emission properties of Na_1/2Bi_1/2TiO₃:Er³⁺ ceramics prepared by the solid-state reaction method were analyzed as a function of Er³⁺ concentration and incident pump power. Strong green (550 nm) and red (670 nm) emission bands were observed with 980 nm excitation at room temperature. Experimental results showed that the emission bands can be tuned by changing Er³⁺ concentration. Upconversion processes in these samples result from not only a two-photon excited-state absorption process but also a nonradiative energy transfer and cross-relaxation process.     

Origin of Microwave Dielectric Loss in ZnNb2O6-TiO2

(1− x )ZnNb₂O₆· x TiO₂ ceramics were prepared using both anatase and rutile forms of TiO₂. At a composition of x = 0.58, a mixture region of ixiolite (ZnTiNb₂O₈) and rutile was observed and the temperature coefficient of resonant frequency (τ_f) was ∼0 ppm/°C. We found that although ɛ_r and τ_f were comparable, the quality factor ( Q × f , Q ≈ 1/ tan δ, f = resonant frequency) of 0.42ZnNb₂O₆·0.58TiO₂ prepared from anatase and rutile was 6000 and 29 000, respectively. The origin of the difference in Q × f of both samples was investigated by measuring electrical conductivity and by analysis of the anatase–rutile phase transition. The anatase-derived sample had higher conductivity, which was related to the reduction of Ti⁴⁺. It is suggested that the increase of dielectric loss originates from an increase in Ti³⁺ and oxygen vacancies due to an anatase–rutile phase transition.     

Synthesis and Characterization of (Ce0.67Tb0.33)MnxMg1−xAl11O19 Phosphors Derived by Sol–Gel Processing

A (Ce_0.67Tb_0.33)Mn _x Mg_{1− x} Al₁₁O₁₉ phosphor powder was synthesized, using a simple sol–gel process, by mixing citric acid with CeO₂, Tb₄O₇, Al(NO₃)₃·9H₂O, Mg(OH)₂·4MgCO₃·6H₂O, and Mn(CH₃COO)₂. The phosphor crystallized completely at 1200°C, and the phosphor particle size was between 1 and 5 μm. The excitation spectrum was characteristic of Ce³⁺, while the emission spectrum was composed of lines from Tb³⁺ and Mn²⁺. The Mn²⁺ gave a green fluorescence band, and concentration quenching occurred when x > 0.10. The luminescent properties of the phosphor were explained by a configurational coordinate model.     

Energetics of Substituted Pollucites Along the CsAlSi2O6–CsTiSi2O6.5 Join: A High-Temperature Calorimetric Study

Enthalpies of drop solution for a suite of substituted pollucites with the compositions CsTi _x Al_{1− x} Si₂O_{6+0.5 x} , 0 ≤ x ≤ 1, which are synthesized using the sol–gel method, have been measured in molten lead borate (2PbO·B₂O₃) at 701°C. As Ti⁴⁺ substitutes for Al³⁺, the enthalpies of drop solution become less endothermic and show exothermic heats of mixing within the composition range from x = 0.3 to 1. This nonideal mixing behavior is consistent with the trend seen in variation of lattice parameters, and we interpret it to be a result of the short-range order associated with the framework cations Al³⁺, Si⁴⁺, and Ti⁴⁺ in the structure. Using enthalpies of drop solution of SiO₂, Al₂O₃, TiO₂, and Cs₂O, standard molar enthalpies of formation of these phases from their constituent oxides and from the elements are derived for the first time.     

Formation of Sm2+ lons in Sol-Gel-Derived Glasses of the System Na2 O-Al2O3-SiO2

Samarium ions (Sm²⁺) incorporated into aluminosilicate glasses by a sol-gel process showed persistent spectral hole burning at room temperature. Gels of the system Na₂O-Al₂O₃SiO₂ synthesized by the hydrolysis of Si(OC₂H₅)₄, Al(OC₄H₉)₃, CH₃ COONa, and SmCl₃·6H₂O were heated in air at 500°C, then reacted with H₂ gas to form Sm²⁺ ions. Whereas Al³⁺ ions effectively dispersed the Sm³⁺ ions in the glass structure, Na⁺ ions were not effective. The Al₂O₃-SiO₂ glasses proved appropriate for reacting the Sm³⁺ ions with H₂ gas and exhibited the intense photoluminescence of Sm²⁺ ions. The reaction of Sm³⁺ ions with H₂ in the Al₂O₂-SiO₂ glasses was determined by first-order kinetics, and the activation energy equaled 95 kJ/mol. At 800°C, the maximum photoluminescence of the Sm²⁺ ions was achieved within 20 min.     

Phase Transitions and Electrical Properties of (Na1−xKx)(Nb1−ySby)O3 Lead-Free Piezoelectric Ceramics With a MnO2 Sintering Aid

Lead-free piezoelectric ceramics (Na_{1− x} K _x )(Nb_{1− y} Sb _y )O₃+ z mol% MnO₂ have been prepared by a conventional solid-state sintering technique. Our results reveal that Sb⁵⁺ diffuses into the K_0.5Na_0.5NbO₃ lattices to form a solid solution with a single-phase orthorhombic perovskite structure. The partial substitution of Sb⁵⁺ for B-site ion Nb⁵⁺ decreases the paraelectric cubic-ferroelectric tetragonal phase transition ( T _c) and the ferroelectric tetragonal-ferroelectric orthorhombic phase transition ( T _O–F), and retains strong ferroelectricity. A small amount of MnO₂ is enough to improve the densification of the ceramics. The co-effects of MnO₂ doping and Sb substitution lead to significant improvements in ferroelectric and piezoelectric properties. The ceramics with x =0.45–0.525, y =0.06–0.08, and z =0.5–1 exhibit excellent ferroelectric and piezoelectric properties: d ₃₃=163–204 pC/N, k _P=0.47–0.51, k _t=0.46–0.52, ɛ=640–1053, tan δ=1.3–3.0%, P _r=18.1–22.6 μC/cm², E _c=0.72–0.98 kV/mm, and T _C=269°–314°C.     

Effect of Fe4+ in the System SrFeO3-SrTiO3

Perovskites of the system SrFeO₃-SrTiO₃ were prepared, and measurements were made of their magnetic and electrical behavior. Chemical analysis showed that the percentage of Fe⁴⁺ varied from 72.5% for SrFeO_2.86 to about zero for Sr(Fe_0.1Ti_0.9)O_2.95; the remainder of the iron was in the Fe³⁺ state and electrical balance was achieved by oxygen loss. Sr(Fe_{1- x} Ti _x )O₃ was antiferromagnetic between x = 0 and x = 0.9, with a Néel temperature below 60°K. A parasitic ferromagnetic component developed when these compounds were cooled in a magnetic field, the magnitude of this component being dependent on the cooling field. The conductivity of these perovskites ranged from 10⁻⁸ ohm⁻¹ cm⁻¹ for x = 1.0 to 10⁻² for x = 0.0 and showed a marked change at x = 0.8. The break corresponded to a change in slope of the lattice parameter and the disappearance of Fe⁴⁺. The Fe⁴⁺ content depended on the heat treatment and atmosphere during formation.     

Effect of MnO2 Addition on the Structure and Electrical Properties of Pb(Zn1/3Nb2/3)0.20(Zr0.50Ti0.50)0.80O3 Ceramics

Pb(Zn_1/3Nb_2/3)_0.20(Zr_0.50Ti_0.50)_0.80O₃ ceramics of pure perovskite structure were prepared by the two-stage method with the addition of 0–3.0 wt% MnO₂ and their piezoelectric properties were investigated systematically. The MnO₂ addition influences in a pronounced way both the crystal structure and the microstructure of the materials. The materials are transformed from the tetragonal to the rhombohedral structure, and the grain size is enhanced when manganese cations are added. The distortion of crystal structure for samples with MnO₂ addition can be explained by the Jahn–Teller effect. The values of electromechanical coupling factor ( k _p) and dielectric loss (tan δ) are optimized for 0.5-wt%-MnO₂-doped samples ( k _p= 0.60, tan δ= 0.2%) and the mechanical quality factor ( Q _m) is maximized for 1.0-wt%-MnO₂-doped samples ( Q _m= 1041), which suggests that oxygen vacancies formed by substituting Mn³⁺ and Mn²⁺ ions for B-site ions (e.g., Ti⁴⁺ and Zr⁴⁺ ions) in the perovskite structure partially inhibited polarization reversal in the ferroelectrics. The ceramics with 0.50–1.0 wt% MnO₂ addition show great promise as practical materials for piezoelectric applications.