Fe-Ni/NiFe_2O_4纳米复合颗粒的制备与磁性研究

结合共沉淀法和氢气还原法成功制备出FeNi/NiFe2O4纳米复合颗粒,所制备的纳米复合颗粒包含NiFe2O4和Fe-Ni合金,其中Fe-Ni合金具有体心立方和面心立方两种结构。用XRD和TEM对所得样品进行结构分析。用SQUID测量样品在室温时的磁滞回线,发现Fe-Ni/NiFe2O4纳米复合颗粒的矫顽力和饱和磁化强度与制备态NiFe2O4纳米颗粒相比随着退火时间的增加呈现出逐渐增加的趋势。为了进一步研究所制备的纳米复合颗粒的磁性特征,测量退火时间相同而退火温度不同的两个样品在零磁场冷却(ZFC)和带磁场冷却(FC)条件下的M-T曲线。     

单相Bi0.95Eu0.05Fe0.95Co0.05O3纳米颗粒的结构及其铁磁特性

采用溶胶-凝胶法制备了单相Bi0.95 Eu0.05Fe0.95 Co0.05 O3纳米粉末。用X射线衍射仪(XRD)和扫描电子显微镜(SEM)测量分析了其结构和形貌,结果表明样品仍为钙钛矿菱方结构。样品Fe2p的X射线吸收谱(XAS)表明样品中Fe的价态处于Fe2+和Fe3+的混合态。利用振动样品磁强计(VSM)测量样品的磁性特征,结果表明样品具有完整闭合的磁滞回线,表现出室温的铁磁性,相比BiFeO3样品磁性得到明显增强。     

xCoAl_(0.2)Fe_(1.8)O_4+(1-x)BaTiO_3纳米磁电复合材料的磁、介电和磁电特性研究

采用溶胶-凝胶方法制备了xCoAl0.2Fe1.8O4+(1-x)BaTiO3纳米磁电复合材料.XRD图谱分析表明烧结后的样品是复合的钙钛矿(BaTiO3)和尖晶石(CoAl0.2Fe1.8O4)结构,SEM图像显示复合材料颗粒大小均匀.用磁滞回线研究了材料的磁性能,并通过Koops双层异质结构模型解释了复合材料的介电频散现象.测量结果表明:0.20CoAl0.2Fe1.8O4+0.80BaTiO3的样品在偏置磁场为1.35×105A/m时表现出最大的磁电电压系数1.075×10-2 V/A.     

SnO2/Fe3O4磁性光催化微纳米材料的制备与性能研究

以磁性纳米颗粒Fe3O4为核,SnCl4.5H2O、氨水、无水乙醇为原料,采用液相共沉淀法在Fe3O4表面包覆一层SnO2光催化剂。采用X射线衍射仪(XRD)及扫描电镜(SEM)分析了其成分和表面形貌。结果显示:Fe3O4纳米颗粒在实验过程中发生了团聚,尺寸增大;当Fe3O4与SnCl4.5H2O物质的量比为(1∶2)～(1∶4)时,SnO2能被较好地包覆在Fe3O4表面,形成核-壳结构的SnO2/Fe3O4复合光催化材料;600℃热处理能够形成结晶性良好的SnO2晶体,但此时Fe3O4转变为Fe2O3,失去了磁性。     

磁场中磁性纳米流体热导率的研究

进行了提高磁场中含四氧化三铁(Fe3O4)纳米磁性颗粒机油(磁性纳米流体)热导率的研究。在有或无超声波辅助的条件下,采用共沉淀法合成了不同粒度的Fe3O4磁性纳米颗粒,采用一种热常数分析仪对该磁性纳米流体的热导率进行了测定,探讨了纳米磁性颗粒粒度、体积分数以及背景磁场对磁性纳米流体导热性能的影响。实验结果表明,在外磁场中,磁性纳米流体所含Fe3O4纳米颗粒的体积分数越大,磁性颗粒粒度越小,磁性纳米流体的热导率越高;当磁场方向平行于温度梯度时更有利于提高磁性纳米流体的热导率。     

核-壳型罗丹明6G磁性分子印迹固相萃取材料的合成与表征

采用化学共沉淀法制备Fe3O4磁性纳米粒子,以3-氨丙基三乙氧基硅烷(APTES)对其表面进行氨基硅烷化改性,形成Fe3O4@SiO2-NH2纳米粒子。以其作为磁性核,采用表面印迹技术,以罗丹明6G为模板,丙烯酰胺(AM)为功能单体,三羟甲基丙烷三甲基丙烯酸酯(TRIM)为交联剂,在Fe3O4@SiO2-NH2表面形成罗丹明6G分子印迹聚合膜,制备了核-壳型罗丹明6G磁性分子印迹聚合物(Fe3O4@MIPs),对合成条件进行了优化。分别采用红外光谱(FT-IR)、场发射扫描电镜(FESEM)、振动样品磁强分析(VSM)和热重分析(TGA)等仪器分析手段,对Fe3O4@MIPs的结构进行表征。结果表明,所制备的核-壳型磁性分子印迹聚合物具有高吸附容量及显著选择性;在外加磁场作用下Fe3O4@MIPs可快速与样品基质分离,大大提高了实验效率。Fe3O4@MIPs作为一种新型固相萃取材料,可以从样品中选择性分离和富集违规添加的罗丹明6G,可应用于食品的安全检测。     

磁性纳米钌催化剂的制备及对聚苯乙烯催化加氢的催化性能

通过化学共沉淀法制备了Fe3O4,利用硅酸钠水解、缩合制备了具有核壳结构SiO2/Fe3O4复合纳米粒子。利用红外光谱(FT-IR)、扫描电镜(SEM)、X射线衍射(XRD)以及振动样品磁强计(VSM)技术对其进行了表征。将所得的磁性纳米SiO2/Fe3O4用有机硅改性的聚乙烯吡咯烷酮进行表面修饰,利用原位还原RuCl3的方法将金属Ru负载到磁性载体上,制备了磁性纳米催化剂Ru/PVP/SiO2/Fe3O4。探讨了所得催化剂对聚苯乙烯氢化反应的催化性能,考察了反应压力、温度、时间以及溶剂等对催化性能的影响。结果表明,随着反应温度的升高、压力的增加,催化活性提高;当反应温度为393K、氢气压力为8 MPa、反应时间为5 h时,聚苯乙烯氢化度可以达到90%以上。     

热处理温度对纳米CoFe2O4/SiO2复合材料结构和磁性的影响

采用溶胶2凝胶法制备了纳米 Co Fe 2O 4/ SiO 2复合材料。利用 X射线衍射(XRD) 、 透射电镜( TEM) 、 振动样品磁强计(VSM)和 Mssbauer 效应研究了纳米复合材料结构、 晶粒尺寸及磁性。结果表明 , 样品中 Co Fe 2O 4的晶粒尺寸随着热处理温度的提高而增加 , 非晶态 SiO 2的存在有效地抑制了 Co Fe 2O 4晶粒的生长。VSM结果表明 , 样品的比饱和磁化强度和矫顽力随 Co Fe 2O 4晶粒尺寸的增加而变大。Mssbauer 效应结果表明 , 随着热处理温度的提高 , 样品从超顺磁和磁有序的混合状态转变为完全的磁有序状态。     

MnO_2包覆Co纳米颗粒的制备与表征

采用化学还原方法制备出具有纳米尺度的Co颗粒,并在其表面包覆1层MnO2膜,从而制备出具有核/壳结构的Co/MnO2颗粒。应用热处理手段,制备出3种不同类型的核/壳样品,分别通过XRD、TEM、SEM测量手段,对它们进行结构分析。并同时对这种铁磁/反铁磁的核壳结构样品进行磁性研究,发现包覆热处理后的Co颗粒具有可观的交换偏置现象。     

纳米Co_(1-x)Zn_xFe_2O_4/SiO_2复合材料的结构和磁性

为了研究Zn2+含量对CoZn铁氧体结构和磁性的影响,以正硅酸乙酯和硝酸盐为原料,用溶胶-凝胶法制备了纳米Co1-xZnxFe2O4/Si O2(0≤x≤1)复合材料。利用XRD、TEM、VSM和M ssbauer效应分析了样品的结构、形貌和磁性。结果表明,经900℃热处理后,Co1-xZnxFe2O4/Si O2复合材料中Co1-xZnxFe2O4为晶粒分布均匀的尖晶石铁氧体结构。Zn2+替代Co2+后引起Co1-xZnxFe2O4晶格膨胀。随Zn2+含量的增加,样品的矫顽力减小,而比饱和磁化强度先增大后减小,样品从磁有序状态转变为顺磁状态。Zn2+的掺杂对Fe3+核处的s电子密度有较大的影响,对尖晶石结构对称性影响较小。     

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Refrigerators Enter a New Era of Health Preservation Frestech initiates the establishment of China's first standard for household sterilization refrigerators

On November 30, 2007, the China Association for Standardization (CAS) held a press conference at Beijing Diaoyutai State Guest House. Leaders from the China Household Electric Appliance Research Institute, the China Household Electric Appliance Association, and the China Consumers' Association attended and made speeches.……     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

A study of centrifugal cast high boron high speed steel

In the present study a high‐boron high speed steel (HSS) roll material was designed. Many expensive alloy elements have been substituted by cheap boron alloy, and high‐boron high speed steel roll has been manufactured by centrifugal casting method. The microstructures, mechanical properties and wear resistance of centrifugal casting high‐boron high speed steel roll have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and X‐ray diffraction (XRD) analysis, hardness test, impact test and wear test. The results indicated that the solidification microstructures of high‐boron high speed steel roll consisted of M₂(B,C), (W,Mo)₂(B,C), M₃(B,C), M₂₃(B,C)₆ type borocarbides and martensite, a small amount of retained austenite. Borocarbides were continuously distributed over the grain boundary. After quenching from 1050 °C, local broken network appeared in partial borocarbides, and fine secondary borocarbide precipitated from the matrix. After tempering from 525 °C, the amount of precipitated borocarbide increased significantly. After heat treatment, the hardness of high‐boron high speed steel roll excelled 60 HRC, and its impact toughness excelled 8.0 J/cm². The single groove steel rolling amount of high‐boron high speed steel rolls increases by 500% than that of bainite cast iron roll, when the rolls are used in K₁ mill housing of bar mill.     

Thixotropy of Systems with Shear Thinning and Plastic Flow Behavior

The definition of the thixotropy is a decrease in viscosity with time in shear and a subsequent recovery of viscosity after the shear deformation is removed.We ...     

Brainstorming for ISO Strategy 2016-2020

正Responding to ISO’s appeal for survey for the to-be-developed ISO Strategy Plan for 2016-2020,SAC hosted a special workshop over the needs and comments of various fi elds on June 8 in Beijing.The workshop was attended by ISO President-elect and Ansteel General Manager Zhang Xiaogang,SAC Vice-Administrator Yu Xinli,and 30 experts from     

CNAS Passes APLAC's PTP Review

正The review group of Asia Pacific Laboratory Accreditation Cooperation(APLAC)carried out a 4-day peer review of the proficiency testing provider(PTP)for China National Accreditation Service for Conformity Assessment(CNAS)from July 28 to 31,2014.CNAS passed the PTP review with excellent performance.Two senior peer reviewers of APLAC made a comprehensive,rigorous and detailed review of CNAS’s PTP accreditation activities,and made the on-spot inspection of the review groups in Shanghai and Shenzhen respectively.