硫酸溶液中水灰比对混凝土腐蚀速率影响研究

以硫酸溶液作为酸性腐蚀介质,开展水灰比分别为0.4、0.5、0.6的试样在酸性溶液腐蚀条件下,试样外观、抗压强度、质量、强度退化深度等随腐蚀时间变化的耐酸腐蚀试验。试验结果表明:腐蚀初期,硫酸溶液对水灰比较小试样外观影响较大,后期均产生明显裂纹,表面剥落;随腐蚀时间的增加,试样抗压强度初期缓慢增加,随后逐渐减小,水灰比较大试样在腐蚀初期抗压强度增加明显;试样质量呈先增大,后逐渐减小的变化趋势,水灰比较大试样在整个腐蚀期质量变化率均为最大;随腐蚀时间的增加,试样强度退化深度逐渐增加,退化深度剧变时间段均约为120 d前后。     

硅灰混凝土的长期性能

1990年秋季在加拿大曾修建了一条试验性的人行道。人行道有11个区段，水泥的含量各不相同(195-405W)，而硅灰的掺入量则为水泥含量的10％到20％不等。某一区段的混凝土只有140kg／m^3水泥，而硅灰的掺入量却多达56kg／m^3。虽然经过一个冬季之后，其抗压强度高达40MPa，但使用五年后由于严重损坏而必须更新。     

粉煤灰对硅灰混凝土性的影响

由于硅灰对新拌混凝土的副作用，例如降低和易性、流动度、可浇注性和饰面性，提高了粘滞度和干硬性，因而在混凝土中掺入高含量硅灰的潜在优点就受到了限制。国外有些施工规程把硅灰的掺入量限制为胶结料重量的10％。     

硅灰对高强混凝土强度影响的试验研究

在高强混凝土中掺入适量的硅灰,对提高混凝土的劈裂抗拉强度有非常明显的效果,也可在一定程度上增强混凝土的抗压强度和抗折强度.掺量低于或高于适量范围,对提高混凝土的强度作用很小.在实际工程混凝土中合理掺用硅灰,不仅可以提高混凝土的强度,而且变废为宝,改善环境,技术、经济和社会效益显著.     

硅灰对混凝土性能的影响

在混凝土中掺入一定量的硅灰可以提高混凝土的工作性能、强度和耐久性能。当混凝土中硅灰的掺量5%时,必须在混凝土中加入一定量的高效减水剂,以保证混凝土的工作性能。     

掺稻壳灰/硅灰混凝土的性能研究

研究了稻壳灰、硅灰、稻壳灰+粉煤灰、硅灰+粉煤灰对混凝土抗压强度、抗折强度、抗硫酸侵蚀能力和抗碳化能力的影响.结果表明:掺加5％～10％稻壳灰或硅灰有助于提升混凝土的抗压强度和抗折强度,且稻壳灰、硅灰掺量越高抗压强度越高,掺硅灰混凝土相对于掺稻壳灰混凝土的抗压和抗折强度更高,掺稻壳灰+粉煤灰、硅灰+粉煤灰试件的抗压和抗...     

苯乙烯-丁二烯乳液与硅灰共掺混凝土的耐久性研究

采用雾室养护和自然养护两种方式,研究了苯乙烯-丁二烯乳液(SB-latex)与硅灰(silicon fume)共掺时,其掺量对混凝土抗水渗透、抗氯离子渗透、抗碳化和抗硫酸腐蚀性能的影响。试验结果表明苯乙烯-丁二烯乳液和硅灰的共掺可显著地改善混凝土的渗透性,不过SB-latex和硅灰掺量较大时,会分别对混凝土的抗硫酸腐蚀和抗碳化性能产生一定的不利影响。     

粉煤灰和硅粉对碾压混凝土抗裂性能的影响

在对某工程碾压混凝土配合比进行优化的基础上，通过试验测定掺入粉煤灰、硅粉后碾压混凝土的抗拉强度、脆性系数，弹强比和极限拉伸值等性能，论述了复掺粉煤灰和硅粉可以提高碾压混凝土的抗裂性能，同时对其机理进行了分析。     

Influence of dry and wet curing conditions on compressive strength of silica fume concrete

This paper reports a part of an ongoing laboratory investigation in which the compressive strength of silica fume concrete is studied under dry and wet curing conditions. In the study, a total of 48 concretes, including control Portland cement concrete and silica fume concrete, were produced with four different water–cement ratios (0.3, 0.4, 0.5, 0.6), three different cement dosages (350, 400, 450 kg/m³) and three partial silica fume replacement ratios (10%, 15%, 20%). A hyperplastisizer was used in concrete at various quantities to provide and keep a constant workability. Three cubic samples produced from fresh concrete were demoulded after a day; then, they were cured at 20±2 °C with 65% relative humidity (RH), and three other cubic samples were cured at 20±2 °C with 100% RH until the samples were used for compressive strength measurement at 28 days. The comparison was made on the basis of compressive strength between silica fume concrete and control Portland cement concrete. Silica fume concretes were also compared among themselves. The comparisons showed that compressive strength of silica fume concrete cured at 65% RH was influenced more than that of Portland cement concrete. It was found that the compressive strength of silica fume concrete cured at 65% RH was, at average, 13% lower than that of silica fume concrete cured at 100% RH. The increase in the water–cementitious material ratios makes the concrete more sensitive to dry curing conditions. The influence of dry curing conditions on silica fume concrete was marked as the replacement ratio of silica fume increased.     

硅灰在超高强混凝土中的应用

研究了硅灰及其掺量对超高强混凝土物理性能、力学性能、耐久性方面的影响。结果表明:硅灰是一种高效的活性掺合料,在混凝土中掺入一定量的硅灰,能够显著提高混凝土的强度、抗渗性,抗冻性和耐久性,是配制超高强混凝土不可缺少的组分。     

高强硅灰水泥研究

本文利用正交试验比较详细地研究了高强硅灰水泥的制备工艺,优化出一组有实际意义的制备工艺参数.同时,借助化学分析、XRD、SEM等探讨了硅灰水泥的高强机理.     

掺硅粉水泥砂浆耐污水腐蚀性能的研究

研究了硅粉对提高污水工程用混凝土中砂浆耐污水腐蚀性能的影响.以污水中常见的硫酸盐、卤盐、弱酸和微生物等作为腐蚀介质,测试了砂浆浸泡于各种腐蚀液中的质量、强度损失.结果表明,硅粉对提高污水管用混凝土中砂浆耐污水腐蚀性能具有一定效果.     

硅灰调控混凝土力学性能的关键界面参数研究

研究了硅灰分别掺加到混凝土基相和界面中对混凝土界面特征及力学性能的影响,并通过界面调控对混凝土力学性能进行优化,提出了调控混凝土力学性能的关键界面参数——界面区域硅灰质量浓度G.结果表明:界面中的硅灰在提高混凝土强度的同时,降低了混凝土脆性,在掺量较低时对混凝土强度的促进作用远大于基相中的硅灰;参数G能够统一基相和界面中的硅灰作用效果,建立硅灰-界面-强度的关联关系,具有重要的应用价值.     

硅灰对轻骨料混凝土抗海水冻融性能的影响

对100mm×100mm×100mm硅灰轻骨料混凝土立方体试块分别进行了25,50,75次海水中的冻融循环试验,通过对试件的质量损失计算、表面剥落观察和超声波探测,分析了硅灰提高轻骨料混凝土抗冻性能的效果.对比研究了试验过程中试件两端减摩与否对轻骨料混凝土力学性能的影响.分别对冻融0次(常态)和不同冻融循环次数后的硅灰轻骨料混凝土试块进行了单轴抗压强度和变形性能试验,得出了极限抗压强度、峰值应力点的应变值、弹性模量等随冻融循环次数变化的规律,并分析了应力-应变全曲线随冻融循环次数变化的规律,结果表明,掺加硅灰能显著提高轻骨料混凝土的抗冻性.     

混凝土成熟度理论研究与应用现状综述

回顾了混凝土成熟度理论的发展历程;梳理了国内外混凝土成熟度与混凝土强度之间相关的数学模型,并探讨了各模型的适用范围;最后概述了当前混凝土成熟度理论的应用现状。