小波变换在爆炸焊接复合板超声检测中的应用

在传统超声波检测的基础上,利用小波变换将超声检测回波信号分解成不同频带上的信号成分,通过分析这些不同频带上的焊接界面回波和底面回波,结合爆炸焊接复合板不同结合界面对超声波传播的影响,检测出爆炸复合板界面的结合形态.钢钛爆炸焊接复合板的实验室检测结果表明,该方法具有检测方便、检测周期短和不破坏材料整体性的优点.     

T2纯铜/2024铝合金爆炸焊接接头界面结构及性能

为研究铜铝异种金属爆炸焊接头界面形成机理,采用爆炸焊对T2纯铜和2024铝合金进行了焊接.通过光学显微镜、扫描电镜、X射线衍射、万能材料试验机和纳米压痕仪,对T2/2024复合板结合界面的显微组织、成分分布和力学性能进行了测试分析.结果表明:T2/2024合金爆炸复合板结合界面呈波状结合,结合界面主要由平直界面、波状界面和局部熔化层界面构成;靠近结合界面处,基体金属发生塑性变形,晶粒细化;反应层主要成分为AlCu和Al_2Cu的混合物.复合板拉剪试验表明,T2/2024合金爆炸复合板平均结合强度为67 MPa,纳米压痕测试反应层平均硬度可达8 GPa.     

相控阵检测在爆炸焊接金属复合板中的应用探究

相控阵检测技术是无损检测超声领域的新技术,将该技术应用到爆炸焊接金属复合板结合界面波纹特征的检测是一种新的尝试。介绍了相控阵检测技术的基本原理和技术特点,分析了爆炸焊接复合板界面超声波传播特点和相控阵C扫成像基本原理,并在多种材质的爆炸焊接金属复合板上进行试验性应用研究,结果发现相控阵扫查方向影响爆炸波纹的成像效果,通过相控阵检测技术,能够快速获取爆炸焊接复合板结合界面的爆炸波纹特征图像,并能够对波纹特征进行清晰识别与准确评判,有效辅助爆炸复合工艺的提升改进,提高爆炸焊接复合板产品质量,同时也实现了以无损检测方法评价爆炸焊接复合质量的新突破。     

1Cr18Ni9Ti-20G爆炸焊接+轧制工艺研究

为了研究在不同爆炸焊接工艺条件下获得的复合板的轧制效果,本文对大波、小波、微波状3种界面的1Cr18Ni9Ti／20G复合板进行轧制实验研究．实验表明：只有用下限获得的微小波状界面的爆炸焊接复合板,才能实现成功轧制,而大波状复合板界面存在一定的缝隙、空洞等微观缺陷,在轧制时由于分层会使轧制失效．爆炸焊接 轧制工艺获得的复合板结合界面的组织、强度和性能的测试结果表明：轧制复合板结合界面的剪切和分离强度虽比爆炸态略低,但延伸率、冲击韧性都大大增强,轧制复合板的耐蚀性能也未降低．     

铝合金-钢爆炸焊接装药量与界面性能的关系(英文)

通过设计不同的爆炸焊接工艺参数爆炸复合了铝合金-钢爆炸复合板,并对复合板的界面性能进行了显微分析和力学性能测试,探讨了爆炸焊接装药量对复合板界面性能的影响。结果表明:在铝合金-钢复合板的的结合界面产生了一层金属间化合物并且在化合物中产生了许多微裂纹。随着装药量的增加,界面化合物的厚度略有增加,其上微裂纹的的数量也有所增加。复合界面的剪切强度随着装药量的增加而有所降低。界面化合物对复合板强度产生不利影响,铝合金-钢爆炸焊接时应尽量采用小药量。     

消除爆炸焊接中心不结合区的实验研究

从理论上分析了消除爆炸焊接中心起爆中心不结合区的可能性 ,并分别采用中心起爆和边缘起爆对SA2 6 6 - 30 4爆炸焊接复合板的结合界面及地基下应力进行了对比测试 .实验结果表明只要合理选择装药参数 ,采用中心起爆可获得最佳的焊接界面 .     

爆炸焊接布药工艺与微观结合界面形貌分析

爆炸焊接是复合材料加工的1项高新技术,不同的爆炸焊接布药工艺对复合板的质量有很大影响。通过对传统的均匀布药工艺和新不等厚度布药工艺进行爆炸焊接试验和理论分析,发现传统的均匀布药工艺所得到的焊接大波状结合界面明显、复合板质量不好,而新不等厚度布药新工艺可以使炸药产生的爆轰压力逐渐减少,并和材料本身振动产生的惯性力协调作用,得到基本一致的微小波状结合界面,同时降低震动和噪声。结论表明新工艺对工业生产和爆炸焊接试验有很好的指导作用。     

不锈钢—碳钢单、双面复合板的爆炸焊接及性能研究

研究了不锈钢－碳钢单面、双面复合板爆炸焊接质量,结合界面的微观结构,剪切强度及耐蚀性能,结果表明,单、双面不锈钢－低碳爆炸焊接复合板的结合界面均为波状结构,结合面两侧存在一定组织变形,近界面处为角结晶组织,稍远处为拉伸变形后的维状组织,结合界面碳钢－侧过渡区存在增碳区,不锈钢一侧有一个脱碳层,双面复合界面的结合过渡区的单面为１．５倍宽,脱碳区也接近单面的１．５倍,采用切割爆炸焊接法有利于改善不锈钢－低碳钢复合板的边缘焊合,在同一基板上进行了双面不锈钢复合时,第一面复合界面的剪切强度比第二面复合界面的差,还是双面复合板,其界面结面强度均由起爆端的末端逐渐降低,结合界面的脱碳层对复合的耐蚀性能无明显影响。     

Pb1-Q245R爆炸焊接复合板结合界面研究

采用电阻测量装置、金相显微镜、透射电镜对爆炸焊接铅-钢复合板结合界面进行了研究.结果表明,铅-钢复合板结合界面导电性能优越;界面结合形态呈准正弦波形,无漩涡区;结合界面两侧的铅元素和铁元素相互扩散,钢侧铅含量降低较快,铅侧铁含量降低较慢,扩散的深度在微米数量级;结合界面组织由铁微晶与铅微晶混合组织组成.     

爆炸焊接复合板在石化装备应用中的关键技术研究

近年来随着爆炸焊接复合板在石化装备等行业中的大量运用,其复合技术及其后续制造工艺的进步愈显重要.根据爆炸焊接复合板在石化装备等工程领域中的应用状况,结合爆炸焊接复合板的可焊性窗口及特点,阐述了不同材质的爆炸焊接金属复合板在生产制造中的热处理参数及使用中焊接、无损检测等关键技术.     

高锰钢-碳钢复合板的制造和应用

介绍了一种高锰钢与结构钢的爆炸焊接工艺，包括表面处理方法、表面处理参数及条件、所采用的炸药和复合板的性能、爆炸焊用材料的准备。进行了成品复板（复合板）的质量检验，给出了该技术的应用实例。     

钛/钢多层爆炸焊接界面的实验研究

为探究膨化硝铵炸药作用下,厚度均为2 mm的钛(Ti)、钢板的最优爆炸焊接参数以及验证一种新的爆炸焊接试验方案,实验采取阶梯型多层基板的爆炸焊接试验方案,以控制药量和间距为变量,并将Ti板作为复板,同时对多层阶梯型钢基板进行爆炸焊接试验;利用金相显微镜对焊接复合板进行观察,并分析多层基板同时焊接的方案可行性以及不同实验参数对界面波形的影响。试验结果和分析表明:通过观察Ti/钢复合板界面波形呈正弦微波状且无明显过渡层,验证了新方案的可行性,同时突出了阶梯型多层基板的同时爆炸焊接方案,能够在单次试验下对比分析不同基复板间距情况下的焊接效果的能力;并经分析得出在单位面积装药为1.048 g/cm~2及装药间距范围为(9~11)mm时,能得到质量较佳的Ti/钢爆炸复合板。     

铜-A3钢爆炸焊接SE型专用炸药实验研究

炸药爆速不稳定和爆速过高是造成复合板结合质量差的主要原因.以2#岩石硝铵炸药为主体,通过加入一定比例的食盐、膨胀珍珠岩配制成了爆速可调的SE型爆炸焊接专用炸药,其加工方便,成本较低,最低爆速为2048m/s.铜-A3 钢爆炸焊接实验表明,该炸药具有爆速低、爆轰稳定、能量适中特点,较好地解决了猛炸药焊接时所出现的问题.研究和配置爆速更低、能够适应更多金属板材以及管状物体焊接的专用炸药是需要进一步研究的课题.     

铝-钢爆炸焊接过渡接头的制造和应用

介绍了铝 钢爆炸焊接的特点 ,铝 钢过渡接头的制造方法、性能 ,以及在现代铝电解行业中的应用。     

Investigation of explosive welding parameters and their effects on microhardness and shear strength

The aim of this study was to investigate the strength of explosive welded metals with the same chemical compositions. Different welding interfaces (straight, wavy and continuous solidified-melted) were used with changing explosive welding parameters [stand-off distance (s), explosive loading (R) and anvils]. Joined metals were investigated under heat-treated and untreated conditions. Results on the microstructure, microhardness, tensile shear strength and bending tests are reported. According to the experimental results, the effect of the anvil on the explosive welding process was only the joining or not-joining performance. It was shown that the bonding interface changed from a straight to a wavy structure when the explosive loading and stand-off distance were increased. For wavy interfaces, when the explosive loading was increased the wavy length and amplitude increased. Results of tensile shear and bending tests showed that heat-treated specimens have more strength than untreated samples. According to tensile shear test results, straight and wavy interfaces had similar strength. In addition, in bending tests of untreated specimens it was shown that the bending zone had some cracks.     

双相不锈钢2205-Q345R复合板焊接性能试验研究

采用爆炸焊接方法制作双相不锈钢2205-Q345R复合板,需将复层2205进行拼焊,以满足不同尺寸要求,未复合区需进行补焊.根据双相不锈钢2205-Q345R复合板的焊接性,对双相不锈钢2205拼焊和2205-Q345R复合板未复合区补焊工艺进行了试验研究,结果表明:焊接接头各项性能均能满足相关指标要求.     

SUS304不锈钢/Q345R碳钢爆炸焊接工艺参数研究

针对实际生产中在爆炸焊接窗口内取值时因为所取参数不同而导致生产的复合板结合强度差异较大这一现状,通过对SUS304不锈钢／Q345R碳钢爆炸焊接窗口内不同工艺条件得到的复合板进行剪切强度测试及金相分析,得到界面结合强度与界面波形的关系以及两者随工艺参数的变化规律,找到窗口内最佳的工艺参数,以提高爆炸焊接复合板质量以及生产效益。研究表明：界面波形的波长和振幅随着装药量的增加而增大,随基复板间距的增加先增大后减小。爆炸焊接窗口内最佳工艺参数取值范围与复板厚度有关。复板为薄板（3mm）时,取得最佳结合强度时界面波形波长为1250μm左右,振幅为200μm左右,对应的最佳装药质量比为1．02,基复板间距为8mm,取值比理论最佳值偏高;复板为厚板（6mm）时,取得最佳结合强度时界面波形波长为900岫,左右,振幅为100μm左右,对应的最佳装药质量比为0．45,基复板间距为14mm,取值靠近下限。当界面波长与振幅相同时,复板为薄板的结合强度要高于厚板。     

The influence of some factors on steel/steel bonding quality on there characteristics of explosive welding joints

Explosive welding is a solid state process in which controlled explosive detonations force two or more metals together at high pressures. The resultant arrangement is joined with a high quality metallurgical bond. The aim of this study was to investigate of strength of explosive welding metals which had same chemical compositions. In this study, it was taken different welding interfaces (straight, wavy and continuous solidified-melted) with changing explosive welding parameters (stand-off distance (s), explosive loading (R) and anvils). Joined metals were investigated in heat treatment and non heat treatment conditions. Microstructures, microhardness, tensile shear strength and bending test results were reported. Effect of anvil on explosive welding process was evaluated in joining/no joining performance. It was shown that bonding interface changed from straight to wavy structure when explosive loading and stand-off distance were increased. On wavy interface, when explosive loading was increased wavy length and amplitude increased. Results of tensile shear and bending tests showed that heat treated specimens have more strength than which of unheat-treated ones. According to tensile shear test results, straight and wavy interfaces had similar strength. Also, bending zone has shown some cracks after the bending test of unheated specimens.     

爆炸焊接不锈钢─钢复合板

通过改善爆炸焊接中、大面积、大厚度的不锈钢─钢复合板的工艺参数，对如何获得高质量的不锈钢─钢复合板作了深入探讨。各项金相、机械性能检验表明，方案具有较高的实用价值。     

5083铝合金与CCSB钢的爆炸焊接研究

对直接爆炸焊接困难的5083铝合金与CCSB钢组合,采用加入中间层板CCSB一次爆炸焊接的可行性进行了试验探讨,确定了界面处的微观结构和爆炸焊接的参数范围。试验表明,爆炸时较大的能量作用在5083-CCSB钢界面区产生气化和熔化反应层是导致直接爆炸焊接困难的原因。通过在二者之间加入CCSB薄板的方法,能有效地减少作用在5083-CCSB界面上的能量,从而实现良好的结合。