环氧丙烯酸树脂改性阴极聚氨酯电泳漆的合成及性能的研究

以环氧丙烯酸树脂为改性扩链剂,合成了侧基含有碳碳不饱和双键的阴极聚氮酯电泳漆。探究了环氧丙烯酸树脂（PPG—EA）用量、引发剂过氧化苯甲酰（BPO）用量、烘烤温度对漆膜性能的影响。结果表明,PPG—EA占聚氨酯阴极电泳漆的质量分数为3．08％、BPO的用量为0．6％、漆膜烘烤温度为150℃时,漆膜表面无缺陷,耐化学腐蚀性较好。     

丙烯酸树脂改性环氧树脂防腐涂料防腐性能研究

用溶液聚合法合成了丙烯酸树脂并对其结构进行了表征。将合成的丙烯酸树脂与环氧树脂以质量比1∶5混合,并与防锈颜料、填料、助剂、溶剂复配成环氧防腐涂料,测试了漆膜的性能;用电化学阻抗技术(EIS)和Tafel极化曲线技术评价了其防腐性能。实验结果表明:甲基丙烯酸缩水甘油酯(GMA)单体完全聚合,合成的丙烯酸树脂中带有环氧基;与纯环氧树脂防腐涂料相比,改性后的环氧防腐涂料层间附着力更高、柔韧性有所改善;带环氧基团丙烯酸树脂改性后的环氧防腐涂料防腐性能优异。     

有机硅改性环氧丙烯酸阴极电泳漆的制备

将正硅酸乙酯(TEOS)与甲基丙烯酸羟丙酯(HPMA)经酸催化合成一种表面带有双键的二氧化硅活性粒子,然后与甲基丙烯酰胺、环氧树脂等共聚制备有机硅改性环氧丙烯酸阴极电泳漆。采用FT-IR对有机硅改性环氧丙烯酸结构进行表征,重点研究了有机硅含量对电泳漆玻璃化转变温度、吸水率、耐热性、耐腐蚀性能的影响。结果表明:随有机硅含量增大,吸水性降低,耐腐蚀性和玻璃化转变温度提高。当有机硅的添加量(质量分数)为1.8%时,电泳漆漆膜的综合性能较好。     

高附着力单组分环氧改性丙烯酸涂料的制备

以常用丙烯酸单体为主要原料,加入顺丁烯二酸酐,合成出侧链带有酸酐基团的丙烯酸树脂,再与环氧树脂反应,制得环氧改性丙烯酸树脂。由其制备的单组分环氧改性丙烯酸涂料对玻璃等难附着基材具有优异的附着力。考察了环氧树脂的不同用量对树脂体系相容性及漆膜物理性能的影响,结果表明:环氧树脂用量在15%左右时,改性树脂保留了丙烯酸树脂涂料的优异性能,而且附着力、硬度、光泽得到了提高,丰满度佳。     

丙烯酸型F-44光敏酚醛环氧树脂的合成

以溴化四丁基铵作催化剂，用丙烯酸改性F-44环氧树脂，合成了一种既含有丙烯酸基又含有环氧基的光敏酚醛环氧树脂。研究了丙烯酸基的引入量对树脂光学性能、力学性能等的影响。结果表明，当改性树脂中的丙烯酸基与环氧基之比等于1：1时，所制得的树脂具有优良的光化学活性，用改性树脂制成的漆膜具有优良的力学性能、耐溶剂性能和耐酸碱性能。     

丙烯酸阴极电泳漆的研制

介绍了采用甲基丙烯酸缩水甘油酯与常用的丙烯酸单体通过溶液聚合,制备丙烯酸阴极电泳漆的简单可行方法。研制的电泳漆克服了环氧-聚氨酯阴极电泳漆的缺点,具有可着色性、高装饰性、高耐候性等特点。讨论了影响电泳漆性能的诸种因素。列举了电泳原漆的技术指标、施工参数和漆膜性能指标。     

有机硅改性丙烯酸阳极电泳漆的合成

以乙醇为溶剂,将正硅酸乙酯(TEOS)与乙烯基三乙氧基硅烷(VTEOS)经酸催化合成了一种表面带有乙烯基的活性二氧化硅粒子,然后将其与丙烯酸树脂聚合得到透明的有机硅改性阳极电泳漆。研究了有机硅的添加方式对反应过程,有机硅含量对改性丙烯酸树脂的玻璃化转变温度、黏度以及电泳漆性能的影响,采用傅里叶变换红外光谱、差示扫描量热和热重分析等对改性丙烯酸树脂进行了表征。结果表明,有机硅的最佳添加方式是与部分单体预混后逐滴滴加。随着有机硅含量的增大,改性丙烯酸树脂的黏度、玻璃化转变温度和耐热性提高。当有机硅添加量为0.8%~1.2%时,电泳漆膜的综合性能较好。     

低黏度柔性UV-热双重固化涂料

用环氧树脂、丙烯酸、自制的甲苯二异氰酸酯预聚物以及聚乙二醇合成了2种改性环氧丙烯酸酯TDI-1和PEG-1。物理混合2种改性EA得到光-热双重固化的改性环氧丙烯酸树脂。通过红外光谱表征了改性前后官能团的变化情况,分析了这2种改性环氧丙烯酸树脂(TDI-1和PEG-1)通过物理混合的UV-热双重固化涂料的性能变化情况。测试结果表明,TDI-1和PEG-12种改性环氧丙烯酸树脂混合使用时比单独使用时涂膜的性能更好。所研制的低黏度柔性UV-热双重固化涂料适合于不耐热、不规则的纸张、木器、塑料、汽车零部件等的双重固化涂装。     

浅色电泳漆的试验研究

本报告简述了树脂的反应机理,介绍了配方、制造工艺及条件试验的情况。水溶性浅色电泳漆是苯乙烯—丙烯酸改性氨基醇酸树脂与颜料调合而成。以丁醇作为助溶剂,三乙醇胺为中和剂。在140℃下烘烤1小时干燥成膜。漆膜的性能与溶剂型氨基醇酸漆相当。树脂中采用氢化蓖麻油酸后,能得到浅色的漆膜。树脂中以三乙醇胺为中和剂,以及加入少量顺丁烯二酸酐改性油能提高电泳漆液的稳定性。     

多元酸改性环氧丙烯酸UV树脂的合成

采用部分多元酸代替丙烯酸对环氧丙烯酸UV树脂进行改性,在一定程度上改善了原树脂的脆性,改性后的树脂具有固化速度快、光泽高、黏度高的特点。讨论了合成时所需的催化剂、多元酸用量等因素对树脂性能的影响。     

金属罐用热固性丙烯酸树脂的研制

用环氧树脂和丙烯酰胺反应,形成环氧酰胺树脂后,再与丙烯酸及其衍生物、苯乙烯等单体用自由基溶液聚合方式,将环氧接枝到丙烯酸树脂上。通过研究确定了树脂合成的最佳工艺,讨论了各种因素对涂料性能的影响。     

底面合一阴极电泳漆的研究

采用丙烯酸树脂与环氧树脂冷拼工艺制备的阴极电泳漆解决了环氧类阴极电泳漆作为底面合一涂层时老化性能差的问题，针对乳液在施工应用中的稳定性，探讨了亲水性溶剂、酸值对乳液及电泳漆漆膜的影响，通过液相色谱仪分析槽液中树脂比例变化，并用人工加速老化实验验证了涂膜的老化水平，结果表明，底面合一型电泳漆在老化、盐雾等方面达到了和谐统一，可满足有关汽车底盘及零部件的综合要求。     

有机氟改性环氧丙烯酸阴极电泳涂料的研究

选择合适的丙烯酸类单体、有机氟单体与环氧树脂接枝共聚合成了用于阴极电泳涂料的阳离子型含氟环氧丙烯酸树脂.探讨了氟单体的用量、接枝反应温度、胺化温度、胺化时间等对树脂反应的影响,并对所得阴极电泳涂料的性能进行了测试.结果表明:在合适的电泳工艺参数下,所得漆膜与不含氟的环氧丙烯酸漆膜相比,其耐盐水性、耐老化性、冲击强度都有所提高.     

室温固化型水性环氧防腐涂料的研制

以BPO为引发剂,用α-甲基丙烯酸与E-44型环氧树脂接枝共聚反应合成了环氧-丙烯酸多元接枝共聚物,并用有机酸中和剂调节pH为7～8,制得水性环氧-丙烯酸乳液,进一步制得水性环氧涂料。涂膜固化中用新型低分子水性聚酰胺固化剂加适量促进剂使固化反应在室温下进行。通过测定该涂料的各项性能,结果表明,该涂料附着力、耐冲击性、耐腐蚀性等各项性能良好且施工简单又环保,适用于不能加热的金属底材的防护。     

Coemulsion and electrodeposition properties of mixtures of cationic epoxy resin and cationic acrylic resin containing blocked-isocyanate groups

2-Ethylhexanol–half-blocked-toluene diisocyanate (2EH-half-blocked TDI) was first reacted with 2-hydroxyethyl methacrylate (HEMA) to prepare HEMA–TDI–2EH monomer containing blocked-isocyanate groups. This monomer was reacted with butyl acrylate, styrene, and N,N-dimethylaminoethyl methacrylate to prepare an acrylic copolymer III ′ containing blocked-isocyanate groups and tertiary amine groups. The acrylic copolymer III ′ can be mixed with an epoxy–amine adduct IV ′, acetic acid, and deionized (D.I.) water to from an electrodepositable coemulsion. The electrophoretic codeposition of the coemulsion and physical and chemical properties of the codeposited film were investigated. The resin composition of film deposited from coemulsion was determined by Fourier transform infrared (FTIR) quantitative analysis to study the coemulsion and electrophoretic codeposition behavior. The applicability of this two-component coemulsion in primer–surface (pricer) electrodepositable paint was also discussed. The results indicate that the deposition yield of cationic acrylic copolymer III is greater than that of cationic epoxy resin IV , i.e., the deposition velocity of III is faster than that of IV . However, resins III and IV can be well codispersed in D.I. water to form stable coemulsion; thus, the resin composition of deposited is almost equal to the resin composition. Moreover, the throwing power of coemulsion is almost equal to that of IV emulsion but greater than that of III emulsion. The optimum resin compositions of coemulsions for obtaining better gel content of deposited films are between 0.65 and 0.8 ( III/III + IV , by weight). © 1994 John Wiley & Sons, Inc.     

低温固化环氧阴极电泳涂料的大分子交联剂的制备

首先以聚乙二醇200(PEG-200)、异佛尔酮二异氰酸酯(IPDI)、二羟甲基丙酸(DMPA)为原料合成了末端为异氰酸根(—NCO)的预聚体,再以N-甲基二乙醇胺(MDEA)为封端剂对—NCO进行全封端反应。通过添加适量的亲水性DMPA,提高了封端大分子的自乳化性能,制备出全封闭型异氰酸酯大分子(P-M-I)乳液,以其作为环氧阴极电泳漆低温固化的交联剂。应用FT-IR、DSC、TG、TEM、粒径分析等检测手段对全封闭型大分子及其乳液进行了结构与性能表征。将其与胺化环氧树脂乳液进行共混,制备了低温固化环氧阴极电泳涂料。通过电泳涂装的金属样片在124～130℃烘烤30 min可完全固化成膜。实验结果表明:该大分子交联剂显著降低了电泳涂料的固化温度,涂膜外观平整光亮、附着力好、铅笔硬度达2H,综合性能良好。     

Effects of acid treatment on adhesive performance of encapsulated aluminium pigments on plastic sheets

In this study, aluminium pigments were encapsulated with hydroxyl group‐containing acrylic resin after surface acid treatment to enhance their adhesive performance in the paint film. The removal efficiency of fatty acid on surface of aluminium particles was studied by means of thermogravimetric analysis and the effect of acid treatment on adhesive performance of aluminium pigments encapsulated with hydroxyl group‐containing acrylic resin in the paint film was investigated by pulling‐off tests. It was found that fatty acid on surface of aluminium particles was removed efficiently by acid ethanol solution, and then hydroxyl group‐containing acrylic resin can be encapsulated onto the surface of the aluminium particles by chemisorptions. The encapsulated aluminium pigments have excellent adhesive performance in the paint film. © 2011 Canadian Society for Chemical Engineering     

太阳能反射镜镜背保护涂料的应用研究

以灰色环氧磷酸锌防腐涂料为底漆、丙烯酸改性聚硅氧烷涂料或丙烯酸聚氨酯涂料为面漆,作为太阳能反射镜镜背保护涂料,对保护涂料的施工工艺以及2种面漆的防护性能等进行了研究,研究表明:丙烯酸改性聚硅氧烷涂料配套体系的附着力、反射率、中性盐雾、CASS喷雾试验、人工加速老化、湿热试验及抗气候循环试验等各项性能指标达到了相应的技术标准,较传统的丙烯酸聚氨酯面漆在恶劣环境中更适合太阳能反射镜的保护。     

环氧丙烯酸树脂合成条件的优化

用双酚A环氧树脂与丙烯酸反应合成环氧丙烯酸树脂。利用正交试验研究了反应温度、催化剂种类和用量、阻聚剂用量对合成反应的影响,得到了合成反应的优化条件。用FTIR对环氧树脂和合成的环氧丙烯酸树脂的结构进行了表征。