The mechanical properties of directionally solidified aluminum-based eutectic castings

Abstract

The mechanical properties for directionally solidified Al-Al₃Ni, Al-Si, and Al-Al₂Cu eutectic castings have been determined and it is shown that the properties of castings (solidified at approximately 80 cm/hour) compare favourably to those obtained for slowly solidified eutectics (solidified at approximately 2 cm/hour). The strengths of Al-Al₂Cu and Al-Si eutectic castings are higher than those obtained for slowly solidified alloys while the strengths for the Al-Al ₃Ni eutectic castings are somewhat lower than for the slowly solidified alloys. The Al-Al₃Ni and Al-Al₂Cu cast eutectics essentially maintain their yield strength up to 300°C whereas the yield strength of the Al-Si eutectic decreases continuously with increasing temperature. It is concluded that the high strengths reported result from a combination of the fine micro-structure obtained from the relatively rapid solidification rate and by strengthening of the intermetallic phase.

Réesumé

Les auteurs ont déterminé les propriétés mécaniques d'alliages eutectiques Al-Al₃Ni, Al-Si et Al-Al₂;Cu solidifiésdirec-tionnellement. Ils montrent que les propriétés des coulées (solidi-fiées à environ 80 cm/h) se comparent favorablement à celles d'eutectiques solidifiés lentement (à environ 2 cm/h). Les résistances mécaniques des coulées eutectiques de Al-Al ₂Cu et Al-Si sont plus élevées que celles obtenues pour des alliages solidifiés lentement tandis que les résistances mécaniques des coulées eutectiques Al-Al₃Ni sont légèrement plus basses que celles des alliages solidifiés lentement. Les limites d'élasticité des alliages eutectiques coulés d'Al-Al₃Ni et Al-Al₂;Cu demeurent élevées jusqu 'à des tempéraptures de 300°C, tandis que lalimite d'élasticité de l'alliage eutec tique Al-Si diminue continuellement quand la température croft. Les auteurs conc1uent que les bonnes propriété s mécaniques obtenues ré sultent de la combinaison de l'effet de la microstructure fine produite par le taux de solidification relativement élevéet de l'effet de fibres produit par la phase intermétallique.     

Effect of Copper Alloying on Fatigue Life and Fatigue Crack Growth Behaviour of Ductile Cast Irons

Abstract

Specimens cut out and machined from Cu alloyed (about 1.6%) and unalloyed (less than 0.012%) ductile cast iron ingots were tested under cycling loading to reveal the effect of copper addition on fatigue performance. The influence of solidification rate and hence the microstructure were also studied by preparing sand cast and die cast ingots from each composition. Some high copper die cast specimens were annealed to spheroidize and homogenize the matrix’s pearlite structure. All experiments were carried out by subjecting CT type specimens to constant load amplitude and tensile to tensile sinusoidal load cycles. Electrical crack foils were employed to measure instantaneous crack sizes. Cu alloyed samples showed higher fatigue lives. Similarly, crack growth rate diagrams pointed out lower fatigue crack velocities and higher near threshold stress intensity factors in high Cu specimens. The spheroidization of pearlitic matrix resulted in an insignificant increase in fatigue crack growth rate and a 10% decrease in near threshold stress intensity value. The fatigue performance of sand cast pieces was better than die cast ones. It is concluded that the fatigue life of ductile cast irons can be improved by copper alloying.

Des éprouvettes coupées et usinées à partir de lingots de fonte ductile alliée au cuivre (approximativement 1.6%) et non alliée (moins de 0.012%) ont été évaluées sous effort cyclique afin de révéler l’effet de l’addition de cuivre sur le comportement de fatigue. On a également étudié l’influence du taux de solidification, et ainsi de la microstructure, en préparant des lingots coulés en sable et d’autres coulés en coquille, à partir de chaque composition. On a recuit quelques éprouvettes à haute teneur en cuivre, coulées en coquille, pour obtenir la sphéroïdisation et l’homogénéisation de la structure perlitique de la matrice. On a effectué toutes les expériences en exposant les éprouvettes de type C-T à des cycles avec charge d’amplitude constante, à charge sinusoïdale traction à traction. On a utilisé des films électriques à fissure pour mesurer la taille instantanée des fissures. Les échantillons alliés au cuivre ont montré une plus grande résistance à la fatigue. De façon similaire, des diagrammes de taux de croissance de la fissure indiquaient des vélocités plus basses de fissure due à la fatigue et des facteurs plus élevés d’intensité de contrainte près de la limite pour les éprouvettes à haute teneur en Cu. La sphéroïdisation de la matrice perlitique a résulté en une augmentation insignifiante du taux de croissance de fissure due à la fatigue et en une diminution de 10% de la valeur d’intensité de contrainte près de la limite. Le comportement de fatigue des pièces coulées en sable était meilleur que celui des pièces coulées en coquille. On conclut que la résistance à la fatigue des fontes ductiles peut être améliorée par alliage au cuivre.     

High modulus steels: new requirement of automotive market. How to take up challenge?

Since the last decade, lightening of automotive structure was mainly achieved by gauge reduction using ultrahigh strength steels such as dual phase and transformation induced plasticity grades. However, gauge reduction can significantly reduce the stiffness. Limits are today reached for some applications such as chassis/suspension part. Development of steel with improved specific stiffness becomes more and more relevant to go further in weight reduction. Development of steel matrix composites (SMCs) with ceramic reinforcements is a promising solution. With an appropriate selection of the ceramic, eutectic solidification can be achieved. This natural production route guarantees a good cohesion of the steel/reinforcement interface and the control of the main parameters, which provide final properties of the product (size, shape, clustering of reinforcement). Significant fraction of ceramic can be obtained (10–25 vol.-%). Eutectic SMC can be produced with conventional industrial process such as continuous casting and hot strip mill which guarantees high productivity and low cost.

Depuis la dernière décennie, l’allègement des structures automobiles a été réalisé en grande partie par la réduction des épaisseurs au travers l’utilisation d’aciers à très haute résistance tels que les aciers DP (biphasés) et TRIP (à plasticité induite par transformation). Cependant, cette réduction des épaisseurs peut entraîner une baisse de rigidité. Aujourd’hui, les limites ont été atteintes pour certaines applications telles que les composantes châssis et suspension. Le développement d’acier à rigidité spécifique améliorée devient une voie de développement de plus en plus pertinente pour progresser dans la réduction de poids. Le développement de composites à matrice d’acier et renfort céramique est une solution prometteuse. Au travers d’une sélection appropriée de la céramique, on peut obtenir une solidification eutectique. Cette route naturelle de production des aciers garantit une bonne cohésion de l’interface acier/renfort ainsi que la maîtrise des principaux paramètres qui contrôlent les propriétés finales du produit (taille, forme, agglomération du renfort). Des fractions significatives de renfort céramique peuvent être atteintes (10–25% en volume). Les composites à matrice métallique (CMM) eutectique peuvent être élaborés par des procédés industriels conventionnels tels que la coulée continue ou le laminage à chaud qui garantissent une productivité élevée et un faible coût.     

Ceramic reinforced high modulus steel composites: processing,microstructure and properties

Ceramic reinforced steel matrix composites are materials for automotive, aerospace, wear and cutting applications. Such metal matrix composites (MMCs) combine attractive physical, mechanical and wear properties with ease of fabrication and low cost. The review focuses on the current state of the art of producing these metal matrix composites, ceramics reinforcements, composition of steel matrix, microstructure evolution and parameters influencing the mechanical and wear properties. Processing methods to fabricate ceramic reinforced steel matrix composites are discussed to produce these composites with low number of defects, homogeneous microstructure and high mechanical and wear performance. The influence of chemical nature of ceramic reinforcements and composition of steel matrix on the microstructure, mechanical and wear properties is presented. The strengthening mechanisms and parameters controlling wear performance of steel MMCs are described as a function of the content of ceramic reinforcements, microstructural design and structure of the steel matrix. Keeping in view the stability of ceramics in steels, suitable ceramic reinforcements and steel matrix materials are discussed. Moreover, the importance of microstructure and interface between ceramic reinforcement and steel matrix in controlling the mechanical properties of steel MMCs is highlighted. The review identifies area of research for development to fully appreciate and tailor the properties of these industrially important composites.

Les matériaux composites à matrice d’acier, renforcés de céramique, sont des matériaux pour application dans l’industrie automobile, aérospatiale, de l’usure et du découpage. Les matériaux composites à matrice métallique (MMCs) en acier et céramique combinent des propriétés attrayantes physiques, mécaniques et d’usure, à la facilité de fabrication et au coût faible. Cette revue se concentre sur l’état de la technique courante de production des matériaux composites à matrice d’acier, renforcés de céramique, sur les renforcements en céramique, sur la composition de la matrice d’acier, sur l’évolution de la microstructure, sur les propriétés mécaniques et sur les paramètres importants qui contrôlent les propriétés mécaniques et d’usure. On discute des méthodes de traitement pour la fabrication des matériaux composites à matrice d’acier, renforcés de céramique afin de produire des MMCs avec peu de défauts, une microstructure homogène et un rendement élevé des propriétés mécaniques et d’usure. On décrit l’influence de la nature chimique des renforcements et de la composition de la matrice en acier sur le développement de la microstructure et sur les propriétés mécaniques et d’usure. On décrit les mécanismes de renforcement et les paramètres contrôlant le rendement à l’usure des MMCs en acier en fonction de la teneur en renforcement de céramique, de la conception de la microstructure et de la structure de la matrice en acier. Gardant en vue la stabilité des céramiques dans les aciers, on discute des matériaux appropriés de renforcements céramiques et de matrice d’acier. De plus, on souligne l’importance de la conception de la microstructure et de l’interface dans le contrôle des propriétés mécaniques des MMCs en acier. Cette revue identifie des sujets de recherche à développer afin de comprendre complètement et de créer sur mesure les propriétés de ces matériaux composites d’importance industrielle.     

EFFECT OF COATING PARAMETERS AND HEAT TREATMENT ON THE ADHESIVE PROPERTIES OF ELECTROLESS Ni-P COATINGS

Abstract

The adhesive properties of coatings have pronounced effects on their quality. The effect of various coating parameters and post-deposition heat treatment on the adhesive properties of low and high phosphorus electroless nickel-phosphorus (EN) coatings was investigated using three-point bending tests. The critical load and mid-span deflection were used as measures of the adhesive strength of the coatings.

A good correlation was found between the coating parameters and the critical load and deflection values at crack initiation. The critical load was found to increase with increasing coating thickness for EN-coated specimens tested in the as-deposited condition. The critical load and mid-span deflection of as-plated EN coatings increased with increasing phosphorus content. However, thick coatings cracked at lower deflection values than thin coatings. Post-deposition heat treatment at 400 °C for 1 hour adversely affected the measured indices due to increase in brittleness of the coatings occasioned by the crystallization of nickel crystals and nickel phosphide (NixPy) precipitates. Further, the critical load and deflection values at cracking were found to be dependent upon the mechanical properties of the substrate material.

Les propriétés adhésives des revêtements ont des effets prononcés sur leur qualité. On a investigué l’effet de divers paramètres du revêtement et du traitement thermique après le dépôt sur les propriétés adhésives de revêtements autocatalytiques de nickel–phosphore (EN) à teneur faible ou élevée en phosphore, en utilisant les essais de flexion en trois points. On a utilisé la charge critique et la flèche à mi-portée comme mesures d’adhérence des revêtements. On a trouvé une bonne corrélation entre les paramètres du revêtement et les valeurs de charge critique et de flèche à l’initiation de fissure.

On a trouvé que la charge critique augmentait avec l’augmentation de l’épaisseur du revêtement pour les spécimens revêtus de EN évalués à l’état brut. La charge critique et la flèche à mi-portée des revêtements EN plaqués bruts augmentaient avec une augmentation de la teneur en phosphore. Cependant, les revêtements épais craquaient à des valeurs plus faibles de flèche que les revêtements minces. Le traitement thermique après dépôt, à 400 °C pendant 1 h, affectait défavorablement les indices mesurés à cause de l’augmentation de la fragilité des revêtements, occasionnée par la cristallisation de cristaux de nickel et de précipités de phosphure de nickel (NixPy). De plus, on a trouvé que les valeurs de la charge critique et de flèche à la fissuration étaient dépendantes des propriétés mécaniques du matériau du substrat.     

Characterisation of Al–B4C composite microstructures and their effect on fluidity

Abstract

Microstructural variables such as particle volume fraction, distribution and agglomeration significantly affect the properties of Al–B₄C metal matrix composites. The aim of the investigation was to study the quantitative characterisation of the microstructural variables and their effects on the fluidity of the composites. The results showed that the particle volume fraction, homogeneity of particle distribution, and volume fraction of agglomerates could be quantitatively analysed by the imaging analysis technique. It was found that the amounts of the particle clusters and networks, as well as the effective volume fraction of total particles augmented with the increase in the holding time. In addition, the longer holding time was, the less homogeneous the particle distribution became. Moreover, the particle agglomerates have a tendency to migrate to the flow end which results in an accelerated stopping of the flow. The increase in the effective particle volume fraction corresponded well with the fluidity deterioration of the composites during the melt holding.

Les paramètres microstructuraux, tels que la fraction volumique, la distribution et l’agglomération des particules affectent de manière significative les propriétés du composite à matrice métallique Al–B₄C. Ce travail porte sur la caractérisation quantitative des propriétés microstructurales ainsi que leurs effets sur la fluidité des matériaux composites. La fraction volumique des particules, l’homogénéité de leur distribution et la fraction volumique des agrégats ont été analysées quantitativement à l’aide de la technique d’analyse d’images. Les résultats montrent une augmentation de la quantité d’agrégats et de la fraction volumique effective des particules avec l’augmentation du temps de maintien. De plus, plus le temps de maintien est long, moins grande est l’homogénéité de la distribution des particules. Par ailleurs, les agglomérats ont tendance à migrer vers l’aval de l’écoulement, ce qui accélère l’arrêt de l’écoulement. L’augmentation de la fraction volumique effective des particules correspond parfaitement à la dégradation de la fluidité des matériaux composites.     

A chemical equilibrium model of the imperial smelting blast furnace

Abstract

A mathematical model of the Imperial Smelting lead-zinc blast furnace was developed to determine the critical reactions and to evaluate certain parameters of its operation. The model was based on the assumption that equilibrium existed throughout, except that carbon was assumed not to react until it reached the tuyeres. The two major reactions occurring in the lower parts of the furnace are found to be:

Zn(g) +CO₂ = ZnO +CO (1)

ZnS + Pb = Zn(g) + PbS(g) (2)

The second one has heretofore been neglected, but it is critical in predicting the furnace behaviour. Large quantities of lead, zinc, and sulphur circulate inside the furnace in the tuyere-equilibrium zone. Results calculated by the model show that sinter sulphur content and tap temperature have a major effect on this circulation and on zinc recovery and slag composition. The predicted results and published furnace data are in good agreement, indicating that a calculation that assumes equilibrium is a useful approximation of a real furnace.

Résumé

Un modèle mathématique du haut--fourneau «Imperial Smelting» a zinc et plomb est proposé pour etablir les réactions critiques et pour évaluer certains paramètres de fonctionnement. Le modéle est basé sur la supposition que le système est entièrement en équilibre, sauf le carbone qui est supposé ne pas réagir avant d'atteindre la région des tuyères. On trouve que les deux réactions principales qui s'effectuent au fond du four sont:

Zn(g) +CO₂ = ZnO +CO (1)

ZnS + Pb = Zn(g) + PbS(g) (2)

Bien que la deuxième réaction ait été ignorée jusqu'à présent, la prise en considération de cette réaction est essentielle si on veut prévoir Ie comportement du four. De grandes quantités de plomb, zinc et soufre circulent dans le four dans la région d'équilibre des tuyères. Des calculs a partir du modèle indiquent que la teneur en soufre des boulettes ainsi que la température de la coulée ont une influence importante sur cette circulation ainsi que sur la récupération du zinc et sur la composition des scories. Le fait que les résultats prévus et les données publiees pour ce haut-fourneau soient en bon accord indique qu'un modèle base sur la supposition de l'équilibre est une approximation valable pour un vrai four.     

Micrbband Formation in Cyclic Extrusion Compression of Aluminum

Abstract

The influence of very large deformations on the properties and microstructures of A199.95 and A199.992 is investigated. The very large deformations are imposed by the cyclic extrusion-compression (CEC) method, which combines extrusion and compression processes. It is found that above true strains of 4 and 8 respectively, the compression proof stresses of A199.992 and A199.95 stabilize. The property stabilization appears to result from the increasing incidence of micro bands which leads to the final constancy of the microstructure parameters. The homogeneous chess-board like microstructure forms during the deformation by the CEC method, as the result of rearrangement of microstructure by the mutually crossing microbands leading to the final dominance of persistent macro shear bands.

Résumé

On a étudié l'influence de très grandes déformations sur les propriétés et la microstructure de l'Al 99.95 et de l'Al 99.992. De très grandes déformations sont imposées par la méthode d'extrusioncompression cyclique (CEC), qui combine des processus d'extrusion et de compression. Au-delà de déformations réelles de 4 et 8 respectivement, les limites apparentes d'élasticité sous compression de l'AI 99.992 et de l'Al 99.95 se stabilisent. Cette stabilisation de la propriété a l'air de résulter de l'augmentation de l'occurrence de micro-bandes, ce qui méne à la constance finale des paramètres de microstructure. La microstructure homogène à apparence d'échiquier se forme lors de la déformation par la méthode CEC, comme résultat du réarrangement de la microstructure par les micro-bandes qui s'entrecroisent mutuellement, menant à la domination finale de bandes persistantes de macro-cisaillement.     

Continously cast lead sheet — production and uses

Abstract

The production of continuously cast thin lead sheet at Cominco's Product Research Centre at Sheridan Park, Ontario is described.

The immersion-drum casting machine costing less than $100,000 produces cast lead sheet 3' .feet wide and in gauges from 1/2 lb/ft² (0.008 inch) to over 3 lb/ft² (0.048 .inch) at a casting rate as high as 10 tons per hour. Casting parameters for sheet between these limits are discussed and illustrated.

The low machine cost and high production rate result in more economical production of lead sheet than is possible by conventional rolling, particularly in the lighter gauges, and is enhancing the development of new uses and the expansion of existing uses for lead sheet. An outstanding example is the growing acceptance of lead sheet for the control of noise in offices and apartments.

Résumé

Les auteurs décrivent la fabrication de tôle fine de plomb, par coulée continue, au Centre de Recherche Cominco sur les produits, à Sheridan Park, Ontario.

La machine de couleé a cylindre immergé, coutant moins de $100,000, permet de produire directement des tôles de plomb de 3 pieds de largeur dans une gamme d'épaisseurs variant de 1/2 1b/pi² (0.008 po) à plus de 3 lb/pi² (0.048 po), à un taux pouvant atteindre 10 tonnes par heure. Les paramètres qui influencent la fabrication de ces tôles sont discutés et leurs effets sont illustrés.

Le faible côt de la machine et le taux élevé de production permettent de fabriquer de la tôle de plomb plus economiquement que par laminage, surtout dans le cas des faibles épaisseurs. Il en résulte une plus grande demande pour les usages conventionnels et la création de nouvelles applications. L'emploi de plus en plus répandu de la tôle de plomb pour contrôler le bruit dans les bureaux et les maisons à logis multiples en est un exemple frappant.     

Pressure leaching of beta-spodumene by sodium chloride

Abstract

The applicability of the pressure leaching technique in the recovery of lithium from a beta-spodumene bearing concentrate has been investigated using sodium chloride as reactant in alkaline medium. Factors such as the concentration of sodium chloride and calcium hydroxide, the temperature, the pulp density, the reaction time and the particle size, which influence the rate and the extent of the lithium dissolution were studied When ever applicable the optimum values were determined. It has been suggested that the kinetics of this reaction are controlled by the diffusion phenomena. This hypothesis is supported by the relatively low activation energy ?H_a=3.6±0.2 Kcal/mol. The possibility of recovering pure lithium chloride from the .leach solutions containing large quantities of sodium chloride is indicated.

Résumé

L'application de la méthode de lixiviation sous pression à l'extraction du lithium d'un concentré de spodumène-beta a été étudiée en employant le chlorure de sodium comme réactif en milieu a1calin. Les principaux paramètres qui affectent la réaction sont: les concentrations du chlorure de sodium et de l'hydroxyde de calcium, la température, la densité de la pulpe, la durée de la réaction et la grosseur des particules. Lorsque possible, l'optimisation des paramètres a été faite. Il est suggéré que la cinétique de cette réaction soit contrôlée par le phénomène de diffusion. En effet, cette hypothèse est supportée par le fait que l' énergie est relativement basse, ?H_a = 3.6 ± 0.2 Kcal/mole. La possibilité de récupération de chlorure de lithium pur à partir de solutions de lixiviation contenant des quantités élevées de chlorure de sodium parait évidente.     

Modification of Roll Pass Design of Low Pearlite,Fine-Grained Sheet Steel Using Numerical Modeling and Processing Maps

Abstract

The main objective of this pass design is to achieve fine-grained structure with high strength properties and good ductility for 2.0 mm thickness steel sheet on a six stand finishing mill. Numerical modeling is used to evaluate the different rolling parameters while processing maps are used to determine a workability “window” in which dynamic recrystallization must occur.

The existing rolling parameters would not lead to a dynamically recrystallized structure. The proposed technique retains the sequence of reduction in thickness at the working temperatures, while it diminishes the rotational speed of the first stand and consequently all the other stands. The first stand is proposed to rotate with 25 rpm at 7.2 s-1 rate of deformation. The final rotational roll speed would be 177 rpm at stand no. 6 with 83.4 s-1 rate of deformation at 850 °C. Rolling force and torque needed in the proposed technique are lower than those in the existing ones at most of the passes. The proposed technique saves energy as it reduces the power consumption.

Le principal objectif de cette conception de passe de laminoir est d'obtenir une structure à grain fin avec des propriétés de résistance élevée et une bonne ductilité pour une tôle d'acier d'une épaisseur de 2.0 mm, sur un laminoir finisseur à six cages. On utilise la modélisation numérique pour évaluer les différents paramètres de laminage alors qu'on utilise les plans de formage pour déterminer une "fenêtre” de fabricabilité dans laquelle doit se produire une recristallisation dynamique.Les paramètres actuels de laminage ne peuvent conduire à une structure dynamiquement recristallisée. La technique proposée retient la séquence de réduction en épaisseur aux températures d'opération, tout en diminuant la vitesse de rotation de la première colonne et, par conséquent, de toutes les autres colonnes. On propose que la rotation de la première colonne soit de 25 rpm, avec un taux de déformation de 7.2 s-1. La vitesse du dernier rouleau serait de 177 rpm à la colonne no. 6, avec un taux de déformation de 83.4 s-1, à 850 °C. La force de laminage et le moment de torsion nécessaires pour la technique proposée sont plus bas que ceux qui existent déjà pour la plupart des passes. La technique proposée conserve l'énergie puisqu'elle réduit la consommation de pouvoir.     

Microstructures and mechanical properties in a turbine disc fabricated from astroloy powder

Abstract

Powder metallurgy processing of nickel-base superalloy turbine discs is described. The discs were prepared from hotisostatically pressed Astroloy powder preforms by a single-stage forging operation, followed by machining. The forgeability, machinability, tensile and stress rupture properties of the powder fabricated material were better than, or equivalent to, those of cast material. The fatigue lifetimes obtained in laboratory push-pull tests and the lifetime obtained in a disc exposed to engine testing and ambient temperature spin-rig testing were also good. However the lifetimes obtained from crack detection to final failure were short, indicating either poor resistance to fatigue crack propagation or poor fracture toughness. This problem is examined in terms of the microstructures and minor phase contents of the discs. The microstructures showed incomplete recrystallization in the bore, carbide laden powder particle boundaries both in the bore and the recrystallized rim, and platelets of a brittle M₂ (SC) phase. Modified processing of powder fabricated discs is suggested to circumvent these deficiencies.

Résumé

Dans cet article, les auteurs décrivent la production, par métallurgie des poudres, de disques de turbine en superalliage au nickel. Les disques sont obtenus en une seule operation par forgeage d'ébauches de poudres d'Astroloy prealablement comprimées à chaud et ils sont ensuite usinés.

La forgeabilité, l'usinabilite et les propriétés mécaniques en traction et en fluage de tels disques sont meilleures que celles des disques obtenus par fonderie. La limite de fatigue déterminée en laboratoire par traction-compression et celle obtenue sur un disq ue soumis aux conditions de service de la turbine et à l'essai «spin-rig» à température ambiante se révèlent etre bonnes. Par contre, les limites de fatigues mesurées a partir de la détection d'une fissure jusqu'à la rupture finale sont faibles, suggérant soit une faible résistance à la propagation des fissures soit une faible résilience.

Ce problème a été etudie par examen de la microstructure et des phases secondaires présentes. Ces études révèlent que la recristallisation est incomplète au centre du disque, que des carbures sont présents aux joints entre les particules de poudres autant au centre du disque que dans l'anneau extérieur recristallisé et que des plaquettes d'une phase fragile M₂ (SC) sont présentes. Des modifications au procédé de fabrication de ces disques sont suggérées afin d'éliminer ces déficiences.     

Effects of compaction technique on processing response of aluminium PM alloys

The objective of this research was to assess the effects of compaction method (uni-axial die compaction and cold isostatic pressing) on two aluminium powder metallurgy alloys. Both systems were mixtures of elemental and master alloy powders. Mechanical and physical properties from samples prepared using both methods were compared. Analyses included the measurement of green and sintered densities, tensile properties and microstructural analyses. Results indicated that sintered products of a largely comparable quality could be realised for both alloys regardless of the compaction approach employed. PM2324 displayed sensitivity to compaction pressure such that low values were preferred for cold isostatic pressing (CIP) whereas higher values yielded superior sintered products when die compaction was implemented. Conversely, compaction pressure had no meaningful impact on the sintering behaviour of PM7075 for CIP or die pressed samples.

Le but de cette recherche consistait à évaluer les effets de la méthode de compaction (compaction uniaxe en moule et compression isostatique à froid) sur deux alliages d’aluminium de la métallurgie des poudres. Les deux systèmes consistaient en mélanges de poudres élémentaires et de poudres d’alliage mère. On a comparé les propriétés mécaniques et physiques des échantillons préparés en utilisant les deux méthodes. Les analyses incluaient la mesure de la densité à cru et frittée, les propriétés de traction et les analyses de la microstructure. Les résultats indiquaient que l’on pouvait réaliser des produits frittés d’une qualité très comparable pour les deux alliages, peu importe l’approche de compaction utilisée. PM2324 démontrait une sensitivité à la pression de compaction de telle sorte que des valeurs faibles étaient préférées pour le CIP alors que des valeurs plus élevées produisaient des produits frittés supérieurs avec la compaction en moule. Inversement, la pression de compaction n’avait pas d’impact significatif sur le comportement de frittage de PM7075 pour les échantillons pressés par CIP ou en moule.     

Effect of pulp rheology on flotation of nickel sulphide ore with fibrous gangue particles

Abstract

Tests are carried out with suspensions of fibrous chrysotile particles and nickel sulphide ore containing chrysotile as a gangue. They corroborate published results, and indicate a very strong effect of particle shape on slurry rheology. Such suspensions exhibit time dependent properties. The flotation tests revealed that the viscosity of this system strongly affects flotation performance. At a solids concentration of 15–20% (w/w), the concentrate yield increases and the concentrate grade dramatically declines. This deterioration is observed when the Casson yield stress exceeds 1·5–2 Pa. The tests imply that the rheological properties of the investigated system are mainly determined by fibrous components. However, because of the presence of anisotropic mineral particles, the effect of particle–particle interactions cannot be separated from the effect of particle shape in this system.

On effectue des essais avec des suspensions de particules fibreuses de serpentine et de minerai de sulfure de nickel contenant de la serpentine comme gangue. Ces essais confirment les résultats publiés et indiquent un effet très prononcé de la forme des particules sur la rhéologie de la boue. De telles suspensions exhibent des propriétés dépendantes du temps. Les essais de flottation ont révélé que la viscosité de ce système affecte grandement le rendement de la flottation. À une concentration en solides de 15 à 20% (poids/poids), la production de concentré augmente et la qualité du concentré décline dramatiquement. Cette détérioration est observée lorsque la contrainte de Casson excède 1·5 à 2 Pa. Les essais impliquent que les propriétés rhéologiques du système étudié sont déterminées principalement par les composantes fibreuses. Cependant, à cause de la présence de particules minérales anisotropes, on ne peut pas séparer l’effet des interactions particule-particule de l’effet de la forme des particules dans ce système.     

Metallurgical developments in the continuous casting of austenitic stainless steel slabs

Abstract

The design concept of Atlas Steels’ new integrated sheet/strip mill at Tracy, Quebec involved direct conversion of continuously cast austenitic stainless steel slabs to coiled hot bands. In early production, a high incidence of surface defects, commonly called ‘slivers’, necessitated hotband conditioning greatly in excess of the anticipated level. Electron probe microanalysis of nonmetallics found in the slivers revealed that the majority of such defects resulted from subsurface entrapment of pouring stream reoxidation products in the continuously cast slabs. The problem was brought under operational control by improved steelmaking practice and modifications of the casting operation to permit pouring through refractory stream protection tubes.

Résumé

Aux usines d'Atlas Steel situées it Tracy dans le Québec, le procédé de production prévoit la coulée continue suivie de laminage à chaud de tôles et de bandes. Dès la mise en marche des usines, le trop grand nombre d'inclusions de surface imposa un parachévement imprévu des bandes laminées à chaud. Des analyses faites par micro-sonde ont fait voir que la plupart des inclusions provenaient d'oxydation au jet de la coulée continue. Des modifications apportées à l'élaboration de l'acier et l'emploi de tubes réfract aires au jet de coulée surmonterent les difficultés occasionnées par les inclusions de surface.     

The effect of processing variables on the mechanical properties and strain ageing of high-strength low-alloy V and V-N steels

Abstract

Laboratory experiments have been conducted on a series of vanadium and vanadium-nitrogen steels. The results indicate that the combination of vanadium plus nitrogen gives an excellent notch toughness in the normalized plates (EA TT < ?80°C). Controlled rolling gives about 100 MPa higher yield strength with somewhat reduced notch toughness (EATT? ?50°C). Aluminum does not improve the properties of a normalized or controlled-rolled vanadium-nitrogen plate. Vanadium is able to combine with nitrogen so effectively that the steel can be considered. to be unsusceptible to strain ageing.

Résumé

Les auteurs ont fait des essais de laboratoire sur une série d'aciers au vanadium et au vanadium-azote. Les résultats indiquent que la combinaison vanadium-azote donne d'excellentes propriétés de résilience pour des tôles fortes normalisées (EA TT < ?80 °C). Le laminage contrôlé conduit à une limite d'élasticité plus élevée d'environ 100 MPa et a une résilience quelque peu réduite (EATT ? -50°C). L'aluminium n'améliore pas les propriétés d'une tôle forte d'acier au vanadium-azote après normalisation ou après laminage contrôlé. L'efficacit;amp;#x00E9; de la réaction entre Ie vanadium et l'azote est telle que l'acier peut être consideéré comme n'étant pas susceptible au vieillissement après écrouissage.     

Nucleation in Zn–Al alloys grain refined with Ti

Abstract

In order to understand more fully the grain refinement of Zn–Al alloys by Ti, the α′ grains in chill cast 7 and 24% Al alloys have been studied by successive polishing and etching of microsections and by scanning electron microscopy of deeply etched specimens.

Idealized models have been deduced for these grains and it appears that lobed forms nucleate and grow preferentially in the 〈111〉 directions of the nucleus cubes. Increased supercooling causes more complex branching. When visible nuclei are absent the 24% Al alloy grains appear to have had a primitive plate-like morphology soon after nucleation.

The results are unique in the field of heterogeneous nucleation because the nuclei are relatively large and have a well-defined crystalline morphology so that their orientations relative to the early grain shapes can be easily studied.

Résumé

Afin de mieux comprendre l'action du Ti sur l'affmage des grains d'alliages Zn–Al, les grain α′ d'alliages à 7 et 24% d'Al, refroidis brusquement après coulée, ont été étuditiés par polissages et attaques successifs de microsections et par microscopie électronique à balayage d'échantil1ons attaques profondément.

Des modèles idéalisés ont été doouits pour ces grains. Il semble que les formes lobées germent et croissent d'une manière privilegiée dans les direction 〈111〉 des germes cubiques. Une surfusion plus prononcée engendre un embranchement plus complexe. Quand il n'y a pas de germes visibles, il semble que les grains de l'alliage à 24% d'Al aient eu une morphologie primitive en forme de plaques peu après la germination.

Les résultats sont uniques dans le domaine de la germination hétérogène parce que les germes sont relativement gros et possèdent une morphologie cristalline bien définie, de telle sorte que leurs orientations par rapport aux formes initiales des grains peuvent être étudiées facilement.     

Electrical Conductivities,Densities and Viscosities of Silver Refining Electrolytes

Abstract

Electrical conductivities, densities and viscosities of silver electrolytes in the composition and temperature ranges employed by industrial silver electrorefineries have been measured and equations describing these properties in terms of electrolyte composition and temperature have been developed. Using the experimental results, a comparison of the electrolyte properties in four major silver refineries has been made and criteria for choosing optimum electrolyte compositions have been developed.

Résumé

On a mesuré la conductivityé électrique, le poids spécifique et la viscosité des électrolytes d'argent utilisés dans les usines d'affinage d'argent électrolytique. Ces mesures ont été prises en fonction de la composition et de la gamme des températures que l'on retrouve dans l'industrie et l'on a ensuite mis au point des équations faisant état de ces propriétés en terme de composition et de température. À partir des résultants des expériences on a pu com parer les propriétés des électrolytes dans quatre importantes affineries d'argent et on a mis au point les critères permettant de trouver la composition électrolytique optimale.     

Preparation of anorthite ceramic using mining tailings and calcium fluoride sludge

Abstract

To solve the disposal problems of mining tailings and calcium fluoride sludge (CFS), waste serpentine tailings (WSTs), waste kaolin tailings (WKTs), and CFS were tested as components for a ceramic product to be used as a building material. The ceramic properties were analyzed by thermal analyses, X-ray diffraction (XRD), morphological structure analyses, Raman spectra, compressive strength measurement, and toxicity characteristic leaching procedure (TCLP). Thermal analyses showed that the significant weight loss of the sample at 1000°C was the release of H₂O and CO₂ rather than HF. X-ray diffraction verified that the main crystalline phase of the ceramic was anorthite. Raman spectra indicated that fluorine in CFS substituted for oxygen to form the structure of SiO_xF_4?x tetrahedra. Toxicity characteristic leaching procedure and corrosion resistance tests indicated that fluorine solidified into anorthite phase did not release into solution. Therefore, converting WST, WKT, and CFS into a ceramic product is in accordance with the concept of sustainable development.

Pour résoudre les problèmes d'élimination des résidus miniers et des boues de fluorure de calcium (CFS), les déchetsrésidus de serpentine (WSTs), les résidus de kaolin déchets (WKTs), et du CFS ont été testés en tant que composants pourun produit céramique pouvant être utilisé comme matériau de construction. Les propriétés céramiques ont été analysées paranalyses thermiques, diffraction des rayons X (XRD), analyses de la structure morphologique, les spectres Raman, mesure de la résistance à la compression, et par lessivage des caractéristiques toxiques (TCLP). Les analyses thermiques ont montré que la perte de poids significative de l'échantillon à 1000°C a été la libérationde H₂O et CO₂ plutôt que de HF. La diffraction des rayons X a vérifié que la phase cristalline principale de lacéramique était anorthite. Les spectres Raman ont indiqué que le fluor contenu dans le CFS a remplacé l'oxygène pourformer la structure de SiO_xF_4-x tétraèdres. Lessivage des caractéristiques toxiques et lestests de résistance à la corrosion ont indiqué que le fluor solidifié en phase anorthite ne s'est pas transformé dans lasolution. Par conséquent, la conversion de WST, WKT, et CSF en un produit céramique est en conformité avecle concept de développement durable.