稻麦草环保型制浆方法——两段氧碱制浆

稻麦草经碱浸渍和氧碱蒸煮的两段氧碱制浆方法能获得较高白度和物理强度的纸浆。本文对氧碱制浆影响因素、氧碱制浆中的化学反应、硅的行为特性作了总体介绍。     

蔗渣两段氧碱制浆的研究

探讨了NaOH用量对蔗渣浸渍和后续氧碱蒸煮制浆的影响,同时,也研究了氧碱制浆过程中氧压、蒽醌用量、蒸煮时间、蒸煮温度及液比等因素对氧碱制浆的影响。研究结果表明,浸渍段NaOH用量分别为4%、8%和14%时,氧碱制浆段NaOH用量为14%可获得较好的制浆效果;当浸渍段NaOH用量分别为6%、10%和12%时,氧碱制浆段NaOH用量为16%可获得较好的制浆效果。研究结果还表明,在相同蒸煮条件下,与蔗渣单段氧碱制浆相比,在获得相同卡伯值和抗碱性（R10）的纸浆时,两段氧碱制浆后纸浆得率更高,即在氧碱制浆前对蔗渣进行浸渍处理,可有效提高细浆得率和抗碱性,同时降低卡伯值。     

麦草氧碱制浆工艺的新探

麦草原料经过碱浸渍和氧气蒸煮的两段氧碱制浆可获得高的得率、白度和强度的纸浆。本文在适宜的碱浸渍基础上,在中浓制浆范围同对NaOH用量、最高温度、保温时间以及碱浸渍和氧碱蒸煮黑液的回用进行了重点探讨。     

蔗渣氧碱制浆工艺探讨

对蔗渣的氧碱制浆进行了初步研究。结果表明,用碱量、氧压是左右制浆效果的主要因素。蔗渣氧碱制浆的最佳工艺条件:用碱量25%,蒸煮最高温度140℃,氧压0.8MPa,转速400r·min-1,保温40min或零保温,液比1∶8,保护剂MgSO4添加量2.0%。在此条件下,制浆的综合质量指标最好。     

稻草NaOH—02／NaOH两段蒸煮及其无氯漂白：第一部分NaOH预处理和O2／NaOH

在对麦草进行了ＮａＯＨ预处理和氧碱蒸者的基础上,按照与麦草类似的蒸煮 方法对稻草进行了ＮａＯＨ－Ｏ２／ＮａＯＨ两段蒸煮试验,结果表明,氢氧化纳预处理－氧碱蒸煮是稻草原料适宜的制浆方法,本色浆的白度高,并具有较好的机械强度。     

麦草氧碱制浆及全无氯漂白

研究了麦草氧碱制浆的最佳工艺条件.结果表明,氧碱制浆可以在比常规烧碱-AQ法节碱35%左右,蒸煮最高温度120℃的条件下,取得64.8%的粗浆得率.对纸浆进行全无氯漂白的结果证明,采用合适的螯合剂和漂白活化剂可以漂至较高的白度.     

脉冲氧碱制浆

普通氧碱制浆效果虽好,但有严重缺点:其一,氧的溶解度低;其二,它与木素反应速度快,在整个木片横截面上脱木素不均匀,难以工业化生产。苏联制浆造纸研究生产综合企业Idel Haland Ovsky博士提出脉冲氧碱制浆,木片经预汽蒸后进入以筛板分隔为若干区域的蒸煮器,氧自筛板下连续送入(100m~3约400kg/t),利用脉冲器(一台脉冲器产生往复脉冲,可供两台蒸煮器使用)的脉冲作用,使氧气充分分散,均匀脱木素;使木片表面已经氧脱木素的纤维分离;一般蒸煮液中不易氧化的物质因而得到降解;并能使木片、蒸煮液及氧保持恒定的运动,锅内始终不会有“死区”。所以脉冲氧碱制浆有蒸煮、筛选及降解不易氧化物质的功能。蒸煮得率比硫酸盐浆高5～7％。排出的气体含有     

稻草的氧碱法制浆(5)——对循环制浆过程黑液的评价

稻草的黑液循环氧碱法制浆在保证获得稳定的制浆质量的前提下,可使碱浸渍黑液和氧气蒸煮黑液的固含量分别提高到１６％和１１％左右,且氧气蒸煮黑液可省去脱硅处理。     

竹子氧碱法制浆工艺条件的探讨

对竹子氧碱法制浆的最佳工艺条件进行了探讨,实验结果表明其最佳工艺条件为:NaOH用量13%,氧压0.8MPa,蒸煮最高温度130℃,液比1:7,杂多酸(HPA)用量1%,MgCO31%.另外比较了竹材在上述工艺条件下的氧碱法制浆与常规下的KP法制浆.     

麦草氧碱法制浆性能的研究

本文以麦草为原料采用O2-NaOH、O2-Na2CO3、O2-Na0H-Na2CO3法蒸煮,研究发现在氧碱蒸煮过程中随着用碱量增加,硅的溶出量也有所增加,而蒸煮温度提高有利于脱木素反应,但纸浆得率较低.因此,温度和用碱量对氧碱制浆影响较大.     

棉短绒烧碱-蒽醌法蒸煮除尘机理的研究

对棉籽壳烧碱-蒽醌法蒸煮脱木素机理和棉短绒烧碱-蒽醌法蒸煮除尘工艺进行了研究,结果表明棉籽壳烧碱-蒽醌法蒸煮时,在升温至100℃时脱除34.57%的木素;当温度升到160℃时,木素的脱除率达到87.11%。因此,棉籽壳烧碱-蒽醌法蒸煮脱木素的阶段性可分为初始脱木素、主要脱木素和残余脱木素三个阶段。另外,影响棉短绒烧碱-蒽醌法蒸煮除尘的主要因素是用碱量,其次为蒸煮最高温度,影响最小的因素为保温时间。     

人工种植桉木深度脱木素的研究：第二部分：实验室模拟EMCC制浆

对人工种植的尾叶桉进行了深度脱森素煮的研究。发现延伸改良连续蒸煮比常规蒸煮 具有高的制浆选择性,可以在保持浆料强度的前提下降低纸浆的卡伯值。     

碱预处理对南方松碱法制浆的影响

本文研究了碱预处理对南方松碱法制浆的影响,结果表明:碱预处理可提高南方松后续蒸煮过程中有效碱的作用效率,增加蒸煮黑液中固形物和木素的含量,减少后续碱法制浆过程中甲醇的产生。同时研究发现,碱预处理可使南方松木片具有更好的制浆性能,可以提高其成浆得率,降低纸浆卡伯值,提高纸浆的白度和强度。     

巴西甘蔗渣烧碱-蒽醌法蒸煮机理的研究

对巴西甘蔗渣原料主要成分和烧碱-蒽醌法蒸煮机理进行了研究。结果表明:巴西甘蔗渣与中国甘蔗渣相比,其克拉森木素含量低,而综纤维素的含量高。巴西甘蔗渣烧碱蒽醌法脱木素的阶段性可分为大量脱木素、补充脱木素和残余脱木素三个阶段:即蒸煮温度升至100℃时,为大量脱木素阶段,木素脱除69.44%;当蒸煮温度从100℃升至160℃,此阶段为补充脱木素阶段,此阶段脱除24.18%的木素;在160℃保温150min期间为残余脱木素阶段,此阶段脱除3.38%的木素。     

Über die Eignung von thermo-mechanischem und chemo-thermo-mechanischem Holzstoff (TMP und CTMP) aus Buchen- und Kiefernholz für die Herstellung von mitteldichten Faserplatten (MDF)

A condensed review on the state of the art of the producton of medium density fibreboards is given. Thereafter, results of investigations on pulping beech and pine wood under differnet conditions according to the TMP- and CTMP-process are presented. The pulps derived from both wood species were analysed for some of their physical and chemical properties. The results reveal: Within the TMP- and CTMP-process, both the chemical and biological oxygen demand increase with increasing pulping temperature. In general, however, waste water from the CTMP-process has higher chemical and biological oxygen demand. The CTMP-process seems to be milder than the TMP-process as it leads to pulps with higher fibre length, especially in case of beech. The content of acetyle groups is much lower in CTMP-pulps than in TMP-pulps, CTMP-pulps emit also more acetic acid than TMP-pulps. With increasing pulping temperature the pH-value decreases and the buffering capacity towards alkali increases. MDF were prepared from TMP- and CTMP-pulps and their properties were evaluated. The results are included in the next parts of the publication.     

中国草类纤维制浆的理论与技术研究

总结了我国多年来研究草类纤维制浆造纸所得到的规律。根据草类纤维原料结构和化学组成的不均匀性和纤维形态分布,论述了强化禾草类秸秆的除尘备料过程,是获得浆料滤水性能好、黑液黏度低的关键。论述了草类纤维制浆与木材的差异,分析了造成差异的内在因素,指出草类原料制浆没有必要采用过高的温度和较长的保温时间。草类纤维制浆的最佳工艺应该是在蒸煮过程中除去85%左右的木素,然后氧脱木素制浆。分析了草类原料制浆污染治理困难的原因,指出草浆黑液的化学组成与物化性能的关系、碳水化合物含量高是造成草浆黑液黏度高的重要内在因素。介绍了当前解决这些问题的一些研究成果。     

麦草氧碱两段蒸煮工艺初探

对麦草进行NaOH／(NaOH O2)两段蒸煮,初步研究了氧蒸煮段最高温度、氧压及保温时间对纸浆性能和黑液中二氧化硅含量的影响：     

竹原料预处理蒸煮技术的可行性

针对竹片密度较大、不利于蒸煮过程中药液渗透的问题,对竹原料预处理蒸煮技术的可行性进行探讨。结果认为:竹原料预处理蒸煮技术对于改进蒸煮过程中的药液渗透效果具有明显作用,蒸煮得率提高、成浆硬度下降、蒸煮最高温度降低、蒸煮时间缩短,不论从技术上还是从经济上都具有可行性。     

绿氧在碱法阔叶木蒸煮中应用的初步探讨

在实验的基础上考查了绿氧在混合阔叶木和桦木的碱法蒸煮中的影响.结果表明在混合阔叶木和桦木的碱法蒸煮中添加少量的绿氧助剂可以提高细浆得率,改善蒸煮的均匀性,减少粗渣量,同时对成浆白度也有所提高.     

Sulfite-Formaldehyde Pulping and Oxygen Delignification of Wheat Straw

In this study,wheat straw pulp was prepared by sulfiteformaldehyde(SF) pulping combined with oxygen delignification to develop a sustainable methodology for chemical pulping of straw materials.The bleachability of oxygen-delignified SF pulp was also evaluated by hypochlorite bleaching.The results indicated that the Na_2SO_3 charge played an important role in lignin removal during SF pulping as well as oxygen delignification.The efficiency of oxygen delignification of wheat straw SF pulp was markedly high.After the oxygenation stage,the Kappa number decreased by over 50%(the original Kappa number of SF pulp was lower than 30) when the Na OH charge was in the range of 3%~5%.The optimal conditions for preparing bleached pulp via combined SF pulping and oxygen delignification involved the use of 12% of Na_2SO_3 and 3% of Na OH,respectively.Pulp with relatively high brightness,a low Kappa number,as well as an acceptable viscosity could be obtained when oxygen-delignified SF pulp was bleached with hypochlorite under a low active chlorine dosage.