不同退火时间对[Ag/FePt]_(10)多层膜磁性能和微结构的影响

采用射频磁控溅射的方法,在玻璃基片上制备了不同Ag层厚度的[Ag/FePt 2nm]10多层薄膜,经550℃真空热处理后,得到L10有序结构的FePt薄膜.实验结果显示,FePt单层薄膜经550℃退火30min后其易磁化轴处于垂直方向和面内方向之间,而550℃退火60min后其易磁化轴处于垂直于膜面方向,垂直矫顽力和面内矫顽力分别为634和302kA/m;真空退火后[Ag/FePt]10多层膜表现为面内磁晶各向异性,550℃退火60min后[Ag 2.8nm/FePt 2nm]10多层薄膜垂直矫顽力和面内矫顽力分别为309和778kA/m,并且随着Ag层的加入,部分FePt颗粒已经被Ag原子隔开了,颗粒之间的交换耦合作用变弱了.     

添加AlN对FePt薄膜结构和磁性的影响

采用射频磁控溅射制备了FePt(50nm)和[FePt(2,3,5nm)/AlN(1nm)]n膜,之后在550℃退火30min,研究了周期数(n)和AlN含量对[FePt/AlN]_n系列多层膜结构及磁性的影响.结果表明,多层膜的矫顽力和矩形比均在n=8时出现较大值;周期数的增大会引起晶粒尺寸的长大;AlN的加入不但可以抑制FePt粒子的长大,使晶粒体积(V_grain)和磁激活体积(V*)趋于一致,而且还能有效地降低晶粒间交换耦合作用,并且AlN含量越大,晶粒间交换耦合作用的程度越弱.     

FePtAg颗粒薄膜的制备及性能表征

采用磁控溅射方法在自然氧化的单晶Si(100)基片上制备了FePtAg颗粒薄膜.通过调整靶材的溅射速率、控制掺杂Ag元素的含量,选择适当的热处理工艺,获得了晶粒尺寸约5nm,分布均匀的FePt颗粒薄膜,矫顽力为3.2×105A/m,磁滞回线具有良好的矩形度,薄膜内部无交换耦合作用,适用于高密度磁记录介质材料.     

Ag衬底层对FePt薄膜结构和性能的影响

采用磁控溅射方法在自然氧化的单晶Si(100)衬底上制备了双层结构的FePt-X/Ag(X=Ag或Pt)薄膜.以20nm厚的Ag做衬底,可以制备出易磁化轴垂直基片的FePt合金薄膜;Ag在FePt薄膜中优先团聚,不利于控制FePt晶粒的长大,调整Pt的含量可以控制热处理过程中FePt薄膜的晶粒尺度;通过XRD、TEM、VSM对薄膜样品的结构、晶粒尺寸的观察和磁性检测,我们认为FePt合金薄膜有序化转变的最佳热处理温度在400℃;经过500℃热处理,薄膜软硬磁耦合较好,晶粒尺寸约为100nm,有最大的矫顽力1.04×106A/m.     

电介质保护膜对磁光记录膜的磁和磁光特性的影响

采用射频磁控溅射法制备了非晶TbFeCo薄膜及其保护层AlN薄膜，并研究保护层对薄膜的磁和磁光特性的影响。结果表明，AlN薄膜可以增强薄膜磁光效应，同时，AlN薄膜对TbFeCo磁光薄膜的矫顽力、垂直磁各向异性以及本征克尔角都有一定的影响。其原因来自于溅射过程中N和Al原子对TbFeCo薄膜表面的轰击而导致的界面特性的改变。     

TbFe/Fe交换耦合磁致伸缩多层膜的制备

采用双靶磁控溅射法制备了 TbFe/Fe交换耦合磁致伸缩多层膜,考察了热处理时间、Fe层厚度、溅射功率以及Ar气分压对多层膜低场磁致伸缩性能的影响。研究结果表明:TbFe 磁致伸缩层与软磁 Fe层之间通过交换耦合作用以及热处理能明显提高薄膜的软磁性能和磁致伸缩性能;TbFe/Fe多层膜的磁致伸缩性能对热处理时间、Fe 层厚度、溅射功率、Ar 气分压等薄膜沉积参数十分敏感;与 TbFe 磁致伸缩薄膜相比TbFe/Fe交换耦合磁致伸缩多层膜水平方向的矫顽力从 16kA/m降低到 9.6 kA/m。在外加磁场为8000 A/m条件下,TbFe/Fe磁致伸缩多层膜最大磁致伸缩系数可达1.58×10-4。     

电介质保护膜对磁光记录膜的磁和磁光特性的影响

采用射频磁控溅射法制备了非晶TbFeCo薄膜及其保护层AlN薄膜 ,并研究保护层对薄膜的磁和磁光特性的影响。结果表明 ,AlN薄膜可以增强薄膜磁光效应 ,同时 ,AlN薄膜对TbFeCo磁光薄膜的矫顽力、垂直磁各向异性以及本征克尔角都有一定的影响。其原因来自于溅射过程中N和Al原子对TbFeCo薄膜表面的轰击而导致的界面特性的改变     

FePt纳米薄膜研究进展

由于FePt在超高密度磁存储材料方面的广阔应用前景及其局限性,研究人员对FePT薄膜进行了大量的研究及改性.根据国外近期在此领域的研究现状,综述了单相、复相及掺杂FePt薄膜的制备以及对结构和性质的影响.复相或掺杂主要是通过结构的改变来降低L10晶相转变温度和FePt颗粒的大小,通过其耦合作用来影响FePt薄膜的磁学性能,使其成为超高密度存储器材料.     

热处理对Tb0.27Dy0.73Fe2巨磁致伸缩薄膜性能的影响

本文研究了热处理对Tb0.27Dy 0.73Fe2薄膜磁性及巨磁致伸缩性能的影响.XRD分析表明制备态的Tb0.27Dy 0.73Fe2薄膜为非晶态,并且在450℃退火仍然保持非晶态,制备态的Tb0.27 Dy0.73Fe2薄膜显示垂直磁各向异性,在退火后向平行磁各向异性变化.热处理提高了Tb0.27Dy0.73Fe2薄膜在低磁场下的磁致伸缩特性.     

热处理对Tb0.27Dy0.73Fe2巨磁致伸缩薄膜性能的影响

本文研究了热处理对Tb0.27Dy0.73Fe2薄膜磁性及巨磁致伸缩性能的影响。XRD分析表明制备态的Tb0.27Dy0.73Fe薄膜为非晶态,并且在450℃退火仍然保持非晶态,制备态的Tb0.27Dy0.73Fe2薄膜显示垂直磁各向异性,在退火后向平行磁各向异性变化。热处理提高了Tb0.27Dy0.73Fe2薄膜在低磁场下的磁致伸缩特性。     

磁性药物载体的合成

随着生物技术、纳米技术和物理化学等多学科的飞速发展,磁性药物载体的研究成为国内外导向药物领域的热门课题.介绍了磁性药物载体的发展现状,分析讨论了磁性微球、磁性毫微粒、磁性纳米脂质体等的制备方法.     

Magnetic alignment and patterning of cellulose fibers

The alignment and patterning of cellulose fibers under magnetic fields are reported. Static and rotating magnetic fields were used to align cellulose fibers with sizes ranging from millimeter to nanometer sizes. Cellulose fibers of the millimeter order, which were prepared for papermaking, and much smaller fibers with micrometer to nanometer sizes prepared by the acid hydrolysis of larger ones underwent magnetic alignment. Under a rotating field, a uniaxial alignment of fibers was achieved. The alignment was successfully fixed by the photopolymerization of a UV-curable resin precursor used as matrix. A monodomain chiral nematic film was prepared from an aqueous suspension of nanofibers. Using a field modulator inserted in a homogeneous magnetic field, simultaneous alignment and patterning were achieved.     

磁性材料在磁性纸中的应用

介绍了常用磁性材料及其制备方法,综述了细胞腔加填法和原位复合法制备磁性纤维和磁性纸的研究情况,进而对两种方法制备的磁性纸的印刷适应性进行分析。     

Magnetic alignment and patterning of cellulose fibers

Abstract

The alignment and patterning of cellulose fibers under magnetic fields are reported. Static and rotating magnetic fields were used to align cellulose fibers with sizes ranging from millimeter to nanometer sizes. Cellulose fibers of the millimeter order, which were prepared for papermaking, and much smaller fibers with micrometer to nanometer sizes prepared by the acid hydrolysis of larger ones underwent magnetic alignment. Under a rotating field, a uniaxial alignment of fibers was achieved. The alignment was successfully fixed by the photopolymerization of a UV-curable resin precursor used as matrix. A monodomain chiral nematic film was prepared from an aqueous suspension of nanofibers. Using a field modulator inserted in a homogeneous magnetic field, simultaneous alignment and patterning were achieved.     

室温磁致冷材料及技术的研究进展

本文简要介绍了磁致冷机的基本工作原理；回顾了室温磁致冷材料及技术的发展历史；概述了具有突破性的最新研究进展。最后本文指出了室温磁致冷的潜在市场及发展趋势。     

磁流体浸没物磁场力分析及磁浮特性

物体浸没于磁流体中表现出磁浮特性，对其受力状态分析是准确描述其悬浮状态的前提和基础。基于非线性磁流体应力张量模型和稳态Bernoulli方程，建立磁流体中浸没物受力模型。借助非磁性体受力模型的简化计算方法以及磁性体与磁流体之间的多场效应关系，分别对非磁性体、磁性体两类浸没物在磁流体中所受磁浮力进行分析，结果表明非磁性浸没物在磁流体中仅受到外加磁场贡献的一次磁浮力，而磁性浸没物除受到一次磁浮力外，还受到其自身激发磁场贡献的二次磁浮力．永磁体在磁流体中位置决定的磁浮力满足一定条件时，永磁体能够自悬浮于磁流体中。     

磁性聚乙烯醇微球的制备及其性质

采用分散聚合法，在Fe3O4磁流体存在下，通过PVA分子单体共聚制备磁性高分子微球。用透射电镜和X射线对磁流体的形貌、粒径进行表征和衍射分析，同时借助于显微拍照和红外光谱，对磁性微球的微观形貌和化学成分进行了研究。通过对比磁性微球的磁响应性及粒径，研究了反应温度、搅拌速度、聚乙烯醇用量、盐酸用量等操作因素对磁性微球性质的影响。结果表明，在70℃操作温度、750r／min的搅拌速度，5ml9％PVA和0．5ml37%盐酸条件下能制备出粒径在8～44μm之间、具有良好磁响应性、表面富含羟基和羧基等官能团的磁性聚乙烯醇微球。     

磁制冷材料中一级磁相变的研究进展

磁制冷技术作为21世纪的新一代制冷技术已经受到了关注。因此近年来具有一级磁相变的磁制冷材料成为全球学术界的一个研究热点,并越来越受到工业界的重视。主要介绍了磁制冷材料中的一级磁相变特点,综述了具有一级磁相变的磁制冷材料的研究进展和应用现状。最后展望了具有一级磁相变的磁制冷材料的发展趋势。     

Measurement of the Viscosity of Dilute Magnetic Fluids

The capillary tube viscometer is used to measure the viscosity of aqueous magnetic fluids under the influence of parallel and perpendicular magnetic fields. The effects of the volume fraction of the suspended magnetic particles, the concentration of surfactants, and the external magnetic field strength, as well as the orientation, on the viscosity of the magnetic fluid are analyzed. The experimental results show that the viscosity of the sample magnetic fluids increases with increases in the concentrations of suspended magnetic particles and surfactants. The external magnetic field is also an important factor that affects the viscosity of the magnetic fluid. The viscosity first increases with the magnetic field and finally approaches a constant as the magnetization attains a saturation state. For the same magnetic fluid, the viscosity in a perpendicular magnetic field is larger than that in a parallel magnetic field for the same magnetic field.Paper presented at the Seventh Asian Thermophysical Properties Conference, August 23–28, 2004, Hefei and Huangshan, Anhui, P. R. China