Novel phosphorus‐containing hardeners with tailored chemical structures for epoxy resins: Synthesis and cured resin properties

A comparative evaluation of systematically tailored chemical structures of various phosphorus‐containing aminic hardeners for epoxy resins was carried out. In particular, the effect of the oxidation state of the phosphorus in the hardener molecule on the curing behavior, the mechanical, thermomechanical, and hot‐wet properties of a cured bifunctional bisphenol‐A based thermoset is discussed. Particular attention is paid to the comparative pyrolysis of neat cured epoxy resins containing phosphine oxide, phosphinate, phosphonate, and phosphate (with a phosphorus content of about 2.6 wt %) and of the fire behavior of their corresponding carbon fiber‐reinforced composites. Comparatively faster curing thermosetting system with an enhanced flame retardancy and adequate processing behavior can be formulated by taking advantage of the higher reactivity of the phosphorus‐modified hardeners. For example, a combination of the high reactivity and of induced secondary crosslinking reactions leads to a comparatively high T_g when curing the epoxy using a substoichiometric amount of the phosphinate‐based hardener. The overall mechanical performance of the materials cured with the phosphorus‐containing hardeners is comparable to that of a 4,4′‐DDS‐cured reference system. While the various phosphorus‐containing hardeners in general provide the epoxy‐based matrix with enhanced flame retardancy properties, it is the flame inhibition in the gas phase especially that determines the improvement in fire retardancy of carbon fiber‐reinforced composites. In summary, the present study provides an important contribution towards developing a better understanding of the potential use of such phosphorus‐containing compounds to provide the composite matrix with sufficient flame retardancy while simultaneously maintaining its overall mechanical performance on a suitable level. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Mechanical characterization of phenolic foams modified by short glass fibers and polyurethane prepolymer

Short glass fibers and polyurethane prepolymer were used to modify phenolic foams. The mechanical properties of the composites were characterized and compared with those of foams unmodified and modified with only polyurethane prepolymer or short glass fibers in terms of friability, compression, and bending properties. It shows that polyurethane prepolymer significantly improved the toughness and reduced the friability of phenolic foams, while short glass fibers markedly increased the compression and bending properties. The compound modified foams exhibited significantly lower friability and higher resistance to cracking behavior than conventional phenolic foams and the foams modified with only short glass fibers, and were much stiffer and stronger than conventional phenolic foams and the foams modified with only polyurethane prepolymer. The compound modified phenolic foams with the 1:3 ratio of short glass fibers to polyurethane prepolymer exhibited excellent integrated mechanical properties. POLYM. COMPOS., 36:1584–1589, 2015. © 2014 Society of Plastics Engineers     

新型磷／氮协同阻燃环氧树脂的合成与性能

以双酚A环氧树脂E－51与DOPO（9,10-dihydrooxa-20－phosph henanthrene－10-oxide）合成含磷环氧树脂（ED）,以三聚氰胺与苯酚反应制备含氮的酚醛固化剂MFP。采用红外光谱对产物进行分析表征,采用热失重分析和UL94V垂直燃烧测试考查树脂的热性能和阻燃性能,同时探讨了阻燃环氧树脂的力学性能。结果表明,随着含磷量的增加,环氧树脂的热稳定性和阻燃性能得到改善,当含磷量为3％时,环氧树脂的初始分解温度高达330℃以上,在700℃下的残炭率达到30％以上,阻燃性能均达到了UL－94 V—0级。而试样的力学性能则随含磷量的增加而降低。     

Flame retardancy and dielectric properties of dicyclopentadiene‐based benzoxazine cured with a phosphorus‐containing phenolic resin

A dicyclopentadiene‐based benzoxazine (DCPDBZ) was prepared and separately copolymerized with melamine–phenol formaldehyde novolac or phosphorus‐containing phenolic resin (phosphorus‐containing diphenol) at various molar ratios. Their curing behaviors were characterized by differential scanning calorimetry. The electrical properties of the cured resins were studied with a dielectric analyzer. The glass‐transition temperatures were measured by dynamic mechanical analysis. The thermal stability and flame retardancy were determined by thermogravimetric analysis and a UL‐94 vertical test. These data were compared with those of bisphenol A benzoxazine and 4,4′‐biphenol benzoxazine systems. The effects of the diphenol structure and cured composition on the dielectric properties, moisture resistance, glass‐transition temperature, thermal stability, and flame retardancy are discussed. The DCPDBZ copolymerized with phosphorus‐containing novolac exhibited better dielectric properties, moisture resistance, and flame retardancy than those of the melamine‐modified system. The flame retardancy of the cured benzoxazine/phosphorus‐containing phenolic resins increased with increasing phosphorus content. The results indicate that the bisphenol A and 4,4′‐biphenol systems with a phosphorus content of about 0.6% and the dicyclopentadiene system with a phosphorus content of about 0.8% could achieve a flame‐retardancy rating of UL‐94 V‐0. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Effect of organo‐phosphorus and nano‐clay materials on the thermal and fire performance of epoxy resins

The results of flame retardance and thermal stability of a reactively modified organo‐phosphorus diglycidylether of bisphenol‐A and an organo‐phosphorus tetraglycidyl diaminodiphenylmethane are reported here. The organo‐phosphorus epoxy resins were synthesized by the reaction of 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide and diglycidyl ether of bisphenol‐A and tetraglycidyl diaminodiphenylmethane, respectively, and then cured with a mixture of 3,5‐diethyltoluene‐2,4‐diamine and 3,5‐diethyltoluene‐2,6‐diamine. In addition to this, between 5 and 7.5% of organically modified polymeric layered silicate nano‐clay was also added to neat epoxy resin or to the phosphorus‐modified epoxy resin to investigate any synergies, or otherwise, a combination of clay and phosphorus on the flame, degradation, and thermal properties are also reported. The reaction kinetics of phosphorus‐modified and epoxy cure were studied by FTIR, ¹H‐NMR, and DSC. Thermal properties and morphology of the final product were analyzed by thermogravimetric analysis, dynamic mechanical thermal analysis, X‐ray diffraction, and cone calorimetry. Improvement in flame retardance by cone calorimetry was demonstrated by the addition of only 3% phosphorus or 7.5% clay into the epoxy compared with unmodified epoxy resins, whereas no evidence of synergy for a phosphorus and clay combination was found. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 1233–1253, 2004     

Synthesis and characterization of epoxy film cured with phosphorous‐containing phenolic resin

Through the electrophilic addition reaction of ? P(O)? H and C?C, a series of novel phosphorus‐containing phenolic resins bearing maleimide (P‐PMFs) were synthesized and used as curing agent for preparing high performance and flame retardancy epoxy resins. The structure of the resin was confirmed with FTIR and elemental analysis. Thermal properties and thermal degradation behaviors of the thermosetted resin was investigated by using differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). The epoxy resins exhibited high glass transition temperature (143–156°C), goof thermal stability (>330°C) and retardation on thermal degradation rates. High char yields (700°C, 52.9%) and high limited oxygen indices (30.6–34.8) were observed, indicating the resins' good flame retardance for the P‐PMFs/CNE cured resins. The developed resin may be used potentially as environmentally preferable products in electronic fields. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 3813–3817, 2007     

Synthesis,thermal and mechanical behavior of a silicon/phosphorus containing epoxy resin

A liquid silicon/phosphorus containing flame retardant (DOPO–TVS) was synthesized with 9,10‐dihydro‐9‐oxa‐10‐phosphapheanthrene‐10‐oxid (DOPO) and triethoxyvinylsilane (TVS). Meanwhile, a modified epoxy resin (IPTS–EP) was prepared by grafting isocyanate propyl triethoxysilane (IPTS) to the side chain of bisphenol A epoxy resin (EP) through radical polymerization. Finally, the flame retardant (DOPO–TVS) was incorporated into the modified epoxy resin (IPTS–EP) through sol–gel reaction between the ethyoxyl of the two intermediates to obtain the silicon/phosphorus containing epoxy resin. The molecular structures of DOPO–TVS, IPTS–EP and the final modified epoxy resin were confirmed by FTIR spectra and ¹H‐NMR, ³¹P‐NMR. Thermogravimetric analysis (TGA), differential scanning calorimetry, and limiting oxygen index were conducted to explore the thermal properties and flame retardancy of the synthesized epoxy resin. The thermal behavior and flame retardancy were improved. After heating to 600°C in a tube furnace, the char residue of the modified resin containing 10 wt % DOPO–TVS displayed more stable feature compared to that of pure EP, which was observed both by visual inspection and scanning electron microscope (SEM). Moreover, the mechanical performance testing results exhibited the modified epoxy resins possessed elevated tensile properties and fracture toughness which is supported by SEM observation of the tensile fracture section. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42788.     

Synthesis and performance of a novel nitrogen‐containing cyclic phosphate for intumescent flame retardant and its application in epoxy resin

A novel nitrogen‐containing cyclic phosphate (NDP) was synthesized and well characterized by ¹H, ¹³C, ³¹P NMR, mass spectra and elemental analysis. NDP was used as an additive intumescent flame retardant (AIFR) to impart flame retardancy and dripping resistance for diglycidyl ether of bisphenol‐A epoxy resin (DGEBA) curied by 4,4′‐diaminodiphenylsulfone (DDS) with different phosphorus content. The flammability, thermal stability, and mechanical properties of NDP modified DGEBA/DDS thermosets were investigated by UL‐94 vertical burning test, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and Izod impact strength and flexural property tests. The results showed that NDP modified DGEBA/DDS thermosets exhibited excellent flame retardancy, moderate changes in glass transition temperature and thermal stability. When the phosphorus content reached only 1.5 wt %, the NDP modified DGEBA/DDS thermoset could result in satisfied flame retardancy (UL‐94, V‐0). The TGA curves under nitrogen and air atmosphere suggested that NDP had good ability of char formation, and there existed a distinct synergistic effect between phosphorus and nitrogen. The flame retardant mechanism was further realized by studying the structure and morphology of char residues using FT‐IR and scanning electron microscopy (SEM). It indicated that NDP as phosphorus‐nitrogen containing flame retardant worked by both of the condensed phase action and the vapor phase action. Additionally, the addition of NDP decreased slightly the flexural strength of the flame retarded DGEBA epoxy resins, and increased the Izod impact strength of these thermosets. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41859.     

Thermochemical characterization of some thermally stable thermoplastic and thermoset polymers

The thermochemical and flammability properties of some thermally stable polymers considered for use in aircraft interiors are described. The properties studied include: (a) thermomechanical properties such as glass transition and melt temperature; (b) dynamic thermogravimetric analysis in anaerobic environment; (c) flammability properties such as oxygen index, flame spread and smoke evolution; and (d) selected physical properties. The thermoplastic polymers evaluated included polyphenylene sulfide, polyaryl sulfone, 9,9-bis(4-hydroxyphenyl)-fluorene polycarbonate-poly(dimethylsiloxane) and polyether sulfone. The thermoset polymers evaluated included epoxy, bismaleimide, a modified phenolic and polyaromatic melamine resin. These resins were primarily used in the fabrication of glass reinforced prepregs for the construction of experimental panels. Test results and relative rankings of some of the flammability parameters are presented and the relationship of the molecular structure, char yield, and flammability properties of these polymers are discussed.     

Simultaneously Improving the Thermal,Flame‐Retardant and Mechanical Properties of Epoxy Resins Modified by a Novel Multi‐Element Synergistic Flame Retardant

To obtain epoxy resins with satisfactory thermal, flame retardant, and mechanical properties, a novel multi‐element synergistic flame retardant (PPVSZ) is synthesized through the reaction between P? H of 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide (DOPO) and C?C of polysilazane (PVSZ) and utilized as a multi‐element synergistic flame retardant for epoxy resins. The flame retardant mechanism is explored by XPS and SEM, confirming that the excellent flame‐retardance efficiency owes itself to an optimal flame retardant way which jointly exerts the flame‐retardant effects in the gaseous and condensed phase. The thermal properties deduced from DSC, TGA, and DMA, indicate the glass transition temperature, maximum weight loss rate, and char yields at 700 °C for EP‐2 increase by about 5.0 °C, 8.4 °C and 8.8%, respectively. Furthermore, mechanical properties such as impact strength, tensile strength, and flexural strength are also increased by 45.38%, 14.16%, and 17.43%, respectively, which show that the incorporation of PPVSZ does not deteriorate the mechanical properties of modified resin. All the results demonstrate that epoxy resins modified by PPVSZ not only have good effect on the flame retardance, but also have good improvement on thermal and mechanical properties, indicating the potential for applications in many fields requiring fire safety.     

Diallyl bisphenol A—novolac epoxy system cocured with bisphenol‐A‐bismaleimide—cure and thermal properties

Novolac epoxy (EPN)—2,2′‐diallyl bisphenol A (DABA) resin system was modified by cocuring it with bisphenol A bismaleimide (BMI). Molar concentration of BMI in the stochiometric blend of EPN and DABA was varied from 0.5 to 2.0. The cure optimization was done using DSC, IR spectroscopy, and rheological studies. The curing proceeded by phenol‐epoxy and Alder‐ene reactions. The performance of the ternary Epoxy‐Allyl phenolic‐Bismaleimide system was evaluated through their thermal and dynamic mechanical characterization. BMI improved the overall thermal stability and the modulus of the resultant composites. The increase in BMI concentration in the system resulted in enhanced glass transition temperature with a consequent improvement in high temperature performance typically estimated by their lap shear strength at high temperatures. The high temperature performance of the epoxy‐phenol‐bismaleimide (EPB) system was found to be far superior to the epoxy‐phenol (EP)system. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Synthesis,thermal properties,and flame retardance of the epoxy‐silsesquioxane hybrid resins

Epoxy/silsesquioxane‐OH (EP‐SDOH, ED) hybrid resins were prepared from cyclohexyl‐disilanol silsesquioxane (SDOH) and diglycidyl ether of bisphenol A via the reaction between silanol and the oxirane group, with the cobalt naphthanate as a catalyst. It was found that incorporation of SDOH allows the reaction between oxirane ring and Si? OH, and the silsesquioxane cage structure can be the main chain or as the side chain of the hybrid resin. The EP‐SDOH hybrid resins with various SDOH contents were cured by 4,4′‐diaminodiphenylsulphone, and the curing reaction was investigated by differential scanning calorimetry. The curing characteristics of EP‐SDOH hybrids had been observed to be influenced by the content of SDOH in the hybrid. The differential scanning calorimetry thermograms indicated that the EP‐SDOH hybrid exhibited a higher initial temperature, peak temperature, as well as final temperature than those of the pure epoxy resin when cured by the same curing agent 4,4′‐diaminodiphenylsulphone. The curing kinetic parameters were calculated by using the Ozawa method and the results indicated that EP‐SDOH hybrids possess the same curing mechanism as the pure epoxy resin. The properties of the cured EP‐SDOH hybrid resins such as the glass transition temperature (T_g), dynamic mechanical analysis, thermal stability, as well as the flame retardance were also investigated, and the results showed that introducing silsesquioxane‐OH unit into epoxy resin successfully modified the local structure, made the chain stiffness, restrict the chain mobility, and eventually improved thermal stability and flame retardance of epoxy resin. POLYM. ENG. SCI., 47:225–234, 2007. © 2007 Society of Plastics Engineers.     

Synthesis and properties of phosphorus containing advanced epoxy resins

A series of advanced epoxy resins with various epoxy equivalent weights were synthesized from a reactive phosphorus‐containing diol, 2‐(6‐oxido‐6H‐dibenz[c,e][1,2]oxaphosphorin‐6‐yl)‐1,4‐dihydroxy phenylene and diglycidyl ether of bisphenol A and then cured with 4,4′‐diaminodiphenyl sulfone, phenol novolac, or dicyandiamide. The parameters of the polymerization reaction (such as reaction time, catalyst) are discussed in this article. Thermal properties of cured epoxy resins were studied using differential scanning calorimetry, dynamic mechanical analysis, and thermal gravimetric analysis. The flame retardancy of cured epoxy resins was tested by limiting oxygen index. The relations between thermal properties, flame retardancy, and epoxy equivalent weights were also studied. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 75: 429–436, 2000     

Performance comparison of epoxy resins modified with diphenylphosphine oxide and DOPO

By curing the reaction mixture of diphenylphosphine oxide (DPO) and diglycidyl ether of bisphenol A with 4,4′‐diaminodiphenylsulfone, flame‐retardant epoxy resins (EP/DPO) were prepared. Flame‐retardant epoxy resins modified with 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide (DOPO) were similarly prepared (denoted as EP/DOPO). The limiting oxygen index value of pure epoxy resin, EP/DPO–P‐0.9 (with a phosphorus content of 0.9 wt%), and EP/DOPO–P‐0.9 are 23.0, 30.5, and 29.4%, respectively. EP/DPO–P‐0.9 reached a UL‐94 vertical burning test V‐0 rating, while EP/DOPO–P‐0.9 failed. The results of the cone calorimetry test, thermo‐oxidative degradation behavior study, and pyrolysis‐gas chromatography/mass spectrometry analysis indicated that both flame retardants mainly act through the gas‐phase activity mechanism. Together, the results of this study suggest that EP/DPO are high performance resins with good thermal stability, high glass transition temperature, and low water absorptivity for practical applications.     

Calcium borate flame retardation system for epoxy molding compounds

A new flame retardation system for epoxy molding compounds was investigated for application to semiconductor packaging. By adding a small volume of calcium borate as a flame retardant, the flammability of the epoxy molding compound decreased. The flammability was not decreased proportionally with the volume of calcium borate. To further enhance flammability, an excess amount of phenolic resin was added to the epoxy molding compound. With the effects of calcium oxide and the excess phenolic resin, we developed an epoxy molding compound which has a flame‐retardant level sufficient to satisfy the V‐0 classification of the UL94 rating. We also found that calcium oxide in the calcium borate accelerates the curing reaction of epoxy compounds due to its absorption of water from the phenolic resin hardener. Calcium hydroxide formed from calcium oxide and water was also considered to contribute to the decrease in flammability by releasing water at high temperatures. The flame retardation mechanism of this developed epoxy compound is also discussed. Finally, the developed epoxy compound was proved to have suitable moldability, mechanical properties, and durability for use as semiconductor packaging. POLYM. ENG. SCI., 46:799–806, 2006. © 2006 Society of Plastics Engineers     

A novel polyurethane prepolymer as toughening agent: Preparation,characterization, and its influence on mechanical and flame retardant properties of phenolic foam

A novel phosphorus‐ and silicon‐containing polyurethane prepolymer (PSPUP) was synthesized by the chemical reaction of phenyl dichlorophosphate with hydroxy‐terminated polydimethylsiloxane (HTPDMS) and subsequently with toluene‐2,4‐diisocyanate. The structure of PSPUP was confirmed by Fourier transform infrared spectroscopy and ¹H nuclear magnetic resonance. Afterward, a series of phenolic foams (PF) with different loadings of PSPUP toughening agent were prepared. The apparent density and scanning electron microscopy results showed that the addition of PSPUP can increase the apparent density of phenolic foam. The compressive, impact and friability test results showed that the incorporation of PSPUP into PF dramatically improved the compressive strength, impact strength, and reduced the pulverization ratio, indicating the excellent toughening effect of PSPUP. The limiting oxygen index of PSPUP modified phenolic foams remained a high value and the UL‐94 results showed all samples can pass V0 rating, indicating the modified foams still had good flame retardance. The thermal properties of the foams were investigated by thermogravimetric analysis under air atmosphere. Moreover, the thermal degradation behaviors of the PF and PSPUP/PF were investigated by real‐time Fourier transform infrared spectra. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Loading the polyol carbonization agent into clay nanotubes for the preparation of environmentally stable UV‐cured epoxy materials

The halloysite nanotubes (HNTs) were loaded with pentaerythritol (PER). The as‐prepared composite (HNT‐P) and ammonium polyphosphate (APP) was subsequently added to the UV‐curable epoxy resins, giving a new flame‐resistant system. Loading of the hydrophilic PER into HNT can reduce the moisture absorption in the UV‐curable epoxy resins. The flame retardancy was evaluated by means of the cone calorimeter and limit oxygen index test. The results showed that the flame retardancy of the modified epoxy resin was greatly improved with an obvious decrease in both the heat release and smoke release. Moreover, it was revealed that HNT could catalyze the reaction of APP and PER, and the burning surface of the epoxy resin should be covered by the polyphosphoric‐HNT intumescent char layer. We have measured the moisture sorption and dynamic mechanical properties of the UV‐cured epoxy resins. As compared to the use of the simple mixture of PER and HNT, the use of the HNT‐P nearly kept the storage modulus at about 1809 Mpa and reduced the moisture absorption by 58.2 wt % at 40 °C. The results proved that the addition of the HNT‐P obtained lower moisture absorption and higher stability of the mechanical properties than adding the simple mixture. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 45045.     

一种含磷酚醛/环氧树脂阻燃性的研究

以双酚S、甲醛和三聚氰胺为原料合成含氮线性酚醛树脂,并用其作为固化剂,结合阻燃剂甲基膦酸酐对环氧树脂进行阻燃改性。利用TGA对环氧/酚醛树脂与环氧/酚醛树脂/膦酸酐两种浇铸体系的热稳定性能进行了比较研究。结果表明甲基膦酸酐为阻燃剂,酚醛树脂固化环氧树脂能得到效果较好的阻燃材料,垂直燃烧试验结果为UL-94V-0级。     

Synthesis and properties of phosphorus‐containing advanced epoxy resins. II

Two phosphorus‐containing diacids were synthesized from 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene 10‐oxide (DOPO) and either maleic acid or itaconic acid and then reacted with diglycidyl ether of bisphenol A (DGEBA) to form two series of advanced epoxy resins. Reaction conditions, such as reaction time, temperature and catalyst, are discussed in this article. After curing with 4,4'‐diaminodiphenyl sulfone (DDS), thermal properties of cured epoxy resins were studied using dynamic mechanical analysis (DMA) and thermal gravimetric analysis (TGA). The flame retardancy of cured epoxy resins was evaluated using a UL‐94 measurement. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 78: 228–235, 2000     

Synthesis of wood‐based epoxy resins and their mechanical and adhesive properties

Wood‐based epoxy resins were synthesized from resorcinol‐liquefied wood. Wood was first liquefied in the presence of resorcinol with or without a sulfuric acid catalyst at high temperature. Because of the hydroxyl groups, the resorcinol‐liquefied wood was considered as a precursor for synthesizing wood‐based epoxy resin. Namely, the phenolic OH groups of the liquefied wood reacted with epichlorohydrin under alkali condition. By the glycidyl etherification, epoxy functionality was introduced to the liquefied wood. The epoxy functionality of the resins was controlled by the concentration of phenolic OH groups in the liquefied wood, which would be a dominant factor for crosslink density and properties of the cured epoxy resins. The flexural strength (150–180 MPa) and the modulus of elasticity (3.2 GPa) of the highly crosslinked wood‐based epoxy resin were equivalent to those of the commercially available epoxy resin, diglycidyl ether of bisphenol A (DGEBA). Also, the shear adhesive strength of the wood‐based epoxy resin was higher than that of DGEBA when plywood was used as the adhesive substrates. The mechanical and adhesive properties suggested that the wood‐based epoxy resins would be well suited for matrix resins of natural plant‐fiber reinforced composites. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 2285–2292, 2006