Synthesis and properties of fluorinated polyimides from 1,1‐bis(4‐amino‐3,5‐dimethylphenyl)‐1‐(3,4,5‐trifluorophenyl)‐2,2,2‐trifluoroethane and various aromatic dianhydrides

A novel aromatic diamine, 1,1‐bis(4‐amino‐3,5‐dimethylphenyl)‐1‐(3,4,5‐trifluorophenyl)‐2,2,2‐trifluoroethane, containing a pendant polyfluorinated phenyl group, a trifluoromethyl group, and methyl groups ortho‐substituted to the amino groups in the structure was synthesized and characterized. The diamine was polymerized with several aromatic dianhydrides, including 3,3′,4,4′‐biphenyltetracarboxylic dianhydride, 3,3′,4,4′‐benzophenonetetracarboxylic dianhydride, 4,4′‐oxydiphthalic anhydride, and 4,4′‐hexafluoroisopropylidene diphthalic anhydride, via a high‐temperature one‐step procedure to afford four polyimides (PIs) with inherent viscosities of 0.47–0.70 dL/g. The PIs exhibited excellent solubilities in a variety of organic solvents. They were soluble not only in polar aprotic solvents but in many common solvents, such as cyclopentanone, tetrahydrofuran, and even toluene at room temperature. The tough and flexible PI films cast from the PI solutions exhibited good thermal stabilities and acceptable tensile properties. The glass‐transition temperatures were in the range 312–365°C, and the 5% weight loss temperatures were all higher than 480°C in nitrogen. The films had tensile strengths in the range 76–99 MPa, tensile moduli of 2.2–2.8 GPa, and elongations at break of 5–8%. In addition, the PI films exhibited excellent transparency in the visible light region with cutoff wavelength as low as 302 nm and transmittance higher than 88% at the wavelength of 450 nm. The PI films showed low dielectric constants ranging from 2.50–2.68 and low moisture absorptions of less than 0.56%. The good combined properties of the PIs mainly resulted from the synergic effects of the different substituents. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Synthesis and characterization of novel polyimides derived from 2‐amino‐5‐(4‐aminophenyl)‐thiazole

A new kind of aromatic unsymmetrical diamine monomer containing thiazole ring, 2‐amino‐5‐(4‐aminophenyl)‐thiazole (AAPT), was synthesized. A series of novel polyimides were prepared by polycondensation of AAPT with various aromatic dianhydrides by one‐step polyimidation process. The synthesized polyimides had inherent viscosity values of 0.36–0.69 dL/g and were easily dissolved in highly dipolar solvents. Meanwhile, strong and flexible polyimide films were obtained, which have good thermal and thermo‐oxidative stability with the glass transition temperatures (T_g) of 276.7–346.1°C, the temperature at 5% weight loss of 451–492°C in nitrogen and 422–440°C in air, as well as have outstanding mechanical properties with the tensile strengths of 94–122 MPa, elongations at breakage of 5–18%. These films also had dielectric constants of 3.12–3.38 at 10 MHz. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Novel low‐dielectric‐constant copolyimide thin films composed with SiO2 hollow spheres

A series of copolyimide/SiO₂ hollow sphere thin films were prepared successfully based on bis[3,5‐dimethyl‐4‐(4‐aminophenoxy)phenyl]methane and 9,9‐bis(4‐(4‐aminophenoxy)phenyl)fluorene (molar ratio = 3 : 1) as diamine, and 4,4′‐(4,4′‐isopropylidenediphenoxy)bis(phthalic anhydride) as dianhydride, with different wt % SiO₂ hollow sphere powder with particle size 500 nm. Some films possessed excellent dielectric properties, with ultralow dielectric constants of 1.8 at 1 MHz. The structures and properties of the thin films were measured with Fourier transform infrared spectra, scanning electron microscope, thermogravimetric analysis, and dynamic mechanical thermal analysis. The polyimide (PI) films exhibited glass‐transition temperatures in the range of 209– 273°C and possessed initial thermal decomposition temperature reaching up to 413–477°C in air and 418–472°C in nitrogen. Meanwhile, the composite films were also exhibited good mechanical properties. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Synthesis and characterization of novel thermally stable and optically active poly(amide‐imide)s derived from N,N′‐(4,4′‐diphthaloyl)‐bis‐L‐leucine diacid and aromatic diamines

A new diacid containing optically active functional groups, N,N′‐(4,4′‐diphthaloyl)‐bis‐L ‐leucine diacid ( 3 ), was synthesized and used in a preparation of a series of poly(amide‐imide)s (PAIs) by direct polycondensation with various aromatic diamines in N‐methyl‐2‐pyrrolidinone (NMP). All polymers derived from diacid ( 3 ) were highly organosoluble in the solvents like N‐methyl‐2‐pyrrolidinone, N,N‐dimethylacetamide, N,N‐dimethylformamide, dimethyl sulfoxide, tetrahydrofuran, γ‐butyrolactone, cyclohexanone, and chloroform at room temperature or upon heating. Inherent viscosities of the PAIs were found to range between 0.34 and 0.61·dL g^?1. All the PAIs afforded flexible and tough films. The glass‐transition temperatures of these PAIs were recorded between 212 and 237°C by differential scanning calorimetry, and the 10% weight loss temperatures were ranging from 372 to 393°C and 336–372°C under nitrogen and air, respectively. The polyimide films had a tensile strength in the range of 63–88 MPa and a tensile modulus in the range of 1.2–1.7 GPa. Optically active PAIs exhibited specific rotations in the range of ?10.58° to ?38.70°. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2007     

Synthesis and characterization of organo‐soluble fluorinated polyimides

A novel fluorinated diamine monomer with a keto group, 4‐[4‐amino‐2‐trifluoromethyl phenoxy]‐4′‐[4‐aminophenoxy]benzophenone (ATAB) was prepared by reacting dihydroxybenzophenone with 4‐chloronitrobenzene and 2‐chloro‐5‐nitrotrifluoromethylbenzene in the presence of potassium carbonate followed by catalytic reduction with palladized carbon (10%). Fluorinated polyimides IVa–e were synthesized from the diamine mentioned above via a two‐step method (thermal and chemical imidization). Polyimides IVa–e have inherent viscosities in the range 0.65–1.06 dL g^?1 (thermal imidization) and 0.82–1.56 dL g^?1 (chemical imidization). The polyimides prepared by chemical imidization exhibit excellent solubility. Polyimide films exhibit tensile strength, elongation and tensile modulus in the ranges 96–106 MPa, 9–13% and 1.1–1.7 GPa, respectively. The T₁₀ values of the polyimides are in the range 540–598 °C in nitrogen and 545–586 °C in air, with more than 50–60% char yield. They have T_g values between 244 and 285 °C. The prepared polyimides show cut‐off wavelengths in the range 365–412 nm and transmittance at 450 nm in the range 80.9–94.2%. The dielectric constants of the polyimide films are in the range 3.10–3.77 at 1 kHz and 3.04–3.66 at 10 kHz, with moisture absorption of 0.14–0.40%. Copyright © 2006 Society of Chemical Industry     

Synthesis and characterization of novel soluble pyridine‐containing polyimides based on 4‐phenyl‐2,6‐bis[4‐(4‐aminophenoxy)phenyl]‐pyridine and various aromatic dianhydrides

A new kind of pyridine‐containing aromatic diamine monomer, 4‐phenyl‐2,6‐bis[4‐(4‐aminophenoxy)phenyl]‐pyridine (PAPP), was successfully synthesized by a modified chichibabin reaction of benzaldehyde and a substituted acetophenone, 4‐(4‐nitrophenoxy)‐acetophenone (NPAP), followed by a reduction of the resulting dinitro compound 4‐phenyl‐2,6‐bis[4‐(4‐nitrophenoxy)phenyl]‐pyridine (PNPP) with Pd/C and hydrazine monohydrate. The aromatic diamine was employed to synthesize a series of new pyridine‐containing polyimides by polycondensation with various aromatic dianhydrides in N‐methy‐2‐pyrrolidone (NMP) via the conventional two‐step method, i.e., ring‐opening polycondensation forming the poly (amic acid)s and further thermal or chemical imidization forming polyimides. The inherent viscosities of the resulting polyimides were in the range of 0.79–1.13 dL/g, and most of them were soluble in common organic solvents such as N,N‐dimethylacetamide (DMAc), NMP, and tetrahydrofuran (THF), etc. Meanwhile, strong and flexible polyimide films were obtained, which had good thermal stability, with the glass transition temperatures (T_g) of 268–338°C and the temperature at 5% weight loss of 521–548°C in air atmosphere, as well as outstanding mechanical properties with tensile strengths of 89.2–112.1 MPa and elongations at break of 9.5–15.4%. The polyimides also were found to possess low dielectric constants ranging from 2.53 to 3.11. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 212–219, 2007     

Chemical modification of 3,3′,4,4′‐biphenyltetracarboxylic dianhydride polyimides by a catechol‐derived bis(ether amine)

Having previously demonstrated that the polyimide derived from 3,3′,4,4′‐biphenyltetracarboxylic dianhydride (BPDA) and 1,2‐bis(4‐aminophenoxy)benzene [termed triphenyl ether catechol diamine (TPEC)] exhibited superior tensile properties in addition to good thermal properties, we now provide a preliminary assessment of the properties of the copolyimides prepared from BPDA, TPEC, and another aromatic diamine. The homopolyimides derived from BPDA and many aromatic diamines generally possessed good mechanical properties and thermal properties; however, they were insoluble in available organic solvents. In several cases, organosoluble BPDA copolyimides could be prepared from BPDA and equimolar mixtures of TPEC and another aromatic diamine. All the copolyimides could be formed into tough films with high moduli and strengths and, in most cases, high extensions to break. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 351–358, 2002; DOI 10.1002/app.10342     

Synthesis and properties of novel alicyclic‐functionalized polyimides prepared from natural—(D)‐camphor

In this article, a new alicyclic‐functionalized diamine, 1,3‐bis(4‐aminophenoxymethylene)‐1,2,2‐trimethylclopentane (BAMT) was successfully synthesized starting from natural —(D)‐camphor through four reaction steps of oxidation to offer a dicaboxylic acid, reduction to offer a diol, nucleophilic substitution to give a dinitro compound and then reduction to give the final diamine. Two alicyclic‐containing polyimides were prepared by polycondensing BAMT with 3,3′,4,4′‐biphenyltetracarboxylic dianhydride (BPDA) and 4,4′‐oxydiphthalicanhydride (ODPA), respectively. For the studies of the structure–property relationships of the polyimides, one aromatic polyimide of 4, 4′‐oxydianiline (ODA) polycondensed with ODPA was prepared in comparison. The alicyclic‐containinig polyimides PI (BPDA‐BAMT) and PI (ODPA‐BAMT) maintain good thermal properties with glass transition temperatures (T_g) of 257°C and 240°C, and temperatures at 5% weight loss (T₅) of 443°C and 436°C in nitrogen, respectively. The alicyclic polyimides exhibit tensile strengths of 91.9–133 MPa, Young's moduli of 2.75—3.24 GPa, and elongations at break of 5.6–18%. Compared with the aromatic polyimide PI (ODPA‐ODA), PI (ODPA‐BAMT) shows improved transparency with the UV‐Vis transmittance at 500 nm over 80%. In addition, PI (ODPA‐BAMT) displays better solubility than PI (ODPA‐ODA), which has been confirmed by the bigger d‐spacing value of PI (ODPA‐BAMT) than that of PI (ODPA‐ODA) calculated from the Wide‐angle X‐ray Diffraction spectra. This study indicates that the renewable forestry compound, such as natural —(D)‐camphor, could be a good origin for the structural designing and preparation of alicyclic‐containing polyimides with outstanding combined features suitable for advanced microelectronic and optoelectronic applications. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Preparation and properties of organo‐soluble polyimides based on 4,4′‐diamino‐3,3‐dimethyldiphenylmethane and conventional dianhydrides

4,4′‐Diamino‐3,3′‐dimethyldiphenylmethane was used to prepare polyimides in an attempt to achieve good organo‐solubility and light color. Polyimides based on this diamine and three conventional aromatic dianhydrides were prepared by solution polycondensation followed by chemical imidization. They possess good solubility in aprotonic polar organic solvents such as N‐methyl 2‐pyrrolidone, N,N‐dimethyl acetamide, and m‐cresol. Polyimide from 4,4′‐diamino‐3,3′‐dimethyldiphenylmethane and diphenylether‐3,3′,4,4′‐tetracarboxylic acid dianhydride is even soluble in common solvents such as tetrahydrofuran and chloroform. Polyimides exhibit high transmittance at wavelengths above 400 nm. The glass transition temperature of polyimide from 4,4′‐diamino‐3,3′‐dimethyldiphenylmethane and pyromellitic dianhydride is 370°C, while that from 4,4′‐diamino‐3,3′‐dimethyldiphenylmethane and diphenylether‐3,3′,4,4′‐tetracarboxylic acid dianhydride is about 260°C. The initial thermal decomposition temperatures of these polyimides are 520–540°C. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 72: 1299–1304, 1999     

Ambipolar and multi‐electrochromic polyimides based on N,N‐di(4‐aminophenyl)‐N′,N′‐diphenyl‐4,4′‐oxydianiline

A series of novel aromatic polyimides were synthesized from N,N‐di(4‐aminophenyl)‐N′,N′‐diphenyl‐4,4′‐oxydianiline and aromatic tetracarboxylic dianhydrides through a conventional two‐step procedure. Most of the polyimides exhibited reasonable solubility in organic solvents and could afford robust films via solution casting. The polyimides exhibited high thermal stability, with glass transition temperatures in the range 227–273 °C and 10% weight‐loss temperatures in excess of 550 °C. All the polyimide films showed ambipolar redox and multi‐electrochromic behaviors. They exhibited two reversible oxidation redox couples at 0.94–0.98 and 1.09–1.12 V versus Ag/AgCl in acetonitrile solution. A coupling reaction between the radical cations of the pendent triphenylamine units occurred during the oxidative process forming a tetraphenylbenzidine structure which resulted in an additional redox state and color change. © 2014 Society of Chemical Industry     

Preparation of poly(amic acid) and polyimide derived from 3,3′,4,4′‐benzophenonetetracarboxylic dianhydride with different diamines by microwave irradiation

Polycondensation‐type poly(amic acid) (PAA) was synthesized with 3,3′,4,4′‐benzophenonetetracarboxylic dianhydride as a dianhydride monomer and 4,4′‐diaminodiphenylmethane and 4,4′‐oxydianiline as diamine monomers under microwave irradiation in dimethylformamide. Then, PAA was used to make polyimide (PI) by imidization at a low temperature. The structure and performance of the polymers were characterized with Fourier transform infrared (FTIR), proton nuclear magnetic resonance (¹H‐NMR), viscosity, X‐ray diffraction (XRD), and thermogravimetry (TG) curve analyses. The FTIR spectra of the polymers showed characteristic peaks of PI around 1779 and 1717 cm^?1. The ¹H‐NMR spectrum of PAA indicated a singlet at 6.55 ppm assigned to ? NHCO? and a singlet at 10.27 ppm assigned to carboxylic acid protons. The XRD spectrum demonstrated that the obtained PI had a low‐order aggregation structure with a d‐spacing of 0.5453 nm. The TG results revealed that the PI was thermally stable with 10% weight loss at 565°C in an N₂ atmosphere. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 2008     

Organosoluble and light‐colored fluorinated polyimides derived from 5,5′‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy) phenyl]‐4,7‐methanohexahydroindan

A novel bis(ether amine) monomer, 5,5′‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy)phenyl]‐4,7‐methanohexahydroindan ( 2 ), was synthesized through the nucleophilic aromatic substitution reaction of 5,5′‐bis‐(4‐hydroxyphenyl)‐4,7‐methanohexahydroindan with 2‐chloro‐5‐nitrobenzotrifluoride to yield the intermediate dinitro compound, followed by catalytic reduction with hydrazine and Pd/C. A series of polyimides were synthesized from 2 and various aromatic dianhydrides using a standard two‐stage process with chemical or thermal imidization of poly(amic acid). All of these polymer films were soluble in amide‐type solvents above 10% w/v, had tensile strengths of 97–117 MPa, and the 10% weight loss temperature was above 464 °C with their residues exceeding 46% at 800 °C in nitrogen. Compared with the non‐fluorinated polyimides, the fluorinated series were observed to have lower dielectric constants (2.92–3.28 at 1 MHz) and lower moisture absorptions (0.15–0.43 wt%) as well as lower color intensity and better solubility. Copyright © 2006 Society of Chemical Industry     

Synthesis and characterization of novel aromatic polyamides derived from 2,2′‐bis(p‐phenoxyphenyl)‐4, 4′‐diaminodiphenyl ether

BACKGROUND: Wholly aromatic polyamides (aramids) are high‐performance polymeric materials with outstanding heat resistance and excellent chemical stabilities due to chain stiffness and intermolecular hydrogen bonding of amide groups. Synthesis of structurally well‐designed monomers is an effective strategy to prepare modified forms of these aramids to overcome lack of organo‐solubility and processability limitations. RESULTS: A novel class of wholly aromatic polyamides was prepared from a new diamine, namely 2,2′‐bis(p‐phenoxyphenyl)‐4,4′‐diaminodiphenyl ether (PPAPE), and two simple aromatic dicarboxylic acids. Two reference polyamides were also prepared by reacting 4,4′‐diaminodiphenyl ether with the same comonomers under similar conditions. M?_w and M?_n of the resultant polymers were 8.0 × 10⁴ and 5.5 × 10⁴ g mol^?1, respectively. Polymers resulting from PPAPE exhibited a nearly amorphous nature. These polyamides exhibited excellent organo‐solubility in a variety of polar solvents and possessed glass transition temperatures up to 200 °C. The 10% weight loss temperatures of these polymers were found to be up to 500 °C under a nitrogen atmosphere. The polymers obtained from PPAPE could be cast into transparent and flexible films from N,N‐dimethylacetamide solution. CONCLUSION: The results obtained show that the new PPAPE diamine can be considered as a good monomer to enhance the processability of its resultant aromatic polyamides while maintaining their high thermal stability. The observed characteristics of the polyamides obtained make them promising high‐performance polymeric materials. Copyright © 2009 Society of Chemical Industry     

Synthesis and characterization of organosoluble and transparent polyimides derived from trans‐1,2‐bis(3,4‐dicarboxyphenoxy)cyclohexane dianhydride

A novel dianhydride, trans‐1,2‐bis(3,4‐dicarboxyphenoxy)cyclohexane dianhydride (1,2‐CHDPA), was prepared through aromatic nucleophilic substitution reaction of 4‐nitrophthalonitrile with trans‐cyclohexane‐1,2‐diol followed by hydrolysis and dehydration. A series of polyimides (PIs) were synthesized from one‐step polycondensation of 1,2‐CHDPA with several aromatic diamines, such as 2,2′‐bis(trifluoromethyl)biphenyl‐4,4′‐diamine (TFDB), bis(4‐amino‐2‐trifluoromethylphenyl)ether (TFODA), 4,4′‐diaminodiphenyl ether (ODA), 1,4‐bis(4‐aminophenoxy)benzene (TPEQ), 4,4′‐(1,3‐phenylenedioxy)dianiline (TPER), 2,2′‐bis[4‐(3‐aminodiphenoxy)phenyl]sulfone (m‐BAPS), and 2,2′‐bis[4‐(4‐amino‐2‐trifluoromethylphenoxy)phenyl]sulfone (6F‐BAPS). The glass transition temperatures (T_gs) of the polymers were higher than 198°C, and the 5% weight loss temperatures (T_d5%s) were in the range of 424–445°C in nitrogen and 415–430°C in air, respectively. All the PIs were endowed with high solubility in common organic solvents and could be cast into tough and flexible films, which exhibited good mechanical properties with tensile strengths of 76–105 MPa, elongations at break of 4.7–7.6%, and tensile moduli of 1.9–2.6 GPa. In particular, the PI films showed excellent optical transparency in the visible region with the cut‐off wavelengths of 369–375 nm owing to the introduction of trans‐1,2‐cyclohexane moiety into the main chain. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42317.     

Syntheses and properties of novel polyimides derived from 2‐(4‐Aminophenyl)‐5‐aminopyrimidine

2‐(4‐Aminophenyl)‐5‐aminopyrimidine (4) is synthesized via a condensation reaction of vinamidium salts and amidine chloride salts, followed by hydrazine palladium catalyzed reduction. A series of novel homo‐ and copolyimides containing pyrimidine unit are prepared from the diamine and 1,4‐phenylenediamine (PDA) with pyromellitic dianhydride (PMDA) or 3,3′,4,4′‐biphenyl tertracarboxylic dianhydride (BPDA) via a conventional two‐step thermal imidization method. The poly(amic acid) precursors had inherent viscosities of 0.97–4.38 dL/g (c = 0.5 g/dL, in DMAc, 30°C) and all of them could be cast and thermally converted into flexible and tough polyimide films. All of the polyimides showed excellent thermal stability and mechanical properties. The glass transition temperatures of the resulting polyimides are in the range of 307–434°C and the 10% weight loss temperature is in the range of 556–609°C under air. The polyimide films possess strength at break in the range of 185–271 MPa, elongations at break in the range of 6.8–51%, and tensile modulus in the range of 3.5–6.46 GPa. The polymer films are insoluble in common organic solvents, exhibiting high chemical resistance. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 5871–5876, 2006     

Organosoluble polyimides derived from asymmetric 2‐substituted‐and 2,2′,6‐trisubstituted‐4,4′‐oxydianilines

We report a new method for the preparation of asymmetric diamines using 4,4′‐oxydianiline (4,4′‐ODA) as the starting material. By controlling the equivalents of bromination agent, N‐bromosuccinimide, we were able to attach bromide and phenyl substituents at the 2‐ or 2,2′,6‐positions of 4,4′‐ODA. Thus, four new asymmetric aromatic diamines, 2‐bromo‐4,4′‐oxydianiline (6), 2,2′,6‐tribromo‐4,4′‐oxydianiline (7), 2‐phenyl‐4,4′‐oxydianiline (8) and 2,2′,6‐triphenyl‐4,4′‐oxydianiline (9), were synthesized by this method. Their structural asymmetry was confirmed using ¹H NMR spectroscopy. Asymmetric polyimides (PI10–PI13) were prepared from these diamines and three different dianhydrides (pyromellitic dianhydride (PMDA), 3,3′,4,4′‐biphenyltetracarboxylic dianhydride and 2,2‐bis(3,4‐dicarboxyphenyl)hexafluoropropane dianhydride) in refluxing m‐cresol. The formed polyimides, except PI10a derived from 6 and PMDA, were all soluble in m‐cresol without premature precipitation during polymerization. These polyimides with inherent viscosity of 0.41–0.96 dL g^?1, measured at a concentration of 0.5 g dL^?1 in N‐methyl‐2‐pyrrolidone at 30 °C, can form tough and flexible films. Because of the structural asymmetry, they also exhibited enhanced solubility in organic solvents. Especially, polyimides PI11a and PI13a derived from 7 and 9 with rigid PMDA were soluble in various organic solvents at room temperature. The structural asymmetry of the prepared polyimides was also evidenced from ¹H NMR spectroscopy. In the ¹H NMR spectrum of PI11a, the protons of pyromellitic moiety appeared in an area ratio of 1:2:1 at three different chemical shifts, which were assigned to head‐to‐head, head‐to‐tail and tail‐to‐tail configurations, respectively. These polyimides also exhibited good thermal stability. Their glass transition temperatures ranged from 297 to 344 °C measured using thermal mechanical analysis. © 2013 Society of Chemical Industry     

Preparation and properties of polyimides based on bis[3,5‐dimethyl‐4‐(4‐aminophenoxy)phenyl]methane

A series of polyimide (PI) thin films were synthesized based on bis[3,5‐dimethyl‐4‐(4‐aminophenoxy)phenyl]methane and conventional aromatic dianhydrides. The structures and properties of the thin films were measured with Fourier transform infrared, NMR, thermogravimetric analysis, dynamic mechanical analysis, and impedance analysis. The PI films exhibited glass‐transition temperatures in the range of 211–300°C and possessed initial thermal decomposition temperature reaching up to 457–482°C in air and 461–473°C in nitrogen. Some PI films had high solubility in organic solvents such as 1‐methyl‐2‐pyrrolidinone, N,N‐dimethylformamide, N,N‐dimethylacetamide, dimethyl sulfoxide, m‐cresol, tetrahydrofuran, and CHCl₃. The mechanical properties of these films were also examined. The dielectric constants of the films were in the range of 2.8–3.3 at 25°C. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci 104: 1265–1270, 2007     

Synthesis and properties of polyamides based on 5,5′‐bis[4‐(4‐aminophenoxy)phenyl]‐hexahydro‐4,7‐methanoindan

A new diamine 5,5′‐bis[4‐(4‐aminophenoxy)phenyl]‐hexahydro‐4,7‐methanoindan ( 3 ) was prepared through the nucleophilic displacement of 5,5′‐bis(4‐hydroxylphenyl)‐hexahydro‐4,7‐methanoindan ( 1 ) with p‐halonitrobenzene in the presence of K₂CO₃ in N,N‐dimethylformamide (DMF), followed by catalytic reduction with hydrazine and Pd/C in ethanol. A series of new polyamides were synthesized by the direct polycondensation of diamine 3 with various aromatic dicarboxylic acids. The polymers were obtained in quantitative yields with inherent viscosities of 0.76–1.02 dl g⁻¹. All the polymers were soluble in aprotic dipolar solvents such as N,N‐dimethylacetamide (DMAc) and N‐methyl‐2‐pyrrolidone (NMP), and could be solution cast into transparent, flexible and tough films. The glass transition temperatures of the polyamides were in the range 245–282 °C; their 10% weight loss temperatures were above 468 °C in nitrogen and above 465 °C in air. © 2000 Society of Chemical Industry     

Synthesis and properties of novel polyimides from 3‐(4‐aminophenylthio)‐N‐aminophthalimide

A novel, asymmetric diamine, 3‐(4‐aminophenylthio)‐N‐aminophthalimide, was prepared from 3‐chloro‐N‐aminophthalimide and 4‐aminobenzenethiol. The structure of the diamine was determined via IR and ¹H‐NMR spectroscopy and elemental analysis. A series of polyimides were synthesized from 3‐(4‐aminophenylthio)‐N‐aminophthalimide and aromatic dianhydrides by a conventional two‐step method in N,N‐dimethylacetamide and by a one‐step method in phenols. These polyimides showed good solubility in 1‐methyl‐2‐pyrrolidinone, m‐cresol, and p‐chlorophenol, except polyimide from pyromellitic dianhydride, which was only soluble in p‐chlorophenol. The 5% weight loss temperatures of these polyimides ranged from 460 to 498°C in air. Dynamic mechanical thermal analysis indicated that the glass‐transition temperatures of the polyimides were in the range 278–395°C. The tensile strengths at break, moduli, and elongations of these polyimides were 146–178 MPa, 1.95–2.58 GPa, and 9.1–13.3%, respectively. Compared with corresponding polyimides from 4,4′‐diamiodiphenyl ether, these polymers showed enhanced solubility and higher glass‐transition temperatures. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Effects of 4,4′‐diaminodiphenyl ether on the structures and properties of isocyanate‐based polyimide foams

A series of thermal insulation, acoustic absorption isocyanate‐based lightweight polyimide (PI) foams with 4,4′‐diaminodiphenyl ether (ODA) units were prepared from polyaryl polymethylene isocyanate (PAPI) and the esterification solution derived from pyromellitic dianhydride (PMDA) and ODA. The structures and properties of the PI foams prepared with different molar ratio of ODA/PMDA were investigated in detail. The results show that the ODA units have great influence on the foam properties. With the increase of the ODA units, the density decreases firstly and then increases. When the molar ratio of ODA/PMDA is 3/10, the foam reaches the minimum density (13.7 kg/m³). Moreover, with increasing the ODA units, the acoustic absorption properties increase firstly and then decrease owing to the variation of the average cell diameter of the PI foams. All PI foams show excellent thermal stability, and the 5% and 10% weight loss temperature are in the range of 250–270 °C and 295–310 °C, respectively. In addition, the PI foams present low thermal conductivity and thermal diffusivity. Furthermore, the mechanical property was also evaluated and the compressive strength of the PI foams is in the range of 33.0–45.7 kPa. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46029.