无热处理高硬度高耐磨性化学镀镍磷合金

研究了一种无需后续热处理且具有高硬度、高耐磨性的化学镀镍磷合金镀层.采用乳酸和乙酸钠作为络合剂，在理论上完全络合镍离子的前提下，通过改变化学镀镍溶液中乳酸和乙酸钠之间的比例，研究了镀速、镀层表面显微硬度以及镀层耐磨性的变化情况,结果表明,随着乳酸比例的增加，镀速出现先升高后下降的现象，并在n(乳酸提供的配位原子)：n(乙酸钠提供的配位原子)为4∶6时，镀速达到最大值，由此溶液得到的镀层，其表面显微硬度在热处理前达到了HV820，且镀层表面平整、致密，具有很高的耐磨性.     

Effect of hydrogen on the friction and wear of Ni-P coatings

The effects of charging and outgassing on the friction and wear of Ni-P amorphous and nanocrystalline coatings were studied under ambient humidity and temperature.The results indicate that hydrogen charging can greatly decrease the volume loss during friction and increase the wear durability.However,the wear durability can be restored after outgassing.There are many cracks on the brittle nanocrystalline before charging,and no crack appears after charging,but there are only a few cracks on the outgassed s...     

镍基纳米碳管复合镀层的摩擦磨损性能

利用化学镀方法制备镍基纳米碳管复合镀层,用扫描电镜分析了镀层的表面形貌,并用销-盘式磨损试验机研究了复合镀层在干摩擦条件下的摩擦磨损行为.结果表明:纳米碳管均匀地嵌入在镍基体中,镍基纳米碳管复合镀层具有优良的耐磨性能;由于纳米碳管的自润滑作用,复合镀层的摩擦系数随着纳米碳管体积分数的增加而逐渐降低.     

钡铁氧体表面化学镀Ni-P合金的制备及性能

为提高钡铁氧体的吸波性能,以钡铁氧体为芯材,采用化学镀的方法制备表面包覆Ni-P镀层的钡铁氧体复合粒子.并利用XRD、SEM、EDS及矢量网络分析仪对其晶体结构、表面形貌、成分、电磁吸收性能进行分析.结果表明:钡铁氧体表面包覆完整的Ni-P合金镀层,化学镀工艺显著改善材料的电磁性能,并提高材料对电磁波的吸收能力,镀后复合粒子在2～18GHz频段内,最大反射率为-24.3dB,大于-10dB的吸收频带宽约2.8GHz.     

聚四氟乙烯、石墨等粒子与镍磷化学共沉积复合镀层的研究

由化学镀得到的聚四氟乙稀、石墨、氟化石墨、硫化钼及氟化钙粒子等与镍磷一起沉积的五类自润滑复合镀层。在环块试验机及销盘试验机上研究了其摩擦磨损特性。得出其摩擦系数与抗磨性、试验负荷、粒子含量和镀层的热处理与否有关。与淬火GCr15和氮化过的钢相比,自润滑复合镀层具有低的摩擦系数,比之纯Hi-p镀层其摩擦系数也较低。 由AES和SEM对磨损表面进行分析,当表面的Ni-p逐步磨去时,固相润滑粒子逐步暴露。对细粒子来说(如小于2μm的PTFE)能在对磨件表面形成转移膜,降低摩擦系数,其磨损率略有提高。但如粒子过大(如大于2μm的石墨)则石墨粒子压延并抛光,或碎裂脱落,也能转移并降低摩擦,但使磨损量大为增加。     

化学镀Ni-P合金的热力学及动力学研究

将Ｂｏｃｋｒｉｓ方程应用于化学镀ＮｉＰ合金铁沉积反应当中,通过测定单位时间、单位面积的沉积量,从而求得化学Ｎｉ－Ｐ合金呱应的热力学函数△Ｇθｄｅｐ、△Ｈ＾θｄｅｐ、△Ｓ＾θｄｅｐ。此外,通过各种因素对化学镀Ｎｉ－Ｐ合金沉积速度的影响的试验,分别确定上述诸因素所对应的动力学参数,从而得出了镀液沉积速度的经验方程。     

化学镀法制备Ni—P／Al2O3特种陶瓷及性能

采用化学镀方法在平均粒径为200nm的Al2O3粉体表面镀覆Ni-P合金,制备出了Ni-P／Al2O3复合粉体,再利用无压烧结将此种复合粉体制备成氧化铝基特种陶瓷。这一方法不仅降低了烧结温度,也进一步提高了陶瓷的性能,尤其是在提高韧性方面。结果表明,粉体镀层为晶态,主要由NiP2相和NiP相组成,镀层中含镍量为9．32％,含磷量为2．38％。为低磷合金镀层,制备特种陶瓷所需的烧结温度由制备单一氧化铝陶瓷所需的1700℃降低至1350℃;断裂韧性也从单一Al2O3陶瓷的3．0MPa·m^1/2提高到6．91MPa·m^1/2,增加了130．3％;耐磨性与纯氧化铝陶瓷相当。     

Tribological properties of electroless Ni-P-SiC composite coatings in rolling/sliding contact under boundary lubrication

Ni-P-SiC composite coatings were prepared under a given bath composition and operation parameters of electroless plating. The tribological properties of the Ni-P-SiC composite coatings after annealing at 400℃ for 1 h were tested in rolling/sliding contact under boundary lubrication condition using a two-roller tribometer. The measurement contained friction coefficient, contact surface temperature, contact electrical resistance, and wear rate of the Ni-P-SiC composite coatings under various slide to roll ratios, loads, and rolling speeds. For the simultaneous examination of the effect of the chosen parameters on the tribological properties of the Ni-P-SiC composite coatings, an orthogonal regression experimental design method was used.     

纳米粒子对复合化学镀镍层性能的影响

在化学镀镍溶液中添加银纳米粒子,在钢铁基体上制备Ni-P／Ag纳米复合镀层。研究了添加银纳米粒子前后镀液的镀速、镀层的厚度、镀态和热处理态的硬度变化,分析了银纳米粒子对镀层性能的影响。研究结果表明,银纳米粒子使得镀层的沉积速率加快,厚度增加,硬度提高。镀层的表面形貌也由于银纳米粒子的存在而发生了改变。     

铝合金化学镀镍磷合金结构和性能

针对质子交换膜燃料电池双极板的需要，以铝合金为基体材料，采用碱性和酸性双溶液体系化学镀镍磷合金．采用电子探针方法测定了镀层中镍磷含量，X衍射方法研究了热处理对镀层结构的影响，伏安法研究了热处理对镀层耐蚀性的影响．试验结果表明，热处理明显影响镀层的结构和耐蚀性，对于P含量为12．1％（质量）的镍磷合金镀层，经过200—250℃热处理后，晶化不明显但耐蚀等性能明显改善，可以用作质子交换膜燃料电池双极板．