有关铝合金焊接的文献

正6061铝合金激光深熔焊等离子体光谱特征与气孔的相关性/李坤,等.焊接学报,2015,36(7):72-76.采用光纤激光器对6061铝合金进行焊接,获得了表面成形良好的焊缝。利用光谱仪和高速摄像机获取等离子体的光谱和图像,分析了激光深熔焊时等离子体的光谱特征,讨论了光谱强度及其波动程度与焊缝气孔     

光纤激光焊接A356铝合金过程气孔敏感性

为减少激光深熔焊接铝合金过程中产生的冶金型气孔和小孔型气孔,达到提高工件力学性能的目的,系统分析激光功率、焊接速度以及离焦量等工艺参数分别对两种气孔造成的影响,同时观察不同焊接参数下小孔上方的金属蒸汽羽烟形状与波动情况,以反映焊接过程中小孔的稳定性。结果显示,增加激光功率或减小激光光斑半径时,小孔上方金属蒸汽羽烟波动剧烈,形状和大小都极不稳定,间接反映小孔的稳定性更差,因此在焊缝根部产生更多小孔型气孔。当由激光能量密度变化引起的小孔深宽比增高时,小孔内部坍塌的可能性升高,并在焊缝中留下更多的气孔。当激光功率为5 kW、离焦量为0、焊接速度为2.0 m/min时,气孔率达到最小值。     

双光束激光填丝焊工艺对铝合金焊接气孔率的影响

以LF6铝合金为材料,CO2激光为热源,开展了双光束激光填丝焊气孔特性分析.与单光束激光填丝焊及双光束自熔焊相比,双光束激光填丝焊能够抑制气孔的产生,尤其是并行双光束激光焊抑制气孔效果更明显.在此基础上进一步分析了保护气体成分和激光能量对焊接气孔率的影响.结果表明,采用氦气保护时,等离子体对激光的屏蔽作用小,能够稳定焊接过程;激光功率过大或者过小都会导致匙孔的不稳定,造成焊缝气孔率增加.     

激光扫描焊接工艺对铝合金焊接气孔率的影响

以6061铝合金为研究对象,研究了激光扫描焊接过程中光束的扫描轨迹、扫描幅度与扫描频率对6061铝合金气孔产生的影响规律.结果表明,与激光非扫描焊接相比,采用光束垂直于焊缝、平行于焊缝和圆形运动3种不同轨迹的扫描方式均有利于抑制铝合金激光焊接气孔的产生,且以光束为圆形轨迹的扫描方式为最佳.光束的扫描幅度及扫描频率对气孔的产生也有重要的影响.采用光束为圆形轨迹的扫描方式,当扫描幅度大于0.65 mm、扫描频率在100~220 Hz范围内时,气孔率可控制在0.5%以内.气孔的产生与焊缝形状有关,减少焊缝深宽比有利于气孔的抑制.     

铝合金激光深熔焊气孔形成机理与控制技术

观察了铝合金激光深熔焊气孔的分布特征和形貌特征,深入分析了气孔的形成机理,研究了双光点能量分布的激光对铝合金激光深熔焊气孔的控制效果.结果表明,铝合金激光深熔焊焊缝中存在分布特征和形貌特征不同的两类气孔,即冶金类气孔和工艺类气孔.冶金类气孔的形成与氢在熔池中的析出、聚集与合并有关,而工艺类气孔产生的根本原因是焊接过程中匙孔的瞬间失稳.采用双光点能量分布的激光焊接铝合金可以扩大匙孔张口和根部直径,改善匙孔壁的波动状态,增强匙孔的稳定性,从而减少工艺类气孔的产生,但对冶金类气孔没有明显影响.     

光纤激光焊接A356铝合金过程气孔敏感性（英文）

为减少激光深熔焊接铝合金过程中产生的冶金型气孔和小孔型气孔,达到提高工件力学性能的目的,系统分析激光功率、焊接速度以及离焦量等工艺参数分别对两种气孔造成的影响,同时观察不同焊接参数下小孔上方的金属蒸汽羽烟形状与波动情况,以反映焊接过程中小孔的稳定性。结果显示,增加激光功率或减小激光光斑半径时,小孔上方金属蒸汽羽烟波动剧烈,形状和大小都极不稳定,间接反映小孔的稳定性更差,因此在焊缝根部产生更多小孔型气孔。当由激光能量密度变化引起的小孔深宽比增高时,小孔内部坍塌的可能性升高,并在焊缝中留下更多的气孔。当激光功率为5 k W、离焦量为0、焊接速度为2.0 m/min时,气孔率达到最小值。     

铝合金双光束激光焊接过程稳定性分析

从成形、气孔、熔深的波动、激光匙孔、光致等离子体、飞溅等方面研究了铝合金高功率单光束激光和双光束激光焊接过程的稳定性。结果表明,在相同工艺参数下,双光束激光焊缝表面成形明显优于单光束,熔深的波动较单光束小;在相同工艺参数及相同熔深条件下,双光束焊缝气孔率较单光束小,小孔及等离子体的波动周期较单光束长,面积波动变异系数较单光束小,飞溅较单光束更加细小均匀。     

压铸AZ91D镁合金氩弧焊缝气孔及消除措施研究

对压铸AZ91D镁合金进行GTAW焊接,采用扫描电子显微镜观察焊缝气孔的形貌、类型及分布特征,研究气孔的形成机制,讨论热输入对焊缝气孔的影响。结果表明,自熔焊焊缝气孔问题严重,微小气孔主要集中分布在焊缝近表皮和熔合线附近,宏观气孔主要分布在焊缝中部区域。随热输入的增大,最大宏观气孔尺寸及气孔率均增大。添加填充材料,能够明显降低焊缝气孔率,减小气孔尺寸,但不能彻底消除焊缝气孔。     

TC4钛合金光纤激光摆动焊抑制小孔型气孔的原因分析

采用光纤激光器对8 mm厚TC4钛合金板进行振镜摆动焊接,采用光谱仪和高速摄像机采集等离子体的光谱、图像及小孔的图像,分析摆动焊接抑制小孔型气孔的原因.结果表明,摆动光束对抑制钛合金小孔型焊接气孔具有显著作用;光束未摆动焊接时,焊缝中的气孔率达9.8%;光束摆动后焊缝中的气孔率均降低,其中焊接参数为5 kW、2 m/min,摆动参数为80 Hz、0.5 mm时,小孔形气孔被完全抑制.与光束未摆动相比,光束摆动焊接的小孔稳定性显著增加,其原因是光束摆动提高了光束与熔池液面的接触面积,金属蒸发增强,驱动小孔张开的径向力和轴向力得以增加.     

铌粉添加量对铝合金激光-电弧复合焊接气孔率的影响

基于6061铝合金板开展激光-电弧复合焊接工艺试验,结合不同铌粉添加量下的焊缝气孔率特征,分析添加铌粉对焊缝气孔的影响机理,获得铌粉添加量的合理范围。结果表明,添加铌粉可以抑制铝合金激光-电弧复合焊接气孔产生,降低气孔率;当铌粉线添加量为8.84 mg/cm时,焊缝横截面气孔率最低,为0.01%;由于铌粉增加了激光吸收率与熔池金属密度,促进了气泡形核与长大,从而促使气泡逸出,减少气孔数量。     

铝合金激光-MIG复合填丝焊稳定性分析

通过与铝合金激光-MIG复合焊方法相对比,主要研究了铝合金激光-MIG复合填丝焊的焊缝成形、熔深稳定性、余高稳定性、焊缝气孔率、激光匙孔特征、等离子体特征. 试验结果表明,在合适的工艺参数条件下,铝合金激光-MIG复合填丝焊焊接过程稳定,焊缝成形良好,额外填入的焊丝可以连续稳定地过渡到熔池中,激光匙孔具有明显的形成、长大、湮灭周期性变化特征;相同工艺参数条件下,铝合金激光-MIG复合填丝焊的焊缝熔深稳定性、余高稳定性与激光-MIG复合焊相当,激光匙孔开口面积约增加15.34%,等离子体+电弧总面积约增加1.95%.     

Keyhole formation and its characteristics in laser welding mode transition

Keyhole is the most important characteristic for laser deep penetration welding, and its formation indicates the beginning of laser deep penetration welding mode. The keyhole developing process was analyzed and the keyhole formation time was calculated according to welding speed and the length of weld bead formed in the keyhole formation process. The results showed that the keyhole forms in 40-70 ms at different rate of change of laser power. In laser deep penetration welding process, the variation of light intensity radiated by laser induced plasma can identify the keyhole formation, but it can not be used to estimate the keyhole formation time because of delay effect.     

A study on the porosity of CO2 laser welding of titanium alloy

0IntroductionTitanium alloys are increasingly applied in aeronauticindustry because of its higher strength to weight ratio thansteel and superior fatigue performance to aluminum alloy.At the same time there are many newtitanium-based alloysoccurring,such as Ti3Al-Nb titanium aluminide[1].Weldsof titanium alloy are prone to porosity,presenting a poten-tial problem for many application requiring sealing,corro-sion and fatigue resistance and good fracture toughness.Many studies have demonstrate…     

铝合金中厚板高功率激光搅拌焊气孔缺陷工艺调控

高功率激光焊接为铝合金中厚板高质高效焊接提供了有效手段,然而面临焊缝气孔多发的问题. 文中开展了铝合金中厚板高功率激光搅拌焊接气孔缺陷的工艺调控研究,阐明了搅拌振幅和搅拌频率对接头气孔率的影响,并提出了工艺参数优化方法. 结果表明,搅拌振幅主要影响光束运动轨迹横向分布和小孔开口面积;搅拌频率主要影响激光光束运动速度和对后方熔池的搅拌次数;搅拌振幅和频率越大,气孔抑制效果越明显,但焊缝熔深难以满足应用要求;通过控制光束运动轨迹和能量密度,可以实现工艺参数的设计,获得大熔深、少气孔的最佳工艺区间,最终得到熔深高达6.4 mm的少气孔焊接接头.     

铝合金厚板激光扫描填丝焊接气孔抑制

为减少大厚板5A06铝合金激光焊接缺陷,提高焊接过程稳定性,采用激光光束以一定方式运动的扫描焊接的新焊接方法,研究了激光束不同的运动轨迹、幅度、频率对铝合金激光深熔焊接焊缝气孔率的影响,并在焊接坡口设计优化基础上应用窄间隙扫描激光填丝焊接技术进行130 mm厚5A06铝合金焊接试验. 结果表明,采用圆形扫描方式,当激光光束的扫描幅度大于1 mm,扫描频率选择最高频率附近时,能够大幅降低焊缝气孔率;采用窄间隙激光扫描填丝的焊接方法,获得了焊缝平均气孔率1%,无侧壁未熔合、层间未熔合、裂纹等焊接缺陷的130 mm厚5A06铝合金优质焊接接头.     

1420铝锂合金激光焊接气孔形成机理

1420铝锂合金与传统的2000、7000系列铝合金相比，密度低12％，弹性模量高8％左右，具有优异的抗腐蚀性和高温性能。激光焊接作为一种快速高效的焊接方法，在焊接1420铝锂合金时存在一个问题，即具有严重的气孔倾向。针对1420铝锂合金激光焊接中气孔产生的原因进行了比较系统的分析。分析认为，表层物质是焊接过程中氢的主要来源，一定要采用适当的方法进行彻底的清除，而Mg、Li等合金元素不仅增加了熔池吸氢倾向，还增加了匙孔末端的不稳定性，应该采用合适的熔透模式，改善熔池的流动，将这种不稳定性降到最低。     

Characteristic of laser-MIG hybrid welding with filling additional cold wire for aluminum alloy

The weld appearance,deposition rate,welding efficiency,stability of arc,laser keyhole characteristic,and weld property were studied by using a novel laser-MIG hybrid welding process with filling wire of aluminum alloy. The results were also compared with those by conventional laser-MIG hybrid welding process. It was found that with the suitable process parameters this novel welding process for aluminum alloy was stable and final weld bead had fine appearance. Compared to conventional laser-MIG hybrid welding process,during this novel welding process the stability of arc,the laser keyhole characteristic and the weld property were similar,while the keyhole cycle frequency and keyhole opening area had differences of 1. 23% and 15. 34%,respectively,and the welding efficiency increased by about 31% without increasing heat input.     

几种常见合金的激光扫描焊接特性及研究现状

激光扫描焊接是一种高效的新型激光焊接技术,具有独特的激光束定位方式、扫描范围广、灵活性高、工作距离长等优点,相比于传统激光焊接,其多点焊接的特性能在很大程度上提升焊接效率.概述了激光扫描焊接技术的工作原理和分类,重点阐述铝合金、镁合金、钛合金、铜及铜合金、铝-钢异质合金几种常用合金的激光扫描焊接特性及研究现状.扫描激光...