Vanadium-based ohmic contacts to n-type Al<Subscript>0.6</Subscript>Ga<Subscript>0.4</Subscript>N

Four vanadium-based contacts to n-type Al_0.6Ga_0.4N were compared in this work. Both V/Al/Pd/Au and V/Al/V/Au contacts with optimized layer thicknesses provided lower specific-contact resistances than did the previously reported V/Al/Pt/Au ohmic contact. Specific contact resistances of the V/Al/Pd/Au (15 nm/85 nm/20 nm/95 nm) and V/Al/V/Au (15 nm/85 nm/20 nm/95 nm) contacts were 3×10⁻⁶ Ω·cm² and 4×10⁻⁶ Ω·cm², respectively. On the other hand, an analogous V/Al/Mo/Au contact never became ohmic, even after it was annealed at 900°C for 30 sec. Compared to the V/Al/Pd/Au contact, the V/Al/V/Au contact required a less severe annealing condition (30 sec at 700°C instead of 850°C). The V/Al/V/Au contact also provided a smoother surface, with a root-mean-square (RMS) roughness of 39 nm.     

Electrical characteristics of thermally stable Ru and Ru/Au ohmic contacts to surface-treated p-type GaN

The electrical and thermal properties of Ru and Ru/Au ohmic contacts on two-step-surface-treated p-GaN have been investigated using current-voltage (I–V) measurements and Auger electron spectroscopy. It is shown that annealing at 700°C for 2 min in a flowing N₂ atmosphere improves the I–V characteristics of the contacts. For example, the annealed Ru and Ru/Au schemes produce a specific contact resistance of 3.4 (±0.9)×10⁻³ and 1.2 (±1.1)×10⁻³ Ωcm², respectively. It is also shown that annealing results in a large reduction (by ∼100 meV) in the Schottky barrier heights of the Ru and Ru/Au contacts, compared to the as-deposited ones. The electrical properties of the two-step-surface-treated Ru/Au contacts are compared with those of the conventionally treated contacts.     

Ohmic contact formation in palladium-based metallizations to n-Type InP

Two Pd-based metallizations have been systematically studied, i.e., Au/Ge/Pd and Pd/Ge contacts to n-type InP, in an attempt to better understand the role of the metallization constituents in forming ohmic contacts. Ohmic contacts were obtained with minimum specific resistances of 2.5 × 10⁻⁶ Ω-cm² and 4.2 × 10⁻⁶ Ω-cm² for the Au/Ge/Pd and the Pd/Ge contacts, respectively. The annealing regime for ohmic contact formation is 300-375°C for the Au/Ge/Pd/InP system and 350-450°C for the Pd/GelnP system. Palladium, in both cases, reacts with InP to form an amorphous layer and then an epitaxial layer at low temperatures, providing good metallization adhesion to InP substrates and improved contact morphology. Ohmic contact formation in both contacts is attributed to Ge doping, based on the solid state reaction-driven decomposition of an epitaxial layer at the metallization/InP interface, producing a very thin, heavily doped InP layer. Gold appears to be responsible for the difference in contact resistance in the two systems. It is postulated that Au reacts strongly with In to form Au-In compounds, creating additional In site vacancies in the InP surface region (relative to the Au-free metallization), thereby enhancing Ge doping of the InP surface and lowering the contact resistance. Both contacts degrade and ultimately become Schottky barriers again if over annealed, due to consumption of additional InP, which destroys the heavily doped InP layer.     

Ta/Au ohmic contacts to n-type ZnO

Ta/Au ohmic contacts are fabricated on n-type ZnO (∼1 × 10¹⁷ cm⁻³) epilayers, which were grown on R-plane sapphire substrates by metal organic chemical vapor deposition (MOCVD). After growth and metallization, the samples are annealed at 300°C and 500°C for 30 sec in nitrogen ambient. The specific contact resistance is measured to be 3.2×10⁻⁴ Ωcm² for the as-deposited samples. It reduces to 5.4×10⁻⁶ Ωcm² after annealing at 300°C for 30 sec without significant surface morphology degradation. When the sample is annealed at 500°C for 30 sec, the specific contact resistance increases to 3.3 × 10⁻⁵ Ωcm². The layer structures no longer exist due to strong Au and Ta in-diffusion and O out-diffusion. The contact surface becomes rough and textured.     

Thermally stable Ge/Cu/Ti ohmic contacts to n-type GaN

The performance of a novel Ge/Cu/Ti metallization scheme on n-type GaN has been investigated for obtaining thermally and electrically stable low-resistance ohmic contacts. Isochronal (2 min.) anneals in the 600–740°C temperature range and isothermal (690°C) anneals for 2–10 min. duration were performed in inert atmosphere. For the 690°C isothermal schedule, ohmic behavior was observed after annealing for 3 min. or longer with a lowest contact resistivity of 9.1 × 10⁻⁵ Ωcm² after the 10 min. anneal for a net donor doping concentration of 9.2 × 10¹⁷ cm^−Ω3. Mean roughness (R_a) for anneals at 690°C was almost constant at around 5 nm, up to an annealing duration of 10 min., which indicates a good thermal stability of the contact scheme.     

Microstructural and electrical investigation of Ni/Au ohmic contact on p-type GaN

Electrical properties of Ni/Au ohmic contacts on p-type GaN were interpreted with the change of microstructure observed under transmission electron microscopy. The contact resistivity was decreased from 1.3×10⁻² to 6.1×10⁻⁴ Ωcm² after annealing at 600°C. The reduction is due to the dissolution of Ga atoms into Au−Ni solid solution formed during annealing, via the generation of Ga vacancies. Thus, net concentration of holes increased below the contact, resulting in the reduction of contact resistivity. At 800°C, N atoms decomposed; reacted with Ni, and forming cubic Ni₄N. Consequently, N vacancies, acting as donors in GaN, were generated below the contact, leading to the increase of contact resistivity to 3.8×10⁻² Ωcm².     

Mechanism investigation of NiO<Subscript>x</Subscript> in Au/Ni/p-type GaN ohmic contacts annealed in air

Recently, Au/Ni/p-type GaN ohmic contacts annealed in an air ambient have been widely investigated. However, to obtain a low specific-contact resistance, the annealing window is limited. In this study, to understand the oxidation function of metallic Ni, the Au/Ni/p-type GaN structure was annealed in an air ambient for 10 min at various temperatures. Using x-ray photoelectron spectroscopy (XPS) analysis, the metallic Ni was oxidized into NiO and NiO_1.3 compositions at annealing temperatures of 500°C and 600°C, respectively. However, metallic Ni still existed on the interface of the Ni/p-type GaN annealed at 400°C. The associated barrier heights of 0.42 eV, 0.21 eV, and 0.31 eV were obtained with p-type GaN for the Ni, NiO, and NiO_1.3 contacts, respectively. The hole concentrations of p-type NiO and p-type NiO_1.3 were 2.6×10¹⁶ cm⁻³ and 2.0×10¹⁸ cm⁻³, respectively. The lower hole concentration of the p-type NiO would lead to reducing the valence-band bending of the p-type GaN, as well as the barrier height for holes crossing from the p-type NiO to the p-type GaN. The formation of NiO was thus an important issue for lowering the specific-contact resistance of the Au/Ni/p-type GaN ohmic contacts annealed in an air ambient.     

Simultaneous formation of p- and n-type ohmic contacts to 4H-SiC using the ternary Ni/Ti/Al system

Fabrication procedures for silicon carbide power metal oxide semiconductor field effect transistors (MOSFETs) can be improved through simultaneous formation (i.e., same contact materials and one step annealing) of ohmic contacts on both the p-well and n-source regions. We have succeeded with the simultaneous formation of the ohmic contacts for p- and n-type SiC semiconductors by examining ternary Ni/Ti/Al materials with various compositions, where a slash symbol “/” indicates the deposition sequence starting with Ni. The Ni(20 nm)/Ti(50 nm)/Al(50 nm) combination provided specific contact resistances of 2 × 10⁻³ Ω-cm² and 2 × 10⁻⁴ Ω-cm² for p- and n-type SiC, respectively, after annealing at 800°C for 30 min, where the doping level of Al in the SiC substrate was 4.5 × 10¹⁸ cm⁻³ and the level of N was 1.0 × 10¹⁹ cm⁻³.     

Low resistance, thermally stable Au/Pt/Ti/WSiN ohmic contacts on n+-InGaAs/n-GaAs layer systems

The electrical properties of the ohmic contact systems Au/Pt/Ti/WSiN and Au/Pt/Ti to n⁺-InGaAs/GaAs layers grown by metalorganic vapor phase epitaxy were investigated and compared to each other. The thermal stability properties of these contact systems were characterized by accelerated stress tests at elevated temperatures and by complementary thin film x-ray diffraction analysis to evaluate the microstructural properties of degraded and nondegraded structures. The goal of these efforts was to develop stable, homogeneous emitter contacts for power heterojunction bipolar transistors. It was found that for both contact systems the best (specific) contact resistance R_c (ρ _c) is about 0.05 Ωmm (2 × 10⁻⁷ Ωcm²) in the as-deposited state. Au/Pt/Ti/WSiN contacts show no degradation after aging at 400°C for more than 20 h. This is in contrast to standard Au/Pt/Ti contacts which significantly degrade even after short time annealing at 400°C. The good long-time stability of the Au/Pt/Ti/WSiN system is related to the advantageous properties of the reactively sputtered WSiN barrier layer.     

Ohmic contact using the Si nano-interlayer for undoped-AlGaN/GaN heterostructures

Excellent ohmic characteristics for undoped-AlGaN/GaN heterostructures have been achieved by using a Si nano-interlayer: a 1-nm Si layer has been evaporated followed by Ti/Al/Mo/Au evaporation. A contact transfer resistance of 0.18 Ω-mm and a specific contact resistivity of 1 × 10⁻⁶ Ω-cm² have been achieved along with excellent surface morphology at an optimized annealing temperature (800°C). Both ohmic contact characteristics and surface morphology are significantly better than those obtained without the Si nano-interlayer. Auger depth profiles and temperature-dependent current-voltage characteristics were investigated to understand ohmic formation. It is suggested that titanium silicide formation at the interface during rapid thermal annealing lowers the barrier height and enhances thermionic emission current.     

Low-resistance and thermally stable Pd/Ru ohmic contacts to p-type GaN

We report on low-resistance and thermally stable Pd/Ru ohmic contacts to surface-treated p-GaN (3 × 10¹⁷ cm⁻³). It is shown that annealing at 500°C for 2 min in a N₂ ambient improves ohmic contact properties. Specific contact resistance is measured to be 9.2(±0.2) × 10⁻⁴ and 2.4(±0.2) × 10⁻⁵ Ωcm² for the as-deposited and annealed samples, respectively. Atomic force microscopy results show that the surfaces of both the contacts are remarkably smooth with a root-mean-square (rms) roughness of about 0.6 nm. The current-voltage-temperature (I-V-T) and calculation results indicate that, for the as-deposited contact, thermionic field emission is dominant, while for the annealed contact, field emission dominates the current flow.     

Effects of Si interlayer conditions on platinum ohmic contacts for p-type silicon carbide

A study of Pt ohmic contacts with Si interlayers on p-type SiC (7.0×10¹⁸ cm⁻³) was performed as a function of the Si interlayer thickness, deposition temperature, and dopant incorporation. All contacts were ohmic after annealing at 1100°C for 5 min in vacuum. The use of a Si layer was found to decrease the specific contact resistance (SCR) relative to Pt contacts that did not contain Si, regardless of the deposition conditions used in this study. The SCR values were reduced further by three independent effects: the deposition of the Si layer at 500°C, the incorporation of B in the layer, and the design of the Pt:Si layer thicknesses in a 1:1 atomic ratio. By combining all of these effects, the lowest average SCR values (2.89×10⁻⁴ Ω cm²) were obtained. After annealing for 5 min at 1100°C, x-ray diffraction of the contacts with the 1:1 Pt:Si ratio showed a single phase of PtSi. Analyses by cross-sectional transmission electron microscopy revealed no reaction of the films with the SiC substrate. The electrical characteristics of these contacts were stable after annealing at 400°C and 600°C for 96 h and 60 h, respectively. These results are in contrast to those observed for pure Pt contacts and for contacts containing a higher Pt:Si ratio.     

Thermal Stability of Nitride-Based Diffusion Barriers for Ohmic Contacts to <Emphasis Type="Italic">n</Emphasis>-GaN

The use of TaN, TiN, and ZrN diffusion barriers for Ti/Al-based contacts on n-GaN (n ∼ 3 × 10¹⁷ cm⁻³) is reported. The annealing temperature (600–1,000°C) dependence of the Ohmic contact characteristics using a Ti/Al/X/Ti/Au metallization scheme, where X is TaN, TiN, or ZrN, deposited by sputtering was investigated by contact resistance measurements and Auger electron spectroscopy (AES). The as-deposited contacts were rectifying and transitioned to Ohmic behavior for annealing at ≥600°C. A minimum specific contact resistivity of ∼6 × 10⁻⁵ Ω-cm⁻² was obtained after annealing over a broad range of temperatures (600–900°C for 60 s), comparable to that achieved using a conventional Ti/Al/Pt/Au scheme on the same samples. The contact morphology became considerably rougher at the high end of the annealing range. The long-term reliability of the contacts at 350°C was examined; each contact structure showed an increase in contact resistance by a factor of three to four over 24 days at 350°C in air. AES profiling showed that the aging had little effect on the contact structure of the nitride stacks.     

Electrical and structural properties of low-resistance Ti/Al/Re/Au ohmic contacts to n-type GaN

Titanium (15 nm)/aluminum (60 nm)/rhenium (20 nm)/gold (50 nm) ohmic contacts to moderately doped n-type GaN (4.07×10¹⁸ cm⁻³) have been investigated as a function of annealing temperature. It is shown that the current-voltage (I–V) characteristics of the contacts are improved upon annealing at temperatures in the range of 550–750°C. Specific contact resistance as low as 1.3 × 10⁻⁶ Ωcm² is obtained after annealing at 750°C for 1 min in a nitrogen ambient. X-ray photoemission spectroscopy (XPS) results show that the Ga 2p core level for the sample annealed at 750°C shifts toward the high binding side by 0.71 eV compared with that of the as-deposited one. It is also shown that the contact does not seriously suffer from thermal degradation even when annealed at 750°C for 30 min. Based on Auger electron spectroscopy (AES), glancing angle x-ray diffraction (GXRD), and XPS results, possible explanations for the annealing-induced improvement of the ohmic behavior are described and discussed.     

Study of contact resistivity, mechanical integrity, and thermal stability of Ti/Al and Ta/Al ohmic contacts to n-type GaN

The annealing conditions and contact resistivities of Ta/Al ohmic contacts to n-type GaN are reported for the first time. The high temperature stability and mechanical integrity of Ti/Al and Ta/Al contacts have been investigated. Ta/Al (35 nm/115 nm) contacts to n-type GaN became ohmic after annealing for 3 min at 500°C or for 15 s at 600°C. A minimum contact resistivity of 5×10⁻⁶Ω cm² was measured after contacts were repatterned with an Al layer to reduce the effect of a high metal sheet resistance. Ti/Al and Ta/Al contacts encapsulated under vacuum in quartz tubes showed a significant increase in contact resistivity after aging for five days at 600°C. Cross section transmission electron microscopy micrographs and electrical measurements of aged samples indicate that the increased contact resistivity is primarily the result of degradation of the metal layers. Minimal reactions at the metal/GaN interface of aged samples were observed.     

Improved ohmic contact to n-type 4H and 6H-SiC using nichrome

Results are reported for ohmic contacts formed on n-type 4H and 6H-SiC using nichrome (80/20 weight percent Ni/Cr). The electrical characteristics of these NiCr contacts are similar to those of contacts formed on 6H-SiC using pure Ni (∼1×10⁻⁵Ω-cm² for moderately doped material), but the contacts exhibit significant improvement with regard to physical stability. Composite Au/NiCr contacts exhibit good stability during long-term anneals (∼2500 h) at 300°C without the requirement of a diffusion barrier layer between the NiCr ohmic contact layer and the Au cap layer. In addition, the use of NiCr results in success rates near 100% for direct wire bonding to the Au cap layers. Characterization of the contacts by Auger electron spectroscopy, Rutherford backscattering spectroscopy, and transmission electron microscopy provides an explanation for the observed behavior.     

Correlation between the electrical properties and the interfacial microstructures of TiAl-based ohmic contacts to p-type 4H-SiC

In order to understand a mechanism of TiAl-based ohmic contact formation for p-type 4H-SiC, the electrical properties and microstructures of Ti/Al and Ni/Ti/Al contacts, which provided the specific contact resistances of approximately 2×10⁻⁵ Ω-cm² and 7×10⁻⁵ Ω-cm² after annealing at 1000°C and 800°C, respectively, were investigated using x-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM). Ternary Ti₃SiC₂ carbide layers were observed to grow on the SiC surfaces in both the Ti/Al and the Ni/Ti/Al contacts when the contacts yielded low resistance. The Ti₃SiC₂ carbide layers with hexagonal structures had an epitaxial orientation relationship with the 4H-SiC substrates. The (0001)-oriented terraces were observed periodically at the interfaces between the carbide layers and the SiC, and the terraces were atomically flat. We believed the Ti₃SiC₂ carbide layers primarily reduced the high Schottky barrier height at the contact metal/p-SiC interface down to about 0.3 eV, and, thus, low contact resistances were obtained for p-type TiAl-based ohmic contacts.     

Influence of Surface Treatment and Annealing Temperature on the Formation of Low-Resistance Au/Ni Ohmic Contacts to <Emphasis Type="Italic">p</Emphasis>-GaN

We have studied the influence of surface treatment and annealing temperature on the specific contact resistance of Au/Ni ohmic contacts to p-GaN with hole concentrations in the range of 10¹⁶ cm⁻³ to 10¹⁸ cm⁻³. The sample with a hole concentration of 1 × 10¹⁸ cm⁻³, treated with the surface treatment HCl:H₂O = 3:1 solution and annealed at 500°C in a 90% N₂ and 10% O₂ atmosphere, yielded the lowest specific contact resistance of ~4 × 10⁻⁵ Ω cm² and ~2 × 10⁻⁷ Ω cm² at room temperature and at 150°C, respectively. To investigate the roles of interdiffusion between layer interfaces and the formation of NiO and nickel gallides, we examined the metallization stacks before and after annealing using high-resolution x-ray diffraction. We conclude that the nickel-gallide formation and the deterioration of the NiO layer are together responsible for the large deviation in contact resistances observed for samples annealed at various temperatures.     

Pd-Ge contact to n-GaAs with the TiW diffusion barrier

Pd-Ge based ohmic contact to n-GaAs with a TiW diffusion barrier was investigated. Electrical analysis as well as Auger electron spectroscopy and the scanning electron microscopy were used to study the contact after it was subjected to different furnace and rapid thermal annealing and different aging steps. All analyses show that TiW can act as a good barrier metal for the Au/Ge/Pd/n-GaAs contact system. A value of 1.45 × 10⁻⁶ Ω-cm² for the specific contact resistance was obtained for the Au/TiW/Ge/Pd/n-GaAs contact after it was rapid thermally annealed at 425°C for 90 s. It can withstand a thermal aging at 350°C for 40 h with its ρ_c increasing to 2.94 × 10⁻⁶Ω-cm² and for an aging at 410°C for 40 h with its ρ_c increasing to 1.38 × 10⁻⁵ Ω-cm².     

Long-term thermal stability of Ti/Al/Mo/Au ohmic contacts on n-GaN

Improved performance of the ohmic contacts on n-GaN has been demonstrated with the use of MoAu as the capping layer on TiAl metallization. Contact resistance as low as 0.13 Θ-mm was achieved in these ohmic contacts when annealed at 850°C for 30 sec. We have studied the long-term thermal stability of these contacts at 500°C, 600°C, 750°C, and 850°C, respectively. The Ti/Al/Mo/Au metallization forms low contact-resistance ohmic contacts on n-GaN that are stable at 500°C and 600°C after 25 h of thermal treatment. The ohmic-contact performance degrades after 10 h of thermal treatment at 750°C, while the contacts exhibit nonlinear current-voltage (I-V) characteristics after 1 h of thermal treatment at 850°C with the formation of oxide on the surface of the contacts accompanied by surface discoloration. The intermetallic reactions taking place in the contacts during the long-term thermal treatments were studied using Auger electron spectroscopy (AES), and the surface morphology was characterized using atomic force microscopy (AFM).