Light ion irradiation effects on stuffed Lu2(Ti2−xLux)O7−x/2 (x = 0, 0.4 and 0.67) structures

We have recently synthesized “stuffed” (i.e., excess Lu) Lu₂(Ti_2−xLu_x)O_7−x/2 (x = 0, 0.4 and 0.67) compounds using conventional ceramic processing. X-ray diffraction measurements indicate that stuffing more Lu³⁺ cations into the oxide structure leads eventually to an order-to-disorder (O-D) transition, from an ordered pyrochlore to a disordered fluorite crystal structure. At the maximum deviation in stoichiometry (x = 0.67), the Lu³⁺ and Ti⁴⁺ ions become completely randomized on the cation sublattices, and the oxygen “vacancies” are randomized on the anion sublattice. Samples were irradiated with 400 keV Ne²⁺ ions to fluences ranging from 1 × 10¹⁵ to 1 × 10¹⁶ ions/cm² at cryogenic temperatures (∼77 K). Ion irradiation effects in these samples were examined by using grazing incident X-ray diffraction. The results show that the ion irradiation tolerance increases with disordering extent in the non-stoichiometric Lu₂(Ti_2−xLu_x)O_7−x/2.     

Oxygen potential measurements of Am0.5Pu0.5O2−x by EMF method

The dependence of the oxygen potentials on oxygen non-stoichiometry and temperature of Am_0.5Pu_0.5O_2−x has been obtained by the electromotive force (EMF) method with the cell: (Pt) air |Zr(Ca)O_2−x| Am_0.5Pu_0.5O_2−x (Pt). The x value of Am_0.5Pu_0.5O_2−x was changed at 1333 K over 0.02 < x ? 0.25 by the coulomb titration method. The temperature dependence of the oxygen potential was also measured over the range of 1173-1333 K. It was found that the oxygen potential decreased from −80 to −360 kJ mol⁻¹ with increasing x from 0.021 to 0.22 at 1333 K and that it remained almost constant at −360 kJmol⁻¹ around x = 0.23. It was concluded that Am_0.5Pu_0.5O_2−x should be composed of the single fluorite-type phase over 0.02 < x ? 0.22 and the mixed phases of fluorite-type and (Am, Pu)₉O₁₆ at around x = 0.23.     

Thermal studies on fluorite type ZryU1−yO2 solid solutions

Solid state reactions of UO₂ and ZrO₂ in mild oxidizing condition followed by reduction at 1673 K showed enhanced solubility up to 35 mol% of zirconium in UO₂ forming cubic fluorite type Zr_yU_1−yO₂ solid solution. The lattice parameters and O/M (M = U + Zr) ratios of the solid solutions, Zr_yU_1−yO_2+x, prepared in different gas streams were investigated. The lattice parameters of these solid solutions were expressed as a linear equation of x and y: a₀ (nm) = 0.54704 − 0.021x - 0.030y. The oxidation of these solid solutions for 0.1 ? y ? 0.2 resulted in cubic phase MO_2+x up to700 K and single orthorhombic zirconium substituted α-U₃O₈ phase at 1000 K. The kinetics of oxidation of Zr_yU_1−yO₂ in air for y = 0-0.35 were also studied using thermogravimetry. The specific heat capacities of Zr_yU_1−yO₂ (y = 0-0.35) were measured using heat flux differential scanning calorimetry in the temperature range of 334-860 K.     

Eutectic crystallization in the FeO1.5-UO2+x-ZrO2 system

Results of the investigation of the FeO_1.5-UO_2+x-ZrO₂ system in air are presented. The eutectic position and the content of the phases crystallized at this point have been determined. The temperature and the composition of the ternary eutectic are 1323 ± 7 °С and 67.4 ± 1.0 FeO_1.5, 30.5 ± 1.0 UO_2+x, 2.1 ± 0.2 ZrO₂ mol.%, respectively. The solubilities of FeO_1.5 and ZrO₂ in the UO_2+x(FeO_1.5, ZrO₂) solid solution correspond to respectively 3.2 and 1.1 mol.%. The solubilities of UO₂ and ZrO₂ in FeO_1.5 are not significant. The existence of a solid solution on the basis of U(Zr)FeO₄ compound is found. The ZrO₂ solubility in this solid solution is 7.0 mol.%.     

Analysis of oxygen potential of (U0.7Pu0.3)O2±x and (U0.8Pu0.2)O2±x based on point defect chemistry

Stoichiometries in (U_0.7Pu_0.3)O_2±x and (U_0.8Pu_0.2)O_2±x were analyzed with the experimental data of oxygen potential based on point defect chemistry. The relationship between the deviation x of stoichiometric composition and the oxygen partial pressure P_O2 was evaluated using a Kröger-Vink diagram. The concentrations of the point defects in uranium and plutonium mixed oxide (MOX) were estimated from the measurement data of oxygen potentials as functions of temperature and P_O2. The analysis results showed that x was proportional to near the stoichiometric region of both (U_0.7Pu_0.3)O_2±x and (U_0.8Pu_0.2)O_2±x, which suggested that intrinsic ionization was the dominant defect. A model to calculate oxygen potential was derived and it represented the experimental data accurately. Further, the model estimated the thermodynamic data, and , of stoichiometric (U_0.7Pu_0.3)O_2.00 and (U_0.8Pu_0.2)O_2.00 as −552.5 kJ·mol⁻¹ and −149.7 J·mol⁻¹, and −674.0 kJ · mol^-1 and −219.4 J · mol⁻¹, respectively.     

Oxygen potential of (U0.88Pu0.12)O2±x and (U0.7Pu0.3)O2±x at high temperatures of 1673-1873 K

The oxygen potential of (U_0.88Pu_0.12)O_2±x (−0.0119 < x < 0.0408) and (U_0.7Pu_0.3)O_2±x (−0.0363 < x < 0.0288) was measured at high temperatures of 1673-1873 K using gas equilibrium method with thermo gravimeter. The measured data were analyzed by a defect chemistry model. Expressions were derived to represent the oxygen potential based on defect chemistry as functions of temperature and oxygen-to-metal ratio. The thermodynamic data, and , at stoichiometric composition were obtained. The expressions can be used for in situ determination of the oxygen-to-metal ratio by the gas-equilibration method. The calculation results were consistent with measured data. It was estimated that addition of 1 wt.% Pu content increased oxygen potential of uranium and plutonium mixed oxide by 2-5 kJ/mol.     

Band gap controlled H loss from passivated Hg1−xCdxTe (MCT) wafers under intense electronic excitations

We report here loss of H monitored by on-line elastic recoil detection analysis (ERDA) technique from passivated Hg_1−xCd_xTe (MCT) wafers due to irradiation by 80 MeV Ni⁹⁺, 120 MeV Au¹⁵⁺ and 200 MeV Ag¹⁰⁺. The loss of H is more in case of the wafer irradiated by Ag ions as compared to other two because of higher electronic energy loss (S_e). For same S_e value, H loss is more in case of the wafer having x = 0.29 as compared to the one having x = 0.204. This is due to higher band gap of the former as compared to the later, which is an important data for proper use of these materials as IR detector in intense radiation zone. These results are explained on the basis of thermal spike model of ion-solid interaction.     

Structural characterization of Nd-doped Hf-zirconolite Ca1−xNdxHfTi2−xAlxO7 ceramics

Because of its high incorporation capacity and of the high thermal neutron capture cross-section of hafnium, Hf-zirconolite (CaHfTi₂O₇) ceramic can be envisaged as a potential waste form for minor actinides (Np, Am, Cm) and plutonium immobilization. In this work, Nd-doped Hf-zirconolite Ca_1−xNd_xHfTi_2−xAl_xO₇ (x = 0; 0.01 and 0.2) ceramics have been prepared by solid state reaction. Neodymium has been used as trivalent actinide surrogate. The ceramic samples structure has been studied by X-ray diffraction and refined by the Rietveld method. This revealed that Nd³⁺ ions only enter the Ca site, whereas part of Hf⁴⁺ ions substitute titanium into Ti(1) sites and Al³⁺ ions mainly occupy the Ti(2) split sites and Ti(3) sites of the zirconolite structure. Using various spectroscopic techniques (electron spin resonance, optical absorption and fluorescence), the environment of Nd³⁺ cations in Hf-zirconolite has been studied and compared with that of Nd³⁺ cations in Zr-zirconolite (CaZrTi₂O₇). Different local environments of Nd³⁺ cations have been detected in Hf-zirconolite that can be attributed to the existence of an important disorder around Nd in the Ca site probably due to the statistical occupancy of the next nearest cationic site of neodymium (a split Ti site) by Ti⁴⁺, Al³⁺ cations and vacancies. No significant differences were observed concerning Nd³⁺ cations environment and distribution in Hf- and Zr-zirconolite ceramics.     

Oxygen non-stoichiometries in (Th0.7Ce0.3)O2−x

Oxygen non-stoichiometry in (Th_0.7Ce_0.3)O_2−x oxide solid solutions was investigated from the viewpoint of Ce reduction. The oxygen non-stoichiometry was experimentally determined by means of thermogravimetric analysis as a function of oxygen potential at 1173, 1273 and 1373 K. Features of the isotherms of oxygen non-stoichiometry in (Th_0.7Ce_0.3)O_2−x similar to those in oxygen non-stoichiometric actinide and lanthanide dioxides were observed. The oxygen non-stoichiometry in (Th_0.7Ce_0.3)O_2−x was compared with those of CeO_2−x and (U_0.7Ce_0.3)O_2−x. It was concluded that the Ce reduction has some relation to defect forms and their transformations in the solid solutions.     

Lattice parameters of (U, Pu, Am, Np)O2−x

The solid solutions of (U_{1−z−y’−y”}Pu_zAm_y’Np_y”)O_2−x (z = 0-1, y’ = 0-0.12, y” = 0-0.07) were investigated by X-ray diffraction measurements, and a database for the lattice parameters was updated. A model to calculate the lattice parameters was derived from the database. The radii of the ions present in the fluorite structure of (U, Pu, Am, Np)O_2−x were estimated from the lattice parameters measured in this work. The model represented the experimental data within a standard deviation of σ = ±0.025%.     

Fabrication method for UO2 pellets with large grains or a single grain by sintering in air

The effects of a powder treatment, the sintering temperature and the sintering time on the grain growth of UO₂ pellets were investigated in air to obtain UO₂ pellets with large grains. Air could be used for sintering because an oxidation path above 1803 K does not pass through a two-phase (UO_2+x + U₃O_8−z) region. The UO₂ pellets sintered by the CO₂-air-CO₂-H₂ process consisted of a single grain or some large grains in the order of several millimeters.     

Thermodynamic properties of ThxU1−xO2 (0 < x < 1) based on quantum-mechanical calculations and Monte-Carlo simulations

Th_xU_1−xO_2+y binary compositions occur in nature, uranothorianite, and as a mixed oxide nuclear fuel. As a nuclear fuel, important properties, such as the melting point, thermal conductivity, and the thermal expansion coefficient change as a function of composition. Additionally, for direct disposal of Th_xU_1−xO₂, the chemical durability changes as a function of composition, with the dissolution rate decreasing with increasing thoria content. UO₂ and ThO₂ have the same isometric structure, and the ionic radii of 8-fold coordinated U⁴⁺ and Th⁴⁺ are similar (1.14 nm and 1.19 nm, respectively). Thus, this binary is expected to form a complete solid solution. However, atomic-scale measurements or simulations of cation ordering and the associated thermodynamic properties of the Th_xU_1−xO₂ system have yet to be determined. A combination of density-functional theory, Monte-Carlo methods, and thermodynamic integration are used to calculate thermodynamic properties of the Th_xU_1−xO₂ binary (ΔH_mix, ΔG_mix, ΔS_mix, phase diagram). The Gibbs free energy of mixing (ΔG_mix) shows a miscibility gap at equilibration temperatures below 1000 K (e.g., E_exsoln = 0.13 kJ/(mol cations) at 750 K). Such a miscibility gap may indicate possible exsolution (i.e., phase separation upon cooling). A unique approach to evaluate the likelihood and kinetics of forming interfaces between U-rich and Th-rich has been chosen that compares the energy gain of forming separate phases with estimated energy losses of forming necessary interfaces. The result of such an approach is that the thermodynamic gain of phase separation does not overcome the increase in interface energy between exsolution lamellae for thin exsolution lamellae (10 Å). Lamella formation becomes energetically favorable with a reduction of the interface area and, thus, an increase in lamella thickness to >45 Å. However, this increase in lamellae thickness may be diffusion limited. Monte-Carlo simulations converge to an exsolved structure [lamellae || ] only for very low equilibration temperatures (below room temperature). In addition to the weak tendency to exsolve, there is an ordered arrangement of Th and U in the solid solution [alternating U and Th layers || {1 0 0}] that is energetically favored for the homogeneously mixed 50% Th configurations. Still, this tendency to order is so weak that ordering is seldom reached due to kinetic hindrances. The configurational entropy of mixing (ΔS_mix) is approximately equal to the point entropy at all temperatures, indicating that the system is not ordered.     

Effects of ion irradiation on the mechanical properties of SiNawOxCyHz sol-gel derived thin films

A study of the effects of ion irradiation of hybrid organic/inorganic modified silicate thin films on their mechanical properties is presented. NaOH catalyzed SiNa_wO_xC_yH_z thin films were synthesized by sol-gel processing from tetraethylorthosilicate (TEOS) and methyltriethoxysilane (MTES) precursors and spin-coated onto Si substrates. After drying at 300 °C, the films were irradiated with 125 keV H⁺ or 250 keV N²⁺ at fluences ranging from 1 × 10¹⁴ to 2.5 × 10¹⁶ ions/cm². Nanoindentation was used to characterize the films. Changes in hardness and reduced elastic modulus were examined as a function of ion fluence and irradiating species. The resulting increases in hardness and reduced elastic modulus are compared to similarly processed acid catalyzed silicate thin films.     

Solubility of ThO2 in Gd2Zr2O7 pyrochlore: XRD, SEM and Raman spectroscopic studies

Solubility of ThO₂ in gadolinium zirconate pyrochlore, a potential host for radioactive materials, has been investigated. The phase relations in Gd_2−xTh_xZr₂O_7+x/2 (0.0 ? x ? 2.0) systems have been established under the slow-cooled conditions from 1400 °C. XRD studies reveal that the compositions corresponding to x = 0.0-0.075 are single phasic in nature and beyond x ? 0.1 the biphasic region starts. The first biphasic region comprising of pyrochlore and thoria exist from x = 0.1-0.8, and from x = 1.2 another biphasic region consisting of gadolinia stabilized zirconia (GSZ) and thoria appears which persists till x = 1.6. The end member (i.e. x = 2.0) of the series is found to be a mixture of monoclinic ZrO₂ and thoria. Interestingly, gadolinia which has wide solubility in thoria, did not show any miscibility in thoria in the presence of zirconia. Irregular grains of Gd_1.8Th_0.2Zr₂O_7.1 as shown in SEM supports its biphasic nature. Raman spectra of heavily thoria doped (x = 0.1 and 0.2) samples, indicates the presence of Zr-O₇ mode which implies the samples are highly disordered in nature.     

Effect of Nd and Pr addition on the thermal and mechanical properties of (U, Ce)O2

The thermal conductivity, Young’s modulus, and hardness of (U_0.65−xCe_0.3Pr_0.05Nd_x)O₂ (x = 0.01, 0.08, 0.12) were evaluated and the effect of Pr and Nd addition on the properties of (U, Ce)O₂ were studied. The polycrystalline high-density pellets were prepared with solid state reactions of UO₂, CeO₂, Pr₂O₃, and Nd₂O₃. We confirmed that all Ce, Pr, and Nd dissolved in UO₂ and formed solid solutions of (U, Ce, Pr, Nd)O₂. We revealed that the thermal conductivity of (U_0.65−xCe_0.3Pr_0.05Nd_x)O₂ (x = 0.12) was up to 25% lower than that of x = 0.01 at room temperature. The Young’s modulus of (U_0.65−xCe_0.3Pr_0.05Nd_x)O₂ decreased with x, whereas the hardness values were constant in the investigated x range.     

Optical properties of InxGa1−xP/InP grown at high fluence Ga implantation on InP using focused ion beam

Single-crystalline InP(1 0 0) substrate was implanted by 30 keV Ga⁺ ions with fluences of 1 × 10¹⁶-1.5 × 10¹⁷ cm⁻² followed by post-annealing treatment at 750 °C to recover implantation-induced structural defects and activate dopants into the lattices. The optical property, composition, and microstructure of the Ga⁺-implanted InP were studied by Raman spectroscopy and transmission electron microscopy (TEM). Raman spectra show that the In_xGa_1−xP phase is formed at a critical fluence of 7 × 10¹⁶ cm⁻². The newly grown phase was identified with the appearance of Ga rich TO_InP and In rich TO_GaP modes of a random alloy in the 1 bond-2 phonon mode configuration along with TEM structural identification.     

Melting behavior of MgO-based inert matrix fuels containing (Pu,Am)O2−x

The melting behavior of MgO-based inert matrix fuels containing (Pu,Am)O_2−x ((Pu,Am)O_2−x-MgO fuels) was experimentally investigated. Heat-treatment tests were carried out at 2173 K, 2373 K and 2573 K each. The fuel melted at about 2573 K in the eutectic reaction of the Pu-Am-Mg-O system. The (Pu,Am)O_2−x grains, MgO grains and pores grew with increasing temperature. In addition, Am-rich oxide phases were formed in the (Pu,Am)O_2−x phase by heat-treatment at high temperatures. The melting behavior was compared with behaviors of PuO_2−x-MgO and AmO_2−x-MgO fuels.     

Phase equilibria in the FeO1+x-UO2-ZrO2 system in the FeO1+x-enriched domain

Experimental results of the investigation of the FeO_1+x-UO₂-ZrO₂ system in neutral atmosphere are presented. The ternary eutectic position and the composition of the phases crystallized at this point have been determined. The phase diagram is constructed for the FeO_1+x-enriched region and the onset melting temperature of 1310 °C probably represents a local minimum and so will be a determining factor in this system and its application to safety studies in nuclear reactors.     

Comparative study of silicate glasses containing Bi2O3, PbO and BaO: Radiation shielding and optical properties

The radiation shielding and optical properties of xBi₂O₃:(100-x)SiO₂, xPbO:(100-x)SiO₂ and xBaO:(100-x)SiO₂ glass systems (where 30 ? x ? 70 is the composition by weight%) have been investigated. Total mass attenuation coefficients (μ_m) of glasses at 662 keV were improved by increasing their Bi₂O₃ and PbO content, which raised the photoelectric absorption in glass matrices. Raising the BaO content to the same fraction range, however, brought no significant change to μ_m. These results indicate that photon is strongly attenuated in Bi₂O₃ and PbO containing glasses, and but not in BaO containing glass. The results from the optical absorption spectra show an edge that was not sharply defined; clearly indicating the amorphous nature of glass samples. It is observed that the cutoff wavelength for Bi₂O₃ containing glass was longer than PbO and BaO containing glasses.     

Structural study of Pu1−xAmxO2 (x = 0.2; 0.5; 0.8) obtained by oxalate co-conversion

This study describes the synthesis and the characterisation of Pu_1−xAm_xO₂ (x = 0.2; 0.5; 0.8) mixed oxides obtained by oxalate co-conversion. We studied the self-irradiation effect in these compounds at the structural scale. We determined, for each composition, the initial lattice parameter and the equation describing its variation versus time and displacements per atom. Similarly to other α emitting compounds, it was observed a fast lattice parameter expansion rate, followed by a stabilisation at a maximum value. The observations also showed that the initial expansion rate varies according to the Am content and the maximum value to the Pu content. However, for all compositions, the lattice parameter relative variations are the same.