甘蔗叶活化时的热解历程及其活性炭的研制

采用热重分析仪(TG-DTG)分析了NH4H2PO4活化甘蔗叶时的热解历程和活化反应机理,研究了活化剂浓度、液料比、浸泡时间、活化温度及活化时间等工艺因素对甘蔗叶活性炭样品得率、碘吸附值的影响,并运用扫描电子显微镜(SEM)对甘蔗叶及其活性炭样品进行了表征。结果表明,甘蔗叶制备活性炭的反应为4C+2NH4H2PO4→P2O3+CH4↑+CO2↑+2CO↑+2NH3↑+H2O↑甘蔗叶活性炭的碘吸附值随着活化时间的延长而增加,随着活化剂浓度、液料比、浸泡时间、活化温度的增加而呈现先增后减的变化规律;甘蔗叶活性炭的最优制备工艺条件为活化剂浓度2.5%(质量分数),液料比为5∶1,浸泡时间为20 h,活化温度为700℃,活化时间为60 min,所制备的活性炭样品具有丰富的管束结构,其得率和碘吸附值分别为30.9%、993.33 mg/g。     

KOH作用下稻壳制备高比表面积活性炭的研究

以稻壳为原料、KOH为活化剂,制备了高比表面积活性炭,研究了活化剂用量、活化温度和活化时间对活性炭吸附性能的影响.研究结果表明,活化剂与稻壳的质量比为3:1,在800℃活化1h,制得的活性炭碘吸附值为1520.32mg/g,亚甲蓝吸附值为3442.50mg/g,比表面积为2027.42m2/g.SEM和XRD观察发现,干馏过程及活化过程的共同作用使活性炭产生多孔结构.     

NaOH活化法制备高比表面积稻壳活性炭

以农业废弃物稻壳为原料,NaOH为活化剂,制备了中孔发达的高比表面活性炭,研究了碱炭比、活化温度对样品碘吸附值和亚甲基蓝吸附值的影响;采用SEM、TEM表征了活性炭的形貌,通过BET法计算了活性炭的比表面积,BJH方程计算出活性炭的孔径分布.结果表明,在碱炭比为3∶1、活化温度为750℃的工艺条件下制备的稻壳活性炭同时具有较高的碘吸附值和亚甲基蓝吸附值;稻壳活性炭比表面积高达2164m2/g,中孔含量达到63.67%,总孔容达到1.544mL/g.     

ZnCl2活化茄子秸秆制备活性炭及表征

以茄子秸秆为原料、ZnCl2为活化剂制备活性炭。通过正交实验方法确定了制备活性炭的最佳工艺条件,采用低温氮气吸附、BET、Langmuir和BJH理论对其孔结构进行了表征,利用红外光谱分析样品的表面官能团,扫描电镜观察表面形貌。结果表明以茄杆活性炭的最佳工艺条件:浸渍比为2,浸渍时间为8h,活化温度为550℃,活化时间为60min,所得的活性炭的碘吸附值为1270.06mg/g,亚甲基蓝吸附值为17.4mL/g;BET和Langmuir比表面积分别为1649.615和1851.649m2/g,吸附总孔容为0.488cm3/g,吸附平均孔径为2.241nm。     

油菜秸秆基活性炭的制备与应用

以农业废料中的油菜秸秆为原料,利用化学活化的方法制备活性炭。利用活性炭对甲基橙的吸附探讨了料液比、活化剂磷酸浓度、活化时间、活化温度、浸泡时间对活性炭吸附能力的影响,得出了活性炭制备的最佳工艺条件,最佳的工艺条件为料液比1∶3,活化剂浓度60%,活化时间4h,活化温度400℃。     

超高比表面积活性炭的制备与表征

以无患子残渣为原料,KOH与K2CO3作为活化剂,采用微波炭化和活化两步法制备超高比表面积活性炭,通过正交实验优化活性炭的制备工艺,探讨了碱炭比、活化温度和活化时间对活性炭吸附亚甲基蓝吸附值的影响。利用N2吸脱附实验、XRD、FT-IR等实验技术,对制备的活性炭结构与性能进行了表征。结果表明,在碱炭质量比为4∶1、活化温度800℃、活化时间30 min的条件下,所制备的活性炭对亚甲基蓝吸附值为595 mg/g,BET比表面积为3 479 m2/g,吸附累积总孔容达1.8262 cm3/g,平均孔径为2.0997 nm。     

稻壳基脱硅活性炭的制备及其对油气吸附性能研究

利用碳酸钠对稻壳进行水热脱硅,得到脱硅稻壳炭(RHC),并以RHC为原料,分别使用一定浓度的NaOH、H3PO4和ZnCl2在一定温度下对RHC进行活化改性制得稻壳基脱硅活性炭(RHAC)吸附剂,并依据RHAC对正己烷的静态吸附率进行实验条件优选,并对优选条件下制得的RHAC进行油气动态吸附实验及其物性参数表征。结果表明:H3PO4溶液活化RHC制备RHAC为最佳活化剂,最优实验条件为H3PO4溶液浓度34%,浸渍时间6h,活化时间60min,活化温度500℃;RHAC对油气的饱和吸附率为26.39%,比表面积为823.68m2/g,总孔容为0.645cm3/g,平均孔径为2.163nm。     

K_2CO_3活化法制备芋叶柄基活性炭的研究

以废弃的芋叶柄为原料,K2CO3为活化剂,制备芋叶柄基活性炭,考察炭化和活化工艺条件对活性炭吸附性能的影响,采用等温氮吸脱附测试、扫描电子显微镜(SEM)对样品材料进行了测试。结果表明:若以碘吸附值作为评价指标,最佳工艺条件为K2CO3浓度200g/L、活化温度850℃、活化时间35min,碘值为1930.4mg/g,BET比表面积为633.215m2/g,孔容为0.194cm3/g,孔径为18.45nm。以亚甲基蓝吸附值作为评价指标,最佳工艺条件为K2CO3浓度175g/L、活化温度875℃、活化时间35min,亚甲基蓝吸附值为298.8mg/g,BET比表面积为604.708m2/g,孔容为0.076cm3/g,孔径为18.533nm。     

化学活化法制备重质沥青基活性炭的研究

以重质沥青为原料，采用化学活化法制备重质沥青基活性炭，探究空气预氧化与硝酸钾预氧化、不同碱炭比及不同活化时间和活化温度对重质沥青基活性炭性能的影响，并采用碘吸附值与二氧化硫吸附量来确定活性炭的吸附性能。结果表明：在硝酸钾预氧化及碱炭比为4∶1的条件下，活化时间80min、活化温度850℃时制备的重质沥青基活性炭具有较为发达的微孔结构，碘吸附值为1052.2mg/g,二氧化硫吸附量为319.1mg/g。其性能优于物理活化法制备的活性炭，有望应用于吸附脱硫环保领域。     

椰壳纤维基高比表面积中孔活性炭的制备

以椰壳纤维为原料,制备高比表面积中孔活性炭.采用正交试验设计实验方案,研究KOH和NaOH复合活化法制备活性炭的实验方案与工艺条件.考察了活化剂配比、炭化温度、活化温度、时间和升温速率对所制活性炭吸附性能的影响.在最佳工艺条件下,所制活性炭的比表面积达到2032m2/g,中孔发达,特别是2nm～4nm的,中孔比例达到28%.活性炭对的碘吸附值为1435mg/g,亚甲基蓝吸附值为495mg/g,产率为49%.     

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Refrigerators Enter a New Era of Health Preservation Frestech initiates the establishment of China's first standard for household sterilization refrigerators

On November 30, 2007, the China Association for Standardization (CAS) held a press conference at Beijing Diaoyutai State Guest House. Leaders from the China Household Electric Appliance Research Institute, the China Household Electric Appliance Association, and the China Consumers' Association attended and made speeches.……     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

A study of centrifugal cast high boron high speed steel

In the present study a high‐boron high speed steel (HSS) roll material was designed. Many expensive alloy elements have been substituted by cheap boron alloy, and high‐boron high speed steel roll has been manufactured by centrifugal casting method. The microstructures, mechanical properties and wear resistance of centrifugal casting high‐boron high speed steel roll have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and X‐ray diffraction (XRD) analysis, hardness test, impact test and wear test. The results indicated that the solidification microstructures of high‐boron high speed steel roll consisted of M₂(B,C), (W,Mo)₂(B,C), M₃(B,C), M₂₃(B,C)₆ type borocarbides and martensite, a small amount of retained austenite. Borocarbides were continuously distributed over the grain boundary. After quenching from 1050 °C, local broken network appeared in partial borocarbides, and fine secondary borocarbide precipitated from the matrix. After tempering from 525 °C, the amount of precipitated borocarbide increased significantly. After heat treatment, the hardness of high‐boron high speed steel roll excelled 60 HRC, and its impact toughness excelled 8.0 J/cm². The single groove steel rolling amount of high‐boron high speed steel rolls increases by 500% than that of bainite cast iron roll, when the rolls are used in K₁ mill housing of bar mill.     

Thixotropy of Systems with Shear Thinning and Plastic Flow Behavior

The definition of the thixotropy is a decrease in viscosity with time in shear and a subsequent recovery of viscosity after the shear deformation is removed.We ...     

Brainstorming for ISO Strategy 2016-2020

正Responding to ISO’s appeal for survey for the to-be-developed ISO Strategy Plan for 2016-2020,SAC hosted a special workshop over the needs and comments of various fi elds on June 8 in Beijing.The workshop was attended by ISO President-elect and Ansteel General Manager Zhang Xiaogang,SAC Vice-Administrator Yu Xinli,and 30 experts from     

CNAS Passes APLAC's PTP Review

正The review group of Asia Pacific Laboratory Accreditation Cooperation(APLAC)carried out a 4-day peer review of the proficiency testing provider(PTP)for China National Accreditation Service for Conformity Assessment(CNAS)from July 28 to 31,2014.CNAS passed the PTP review with excellent performance.Two senior peer reviewers of APLAC made a comprehensive,rigorous and detailed review of CNAS’s PTP accreditation activities,and made the on-spot inspection of the review groups in Shanghai and Shenzhen respectively.