Photoluminescence Characteristics of Gd2Mo3O9 ： Eu Phosphor Particles by Solid State Reaction Method

Eu^3＋-doped Gd2Mo3O9 was prepared by solid-state reaction method using Na2CO3 as flux and characterized by powder X-ray diffractometry. According to X-ray diffraction, this material belonged to a tetragonal system with space group I41/α. The effects of flux content and sintering temperature on the luminescent properties were investigated with the emission and excitation spectra. The results showed that flux content and sintering temperature had effects on the luminescent properties, the optimized flux content and the best temperature was 3 % and 800 ℃ respectively. The excitation and emission spectra also showed that this phosphor could be effectively excited by C-T band （280 nm）, ultraviolet light 395 nm and blue light 465 nm. The wavelengths at 395 and 465 nm were nicely fitting in with the widely applied output wavelengths of ultraviolet or blue LED chips. Integrated emission intensity of Gd2Mo3O9 ： Eu was twice higher than that of Y2O2S ： Eu^3 ＋ under 395 nm excitation. The Eu^3＋ doped Gd2Mo309 phosphor may be a better candidate in solid-state lighting applications.     

Luminescent characteristics of Ba3Y2（BO3）4：Eu^3＋ phosphor for white LED

The Ba3Y2（BO3）4：Eu^3＋ phosphor was synthesized using a high temperature solid-state reaction method and the luminescent characteristics were investigated. The emission spectrum exhibited one strong red emission at 613 nm, corresponding to the electric dipole 5D0-TF2 transition of Eu^3＋, under 365 nm excitation. The excitation spectrum of 613 nm indicated that the Ba3Y2（BO3）n：Eu^3＋ phosphor was effectively excited by ultraviolet （UV） （254, 365 and 400 nm） and blue （470 nm） light. The effect of Eu^3＋ concentration on the 613 nm emission of the Ba3Y2（BO3）n：Eu^3＋ phosphor was measured. The results showed that the emission intensity increased with increasing Eu^3＋ concentration, and then decreased. The CIE color coordinates of Ba3Y2（BO3）4：Eu^3＋ phosphor were x=0.641 and y=0.359 at 15 mol.% Eu^3＋.     

Luminescence of Eu^3 ＋ in LnAlO3 （Ln = Gd, Y） under UV and VUV Excitation

Single phases of LnAlO3 : Eu^3 ( Ln = Gd, Y ) were obtained by the process of evaporation of their nitric acid solution, and then pyrolysis of their nitrate salts. On monitoring by 613 nm emission, broad bands at around 270 and 170nm were observed in the excitation spectrum of Gd0.95Eu0.05AlO3. These peaks could be assigned to charge transfer (CT)transitions of Eu^3 -O^2- and Gd^3 -O^2- respectively. All the transitions observed in Gd0.95Eu0.05AlO3 are faithfully reproduced in the Y0.95Eu0.05AlO3, but with an exception of the ^8S7/2→^6I11/2 transition of Gd^3 . The 153 nm broad band could be the CT transition of Y^3 -O^2 - . Accordingly, the efficiency luminescence of (Gd, Y) BO3 : Eu^3 was explained as a result of CT transitions of Gd^3 -O^2- and Y^3 -O^2- under 147 nm excitation. Under VUV excitation, Gd0.95Eu0.05AlO3 exhibits a bright red luminescence with CIE chromaticity coordinates of (0.623, 0. 335) with a PL intensity of 30 of the commercial phosphor (Gd, Y) BO3 : Eu^3 (KX-504A). The PL spectrum of Y0.95Eu0.05AlO3 is similar to that of Gd0.95Eu0.05AlO3. Calculation of the color coordinates gives x = 0. 636, y = 0. 340 with a PL intensity of 50 of the (Gd, Y) BO3 : Eu^3 ( KX-504A) for Y0.95Eu0.05AlO3, and confirms that it has the appearance of pure spectral red, corresponding approximately to 608 nm. It can be concluded that LnAlO3:Eu^3 is a promising red VUV phosphor.     

Research of Luminescence Properties on MO-RE2 O3 -B2 O3:Eu, Mn(M=Mg, Ca, Sr; RE=Y, La, Gd)

A series of phosphor of MO-RE2 O3-B2 O3: Eu, Mn ( M = Mg, Ca, Sr; RE = Y, La, Gd) were prepared and studied.Excitation spectra exhibited high absorption in UV region (370 ～ 400 nm).There existed two valence states for europium ions Eu2 and Eu 3 , the broad emission band peaking at 515 nm correspond to the 5d-4f emission transition of Eu2 , the sharp emission peaking at 590 and 610 nm correspond to the 5D0→7FJ(J = 1,2,3,4) emission transition of Eu 3 By the introduction of Mg and Y into MO-RE2O3-B2O3: Eu, blue-green emission was restrained ultimately and red emission peaking at 610 nm was enhanced strongly, intensity and colorimetric purity of red light were both enhanced.Furthermore, Mg1-xSrxO-Y2O3-B2O3: Eu was also researched, the introduction of Sr into MgO-Y2O3-B2O3:Eu gives rise to a shift to longer wavelengths of the position of the excitation peak, and the emission spectra varies with the increasing of x simultaneously.     

Luminescent properties of Ba3Gd（BO3）3：Eu^3＋ phosphor for white LED applications

Luminescent material Ba3Gd(BO3)3 doped with Eu3+ ion was prepared by high temperature solid-state method. The preparing conditions, luminescent properties, and particle morphology of Ba3Gd(BO3)3:Eu3 + phosphor were studied with X-ray diffraction (XRD), fluorescence spectroscopy, and scanning electron microscopy (SEM). The results obtained by XRD showed that pure phase of Ba3Gd(BO3)3 was obtained at 1000℃. Images from SEM displayed that the particles of Ba3Gd(BO3)3:Eu3+ phosphor had a spherical shape with an average diameter of about 200-400 nm. The luminescence spectra showed that Ba3Gd(BO3)3:Eu3+ phosphor was effectively excited by the near ultraviolet (UV) light (396 nm) and blue light (466 nm). The main emission peaks of Ba3Gd(BO3)3:Eu3+ phosphor were assigned to the supersensitive transition 5D0-7F2 (611 and 616 nm) of Eu3+ ion when samples were excited at 255 and 396 nm, respectively, and the luminescent intensity of Ba3Gd(BO3)3:Eu3+ at 611 and 616 nm reached to the maximum when the doped content of Eu3+ ion was 10mol.%. Therefore, this phosphor could be a promising red component for possible applications in the field of white LED.     

Effect of gadolinium incorporation on optical characteristics of YNbO_4：Eu~（3＋） phosphors for lamp applications

Eu3+-doped (Y,Gd)NbO4 phosphor was synthesized by solid-state reaction for possible application in cold cathode fluorescent lamps. A broad absorption band with peak maximum at 272 nm was observed which was due to the charge transfer between Eu3+ ions and neighboring oxygen anions. A deep red emission at the peak wavelength of 612 nm was observed which could be attributed to the 5D0→7F2 transition in Eu3+ ions. The highest luminance for Y1-x-yGdyNbO4:Eux3+ under 254 nm excitation was achieved at Eu3+ concentration of 18 mol.% (x=0.18) and Gd3+ concentration of 8.2 mol.% (y=0.082). The luminance of Y0.738Gd0.082NbO4:Eu3+0.18 was higher than that of a typical commercial phosphor Y2O3:Eu3+ and the CIE chromaticity coordinate was (0.6490, 0.3506), which was deeper than that of Y2O3:Eu3+. The particle size of the synthesized phosphors was controlled by the NaCl flux and particle size as high as 8 μm with uniform size distribution of particles was obtained.     

Synthesis and luminescence properties of europium activated Ca3Al2O6-Sr3Al2O6 system

Divalent europium activated tristrontium dialuminum hexaoxide phosphor, (Sr1-xEux)3Al2O6, was obtained by solid state reaction. Crystal structure and luminescence properties of synthesized (Sr1-xEux)3Al2O6 were investigated. The major excitation band of (Sr1-xEux)3Al2O6 located in blue light region, the photoluminescence spectrum showed red light emission peaked at 618 nm which could be attributed to the d-f transition of the Eu2+. The influence of Ca2+ substitution for Sr2+ on structural and luminescence properties of Eu2+ doped Sr3Al2O6 was also studied. The photoluminescence peak position of (Sr1-yCay)2.94Eu0.06Al2O6 varied from 618 to 655 nm with increasing y value. The reason for redshift in the emission band of (Sr1-yCay)2.94Eu0.06Al2O6 phosphor was also discussed.     

Influence of annealing temperature on luminescent properties of Eu~(3+)/V~(5+) co-doped nanocrystalline Gd_2Ti_2O_7 powders

Nanosized Gd2(1-x)Eu2xTi2O7:yV5+ phosphors were prepared via sol-gel method and characterized with X-ray diffraction,Raman spectroscopy,diffuse reflectance spectra and photoluminescence spectra.Their PL properties were investigated as functions of the Eu3+ doping concentration and annealing temperature.The results indicated that the as-prepared samples showed a strong emission of Eu3+ under the irradiation of 303 nm.For Eu3+-doped Gd2Ti2O7,the orange emission at 586 nm was the strongest,which was correspond...     

Eu3+激活的Li2Gd4（MoO4）7钼酸盐红色荧光体及其发光性质

由高温固相反应首次合成Li2(Gd1-xEux)4(MoO4)7(0相似文献   

作为白光LED用铕掺杂氟化镧红色荧光粉的制备与光谱性能研究

采用水热法制备具有单一相六方晶系的LaF₃:Eu3+纳米荧光粉.通过X射线粉末衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、光致发光光谱(PL)和荧光衰减曲线对LaF₃:Eu3+纳米荧光粉进行表征.LaF₃:Eu3+荧光粉的激发光谱主要由250 nm处的宽带(O2-→Eu3+的电荷转移跃迁)和一些尖峰(Eu3+ f-f跃迁)构成,其中位于近紫外区396 nm处有一较强的激发峰.通过发射光谱探测Eu3+在LaF₃晶体中的局部晶场环境.在298 K下激发光谱和发射光谱可知,在六方晶系的LaF₃纳米晶体中的Eu3+晶格位置从D_4h降至到C_2v,这是由于晶格变化所造成的.在396 nm激发下,观测到较优掺杂浓度为10%的LaF₃:Eu3+荧光粉在591 nm(5D₀→7F₁跃迁)处有强烈的红色发射峰.其发光性能表明,LaF₃:Eu3+红色荧光粉在近紫外发光二极管领域具有潜在的应用价值.      

Characterization of (Y,Gd) BxV1-xO4-x:Eu Phosphor Prepared by Coprecipitation Reaction

White body-color (Y, Gd)BxV1- xO4-x :Eu3 phosphors were prepared by coprecipitation reaction. Under VUV excitation at 147 nm, the red emission colorimetric purity of (Y, Gd)BxV1- xO4-x :Eu3 phosphor is much better than that of commercial PDP (plasma display panels) phosphor (Y, Gd)BO3:Eu3 . But its relative emission intensity is only about 90% of the commercial phosphor.     

Red Emitting Phosphor (Y, Gd) Bx V1- x O4- x :Eu3 + with High Color Purity for Plasma Display Panels

(Y, Gd)BxV1- xO4-x :Eu3 phosphors were prepared by solid state reaction. The red emission color purity of (Y, Gd)Bx V1 - x O4-x :Eu3 phosphor is much better than that of the recent widely-used commercial red emitting phosphor (Y,Gd)BO3:Eu3 and its relative emission intensity is 84% of the commercial phosphor (Y, Gd)BO3 :Eu3 . It is expected that (Y, Gd) Bx V1 -x O4: Eu3 phosphor will be a promising candidate for PDP (plasma display panels) application.     

Cooperative energy transfer in Eu3+,Yb3+ codoped Y2O3 phosphor

Under 980 nm laser excitation,red emission(5D0-7FJ(J=0,1,2)) of Eu3+ was observed in cubic Y2O3 codoped with Eu3+ and Yb3+.The dependence of the upconverted emission on doping concentration and laser power was studied.Yb3+ emission around 1000 nm(2F5/2-2F7/2) was reported upon excitation of Eu3+ ions.The decay curves of 5DJ(J=0,2) emission of Eu3+ under excitation of 266 nm pulse laser were examined to investigate the Eu3+→Yb3+ energy transfer process.Cooperative energy transfer process was discussed as the possible mechanism for the visible up-conversion luminescence of Eu3+ and near-infrared down-conversion emission of Yb3+.     

Gd2-xEuxWO6红色荧光粉的溶胶-凝胶合成及其荧光性能分析

利用溶胶-凝胶法制备系列Gd2-xEuxWO6红色荧光粉,XRD测试表明Gd2-xEuxWO6具有单斜晶系结构;在298 nm或395 nm激发下,荧光粉主要发射出对应于Eu3+5的D0→7 F2能级跃迁的612 nm红光;当Gd2-xEuxWO6中Eu3+的掺杂量为50％时,荧光粉612nm红光强度最强;在合成过程中适当添加聚乙二醇(PEG)和柠檬酸能改善荧光粉的红光发射强度.     

Luminescence and Energy Transfer Properties of Ca2Gd8(SiO4)6O2∶ A (A=Pb2+,Tm3+)Phosphors

Ca2Gd8(SiO4)6O2∶ A(A=Pb2 , Tm3 )phosphors were prepared through the sol-gel process. X-ray diffraction(XRD), scanning electron microscopy(SEM)and photoluminescence spectra were used to characterize the resulting phosphors. The results of XRD indicate that the phosphors crystallized completely at 1000 ℃. SEM study reveals that the average grain size is 300～1000 nm. In Ca2Gd8(SiO4)6O2∶ Tm3 phosphors, the Tm3 shows its characteristic blue emission at 456 nm(1D2-3F4)upon excitation into its 3H6 - 1D2(361 nm), with an optimum doping concentration of 1mol% of Gd3 in the host lattices. In Ca2Gd8(SiO4)6O2∶ Pb2 , Tm3 phosphors, excitation into the Pb2 at 266 nm(1S0-3P1)yields the emissions of Gd3 at 311 nm(6P-8S)and Tm3 at 367 nm(1D2 -3H6)and 456 nm(1D2-3F4), indicating that energy transfer processes of Pb2 - Gd3 and Pb2 - Tm3 have occurred in the host lattices.     

Photoluminescent properties of Ca2RE8(SiO4)6O2:A (RE=Y, Gd; A=Pb2+, Mn2+) phosphor films prepared by sol-gel process

Ca2RE8(SiO4)6O2:A (RE=Y, Gd; A=Pb2 , Mn2 ) phosphor films were dip-coated on quartz glass substrates through the sol-gel process. X-ray diffraction (XRD), photoluminescence (PL) spectra as well as lifetimes were used to characterize the resulting films. Under short wavelength UV excitation, the film showed a red emission with medium intensity. The decay curve of Mn2 luminescence in Ca2Gd8(SiO4)6O2:Pb Mn film could be fitted into a single exponential function. The lifetime of Mn2 was 10.21 ms in Ca2Gd8(SiO4)6O2.     

复合熔盐法合成Y2O3.Eu3+红色荧光粉

以草酸钇铕(Y2(C2O4)3:Eu3+)为前驱体,采用复合熔盐(NaCl+S+Na2CO3)协助焙烧法合成Y2O3:E.u3+红色荧光粉.利用XRD、SEM、光谱分析等测试和分析荧光粉粒径、颗粒形貌以及发光性能.主要考察复合熔盐配比、用量以及焙烧温度和时间对Y2O3:Eu3+荧光粉发光性能的影响.结果表明,NaCl在...     

Flux and concentration effect on Eu^3＋ doped Gd2（MoO4）3 phosphor

A novel red emitting phosphor Gd2（MoO4）3：Eu^3＋ was prepared by solid reaction, using Gd2O3, Eu2O3 and WO3 as starting matedals and NH4F as flux. The effects of flux content and Eu^3＋ concentration on the crystal structure, morphology and luminescent properties were investigated using XRD, SEM and fluorescent spectrum measurement. The XRD patterns showed that the resultants had the monoclinic structure. With the increase in flux amount, their crystallization significantly improved. The SEM images indicated that the mean size of the phosphor particles was around 2 μm, and agglomeration of the phosphor particles appeared while introducing higher flux amount. The excitation spectra exhibited more intense f-f transitions originating from ground state 7^F0 to upper states 5^L6 and 5^D2 than the charge transfer band. The concentration quenching of Eu^3＋ emission indicated that energy transfer from Eu^3＋ to molybdate host existed even at lower Eu^3＋ concentration.     

红色荧光粉La2O3：Eu3＋的合成及发光性质

利用复合沉淀法制备了性能稳定的红色荧光粉La2O3：Eu3＋,同时研究了煅烧温度及掺杂Eu3＋浓度对La2O3：Eu。’发光性能的影响．通过X射线粉末衍射（XRD）和扫描电子显微镜（SEM）来表征荧光粉的晶体结构和颗粒大小及形貌：用激发光谱和发射光谱以及荧光衰减曲线来袁征荧光粉的荧光性能．结果表明：煅烧温度在900℃时,所制备样品为六方晶系La2O3：Eun;SEM图显示掺杂Eu0＋含量为5％的La2O3颗粒直径为15μm左右．最大发射波长和激发波长分别为626nm和396nm,发射光谱中596nm和626nm的发射峰对应的是Eu3＋离子的0D—F1和5D—F2跃迁,其荧光寿命为0．754ms．     

Luminescent properties of MMgP_2O_7：Eu~（3＋）（M=Ca,Sr,Ba） phosphor

A series of red phosphors Eu3+-doped MMgP2O7(M=Ca,Sr,Ba) were synthesized by solid-state reaction method.X-ray powder diffraction(XRD) analysis confirmed the formation of pure CaMgP2O7,SrMgP2O7 and BaMgP2O7 phase.Photoluminescence spectra of MMgP2O7(M=Ca,Sr,Ba):Eu3+ phosphors showed a strong excitation peak at around 400 nm,which was coupled with the characteristic emission(350-400 nm) from UV light-emitting diode.The CaMgP2O7:Eu3+,SrMgP2O7:Eu3+ and BaMgP2O7:Eu3+ phosphors showed strong emission bands peaking at 612,593 and 587 nm,respectively.Due to the difference of the ion sizes between Ba2+(0.142 nm),Sr2+(0.126 nm),Ca2+(0.112 nm),Mg2+(0.072 nm) and Eu3+(0.107 nm),Eu3+ ions were expected to substitute for different sites in CaMgP2O7,SrMgP2O7 and BaMgP2O7 lattice.