木质素、聚羧酸及其复配型和共聚型减水剂性能比较研究

将共聚型木质素-聚羧酸系高效减水剂、未聚合木质素磺酸钙的聚羧酸系高效减水剂、木质素磺酸钙和复配型木质素-聚羧酸系高效减水剂的性能进行比较,探讨了四种不同减水剂对水泥水化的影响。结果表明:共聚型木质素磺酸钙-聚羧酸系高效减水剂可以使木钙中含有使水泥净浆产生闪凝现象的杂质得以减少或消除,使聚羧酸系高效减水剂的保水性提高,且成本远低于聚羧酸系高效减水剂。复配型木质素磺酸钙-聚羧酸系高效减水剂随掺量增加,水泥净浆强度下降,产生负面叠加效果,共聚型木质素磺酸钙-聚羧酸系高效减水剂随掺量增加,水泥净浆强度提高,改善了木钙造成水泥净浆强度降低的缺陷。共聚型的木质素磺酸钙-聚羧酸系高效减水剂相对于复配型对硅酸三钙水化有一定的促进作用。     

我国混凝土外加剂概况与聚羧酸系高性能减水剂的主要性能特点

本文介绍了我国混凝土外加剂概况,重点介绍减水剂发展史上第三次重大突破的聚羧酸系高性能减水剂对水泥的适应性与混凝土主要性能的研究,并与氨基磺酸盐、脂肪族、萘系等高效减水剂做了对比试验,表明KS—JS具有独特的优点：对多种水泥的适应性更好,掺量低（0．15％-0．4％,相当于其他高效减水剂的1／3～1／5）、减水（20％～35％）增强（早期增加30％～140％,后期增加20％～80％）幅度大,混凝土塌落度损失小,特别适于配制高强高性能混凝土,综合性能聚羧酸系KS—JS优于氨基KJ—FB〉脂肪族KJ〉萘系：不必用甲醛,生产与使用过程对环境无任何不良影响,是一种安全、绿色环保型高性能减水剂。     

聚羧酸系高性能减水剂的研制及其性能

根据聚羧酸系高效减水剂的结构特点，采用正交试验分析法，分析研究了带羧基、磺酸基、聚氧化乙烯链酯基等活性基团的不饱和单体的物质的量之比（摩尔数比）及聚氧化乙烯链的聚合度等因素对聚羧酸系减水剂性能的影响，从而得出合成聚羧酸系高性能减水剂的一种最佳配方，并对试制产品进行了性能试验。结果说明，聚羧酸减水剂具有优良的分散能力，能较长时间地保持其流动性，与不同水泥的相容性好，水泥浆体粘聚性好，配制的混凝土性能良好。     

聚羧酸系高效减水剂在商品混凝土中的应用

探讨聚羧酸系高效减水剂的作用机理,剖析其在商品混凝土中应用的技术特点,说明聚羧酸系高效减水剂具有减水率高、坍落度损失小和水泥适应性好等优点,具有良好的技术经济效益.     

聚羧酸高效减水剂与其它高效减水剂的复合效应研究

本文介绍了聚羧酸系减水剂的性能特点及研究状况,并在此基础上,研究了聚羧酸系高效减水剂与萘系、氨基磺酸盐系及脂肪族系高效减水剂复合使用对水泥净浆流动度的影响。结果表明:聚羧酸系高效减水剂与萘系及氨基磺酸盐系高效减水剂的复合效应差,而与脂肪族系高效减水剂的复合效应较好。     

聚羧酸系高效减水剂在商品混凝土中的应用

探讨聚羧酸系高效减水剂的作用机理,分析其在商品混凝土中应用的技术特点,工程实践表明;聚羧酸系高效减水剂具有减水率高、坍落度损失小、水泥适应性好等优点,具有良好的技术经济效益。     

几种复合减水剂的分散效应与作用机理

采用合适比例的聚羧酸系高效减水剂复合改性脂肪族系、三聚氰胺系和萘系高效减水剂,制备了3种复合减水剂,研究了它们对水泥净浆性能及混凝土性能的影响;通过Zeta电位测定和X射线光电子能谱(XPS)分析研究了复合减水剂的分散作用机理.结果表明:脂肪族系-聚羧酸系复合减水剂是静电斥力起了主导作用,三聚氰胺系-聚羧酸系复合减水剂和萘系-聚羧酸系复合减水剂是聚羧酸系减水剂的空间位阻效应起了主导作用.     

聚羧酸系减水剂的合成及其性能研究

合成了聚羧酸系减水剂（TW—PS）。实验表明,TW—PS对水泥具有很好的分散性和分散保持性,其综合性能明显优于茶系和氨基磺酸系减水剂．与国外同类产品性能相当。     

梳形聚羧酸系减水剂与水泥的相容性研究

选用4种梳形聚羧酸系减水剂、4种水泥、3种可溶性硫酸盐、2种矿物超细粉等原材料，通过测试掺减水剂水泥浆体的Zeta电位、净浆流动度损失以及混凝土性能等，说明聚羧酸系减水剂结构与性能、水泥组成与性能、电解质多价阳离子及矿物超细粉掺量等对聚羧酸系减水剂与水泥之间的相容性有重要影响．     

聚羧酸系高性能减水剂的合成与性能

分析了聚羧酸系高性能减水剂的分析结构与作用机理，并由（甲基）丙烯酸，（甲基）丙烯磺酸钠，聚氧乙烯链基烯丙酯等单体在过硫酸盐的引发作用下共聚合成聚羟酸系PC23高性减水剂，该产品具有优良的分散功能，保持流动性的时间较长，与不同水泥的相容性好，水泥浆体粘聚性好，其分散作用效果远远大于萘系高效减水剂，与国外同类产品的性能相当。     

含乙烯基苯磺酸钠单体聚羧酸减水剂的合成

本文以丙烯酸(AA),甲基丙烯酸甲酯(MMA),对乙烯基苯磺酸钠(p-VBS)为主要原料,以过硫酸铵为引发剂,采用水溶液聚合的方法合成了一种聚羧酸系减水剂。通过正交试验,以净浆流动度为主要指标,分析得出了原料的最佳配比AA∶MMA∶p-VBS=1.2∶2∶1,反应时间为6小时。加大引发剂用量可以提高水泥的净浆流动度,加料方式对转化率及产物的性能有较大影响,采用混合单体和引发剂溶液同时滴加得到产物的净浆流动度较大。     

聚醚型聚羧酸减水剂的侧链结构对其性能的影响

采用烯丙基聚氧乙烯醚(APEG)、丙烯酸(AA)、马来酸酐(MA)及甲基丙烯磺酸钠(MAS)为单体,以过硫酸铵为引发剂,在水溶液中共聚合成了具有不同长度侧链的聚醚型聚羧酸减水剂。利用凝胶渗透色谱(GPC)测定了不同侧链结构减水剂的分子质量,进而研究了不同分子质量的聚醚型聚羧酸减水剂在水泥颗粒表面的吸附行为对水泥的分散性能和水泥早期水化的影响。结果表明,水泥颗粒对聚醚型聚羧酸减水剂的吸附具有选择性,在相同条件下,水泥颗粒会优先吸附单一侧链结构聚醚型聚羧酸减水剂中分子质量较高的减水剂分子;分子质量适中的复合侧链聚醚型聚羧酸减水剂比单一侧链和分子质量过大或过小的复合侧链聚醚型聚羧酸减水剂更容易在水泥颗粒表面上发生吸附,对水泥颗粒具有显著的分散性能,同时能够显著地延缓水泥早期水化。     

The compressive strength of cement blocks permeated with an organic phase change material

The authors investigate the feasibility of constructing walls and partitions with enhanced heat storage capability from cement blocks permeated with an organic phase change material (pressed stearic acid). The blocks are lightweight, easy to produce and are cured in the same way as cement or concrete.The ratio of components (cement, stearic acid (SA) and water) was optimized with respect to compressive strength. With normal portland cement, the best compressive strength 2.2 MPa was obtained with a ratio C:SA:W of 1:0.8:0.65 (i.e. 32% stearic acid) after 28 days of curing. This was increased to 4.4 MPa when high early strength cement was used, about as strong as Sipporex, lightweight concrete or lightweight clay bricks.As expected, the compressive strength decreased linearly with temperature between 25°C and 100°C, at a rate of 15 kPa/°C. The drying shrinkage of the modules was found to be 50% greater than for cement mortars. The addition of fibreglass gave only a 15% increase in the compressive strength. Samples containing 35% fatty acid showed surface deterioration after 200 thermal cycles (between ?5°C and 6 °C) while none was observed with those containing 32%. The dynamic modulus of elasticity did not change after 200 cycles.     

新型聚羧酸减水剂的研究

以丙烯酸类单体及聚乙二醇单甲醚为主要原料,制得聚乙二醇单甲醚—丙烯酸酯类大分子单体,再与丙烯酸类单体聚合制备了一种新型HPA聚羧酸减水剂。HPA对水泥具有高分散性,其掺量为0.15%、水灰比为0.29时,水泥净浆流动度可达250-290mm。     

一种聚羧酸高性能缓凝减水剂的制备与性能测试

以顺丁烯二酸酐(MA),α-甲基丙烯酸(MAA),烯丙基聚氧乙烯醚-1000(APEG- 1000)为单体,过硫酸铵(NH4S2O8)为引发剂,合成一种聚羧酸高性能缓凝减水剂.通过红外光谱对减水剂分子共聚反应进行表征,扫描电镜观察水化物微观结构,X射线衍射观察对水化物的影响,进行水泥净浆性能测定.结果表明,在水灰比0.29,减水剂掺量为水泥质量0.3％的情况下,水泥净浆流动度达到340mm,减水率达到30.4％,具有较强的缓凝效果,初凝和终凝时间达到483mm和1320mm.硬化水泥浆体抗压强度得到提高,与空白样对比,7d和28d抗压强度比达到了121.6％、138.2％.     

石膏种类对缓凝剂辅助塑化效应的影响

以前人们主要通过试验研究减水剂-水泥二元体系中不同石膏品种所起作用,本文使用自磨水泥,萘系高效减水剂,采用三聚磷酸钠、葡萄糖酸钠、六偏磷酸钠、柠檬酸及白糖等缓凝剂,通过水泥净浆试验（测定净浆流动度和流动度经时损失）,研究了不同石膏种类及掺量高效减水剂-缓凝剂-水泥三元体系的缓凝剂的辅助塑化效应。     

水泥加固酸污染土无侧限强度特征

污染土是利用水泥固化处理后,土体的强度得到提高。针对该项技术,采用水泥固化法处理酸污染土,通过两种试验方案,对水泥加固酸污染土的无侧限抗压强度特性进行研究。试验所用酸污染土用浓硫酸配置人工制备而成,并考虑了不同水泥掺量、不同硫酸浓度和不同龄期对水泥加固酸污染土强度的影响。试验表明:水泥固化酸污染土的强度与水泥掺量和硫酸含量有密切关系,二者共同作用决定其强度的变化。在一定硫酸浓度(2~16g/kg)条件下,伴随硫酸含量的升高,水泥掺量较低时,无侧限抗压强度整体呈明显下降的趋势;水泥掺量较高时,无侧限抗压强度呈缓慢上升的趋势。随着水泥掺量提高,土样的无侧限抗压强度达到峰值时所对应的硫酸含量也逐渐变大。     

不同缓凝剂对高贝利特硫铝酸盐水泥性能的影响及机制

以凝结时间和流动度等宏观测试为基础,结合水化热、热分析(TG-DTG)和X射线衍射(XRD)等微观测试,研究了硼酸、柠檬酸和葡萄糖酸钠对高贝利特硫铝酸盐水泥性能的影响以及影响机制.结果表明:3种缓凝剂对高贝利特硫铝酸盐水泥的缓凝作用和流动性均有积极的影响,硼酸主要通过阻碍水泥熟料溶解来延缓砂浆的凝结,柠檬酸和葡萄糖酸钠主要通过对水泥熟料溶出的Ca^2+、Al^3+等离子的络合和吸附作用来阻碍AFt晶体的形成,从而起到对砂浆的缓凝作用;3种缓凝剂通过影响AFt晶体的微观形貌和分布,对水泥石的力学性能产生了不同的影响.     

生物基减水剂对水泥水化进程影响及减水机理

将玉米化工醇釜残物开发为新型的生物基减水剂,采用傅里叶变换红外光谱（FTIR）对其进行表征.结合X射线衍射（XRD）图谱分析和扫描电镜（SEM）研究生物基减水剂对水泥水化产物生成和微观形貌的影响,进一步从ζ 电位、减水率、凝结时间和抗压强度分析     

改性醚类聚羧酸超塑化剂的制备及性能研究

本文以甲基烯丙醇聚氧乙烯醚(TPEG)、丙烯酸(AA)和甲基丙烯酸羟乙酯(HEMA)为主要原料,通过水溶液共聚反应合成一种聚羧酸高效减水剂,探讨了丙烯酸、甲基丙烯酸羟乙酯用量对减水剂性能的影响。此外还进行了不同种类聚羧酸减水剂的性能对比研究。