介绍连铸轴承钢降低钢中氧含量采取的一些保护浇注措施。工业试验结果表明,在连铸生产过程中,开浇阶段钢水的二次氧化是钢中氧含量增加的主要原因。采取保护浇注措施可使轴承钢连铸坯的增氧量减少,氧含量可降低到10×10~(-6)以下。     

Pulsating electromagnetic casting technique for slab casting

Abstract

To improve the surface quality of cast slabs in the steelmaking process, the pulsating electromagnetic casting (EMC) technique was developed and assessed using a slab casting bench scale test. Numerical simulation of the magnetohydrodynamic field and numerical simulation of the toughness of the mould were also conducted for the slab casting plant test. Consequently, the mould and coil for slab casting plant tests with pulsating EMC were manufactured and the basic functions were verified. Finally slab casting plant tests with the pulsating EMC technique were conducted.     

汽车压铸及铸造铝合金

介绍了汽车铝合金中压铸、铸造合金的比例,变化趋势,在某些国家地区的产量。详细介绍了日本和美国近些年来各类汽车铝材的发货量,中国和日本压铸、铸造铝合金的化学成分、性能、特点及应用,各种铸造铝合金的热处理规范,汽车用高强度铸造铝合金的特点,典型汽车铸造铝产品的选材、生产与性能。介绍了压力铸造、金属型低压铸造、科斯沃斯法、气化模铸造工艺,列出了低压铸造工艺生产的各类铸件特征、材料和工艺。预测了汽车用铝的前景。     

低液位铸造技术在铝合金扁锭生产中的应用

介绍低液位铸造技术的核心,石墨内衬对铸造的扁锭提供了理想的表面,铸造出的扁锭表面平滑无偏析瘤,偏析深度仅200μm～500μm,铸锭壳区厚约1μm,可减少铣面量50％,两大面只需铣削2mm～4mm,减少热轧切边量17％,大大提高了扁锭的成材率。     

高强Al-Ni系铸造铝合金的挤压铸造及强化机制

为了开发新的高强铸造铝合金材料,分别采用3种铸造工艺,砂型铸造、金属型铸造和挤压铸造,制备了一种以Al-Ni共晶体系为基础的AlZn6Ni4Mg2Cu铸造铝合金材料。研究了Ni元素、热处理和铸造工艺对其微观组织、力学性能的影响规律,揭示了其强化机制。结果表明:4%(质量分数)的Ni在该铝合金中形成了大量的共晶组织(α-Al+Al_3Ni),同时改善其力学性能和铸造性能,起到了共晶强化的作用;固溶和时效热处理导致Al_3Ni相的球化和MgZn_2相的时效析出,提高了该铝合金的强度;相比砂型铸造和金属型铸造,挤压铸造时该铝合金的晶粒和Al3Ni相最细小,力学性能最佳,抗拉强度为586 MPa,断后伸长率为3.5%。由此得出:AlZn6Ni4Mg2Cu铸造铝合金的强化机制为η(MgZn_2)相的时效强化和Al_3Ni相的弥散强化,挤压铸造加T6热处理后,该铝合金的力学性能达到最佳值。     

薄板坯连铸高拉速技术研究

介绍了唐钢薄板坯连铸机实现高拉速的关键技术。通过对结晶器铜板冷却、结晶器液位检测及LQG控制、抗鼓肚模型、INMO结晶器振动台、高拉速浸入式水口、高拉速保护渣、扇形段非均匀辊列设计及二次冷却等技术的研究、优化和应用,使薄板坯连铸拉速达到6 m/min,并且结晶器液位稳定,铸坯合格率达到99.8%以上。     

板坯高拉速的研究与实践

连铸机的高拉速生产是大幅度提高连铸生产效率的最有效措施之一。为了解决连铸中间包寿命低与连铸机拉速慢而导致炉机不匹配的问题,从中间包寿命提高与拉坯速度调控两方面入手,通过优化设备结构与提高连铸机效率两种手段对生产工艺进行优化。结果表明,整体工艺优化后可以大幅提高炉机匹配能力,加快钢水消耗,并提高了连铸机的生产效率,为高效连铸打下了坚实基础。     

连铸坯拉速对结晶器卷渣现象的影响

高拉速连铸具有高效、低成本的特点,是未来连铸的发展方向。以常规板坯结晶器为研究对象,采用大涡模拟方法对结晶器内的卷渣现象深入分析。结果表明,在连铸坯拉速较低的情况下,结晶器流场较为稳定,钢液冲击速度较小,上返流速度较小,界面波动幅度不大。在高拉速的情况下,钢液冲击速度增加,渣金界面速度及卷渣数量明显提高。通过界面最大速度分析,建立了一个临界卷渣速度的计算准则,发现不同拉速情况下的临界卷渣速度是不一样的,造成这种现象的原因在于卷渣机理的不同。本模型对控制常规板坯高拉速连铸生产具有一定指导意义。     

Vacuum casting of steel

Despite potential difficulties indicated by a preliminary survey, the seriousness of the hydrogen problem necessitated development of a satisfactory vacuum casting technique.     

非稳态连铸过程拉速-冷却水协同优化方法

针对非稳态连铸冷却强度异常易导致铸坯质量缺陷的问题,从系统冷却角度提出一种改进的遗传算法对连铸拉速、冷却水等工艺进行协同优化。基于国内某钢厂3个月的工业连铸数据分析发现,开浇、终浇、换中间包、换水口等非稳态连铸由于拉速与冷却水协同不好导致冷却强度不足,影响铸坯质量与连铸效率。建立过程冷却强度优化模型,从优化目标、选择算子等方面对遗传算法进行改进,在生成可行解的同时提高模型收敛速度与优化能力。结果表明,模型优化方案符合现场工艺规则,通过适当提高二冷水量,非稳态连铸系统热量释放平均由45.87%提升至49.05%,处于合理区间内。该优化方法可为连铸系统生产管控提供指导。     

Microstructures of electromagnetic casting and direct chill casting LY12 aluminum alloys

1　INTRODUCTIONElectromagneticcasting (EMC)isatechnologydevelopedbythecombinationofmagnetohy drodynamics (MHD )andcastingengineering[13] .TheEMCtechnologydependsontheelectromagneticforcetopreventthemetalfromtouchingthemold .Dependingontheinteractionofeddycurrentsinducedinthemetalandthemagneticfieldoftheinductor ,theliquidmetalcolumniskeptstable[4 6 ] .Thecon tactlesscastingofEMCmayeliminatetheliquidationbuild upsandfeathercrystals ,relievethescalpingop erationbeforethehotrollprocess …     

消失模铸造工艺在阳极钢爪铸造中的应用

介绍了消失模铸造工艺特点，以及在钢爪铸造过程中的特殊要求。丹江铝业公司四期技改工程中阳极钢爪的铸造全部采用消失模铸造工艺，这在铝行业的阳极钢爪铸造技术上属新工艺。     

Permanent mold casting

<正>Spring and Autumn Period(770 B.C.-476 B.C.)Bronze Height:32.4 cm As early as 2,500 years ago in ancient China,the permanent mold(metallic mould)was adopted to cast bronze coins.Due to its high production efficiency,the permanent mold casting was then widely used in the production of farm     

方坯连铸拉速波动时铸坯温度场的研究

根据连铸大方坯的凝固传热特点，应用二维非稳态传热有限元数学模型，分析在拉速波动过程中铸坯凝固时的温度分布情况，为避免在生产中由于拉速波动而产生缺陷提供了一定的理论依据。     

应用PMO提高连铸坯生产拉速及成分均匀性

为了实现电炉厂提产增效的目标,研究了脉冲磁致振荡(PMO)在提高铸坯生产拉速中的应用潜能。结果表明,优化PMO处理参数可以适应生产拉速提高的要求,并改善铸坯的中心偏析和宏观偏析。当连铸拉速提至1.05 m/min,PMO脉冲频率为1.16K_f Hz,峰值电压为1.00K_iV处理参数(K_f和K_i分别为仪器的放电频率和电压峰值)时, 铸坯横断面碳偏析指数可控制在1±0.05内;当连铸拉速提至1.15 m/min,PMO脉冲频率为1.28K_fHz,峰值电压为1.00K_iV处理参数时,铸坯横断面碳偏析指数可控制在1±0.07内。试验证明,在高拉速条件下通过保证单位时间内对钢液施加的脉冲能量可以使连铸坯质量得到有效改善。     

高拉速连铸结晶器的非正弦振动振幅

利用结晶器传热模型、热/应力模型和现场数据,建立了结晶器内液体摩擦力计算模型,利用该模型分析了某钢厂2.0m/min拉速下结晶器非正弦振动振幅对液体摩擦力的影响,给出了振幅选取原则和确定方法。结果表明:拉速一定时采用小振幅振动可限制最大液体摩擦力,增大保护渣耗量,减小负滑脱时间,随拉速提高应适当增大振幅,以改善振动效果;结合现场工艺,确定拉速2.0m/min时的适宜振幅为±4mm,拉速升至2.2m/min,振幅相应增至±4.5mm;保护渣膜厚度计算结果符合生产实际,为研究结晶器内润滑机理提供了条件。     

压铸模具的试模

简述了压铸模具试模的目的及操作注意事项,阐述了试模工艺参数对压铸件品质的影响以及参数调整要领。通过模具实例介绍了压铸模具试模件缺陷的分析思路及处理方法。     

拉速对包晶钢镀锡板连铸坯中夹杂物的影响

为了研究提高拉速对包晶类镀锡板连铸坯中夹杂物的影响,采用自动扫描电镜研究了不同拉速下包晶类镀锡板连铸坯中夹杂物的分布规律。结果表明,将包晶类镀锡板连铸拉速从1.3 m/min依次提高到1.4和1.5 m/min时,结晶器液面波动大于3 mm的比例都小于0.40%。拉速为1.4和1.5 m/min下连铸坯厚度四分之一处大于3μm的夹杂物数密度平均值分别为1.15和1.36个/mm²,面积百分数平均值分别为0.001 9%和0.002 4%,均低于拉速为1.3 m/min时的测量值。将拉速从1.3 m/min提高到1.5 m/min过程中,结晶器液面控制平稳,连铸坯表层大于10μm夹杂物数密度和面积百分数均呈减小趋势,最终实现了包晶类镀锡板高拉速稳定的工业化生产。