Functionalized Ethylene Propylene Rubber Prepared in a Co-Rotating

The functionalization of EPR with glycidyl methacrylate (GMA)function by melt free radical grafting in a co-rotating twin-screw extruder is investigted. GMA is used as the monomer,styrene (St) is used as the comonomer in order to enhance the dispersion between EPR and GMA. The potential of using a GMA modified EPR (EPR-g-GMA) as the toughness precursor is examined as well. The presence of EPR-g-GMA reduced the particle size of the dispersed phase (PBT) along with improved cohesion between EPR and PBT phases. The results show that the grafting yield of EPR-g-GMA is up to 4.7 phr (grams per 100 grams of EPR) and the particle size of the dispersed phase attain-s to about 0.5μm, the Izod notch impact strength of PBT/EPR-g-GMA can reach to 51.6 KJ/m2 , which is 31 times of the pure PBT.     

Toughness and characterization of reactive powder concrete with ultra-high strength

A number of three-point bending and fracture tests of 200 MPa-level reactive powder concrete (RPC) with the various fiber contents have been conducted to probe the nature and characteristics of toughness of RPC200. The contribution of the embedded fibers to improving the crack-resistant capacity, energy absorption capacity and toughness with various deformation mechanisms has been analyzed. Taking account of that the first-crack deformation, peak-load deformation and their improvement varied with the fiber contents and that the deformation mechanism affected differently the performance at the first crack and the peak load, we took the peak-load deformation of plain RPC200 as the reference deformation to measure the toughness of fibered RPC200. Two toughness indices T _2(n−1)(n) and FT _2(n−1)(n) have been formulated based on P-δ responses and P-CMOD responses. The indices quantify the toughness of RPC200 with the various deformation mechanisms relative to perfectly elastoplastic materials by setting the toughness level 2(n−1) as the initial reference. It is shown that the toughness index T _2(n−1)(n) reflects the function of fibers to improve the toughness of RPC with the deformation throughout specimens, but overestimates the contribution to enhancing the toughness in post-peak periods. It underestimates, on other hands, the contribution to improving the toughness in the period from the first crack to the peak load. In contrast, the toughness index FT _2(n−1)(n) properly presents the capability that fibers absorb energy and constrain crack propagation in the matrix when the deformation is concentrated on the open crack. The proposed index unveils the contribution of fibers to toughening RPC200 both in the period from the first-crack to the peak load and in the period of post peak. This characterization method not only reveals the nature of toughness but also levels the toughness of RPC200. It could provide a way to establish an objective toughness characterization for RPC200 and facilitate its applications. Supported by the New Century Excellent Talents Program (Grant No. NCET-05-0215), the Natural Science and Engineering Research Council of Canada (Grant No. PGS D2 2006), the Laboratory Innovation Plan of Beijing Science and Education Committee (Grant No. JD102900671) and the National Basic Research Project of China (“973” Project) (Grant No. 2002CB412705)     

新的陶瓷缺口试件制备方法及其在断裂韧性测试中的应用

利用模压注塑的方法制出陶瓷缺口试件生坯,然后烧结制成缺口试件。这种方法制备的缺口试件其缺口半径可按需要在很大范围内变化以供选用,其最小可达几μｍ;而且缺口光洁度一致性好;可以很好地用于陶瓷材料缺口强度和断裂韧性的测试。     

微波活化催化法由丙烷制取丙烯和乙烯

用微波活化催化法从丙烷制取了丙烯和乙烯。在 Pd/c 催化剂情况下,其丙烯、乙烯综合收率可达73.35%。催化剂活性在2小时内无明显变化。     

灰口铸铁HT100及其补焊焊缝断裂韧性的研究

采用短棒试样测定了普通灰口铸铁及其补焊焊缝的平面应变断裂韧性ＫＩＣ。结果表明：ＨＴ１００灰口铸铁ＫＩＣ值可达２５ＭＰａｍ,经手工电弧焊或气焊补焊后的ＫＩＣ值明显下降,这在重要铸铁件的补焊过程中应引起注意     

XI00高钢级管线钢的组织特征及其对强韧性性能的影响

对两种化学成分相近但SEM组织差异较大的X100管线钢的SEM、TEM、EBSD组织特征研究和CVN测试分析表明,X100管线钢的组织特征为具有少量渗碳体、大量MA岛、马氏体板条和大量位错包．较低的奥氏体温度、塑性变形温度及较高的冷却速度是获得具有弥散分布的MA岛的关键因素．具有这种组织的X100管线钢具有优良的强韧性匹配性能．     

X100高钢级管线钢的组织特征及其对强韧性性能的影响

对两种化学成分相近但SEM组织差异较大的X100管线钢的SEM、TEM、EBSD组织特征研究和CVN测试分析表明,X100管线钢的组织特征为具有少量渗碳体、大量MA岛、马氏体板条和大量位错包.较低的奥氏体温度、塑性变形温度及较高的冷却速度是获得具有弥散分布的MA岛的关键因素.具有这种组织的X100管线钢具有优良的强韧性匹配性能.     

挤出机螺棱间隙内温度分布的近似解析解及最高温度计算

导出了挤出机螺棱间隙内温度分布的近似解析解，并由此计算和比较了在不同情况下的温度分布和最高温度。结果表明：各有关参数对温度分布和最高温度的影响都可以反映到无量纲数Ｇ，Ｃ和Ｂｒ对它们的影响中。建议以最高温度作为判断熔体是否会在间隙中发生热降解的定量指标，因此对如何在工程实际中避免这一不利现象具有指导意义。     

Preparation of Plate Fe_(60)Co_8Zr_(10)Mo_5W_2B_(15) Bulk Amorphous Alloy and Its Fracture Toughness

1Introduction Duwez[1]synthesizedthefoilAu Siamorphousalloyforthefirsttimewithrapidsolidification,whichinitiatedthepreparationofamorphousalloysintheprocessofalloysolidification,andthereaftertheresearchonamorphousal loysdevelopedrapidly.Since1980s,withthec…     

12Cr1MoV短期高温冲击断裂韧性及其参数的研究

针对实际运行中短期高温冲击对12Cr1MoV材料的断裂韧性及其参数的影响,根据实际工况温度的条件,对12Cr1MoV实施短期高温冲击,并通过裂纹张开位移(COD)三点弯曲实验的方法得出短期高温冲击后12Cr1MoV的断裂韧性及其参数.结果显示,经过短期高温冲击后的12Cr1MoV的材料与常温下所获得的断裂韧性及其参数具有较大的变化,说明短期高温冲击对材料的影响较大.     

混凝土中骨-浆界面断裂韧度的分布特性

在已有的断裂准则和试验数据的基础上，运用概率断裂力学与数理统计的基本理论和方法，对粗骨料与硬化水泥浆体界面断裂韧性的分布特性进行了研究，并提出了确定断裂韧性试验最少件数的途径。由于Weibull分布或对数正态分布常用来分析寿命分布问题，故优先考虑这2种模型。通过分析和计算得出：粗骨料与硬化水泥浆体界面断裂韧性服从对数正态分布，在置信度为0．9，相对偏差不超过5％的条件下，对应的断裂韧性最少件数估计在13件左右。通过断裂韧性分布特性的研究，将为粗骨料与硬化水泥浆体界面概率断裂分析与施工控制提供了参考依据。     

Nb-Ti微合金钢大线能量焊接热影响区组织和韧性的研究

在使用大线能量焊接低合金高强度钢时,为了提高焊接热影响区（HAZ）韧性,通常加入Ti或Nb。利用正交分析进行9组冶炼试验研究,对Ti、Nb2种元素进行多种添加量的重点考察。利用轧制的实验钢进行大线能量气电立焊实验,检验这2种元素对钢板强度、钢板韧性、钢板焊接热影响区韧性的影响。实验结果表明,Nb对钢板的强度和韧性都有很大影响,随着Nb含量的提高,强度增加;当w（Nb）≥0．005％时,随Nb含量提高,韧性呈下降趋势;对钢板焊接热影响区韧性影响最大的是Ti,Ti能阻碍晶粒长大,使热影响区性能得到改善。     

钢纤维掺量和基体强度对混凝土弯曲韧性的影响

采用两个基体强度和钢纤维的五种体积掺量进行组合试验，通过方差分析研究钢纤维体积掺量和混凝土基体强度对提高极限弯曲强度和达到极限弯曲强度后一定挠度区间内继续消耗能量影响的显著性，比较钢纤维体积掺量和基体强度不同组合时的增韧效果．研究结果表明：钢纤维体积掺量和基体强度均为影响钢纤维混凝土弯曲韧性的显著因素．     

新型受阻酚防老剂合成及对橡胶防护性能研究

以3-（3,5-二叔丁基-4-羟基苯基）丙酸和正丁醇为原料,采用酯化反应,合成了新型受阻酚防老剂。并采用红外光谱、热重分析及荧光测试对合成的防老剂结构进行表征。结果表明,合成的防老剂是3-（3,5-二叔丁基-4-羟基苯基）丙酸正丁酯。受阻酚防老剂最佳合成实验条件是回流时间8h、催化剂质量分数3.2%、丙酸与正丁醇物质的量比为1∶2。采用力学性能测试、红外光谱、热重分析等方法研究了受阻酚防老剂对NR硫化胶的防护性能,结果表明受阻酚防老剂对NR硫化胶有显著的防老化作用,其防老化效果优于防老剂BHT,且对橡胶无色泽污染性。     

橡胶调节剂二哌啶乙烷的合成及其在聚丁二烯橡胶合成中的应用

为了合成特殊结构的聚丁二烯橡胶，在国内我们首次合成了二哌啶乙烷（ＤＰＥ），并进行了分析与鉴定．首次采用ＤＰＥ做丁二烯阴离子聚合的调节剂，考察了ＤＰＥ／ｎ－ＢｕＬｉ（正丁基锂）和ＤＰＥ／α－ＭＮＬｉ（α－甲基萘锂）比值对形成１，２－聚丁二烯（１，２－ＰＢ）微观结构调节规律，得到了１．２－结构为１００％的聚丁二烯．采用高分子设计方法，通过引入ＤＰＥ，合成了１，４－１，２两嵌段和１，２－１，４－１，２三嵌段聚丁二烯，ＤＳＣ－ＤＴＡ示差扫描量热仪测示表明：聚丁二烯的１，２－结构含量影响其玻璃化转变温度（Ｔｇ），一定嵌段比的聚丁二烯可以产生微观相分离．     

台区低压无功自动补偿对线损影响的研究

无功功率是影响低压网络线损的重要因素,利用低压无功功率自动补偿装置可实现配网无功功率动态补偿.通过对重庆市沙坪坝供电局某台区低压无功补偿的实际测试数据的比较,提出了台区低压无功补偿方案的建议.     

新型稀土防老剂的合成及对天然橡胶防护性能的研究

以3-（3,5-二叔丁基-4-羟基苯基）丙酸、La（NO3）3·H2O和氢氧化钠为原料,制备-种新型稀土橡胶防老剂。并采用红外光谱、热重分析及荧光测试对合成的防老剂结构进行表征,结果表明合成的防老剂为稀土镧与3-（3,5-二叔丁基-4-羟基苯基）丙酸配体中羰基配位得到的-种配合物。优化后得到稀土防老剂最佳合成实验条件：3-（3,5-二叔丁基-4-羟基苯基）丙酸与硝酸镧物料物质的量比为2：1,回流时间6h。采用力学性能测试、红外光谱、热重分析等方法研究了稀土防老剂对NR硫化胶的防护性能。结果表明,防老剂对NR硫化胶具有显著的防老化作用,其防老化效果优于市售酚类BHT防老剂,与胺类4010NA防老剂相当,且对橡胶无色泽污染性。     

碳纳米管的力学特性及其在改善水泥基材料性能中的应用

通过理论分析和数值模拟研究了碳纳米管的力学性能参数和其在轴向压缩以及弯曲荷载作用下的屈曲行为,并进行了用碳纳米管提高水泥基复合材料强度和韧性等力学性能的实验.结果表明:当好的分散效果被获得后,水泥基复合材料的强度和韧性可以得到明显的改善,而碳纳米管容易发生屈曲的特性是影响其作为理想增强材料的一个内在原因.     

煤中重金属元素的溶出潜力及其影响因素

水-煤相互作用是影响煤矿矿井水水质的重要因素之一。为揭示煤中重金属元素的溶出机制,利用连续化学提取、浸溶实验等方法分析了煤中10种重金属元素赋存形态,量化了水-煤相互作用过程中重金属元素平均溶出浓度,梳理了影响煤中重金属元素溶出的内在和外在因素。结果表明:①煤中的Hg和Cr主要以残渣态存在; Mo主要以残渣态和可氧化态存在; Ni、Cu、Co、Zn和Cd主要以残渣态、可氧化态和弱酸提取态存在; As和Pb主要以残渣态、可氧化态和可还原态存在。②各重金属元素的平均溶出浓度从高到低依次为Zn、Cu、Ni、Cr、Co、Mo、As、Cd、Pb、Hg,对应浓度分别为25.73、25.21、18.12、13.22、8.10、4.31、0.77、0.60、0.50、<0.10 μg·L^-1。③影响煤中重金属元素溶出的内在因素包括元素赋存含量、元素赋存状态和存在形式、煤炭产酸性能、水体Eh值等; 外在因素包括氧暴露条件、水-煤相互作用时间等。在内在和外在因素的共同影响下,导致了不同地区煤中重金属元素溶出特征具有较大差异。     

农村电网无功补偿措施及其经济效益分析

无功补偿是农村电网降损节能的重要措施,理论和实践证明,针对农村电网无功负荷的特点采取合理的无功补偿措施,能产生长久、可观的经济效益。