异步轧制高纯铝箔立方织构形成的微观过程

采用EBSD微取向分析方法,通过分析高纯铝箔冷轧后退火的再结晶初期立方取向晶核的形成过程,以及立方取向晶粒的长大行为,探讨了异步轧制高纯铝箔立方织构形成的微观过程。结果表明,异步轧制的样品中产生较强的C织构{112}111和旋转立方织构{001}110。立方亚晶优先在C取向形变基体内形核并长大,定向形核机制为主要因素。旋转立方织构有利于异步轧制高纯铝箔立方织构{001}100的形成和发展。     

冷轧变形量对Al-Mg-Si合金织构的影响

利用光学显微镜、扫描电镜分析了不同冷轧变形量对Al-Mg-Si合金显微组织和微观织构的影响。结果表明:随着变形量的增加,再结晶织构Cube{001}<100>会经由Goss{011}<100>逐渐演变为以Copper{112}<111>和S{123}<634>为主要取向的形变织构,而Goss{011}<100>的体积分数表现为先增大后减小的趋势;合金形变带织构主要由强度较高的Copper{112}<111>织构和强度较弱的Cube{001}<100>织构组成;当变形量小于20%时,晶粒主要取向为{001}、{012},变形量大于40%时,{011}、{112}、{123}成为主要的晶粒取向。     

CSP冷轧薄板退火过程再结晶机理的研究

采用EBSD分析方法,对CSP试验钢冷轧板退火过程中组织转变和再结晶织构的演变进行分析。结果表明,试验用钢的再结晶过程属定向形核,冷轧基体织构主要是成条状的{111}<110>、{111}<112>和{001}<110>取向。新的再结晶晶粒主要是{111}<112>和{111}<110>取向,且两种取向相互生成。在再结晶温度区间有利于形成{111}<110>和{111}<112>取向,在晶粒长大阶段会生成大量的对深冲性能无明显影响的{112}<110>取向转变。因此,控制再结晶温度区间内形成的{111}取向稳定存在而不发生转变,将有利于提高材料的深冲性能。     

湿H2气氛下CGO硅钢初次再结晶织构演变行为

通过对湿H2气氛下,相同退火温度、不同退火时间的CGO硅钢初次再结晶样品进行金相组织观察,并进行了EBSD微观织构分析,研究了CGO硅钢初次再结晶过程中的组织及再结晶织构演变行为。结果表明,在湿H2气氛下,820℃保温,CGO硅钢初次再结晶过程约在120 s时完成。随着退火时间的延长,γ面上{111}<112>织构含量逐渐减少,{111}<110>织构先减少后增多,随着再结晶的完成,部分{111}<112>取向晶粒向高斯{110}<001>取向转化的同时,也向{111}<110>取向转化,高斯{110}<001>织构含量逐渐增多。高斯取向晶粒较多是由{111}<112>取向晶粒转化而来,同时也证明了CGO硅钢高斯取向晶粒的二次再结晶异常长大生长机制为择优形核。     

形变诱导Inconel 625合金管材静态再结晶行为

使用室温压缩变形与再结晶退火处理研究了Inconel 625高温合金冷变形及再结晶行为,采用EBSD技术分析冷变形过程中的应变分布、晶粒尺寸变化、组织与织构演变,分析冷变形Inconel 625合金再结晶过程中再结晶分数、晶粒尺寸、组织及织构演变。研究表明,Inconel 625合金在变形量为35%~65%时具有良好的塑性,随着变形量的增加,晶粒尺寸减小,应变分布越均匀,{111}<112>织构和{110}<001>织构逐渐减弱,而{001}<110>织构和{112}<111>织构略为增强。冷变形Inconel 625合金再结晶退火处理后,随着退火温度与保温时间的升高,再结晶分数增大;随着变形量的增大,Inconel 625合金发生完全再结晶时温度减小,且发生完全再结晶时的晶粒尺寸变小,变形量为35%时,再结晶过程主要是{112}<111>织构{123}<634>变形织构转变为{110}<112>织构、{001}<100>织构与{124}<211>织构。随着变形量增加到50%及65%时,冷变形产生的{123}<634>织构在再结晶过程中转变成了{124}<211>织构。     

退火工艺和稀土元素对SPCC冷轧板再结晶过程及织构的影响

研究了退火工艺和添加微量稀土元素对SPCC冷轧低碳钢板再结晶过程及织构的影响。试验结果表明,提高加热温度加快了SPCC冷轧板再结晶过程,促进晶粒长大;稀土元素的加入阻碍了再结晶过程,抑制了晶粒长大,也明显地提高了稀土SPCC冷轧板有利于深冲性能的{111}<011>织构、{111}<112>织构和{001}<100>立方织构的密度。     

CGO硅钢各阶段织构遗传继承性的EBSD分析

利用EBSD技术对CGO硅钢热轧、中间退火、脱碳退火及二次再结晶退火组织及织构进行分析,研究了CGO硅钢各阶段加工制备过程中高斯{110}001晶粒的形状、尺寸及分布特点,分析了高斯取向晶粒在各工序过程中的遗传继承性特点。结果表明,CGO硅钢热轧板的次表层存在Goss取向晶粒,历经一次冷轧及中间退火后Goss取向晶粒基本消失,一次再结晶之后Goss织构仍不是主要织构,主要织构为{111}110和{111}112,说明Goss取向晶粒在二次再结晶退火前数量及尺寸上并不占优势,二次再结晶过程中Goss取向晶粒异常长大形成锋锐Goss织构。{111}110和{111}112织构组分的强度在一次冷轧中不断增加,{111}112织构组分的强度在二次冷轧后达到最大而{111}110织构组分是在初次再结晶后变强。     

新能源汽车用含稀土无取向硅钢生产过程中组织、织构演变

采用光学显微镜、X射线衍射仪及扫描电镜对含稀土无取向硅钢整个生产流程中的显微组织及织构演变进行研究。结果表明,热轧板在厚度方向上有显著的分层,即表层的再结晶层、过渡层、中间层的变形组织层,其织构主要包含铜型、黄铜型织构;正火后晶粒发生了完全再结晶,织构类型相对热轧基本无变化,但强度减弱;两次冷轧后的组织均为纤维组织,形成了以α、γ线性织构为主的织构类型,还出现了强度较高的反高斯织构如{001}<110>、{112}<110>、{111}<110>;脱碳退火后发生部分再结晶,织构相对于冷轧态α、γ线性织构强度均减小;在高温退火阶段晶粒发生再结晶,存在以{111}<112>、{111}<110>为主的γ织构,以及{100}<001>织构。     

高磁感取向硅钢轧制及热处理过程中的晶界和织构演化

采用电子背散射衍射(EBSD)对不同轧制和热处理态的高磁感取向硅钢的重合位置点阵(CSL)晶界和织构进行了研究。结果表明,热轧态取向硅钢截面织构呈层状分布,表层主要为{110}<001>Goss织构,1/4厚度主要为{001}<110>立方织构、{112}<111>铜型织构和{110}<001>Goss织构,而心部则形成较强的{112}<111>铜型织构、{111}<110>形变织构和{110}<001>Goss织构;常化处理后截面织构梯度变化不明显,但中心位置{112}<111>织构向{110}<001>Goss织构转变。冷轧退火态主要织构为{110}<001>Goss织构、{112}<111>织构和{111}<110>形变织构。二次再结晶后,则生成强烈的{110}<001>Goss织构。随着织构的变化,CSL晶界也发生了明显的转变。热轧态CSL重位晶界中∑3~∑29均有出现,但比例较低;常化处理后CSL重位晶界比例增加,冷轧退火后CSL晶界比例大幅提高,特别是∑3、∑7、∑9和∑15等晶界;二次再结晶后,由于CSL晶界发生了转化,CSL晶界类型减少,∑3、∑13等晶界比例增加,∑9晶界消失。     

基于CSP工艺一段式脱碳退火对取向硅钢初次再结晶晶界特征的影响

利用背散射衍射技术(EBSD),在一段式840 ℃不同时间脱碳退火条件下,研究了基于CSP工艺取向硅钢初次再结晶过程中的组织和结构变化。结果表明,在初次再结晶退火时间为4 min时织构类型较多,分别为{332}<`533>、{554}<225>、{111}<110> 、{001}<100>、 {111}<112>、{001}<110>、{110}<001>、{110}<110> 、 {112}<110>、{110}<112>、{112}<1`10>、{012}<001>和{111}<231>等。当初次再结晶退火时间延长为5 min时, {111}<112>取向晶粒数量明显增多,而{332}<`533>和{012}<001>取向晶粒比例下降。同时Σ3、Σ5和Σ9晶界比例升高,小角度晶界比例较少,而大角度晶界比例较多,这将有助于在二次再结晶退火时发生高斯织构。继续延长退火时间到6 min以后,Σ3、Σ5和Σ9晶界比例下降,小角度晶界比例提高,此时再结晶晶粒长大。     

The effect of precipitation on the evolution of recrystallization textures in an AA 8011 aluminum alloy sheet

The texture of an AA 8011 aluminum alloy sheet cold rolled by 95% showed a typical β-fiber, which runs from the copper orientation [C={112}〈111〉] over S [{123}〈634〉] to brass [B={011}〈112〉]. The development of annealing textures depended on annealing temperatures due to the interaction between precipitation and recrystallization. Upon annealing at a low temperature of 275°C, precipitation took place before recrystallization. This led to a weak recrystallization texture consisting of {011}〈122〉, {001∼〈100〉, and {hk0}〈001〉, among which the {011}〈122〉 orientation developed near large FeAl₃ particles as the main orientation and the cube [{001}〈100〉] orientation originating from the matrix was relatively weak. After annealing at 350 and 500°C, a strong cube texture developed along with a weak {011}〈122〉 orientation. When the cube orientation developed, the copper orientation disappeared most rapidly. These results were discussed based on the interaction between precipitation and recrystallization.     

高锰TWIP钢的冷轧变形行为

研究了低层错能奥氏体TWIP钢的冷轧组织和织构的演变。随着应变的增加,孪晶变形机制被激活。TEM、XRD等观察结果显示:随着应变量的增加,孪晶增加。在不同应变水平上,G{011}<100>织构都占主要位置。变形初始时,B{011}<211>织构强度较低,随着应变增加其强度显著增加。而E{111}<011>、Y{111}<112>、RG{011}<011>、Cu{112}<111>、CuT{552}<115>等织构在不同应变水平呈不同变化趋势。与其他织构相比,Cube{001}<100>织构强度相当低。     

MGH754合金挤压棒材的二次再结晶与织构

研究了ＭＧＨ７５４合金在二次再结晶过程中的组织和结构变化。结果表明，合金大热挤压状态具有细小的等轴晶组织，织构微弱，有利于进行殂变加工；二次再结晶后，组织为粗大的柱状晶，且出现强烈的织构；随着退火时间延长，「１１０」〈００１》和「１００」〈００１〉织构含量明显增加，而「１１０」〈１１１〉，「１１０」〈１１３〉和「１１２」〈１１１〉等织构的含量减少，合金棒材的纵向主要为〈００１〉取向。     

3104铝合金固溶及时效处理后的冷轧织构

应用取向分布函数（ODF）研究了3104铝合金经不同温度固溶及时效处理后的冷轧织构组态。结果表明：经固溶时效处理后其冷轧织构中存在强度较高的旋转立方织构v{001}〈110〉组分,此外也含有一定强度的c{112}〈111〉、B{110}〈112〉和S{123}〈634〉织构组分,明显不同于未经固溶时效直接冷轧样品的织构组态特征。可能的原因是经固溶和时效处理后溶质原子和析出相粒子形态和数量的变化,它们在变形过程阻碍了位错滑移,使晶粒转动受阻,进而使不稳定取向旋转立方织构被不同程度的保留下来;此外,固溶温度越高,冷轧样品中不稳定取向旋转立方织构组分取向密度越小,时效温度对后继冷轧织构的影响也应归结为析出相粒子在变形过程中对位错滑移的阻碍,进而影响晶粒转动。     

柱状晶对Fe-3%Si电工钢冷轧织构演变规律的影响

Fe-3%Si电工钢铸锭中普遍存在柱状晶,其晶体学及形状各向异性对随后的热轧、冷轧及退火织构产生很大的影响.利用xRD与EBSD技术对长轴分别平行于轧面法向(ND),轧制方向(RD)和横向(TD)的柱状晶冷轧样品的织构及组织进行了研究,并对晶界的特殊作用进行了分析.结果表明,中等压下量下,3种柱状晶样品具有不同程度的{001}织构遗传性,即3种样品均不同程度的摆脱了{111}线织构的形成;柱状晶长轴平行于ND和TD时,{001}取向在冷轧时得到大的保留;柱状晶长轴平行于RD时,得到最强的{111}〈112〉织构;柱状晶长轴平行于TD时,冷轧组织中旋转立方织构及{111}〈110〉织构较强.此外,3种样品的织构均表现出由立方→{001}〈130〉→{113}〈251〉的过渡路径,与等轴多晶样品沿α线和γ线转动的路径不同.不同方向的柱状晶晶界对冷轧变形过程中晶粒转动的作用不同,但因晶粒尺寸大而作用有限,且与初始取向相关.     

横轧3 104铝合金变形织构的研究

应用极图分析及织构定量计算的方法，研究了横轧对3104铝合金变形织构的影响，结果表明：在与常规轧制相同压下量的横向轧制下，3104铝合金中的｛112｝，｛213｝丝织构体积百分数均低于常规轧制时各组分的体积百分数，而横向轧制则使得｛102｝丝织构增加较多，在横向轧制过程中出现强旋转立方织构和新｛110｝＜557＞取向的织构。     

退火温度对新能源汽车用含Ce无取向电工钢组织和织构的影响

采用SEM、EBSD和XRD等分析手段研究了退火温度对含Ce新能源无取向电工钢组织及织构的影响。结果表明:800 ℃退火后,试验钢边部和中心部位均能观察到再结晶组织及亚晶组织,α线织构中的{112}<110>取向密度最高,γ线织构中的{111}<112>取向密度较弱,退火板存在少量η织构;830～920 ℃退火后,温度越高,再结晶越充分,α线织构取向密度下降,γ线织构取向密度增加,η织构基本消失;试验钢在950 ℃退火后发生了完全再结晶,平均晶粒尺寸为48.29 μm,γ线织构中的{111}<112>取向密度最高,为11.36。     

COLD-ROLLING AND RECRYSTALLIZATION OF (110)[110] IRON-SILICON SINGLE CRYSTALS

After70-90% cold-rolling,strong{111}〈110〉and weak {111},〈112〉 cold-rolled tex- tures and perfect{111}〈112〉 recrystallization texture were obtained in Fe-Si single crys- tals.The cold-rolled textures with different orientations possesses different ability for recov- ery because of the difference of dislocation structure and store energy alter cold-rolling.The recovery taking place at{111}〈112〉orientation region was prior to that at{111}〈110〉 orientation region.hese subgrains with{111}〈112〉 orientation became recrvstallization nuclei during their growth at expending the surrounding matrix which was sluggish in recovery process.The development of recrystallization textures may be suggested as a process of “nucleation in-situ-selective growth”.The formation of(111)textures in low carbon steel sheets has been discussed in the light of this suggestion.     

390MPa级超低碳BH钢织构演变规律

采用ODF织构分析方法,对390 MPa级超低碳BH钢板热轧、冷轧、退火过程织构演变规律进行研究,并对不同冷轧压下量和不同退火工艺织构进行分析。结果表明:经冷轧变形后的钢板有较强的择优取向,具有典型的{112}<110>和{111}<110>织构,形变织构中的不利织构{001}<110>较强;冷轧压下率为80%时再结晶退火后钢板具有较强的γ织构,{111}<112>织构取向密度高达11.7;退火温度和保温时间对α织构影响不大,提高退火温度和延长保温时间使γ织构增强,r值增加。