家电用含磷高强IF钢的抗时效性能分析

研发了一种新的增加C、P元素的高强IF钢热镀锌家电板,借助于材料计算软件,模拟计算P元素在铁素体中固溶含量情况,利用扫描显微镜EBSD和拉伸试验机,对比高强P-IF钢和普通IF钢的晶粒尺寸、晶界角度、力学性能.通过开展试验室静态应变时效和烘烤时效模拟试验,研究P元素的添加对无间隙原子钢的耐时效特性的影响.研究结果表明:...     

高强度船板抗应变时效敏感性研究

采用夏比冲击法测定了热轧、热轧+正火及TMCP 3种工艺下EH36高强度船板的应变时效敏感性,通过金相显微镜、透射电镜等观察了显微组织、精细结构和二相粒子析出形貌。结果表明,TMCP工艺下所获得的细化的F+P显微组织和大量细小弥散析出的二相粒子,减少了碳、氮间隙原子固溶,并阻碍了它们的扩散,使高强船板具有优良的低温韧性和抗应变时效敏感性。     

固定海上结构用大厚度S460G2+QT钢板的开发研究

介绍了固定海上结构用大厚度钢板S460G2+QT的主要技术难点和试制生产工艺,通过理论分析及试验,确定了大厚度钢板的成分体系及关键生产工艺。结果表明:试制钢板的成分设计合理,各项力学性能良好,组织均匀细化,易焊接。     

130mm Q345EZ35风电塔筒用特厚钢板的研制开发

针对采用连铸坯生产特厚板的特点,通过严格控制炼钢工艺以提高连铸坯的内部质量,热轧过程中采用大变形系数轧制,以确保铸坯在热轧过程中沿厚度方向变形的均匀性和晶粒的进一步细化,以及合理的正火工艺,成功开发了130mmQ345EZ35钢板。对正火态钢板的组织性能检测表明,试制钢板力学性能满足标准和用户要求,钢板板型和表面质量良好,且具有较大的工艺窗口,易于实现工业化生产。     

热轧屈服强度550MPa高强度钢板组织性能

为开发屈服强度大于550MPa、-60℃冲击功高于37J的高强度热轧厚钢板,开展了系列试验研究.提出2种试验钢,即CSiMnCuNiMo(A)和CsiMnCuNiCrMo(B)低合金钢.采用Gleeble 3800热模拟试验机,系统研究了钢A在热机变形条件下奥氏体连续冷却相变动力学和显微组织变化规律.在二辊可逆试验轧机...     

高炉及配套热风炉炉壳用钢拓展性的研究

针对高炉及热风炉炉壳用钢在服役条件下所承受热疲劳和压力的要求,结合国标《钢铁企业冶炼工艺炉技术规范》的编制要求,对Q345(B,C,GJC)、Q390(GJC,D)钢的热疲劳性能和应变时效性能进行了研究,并和原使用钢种BB502、BB503钢的相应性能进行了对比分析,本文的研究成果不仅为规范的编制提供了大量可靠的试验数据,也为高炉及其配套热风炉炉壳用钢种的拓展进行了可行性分析。     

国内风电用钢市场分析与技术开发

结合国内外风电行业发展状况,以及对风电工程中主要原材料使用状况的剖析,对风电工程建设所需的主要钢材品种及市场状况、国内风电用钢技术的突破与国际市场的发展方向、国内风电用钢生产面临的主要问题和挑战进行了探讨,为风电工程用钢的未来发展进行了有益的探索。     

基于网格应变分析的深冲用钢DC06车门成型过程的形变研究

深冲用钢具有较高的延展性,适用于制造复杂大变形的零件,其中汽车车门内板由于结构设计与性能要求较高,具有复杂的形面和较大的拉延深度,加工难度大,为深冲用钢的典型应用.针对车门内板拉延成形的过程,基于实测的DC06材料性能数据,利用网格应变分析技术,检测零件关键位置的主次应变,以成形极限FLC曲线为判据,得到成形安全裕度;...     

NVB级船板应变时效敏感性试验

研究了不同塑性变形量的应变时效对NVB钢板的强度、塑性及低温韧性和脆性转变温度的影响.结果表明,NVB钢板的应变时效敏感性较低,经5%时效后仍具有较好的低温韧性.通过微观组织分析,探讨了不同温度下的金相组织和冲击断口形貌特征.实验表明,带状组织易导致材料韧性的恶化, 钙硅酸盐类非金属夹杂物对脆性转变温度有不良作用,容易加速钢板的脆化倾向.还从位错角度对应变时效的微观机理进行了简要阐述.     

Study of Low-Carbon Pipe Steel Strain Ageing

Metallurgist - Strain aging of pipe steels 06G2FB and 07G2MFB with ferrite-pearlite and ferrite-bainite structures is investigated. It is established that a ferrite-bainite structure is more...     

时效退火对碳结钢强度性能的影响

冷拔材以尺寸精度高、表面光洁度和机械性能指标好的特点受到用户的青睐,随着成品质量的不断提高和对产品指标高标准要求,通过不断地探索对工艺的改进得到高性能指标的产品,满足市场及用户的需求。     

Effect of Tempering Temperature on Microstructure and Properties of E690 Offshore Plate Steel

 A new kind of Mn-Mo-Nb-Cu-B bainite steel which satisfied mechanical demands of E690 offshore plate steel was designed. The effect of two processes——thermomechanical control process (TMCP)+tempering (T) and thermomechanical control process (TMCP)+reheating and quenching (RQ)+tempering (T)——on microstructure and mechanical properties were studied by means of scan electron microscope (SEM), transmission electron microscope (TEM) and electron back scatter diffraction (EBSD). The results showed that optimal mechanical properties were available when tempering at 550 ℃ for both processes. The microstructure of the TMCP+T treated sample tempering in the range of 450 to 550 ℃ for 1 h did not change dramatically yet the lath in the TMCP+RQ+T treated sample merged together and transformed into polygonal ferrite. At the same time, the sub-structure of grain bainite transformed from lath to cell-shape to refine grains with tempering temperature mounting. Lots of sub-grain boundaries were located within bainite and adjacent bainite grain boundaries were high angle.     

多约束条件下的中厚板生产线订单生产交付模式探讨

通过分析炼钢炉次、钢种连浇、浇次、生产负荷、冶金条件、新产品试制等约束条件对生产计划编制的影响,济钢从异钢种合炉次冶炼、内控成分冶炼、国标判定、消化库存、整数加分数、拆分式、柔性等多个生产计划编制模式对约束条件进行了分解,并应用到生产计划编制当中,取得了良好的效果。     

时效对77MnA高碳钢盘条性能的影响

高碳钢盘条轧后自然放置一段时间后的力学性能发生较大变化,尤其是断面收缩率提高较为明显.通过测定77MnA盘条在不同停放时间的力学性能,同时对断口形貌和显微组织进行观察分析,初步探明77MnA盘条经自然放置不同时间时效前后力学性能变化的原因及规律.     

海上风塔用焊接结构钢板S355G10+N的研制

详细介绍了海上风塔用钢板S355G10+N的设计思路、生产工艺过程和综合性能研究。检验结果表明,S355G10+N钢板具有良好的综合性能,各项性能指标超过标准要求。     

经TMCP处理的ABS-EQ47海工厚板钢的组织性能

 以工业生产的ABS-EQ47钢为对象,研究了奥氏体连续冷却相变行为,在中试工厂使用热机轧制（thermo-mechanical control process, TMCP）工艺成功开发出35mm和40mm 厚钢板,考察了钢板经单道次模拟焊接热循环后的组织性能。结果表明,所开发钢板的组织为针状铁素体+细粒状贝氏体,屈服强度(Rp0.2)高于500MPa,抗拉强度(Rm)高于630MPa,伸长率(A)大于20%,在-60℃下横向Charpy冲击吸收能量(KV2)大于200J。TMCP型钢板的屈强比低于同成分调质（QT）钢板的屈强比,但其Rm高于QT型钢板。模拟焊接热输入为30kJ/cm时,粗晶区HAZ试样的KV2不低于40J。     

TMCP工艺生产E420海洋平台用钢板的组织与性能研究

介绍了E420海洋平台用钢板的成分性能要求,根据成分和工艺参数对力学性能的影响,对采用TMCP工艺生产的钢板组织与性能进行了研究,通过回火工艺验证,最终成功研发出组织和性能符合要求的E420钢板,为更高级别、更大厚度海洋平台用钢板的开发提供了技术储备。     

API 2W-130海洋结构用钢板的时效行为试验研究

对不同时效条件下的1 200 MPa级海洋工程用钢板进行力学试验和组织分析,发现随着时效温度的升高,屈服强度、抗拉强度、硬度呈先升后降的变化趋势,证明400℃是最佳时效温度。通过对析出物进行电镜和能谱分析,发现ε-Cu颗粒、Nb和Ti的碳氮化物析出相弥散在基体,并随着时效温度的升高,颗粒减少,间距增大。