氩弧熔敷原位自生TiC-TiB_2/Fe复合涂层组织与磨损性能的研究

以Ti、B4C和Fe粉为原料,利用氩弧熔敷技术在Q235钢基体表面制备出原位自生TiC-TiB2增强Fe基复合涂层。利用扫描电镜(SEM)、X射线衍射仪(XRD)、显微硬度计和滑动磨损试验机对复合涂层的显微组织、硬度、耐磨性进行了研究。结果表明:熔敷层组织为TiC、TiB2和α-Fe,TiC以四面体和花瓣状先析出,后析出的TiB2多以六边形、短棒状存在,涂层中TiB2含量大于TiC含量;熔敷层与基体呈冶金结合,无裂纹、气孔等缺陷;涂层维氏硬度为8300～9000MPa,比基体提高近4倍;最大耐磨性比基体提高近20倍,在室温干滑动磨损试验条件下具有优异的耐磨损性能。     

原位自生TiC-TiB2增强Fe基复合涂层的凝固特性及形成机理

以Ti、B4C和Fe粉为原料,利用氩弧熔敷技术在Q235钢基体表面制备出原位自生TiC-TiB2增强Fe基复合涂层.利用扫描电镜(SEM)、X射线衍射仪(XRD)对涂层的显微组织进行了分析.并分析了TiC和TiB2颗粒的形成机理和氩弧熔池的凝固特性.实验结果表明:熔敷层组织为TiC和TiB2弥散分布在α-Fe中,熔敷层与基体呈冶金结合,无裂纹、气孔等缺陷;涂层中TiC和TiB2的体积分数约为68%.形成机理主要是以固态扩散机制为主,TiC以小颗粒状和花瓣状先析出,后析出的TiB2多以六边形、短棒状存在,TiB2的组织比较粗大,TiC颗粒比较细小,TiB2的含量大于TiC含量.     

激光熔覆B4C-TiO2-Al粉末制备原位TiB2+TiC/Fe复合涂层（英文）

采用B4C、TiO2、Al以及Fe基自熔合金粉末为前驱体,利用激光熔覆技术在钢基体上制备TiB2+TiC颗粒增强Fe基复合涂层。结果表明,激光熔覆过程通过B4C-TiO2-Al反应生成了均匀分布于基体的TiB2-TiC复合陶瓷相。TiB2颗粒呈长条块状,TiC以不规则形状分布于基体中。涂层具有比基材1045钢更好的耐磨性能,但涂层的摩擦因数小。     

氩弧熔覆 TiC 颗粒增强 Fe 基涂层组织性能研究

目的研究氩弧熔覆条件下TiC颗粒增强Fe基涂层的组织和性能。方法在Fe45自熔性合金粉末中添加TiC颗粒,利用氩弧熔覆技术在Q235钢基材表面制备出含TiC颗粒增强的Fe基合金复合涂层,并对熔覆层的显微组织结构、硬度分布及耐磨性能进行分析研究。结果复合涂层是由(Fe,Ni)形成的枝晶和枝晶间的(Fe,Cr)23(C,B)6,Fe3(C,B)共晶组织以及TiC增强颗粒组成,TiC颗粒细小弥散分布在基体金属内,部分TiC颗粒聚集生长为棒状、十字状和放射状。结论熔覆层的显微硬度最高可达980HV,较Q235钢提高了4倍,耐磨性提高了约11倍。     

TiB2对Ni基合金激光熔覆层组织与性能的影响

采用5 kW CO2激光器在低碳钢表面熔覆Ni基合金层及TiB2/Ni基合金金属陶瓷涂层,研究了两种涂层的组织、显微硬度以及滑动磨损特性.结果表明,Ni基合金层主要组成相为γ-(Ni,Fe),Cr23C6等,TiB2/Ni基合金复合涂层组成相主要有γ-(Ni,Fe),Ni3B,TiB2和TiC等;Ni基合金层由发达γ-(Ni,Fe)枝晶和其间共晶组织所组成,TiB2/Ni基合金复合涂层典型组织为等轴固溶体以及其间细小共晶组织;TiB2对熔覆层的组织有显著的影响,使熔覆层组织细化,并由树枝晶转变为等轴晶;加入TiB2可显著提高Ni基合金涂层的显微硬度及耐磨性能.     

等离子弧熔覆添加Al2O3+TiO2铁基合金涂层组织和耐磨性

在Q235钢表面用等离子弧熔覆Ni-Cr-B-Si-Fe铁基合金涂层及添加不同含量Al2O3 TiO2铁基合金复合涂层,比较研究了这两种涂层的组织、显微硬度和磨损性能。结果表明,添加Al2O3 TiO2后的铁基复合涂层界面的生长形态发生变化,由初生的细长柱状树枝晶转变为小的枝晶,并且提供了形核的核心,细化了晶粒;其组织主要由晶粒细小的γ-Fe为基,以Cr23C6,Fe3C,Al2O3 TiO2为增强相的复合涂层;熔覆层的显微硬度可达600～655HV0.2。     

NiAl含量对反应合成TiC-TiB_2-NiAl物相及组织结构的影响(英文)

以Ti、B4C、Ni、Al粉末为原料,通过自蔓延高温反应合成工艺(SHS)制备TiC-TiB2-NiAl复合材料,研究NiAl含量对反应产物的物相组成及组织结构的影响。结果表明:Ti+B4C+Ni+Al粉末SHS反应产物的物相组成为TiB2、TiC和NiAl,随着Ni+Al添加量的增多,NiAl相的衍射峰强度逐渐增强;TiB2、TiC和NiAl在基体中呈现不同的形态,其中TiB2呈六边形或长条状,TiC呈圆形,NiAl填充在TiC和TiB2颗粒之间;随着NiAl含量的增加,TiC-TiB2-NiAl复合材料的晶粒逐渐被细化,致密度和抗压强度均被提高,TiC的形态由不规则形状转变为圆形。复合材料的断裂方式由单纯的沿晶断裂转变为混合的沿晶断裂和穿晶断裂。     

TC4合金氩弧熔覆Ni60+B4C复合涂层组织及耐磨性

利用氩弧熔覆技术在TC4合金表面成功制备出TiC、TiB、TiB2增强Ti基复合涂层.利用SEM、XRD和EDS分析了熔覆涂层的显微组织;利用显微硬度仪测试了复合涂层的显微硬度;利用摩擦磨损试验机测试了涂层在室温干滑动磨损条件下的耐磨性能.结果表明:氩弧熔覆涂层组织均匀致密,熔覆层与基体呈冶金结合,TC4合金表面有颗粒状TiC、粗大棒状相TiB2、细小棒状相TiB生成;复合涂层明显改善了TC4合金的表面硬度,涂层的最高显微硬度可达1300 HV0.2;复合涂层在室温干滑动磨损试验条件下具有优异的耐磨性,磨损机制主要是魔力磨损,其耐磨性较TC4合金基体提高近10倍.     

TC4钛合金表面激光熔覆掺Y2O3复合涂层的显微组织和性能

目的提高钛合金表面的耐磨性能。方法在TiB_2:TiC=1:3的粉末配比下,添加不同质量分数Y_2O_3稀土氧化物,制备成膏状混合粉末。采用5 k W横流CO_2激光器,在TC4钛合金表面激光熔覆掺Y_2O_3的TiB_2和TiC粉末,制备耐磨性复合涂层。通过扫描电子显微镜(SEM)、X射线能谱仪(EDS)、X射线衍射仪(XRD)对激光熔覆层的微观形貌和组织成分进行了分析;用显微维氏硬度计对熔覆层的显微硬度进行了测量;用万能摩擦磨损试验机对熔覆层的耐磨性能进行了测试。结果添加4%Y_2O_3后,熔覆层中部组织明显细化,结合区由致密组织结构转变为晶须网状结构;熔覆层的最高显微硬度为1404.6HV0.2,是基体的3.7倍;熔覆层的磨损量减少了66.67%,且其摩擦系数有明显的降低。结论添加4%Y_2O_3对TC4钛合金表面激光熔覆TiB/TiC复合熔覆层耐磨性能有显著的提高。     

稀土对氩弧熔覆复合涂层组织和性能的影响

以Ti,B4C,Y2O3和Ni60A粉末为原料,利用氩弧熔覆技术在Q235钢基材表面成功制备出镍基增强相复合涂层,运用 XRD,SEM等分析手段研究了复合涂层的显微组织,利用显微硬度仪测试了复合涂层的显微硬度,并用磨损试验机分析了其在室温干滑动磨损条件下的耐磨性能. 结果表明,复合涂层与基体界面无气孔、裂纹,呈冶金结合. 复合涂层由TiC,TiB2,Cr23C6和γ-Ni组成. 稀土加入改变了TiC和TiB2的长大形态,呈颗粒状均匀、细小的分布在熔覆涂层中. 显微硬度和耐磨性测试结果表明,稀土加入后提高其显微硬度和磨损性能.     

Effects of Post-weld Heat Treatment on Microstructure,Mechanical Properties and the Role of Weld Reinforcement in 2219 Aluminum Alloy TIG-Welded Joints

In as-welded state, each region of 2219 aluminum alloy TIG-welded joint shows diff erent microstructure and microhardness due to the diff erent welding heat cycles and the resulting evolution of second phases. After the post-weld heat treatment, both the amount and the size of the eutectic structure or θ phases decreased. Correspondingly, both the Cu content in α-Al matrix and the microhardness increased to a similar level in each region of the joint, and the tensile strength of the entire joint was greatly improved. Post-weld heat treatment played the role of solid solution strengthening and aging strengthening. After the post-weld heat treatment, the weld performance became similar to other regions, but weld reinforcements lost their reinforcing eff ect on the weld and their existence was more of an adverse eff ect. The joint without weld reinforcements after the post-weld heat treatment had the optimal tensile properties, and the specimens randomly crack in the weld zone.     

The First Phase of the SRIF Industrialized Base in ＂West Area＂ Has Been Put into Operation

After nearly two years＇ tense construction, the first phase of industrialized base of Shenyang Research Institute of Foundry （SRIF）, located at the Tiexi Casting and Forging Industrial Park in the west of Tiexi District, has now been completed and formally put into operation.     

Thermodynamics Study on the Decomposition of Chromite with KOH

Institute of Process Engineering, Chinese Academy of Sciences, China, has proposed a method for oxidative leaching of chromite with potassium hydroxide. Understanding the mechanism of chromite decomposition, especially in the potassium hydroxide fusion, is important for the optimization of the operating parameters of the oxidative leaching process. A traditional thermodynamic method is proposed and the thermal decomposition and the reaction decomposition during the oxidative leaching of chromite with KOH and oxygen is discussed, which suggests that chromite is mainly destroyed by reactions with KOH and oxygen. Meanwhile, equilibrium of the main reactions of the above process was calculated at different temperatures and oxygen partial pressures. The stable zones of productions, namely, K2CrO4 and Fe2O3, increase with the decrease of temperature, which indicates that higher temperature is not beneficial to thermodynamic reactions. In addition, a comparison of the general alkali methods is carried out, and it is concluded that the KOH leaching process is thermodynamically superior to the conventional chromate production process.     

Influence of Heat Treatment on Damping Behaviour of the Magnesium Wrought Alloy AZ61

The effect of isochronal heat treatments for 1h on variation of damping, hardness and microstructural change of the magnesium wrought alloy AZ61 was investigated. Damping and hardness behaviour could be attributed to the evolution of precipitation process. The influence of precipitation on damping behaviour was explained in the framework of the dislocation string model of Granato and Lücke.     

Effect of Rare Earth Doping on Impedance,Modulus and Conductivity Properties of Multiferroic Composites:0.5(BiLa_xFe_(1-x)O_3)–0.5(PbTiO_3)

The Lanthanum-doped bismuth ferrite–lead titanate compositions of 0.5(Bi LaxFe1-xO3)–0.5(Pb Ti O3)(x = 0.05,0.10,0.15,0.20)(BLxF1-x-PT) were prepared by mixed oxide method.Structural characterization was performed by X-ray diffraction and shows a tetragonal structure at room temperature.The lattice parameter c/a ratio decreases with increasing of La(x = 0.05–0.20) concentration of the composites.The effect of charge carrier/ion hopping mechanism,conductivity,relaxation process and impedance parameters was studied using an impedance analyzer in a wide frequency range(102–106Hz) at different temperatures.The nature of Nyquist plot confirms the presence of bulk effects only,and non-Debye type of relaxation processes occurs in the composites.The electrical modulus exhibits an important role of the hopping mechanism in the electrical transport process of the materials.The ac conductivity and dc conductivity of the materials were studied,and the activation energy found to be 0.81,0.77,0.76 and 0.74 e V for all compositions of x = 0.05–0.20 at different temperatures(200–300 °C).     

Quantitative Analysis of the Crystallographic Orientation Relationship Between the Martensite and Austenite in Quenching–Partitioning–Tempering Steels

The orientation relationships(ORs)between the martensite and the retained austenite in low-and medium-carbon steels after quenching–partitioning–tempering process were studied in this work.The ORs in the studied steels are identified by selected-area electron diffraction(SAED)as either K–S or N–W ORs.Meanwhile,the ORs were also studied based on numerical fitting of electron backscatter diffraction data method suggested by Miyamoto.The simulated K–S and N–W ORs in the low-index directions generally do not well coincide with the experimental pole figure,which may be attributed to both the orientation spread from the ideal variant orientations and high symmetry of the low-index directions.However,the simulated results coincide well with experimental pole figures in the high-index directions{123}_(bcc).A modified method with simplicity based on Miyamoto’s work was proposed.The results indicate that the ORs determined by modified method are similar to those determined by Miyamoto’method,that is,the OR is near K–S OR for the low-carbon Q–P–T steel,and with the increase of carbon content,the OR is closer to N–W OR in medium-carbon Q–P–T steel.     

Using Finite Element and Contour Method to Evaluate Residual Stress in Thick Ti-6Al-4V Alloy Welded by Electron Beam Welding

This work was to reveal the residual stress profile in electron beam welded Ti-6Al-4V alloy plates(50 mm thick) by using finite element and contour measurement methods.A three-dimensional finite element model of 50-mmthick titanium component was proposed,in which a column–cone combined heat source model was used to simulate the temperature field and a thermo-elastic–plastic model to analyze residual stress in a weld joint based on ABAQUS software.Considering the uncertainty of welding simulation,the computation was calibrated by experimental data of contour measurement method.Both test and simulated results show that residual stresses on the surface and inside the weld zone are significantly different and present a narrow and large gradient feature in the weld joint.The peak tensile stress exceeds the yield strength of base materials inside weld,which are distinctly different from residual stress of the thin Ti-6Al-4V alloy plates presented in references before.     

Microstructures and Tensile Properties of Ultrafine-Grained Ni–(1–3.5) wt% SiC_(NP) Composites Prepared by a Powder Metallurgy Route

Silicon carbide nanoparticle-reinforced nickel-based composites(Ni–Si CNP),with a Si CNPcontent ranged from1 to 3.5 wt%,were prepared using mechanical alloying and spark plasma sintering.In addition,unreinforced pure nickel samples were also prepared for comparative purposes.To characterize the microstructural properties of both the unreinforced pure nickel and the Ni–Si CNPcomposites transmission electron microscopy(TEM) was used,while their mechanical behavior was investigated using the Vickers pyramid method for hardness measurements and a universal tensile testing machine for tensile tests.TEM results showed an array of dislocation lines decorated in the sintered pure nickel sample,whereas,for the Ni–Si CNPcomposites,the presence of nano-dispersed Si CNPand twinning crystals was observed.These homogeneously distributed Si CNPwere found located either within the matrix,between twins or on grain boundaries.For the Ni–Si CNPcomposites,coerced coarsening of the Si CNPassembly occurred with increasing Si CNPcontent.Furthermore,the grain sizes of the Ni–Si CNPcomposites were much finer than that of the unreinforced pure nickel,which was considered to be due to the composite ball milling process.In all cases,the Ni–Si CNPcomposites showed higher strengths and hardness values than the unreinforced pure nickel,likely due to a combination of dispersion strengthening(Orowan effects) and particle strengthening(Hall–Petch effects).For the Ni–Si CNPcomposites,the strength increased initially and then decreased as a function of Si CNPcontent,whereas their elongation percentages decreased linearly.Compared to all materials tested,the Ni–Si CNPcomposite containing 1.5% Si C was found more superior considering both their strength and plastic properties.     

Directional Growth of Tin Crystals Controlled by Combined Solute Concentration Gradient Field and Static Magnetic Field

A new method was introduced to achieve directional growth of Sn crystals. Microstructures in liquid(Pb)/liquid(Sn) diffusion couples were investigated under various static magnetic fields. Results show that the β-Sn crystals mainly reveal an irregular dendritic morphology without or with a relatively low static magnetic field(B0.3 T). When the magnetic field is increased to 0.5 T, the β-Sn dendrites close to the final stage of growth begin to show some directional character. With a further increase in the magnetic field to a higher level(0.8–5 T), the β-Sn dendrites have an enhanced directional growth character, but the dendrites show a certain deflection. As the magnetic field is increased to 12 T, the directional growth of the β-Sn dendrites in the center of the couple is severely destroyed. The mechanism of the directional growth of the β-Sn crystals and the deflection of the β-Sn crystals with the application of static magnetic field was tentatively discussed.     

电化学噪声数据处理方法概述

综述了常见的电化学噪声数据处理方法,介绍了直流趋势剔除、统计分析、快速傅立叶变换(FFT)法计算功率谱密度(PSD)以及小波变换处理电化学噪声信号的基本过程,并阐释了各种数学处理及所得参数的物理意义。