Fischer–Tropsch synthesis on monolithic catalysts of different materials

Monolithic structures made of cordierite, γ-Al₂O₃ and steel have been prepared as catalysts and tested for Fischer–Tropsch activity. The monoliths made of cordierite and steel were washcoated with a 20 wt.% Co–1 wt.% Re/γ-Al₂O₃ Fischer–Tropsch catalyst whereas the γ-Al₂O₃ monoliths were made by direct impregnation with an aqueous solution of the Co and Re salts resulting in a loading of 12 wt.% Co and 0.5 wt.% Re. The activity and selectivity of the different monoliths were compared with the corresponding powder catalysts.

Higher washcoat loadings resulted in decreased C₅₊ selectivity and olefin/paraffin ratios due to increased transport limitations. The impregnated γ-Al₂O₃ monoliths also showed similar C₅₊ selectivities as powder catalysts of small particle size (38–53 μm). Lower activities were observed with the steel monoliths probably due to experimental problems.     

Dehydroisomerisation of n-butane over (Pt,Cu)/H-TON catalysts

Direct formation of isobutene from n-butane was investigated over zeolite TON and γ-Al₂O₃ supported platinum and platinum–copper catalysts. Addition of Cu decreases Pt dispersion, irrespective of preparation methods and nature of catalyst supports. The presence of potassium was found to reduce acidity and Pt dispersion. The experiments were performed in a fixed-bed microreactor system operating at 673 K and atmospheric pressure. Changing the support from γ-Al₂O₃ to TON, shows that n-butane conversion is almost independent of acidity. However, significant changes in products selectivities are observed. The selectivities to isobutene, C₁–C₃ fractions, and aromatics increases drastically from 3.5 to 32.6%, 20.3 to 27.2%, and 3.0 to 20.6%, respectively, for the TON-supported catalyst whereas dehydrogenation is largely predominant when γ-Al₂O₃ is used as support. Addition of Cu, as expected, has an adverse effect on n-butane conversion as less active sites are available due to the reduction in Pt dispersion. Though Cu addition has marginal effect on isobutene selectivity, it certainly suppresses hydrogenolysis which evidences a reduction in size of the Pt ensembles at the surface of the Pt particles.     

Surface properties and reactivity of Cu/γ-Al2O3 catalysts for NO reduction by C3H6: Influences of calcination temperatures and additives

The influences of calcination temperatures and additives for 10 wt.% Cu/γ-Al₂O₃ catalysts on the surface properties and reactivity for NO reduction by C₃H₆ in the presence of excess oxygen were investigated. The results of XRD and XPS show that the 10 wt.% Cu/γ-Al₂O₃ catalysts calcined below 973 K possess highly dispersed surface and bulk CuO phases. The 10 wt.% Cu/γ-Al₂O₃ and 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalysts calcined at 1073 K possess a CuAl₂O₄ phase with a spinel-type structure. In addition, the 10 wt.% La–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K possesses a bulk CuO phase. The result of NO reduction by C₃H₆ shows that the CuAl₂O₄ is a more active phase than the highly dispersed and bulk CuO phase. However, the 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K possesses significantly lower reactivity for NO reduction than the 10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K, although these catalysts possess the same CuAl₂O₄ phase. The low reactivity for NO reduction for 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K is attributed to the formation of less active CuAl₂O₄ phase with high aggregation and preferential promotion of C₃H₆ combustion to CO_x by MnO₂. The engine dynamometer test for NO reduction shows that the C₃H₆ is a more effective reducing agent for NO reduction than the C₂H₅OH. The maximum reactivity for NO reduction by C₃H₆ is reached when the NO/C₃H₆ ratio is one.     

Fe掺杂对Pt-Sn-K/γ-Al_2O_3异丁烷脱氢催化剂性能的影响

采用共沉淀法制备不同Fe含量的Fe(x)-γ-Al_2O_3复合氧化物载体,并采用真空浸渍法制备了Pt-Sn-K/Fe(x)-γ-Al_2O_3催化剂。对制备的催化剂进行XRD、N_2物理吸附-脱附和NH_3-TPD表征,研究Fe的掺杂对Pt-Sn-K/Fe(x)-γ-Al_2O_3催化剂的结构及其催化异丁烷脱氢反应性能的影响。结果表明,Fe的引入可以改变催化剂的反应活性和产物选择性,当Fe_2O_3掺杂质量分数为4%时,催化剂具有最高的异丁烯收率,50 h的平均收率达到42.9%。     

Effect of phosphorus addition on the hydrotreating activity of NiMo/Al2O3 carbide catalyst

A series of phosphorus promoted γ-Al₂O₃ supported NiMo carbide catalysts with 0–4.5 wt.% P, 13 wt.% Mo and 2.5 wt.% Ni were synthesized and characterized by elemental analysis, pulsed CO chemisorption, BET surface area measurement, X-ray diffraction, near-edge X-ray absorption fine structure, DRIFT spectroscopy of CO adsorption and H₂ temperature programmed reduction. X-ray diffraction patterns and CO uptake showed the P addition to NiMo/γ-Al₂O₃ carbide, increased the dispersion of β-Mo₂C particles. DRIFT spectra of adsorbed CO revealed that P addition to NiMo/γ-Al₂O₃ carbide catalyst not only increases the dispersion of Ni-Mo carbide phase, but also changes the nature of surface active sites. The hydrodenitrogenation (HDN) and hydrodesulfurization (HDS) activities of these P promoted NiMo/γ-Al₂O₃ carbide catalysts were performed in trickle bed reactor using light gas oil (LGO) derived from Athabasca bitumen and model feed containing quinoline and dibenzothiophene at industrial conditions. The P added NiMo/γ-Al₂O₃ carbide catalysts showed enhanced HDN activity compared to the NiMo/γ-Al₂O₃ catalysts with both the feed stocks. The P had almost no influence on the HDS activity of NiMo/γ-Al₂O₃ carbide with LGO and dibenzothiophene. P addition to NiMo/γ-Al₂O₃ carbide accelerated CN bond breaking and thus increased the HDN activity.     

Study of Ag/La0.6Sr0.4MnO3 catalysts for complete oxidation of methanol and ethanol at low concentrations

Ag-modified La_0.6Sr_0.4MnO₃-based catalysts with the perovskite-type structure were prepared by using a citric acid sol–gel method, and their catalytic performance for complete oxidation of methanol and ethanol was evaluated and compared with that of the γ-Al₂O₃-supported catalysts, Ag/γ-Al₂O₃, Pt/γ-Al₂O₃, and Pd/γ-Al₂O₃. The results showed that the Ag-modified La_0.6Sr_0.4MnO₃-based catalysts with the perovskite-type structure displayed the activity significantly higher than that of the supported precious metal catalysts, 0.1%Pd/γ-Al₂O₃ and 0.1%Pt/γ-Al₂O₃ in the temperature range of 370–573 K. Over a 6%Ag/20%La_0.6Sr_0.4MnO₃/γ-Al₂O₃ catalyst, the T₉₅ temperature for methanol oxidation can be as low as 413 K. Even at such low reaction temperature, there were little HCHO and CO detected in the reaction exit-gas. However, for the 0.1%Pd/γ-Al₂O₃ and 0.1%Pt/γ-Al₂O₃ catalysts, the HCHO content in the reaction exit-gas reached 200 and 630 ppm at their T₉₅ temperatures. Over a 6%Ag/La_0.6Sr_0.4MnO₃ catalyst, the T₉₅ temperature for ethanol oxidation can be as low as 453 K, with a corresponding content of CH₃CHO in the exit-gas at 782 ppm; when ethanol oxidation is performed at 493 K, the content of acetaldehyde in the exit-gas can be below 1 ppm. Characterization of the catalysts by X-ray diffraction (XRD), TEM, XPS, laser Raman spectra (LRS), hydrogen temperature-programmed reduction (H₂-TPR) and oxygen temperature-programmed desorption (O₂-TPD) methods revealed that both the surface and the bulk phase of the perovskite La_0.6Sr_0.4MnO₃ played important roles in the catalytic oxidation of the alcohols, and that γ-Al₂O₃ as the bottom carrier could be beneficial in creating a large surface area of catalyst. Moreover, a small amount of Ag⁺ doped onto the surface of La_0.6Sr_0.4MnO₃ was able to partially occupy the positions of La³⁺ and Sr²⁺ due to their similar ionic radii, and thus, became stabilized by the perovskite lattice, which would be in favor of preventing the aggregation of the Ag species on the surface and enhancing the stability of the catalyst. On the other hand, modification of the Ag⁺ to the surface of La_0.6Sr_0.4MnO₃ resulted in an increase in relative content of the surface O₂²⁻/O⁻ species highly reactive toward the alcohols and aldehydes as well as CO. Besides, solution of low-valence metal oxides SrO and Ag₂O with proper amounts in the lattice of the trivalent metal perovskite-type oxide LaMnO₃ would also lead to an increase in the content of the reducible Mnⁿ⁺ and the formation of anionic vacancies, which would be favorable for the adsorption-activation of oxygen on the functioning catalyst and the transport of the lattice and surface oxygen species. All these factors would contribute to the pronounced improvement of the catalyst performance.     

Performance and characterization of Ru/Al2O3 and Ru/SiO2 catalysts modified with Mn for Fischer–Tropsch synthesis

Mn effect and characterization on γ-Al₂O₃-, -Al₂O₃- and SiO₂-supported Ru catalysts were investigated for Fischer–Tropsch synthesis under pressurized conditions. In the slurry phase Fischer–Tropsch reaction, γ-Al₂O₃ catalysts showed higher performance on CO conversion and C₅⁺ selectivity than -Al₂O₃ and SiO₂ catalysts. Moreover, Ru/Mn/γ-Al₂O₃ exhibited high resistance to catalyst deactivation and other catalysts were deactivated during the reaction. From characterization results on XRD, TPR, TEM, XPS and pore distribution, Ru particles were clearly observed over the catalysts, and γ-Al₂O₃ catalysts showed a moderate pore and particle size such as 8 nm, where -Al₂O₃ and SiO₂ showed highly dispersed ruthenium particles. The addition of Mn to γ-Al₂O₃ enhanced the removal of chloride from RuCl₃, which can lead to the formation of metallic Ru with moderate particle size, which would be an active site for Fischer–Tropsch reaction. Concomitantly, manganese chloride is formed. These schemes can be assigned to the stable nature of Ru/Mn/γ-Al₂O₃ catalyst.     

Application of Ce0.33Zr0.63Pr0.04O2-supported noble metal catalysts in the catalytic wet air oxidation of 2-chlorophenol: Influence of the reaction conditions

In this work, different procedures, namely carbonate coprecipitation and modified solid–solid diffusion, were used to prepare hexaaluminate samples, unsupported or supported onto θ-Al₂O₃. These samples were used as catalyst for the methane total oxidation as synthesized or after impregnation of 1 wt% Pd. It was observed that the modified solid–solid diffusion procedure is an efficient method to obtain the hexaaluminate structure. At a theoretical ratio x of hexaaluminate onto Al₂O₃ less than 0.6 (xLa_0.2Sr_0.3Ba_0.5MnAl₁₁O₁₉ + (1−x)·Al₂O₃, with x = 0.25, 0.60), samples with high specific surface area and θ-Al₂O₃ structure are then obtained. Large differences in catalytic activity can be observed among the series of sample synthesized. All the pure oxide samples (i.e. without palladium) present low catalytic activity for methane total oxidation compared to a reference Pd/Al₂O₃ catalyst. The highest activity was obtained for the samples presenting a θ-Al₂O₃ structure (with x = 0.60) and a high surface area. Impregnation of 1 wt% palladium resulted in an increase in catalytic activity, for all the solids synthesized in this work. Even if the lowest light-off temperature was obtained on the reference sample, similar methane conversions at high temperature (700 °C) were obtained on the stabilized θ-Al₂O₃ solids (x = 0.25, 0.60). Moreover, the reference sample is found to strongly deactivate with reaction time at the temperature of test (700 °C), due to a progressive reduction of the PdO_x active phase into the less active Pd° phase, whereas excellent stabilities in reaction were obtained on the pure and palladium-doped hexaaluminate and supported θ-Al₂O₃ samples. This clearly showed the beneficial effect of the support for the stabilization of the PdO_x active phase at high reaction temperature. These properties are discussed in term of oxygen transfer from the support to the palladium particle. Oxygen transfer is directly related to the Mn³⁺/Mn²⁺ redox properties (in the case of the hexaaluminate and stabilized θ-Al₂O₃ samples), that allows a fast reoxidation of the metal palladium sites since palladium sites reoxidation cannot occur directly by gaseous dioxygen adsorption and dissociation on the surface.     

Synthesis, characterization and catalytic activity for NO–CO reaction of Pd–(La, Sr)2MnO4 system

La_xSr_2−xMnO₄ (0 ≤ x ≤ 0.8) oxides were synthesized and single-phase K₂NiF₄-type oxides were obtained in the range of 0.1 ≤ x < 0.5. The catalytic activity of La_xSr_2−xMnO₄ for NO–CO reaction increased with increasing x in the range of solubility limit of La. La_0.5Sr_1.5MnO₄ showed the highest activity among La_xSr_2−xMnO₄ prepared in this study, but its activity was inferior to perovskite-type La_0.5Sr_0.5MnO₃. Among the Pd-loaded catalysts, however, Pd/La_0.8Sr_1.2MnO₄ showed the higher activity and the selectivity to N₂ than Pd/La_0.5Sr_0.5MnO₃ and Pd/γ-Al₂O₃. The excellent catalytic performance of Pd/La_0.2Sr_1.2MnO₄ could be ascribable to the formation of SrPd₃O₄ which was detected by XRD in the catalyst but not in the other two catalysts.     

Highly dispersed NiW/γ-Al2O3 catalyst prepared by hydrothermal deposition method

This article describes a novel hydrothermal deposition method for preparing highly dispersed NiW/γ-Al₂O₃ catalysts and demonstrates its advantages over the conventional impregnation method. Via the hydrothermal precipitation reactions between sodium tungstate and hydrochloric acid and between nickel nitrate and urea, respectively, the active species W and Ni were deposited on γ-Al₂O₃. In the hydrothermal deposition of WO₃, a surfactant hexadecyltrimethyl ammonium bromide (CTAB) was used to prevent the aggregation of WO₃. The characterization results obtained by means of X-ray photoelectron spectroscopy (XPS), N₂ adsorption and high-resolution transmission electron microscopy (HRTEM) measurements showed that compared with the catalyst prepared by the conventional impregnation method, the catalyst with the same metal contents prepared by the hydrothermal deposition had much higher W and Ni dispersion, higher specific surface area, larger pore volume, the significantly decreased slab length and slightly increased stacking degree of sulfided W species, leading to the significantly enhanced dibenzothiophene (DBT) hydrodesulfurization (HDS) activity. The DBT HDS assessment results also revealed that the catalyst containing 17.7 wt% WO₃ and 2.4 wt% NiO prepared by the hydrothermal deposition method had the similar DBT HDS activity as a commercial NiW/γ-Al₂O₃ catalyst containing 23 wt% WO₃ and 2.6 wt% NiO, resulting in the greatly decreased amount of active metals for achieving the same HDS activity.     

Palladium–vanadium interaction in binary supported catalysts

We have studied the activity and selectivity of Pd/γ-Al₂O₃, VO_x/γ-Al₂O₃ and Pd–VO_x/γ-Al₂O₃ catalysts for the decomposition of NO and the reduction of NO with CO. Pd–VO_x/γ-Al₂O₃ catalysts were prepared by anchoring Pd(AcAc)₂ on VO_x/γ-Al₂O₃. Characterization of the binary samples by hydrogen chemisorption and TPR measurements indicated that the reduction of VO_x is enhanced by a close contact with palladium and that partially reduced vanadia decorate noble metal particles. This palladium–vanadium interaction alters the catalytic properties of palladium: the activity for NO decomposition is higher for the binary sample and, for the NO–CO reaction, both the activity and the selectivity to N₂ increase when vanadium is in contact with palladium.     

NO reduction by CH4 in the presence of O2 over La2O3 supported on Al2O3

Dispersing La₂O₃ on δ- or γ-Al₂O₃ significantly enhances the rate of NO reduction by CH₄ in 1% O₂, compared to unsupported La₂O₃. Typically, no bend-over in activity occurs between 500° and 700°C, and the rate at 700°C is 60% higher than that with a Co/ZSM-5 catalyst. The final activity was dependent upon the La₂O₃ precursor used, the pretreatment, and the La₂O₃ loading. The most active family of catalysts consisted of La₂O₃ on γ-Al₂O₃ prepared with lanthanum acetate and calcined at 750°C for 10 h. A maximum in rate (mol/s/g) and specific activity (mol/s/m²) occurred between the addition of one and two theoretical monolayers of La₂O₃ on the γ-Al₂O₃ surface. The best catalyst, 40% La₂O₃/γ-Al₂O₃, had a turnover frequency at 700°C of 0.05 s⁻¹, based on NO chemisorption at 25°C, which was 15 times higher than that for Co/ZSM-5. These La₂O₃/Al₂O₃ catalysts exhibited stable activity under high conversion conditions as well as high CH₄ selectivity (CH₄ + NO vs. CH₄ + O₂). The addition of Sr to a 20% La₂O₃/γ-Al₂O₃ sample increased activity, and a maximum rate enhancement of 45% was obtained at a SrO loading of 5%. In contrast, addition of SO⁼₄ to the latter Sr-promoted La₂O₃/Al₂O₃ catalyst decreased activity although sulfate increased the activity of Sr-promoted La₂O₃. Dispersing La₂O₃ on SiO₂ produced catalysts with extremely low specific activities, and rates were even lower than with pure La₂O₃. This is presumably due to water sensitivity and silicate formation. The La₂O₃/Al₂O₃ catalysts are anticipated to show sufficient hydrothermal stability to allow their use in certain high-temperature applications.     

Ethylene epoxidation on Ag catalysts supported on non-porous, microporous and mesoporous silicates

The ethylene epoxidation activity of Ag catalysts supported on non-porous SiO₂, microporous silicalite zeolite and mesoporous MCM-41 and HMS silicates was investigated in the present study in comparison to conventional low surface area -Al₂O₃ based catalysts. The MCM-41 and HMS based catalysts exhibited similar ethylene conversion activity and ethylene oxide (EO) selectivity with the SiO₂ and -Al₂O₃ based catalysts at relatively lower temperatures (up to 230 °C), whereas their activity and selectivity decreased significantly at higher temperatures (≥300 °C). The silicalite based catalyst was highly active for a wide temperature range, similar to the SiO₂ and -Al₂O₃ based catalysts, but it was the less selective amongst all catalysts tested. High loadings of Ag particles (up to ca. 40 wt.%) with medium crystallites size (20–55 nm) could be achieved on the mesoporous materials resulting in very active epoxidation catalysts. The HMS-type silicate with the 3D network of wormhole-like framework mesopores (with average diameter of 3.5 nm), in combination with a high-textural (interparticle) porosity, appeared to be the most promising mesoporous support.     

制备条件对NiMo/γ-Al2O3催化剂上萘加氢生成四氢萘的影响

采用等体积浸渍法制备加氢催化剂NiMo/γ-Al₂O₃,在悬浮床上考察不同的制备条件下NiMo/γ-Al₂O₃对萘加氢生成四氢萘的影响。结果表明,催化剂的制备条件对加氢活性有显著的影响,NiMo/γ-Al₂O₃催化剂的最佳制备条件为共浸渍法负载金属组分Ni和Mo,在500 ℃的温度下焙烧4 h。此条件下制备的催化剂上四氢萘的选择性高达95.2%。     

Catalytic reduction of SO2 over supported transition-metal oxide catalysts with C2H4 as a reducing agent

This work investigates performances of supported transition-metal oxide catalysts for the catalytic reduction of SO₂ with C₂H₄ as a reducing agent. Experimental results indicate that the active species, the support, the feed ratio of C₂H₄/SO₂, and pretreatment are all important factors affecting catalyst activity. Fe₂O₃/γ-Al₂O₃ was found to be the most active catalyst among six γ-Al₂O₃-supported metal oxide catalysts tested. With Fe₂O₃ as the active species, of the supports tested, CeO₂ is the most suitable one. Using this Fe₂O₃/CeO₂ catalyst, we found that the optimal Fe content is 10 wt.%, the optimal feed ratio of C₂H₄/SO₂ is 1:1, and the catalyst presulfidized by H₂+H₂S exhibits a higher performance than those pretreated with H₂ or He. Although the feed concentrations of C₂H₄:SO₂ being 3000:3000 ppm provide a higher conversion of SO₂, the sulfur yield decreases drastically at temperatures above 300 °C. With higher feed concentrations, maximum yield appears at higher temperatures. The C₂H₄ temperature-programmed desorption (C₂H₄-TPD) and SO₂-TPD desorption patterns illustrate that Fe₂O₃/CeO₂ can adsorb and desorb C₂H₄ and SO₂ more easily than can Fe₂O₃/γ-Al₂O₃. Moreover, the SO₂-TPD patterns further show that Fe₂O₃/γ-Al₂O₃ is more seriously inhibited by SO₂. These findings may properly explain why Fe₂O₃/CeO₂ has a higher activity for the reduction of SO₂.     

Pt/Pt-Ce/γ-Al2O3催化氧化甲苯研究

通过等体积浸渍法制备单贵金属Pt/γ-Al₂O₃和双金属Pt-Ce/γ-Al₂O₃催化剂,考察Ce对催化剂活性的影响,确定催化剂最优配比。结果表明,当Pt的负载量为质量分数0.5%时,Pt/γ-Al₂O₃催化活性最高;当Pt的负载量为质量分数0.2%,Ce的负载量为质量分数1.0%时,Pt-Ce/γ-Al₂O₃催化剂的催化活性最高。Pt-Ce/γ-Al₂O₃催化剂的甲苯转化率高于Pt/γ-Al₂O₃催化剂。随着Pt负载量增大,催化剂孔容、孔径减小。粉体式催化剂性能优于整体式催化剂,但差别不大;Ce的添加有助于催化剂活性的提升。     

脲溶液修饰γ-Al_2O_3及其对La_2O_3/γ-Al_2O_3催化肉桂醛MPV反应的影响

采用探针-TPD、探针-IR和电势测量等方法研究不同浓度脲溶液浸泡γ-Al2O3颗粒对γ-Al2O3表面酸碱性质的影响和脲修饰对γ-Al2O3及La2O3/γ-Al2O3催化肉桂醛MPV反应的影响。结果表明,经不同浓度的脲溶液浸泡后,γ-Al2O3表面酸、碱位点强度分布均发生变化,催化肉桂醛MPV反应,生成肉桂醇的选择性随着修饰用脲溶液浓度增加而下降。以脲溶液修饰的γ-Al2O3为载体制备的La2O3/γ-Al2O3催化肉桂醛MPV反应,具有与γ-Al2O3催化该反应类似的变化现象。     

Carbon formation and its influence on ethanol steam reforming over Ni/Al2O3 catalysts

Ethanol steam reforming was studied over Ni/Al₂O₃ catalysts. The effect of support (- and γ-Al₂O₃), metal loading and a comparison between conventional H₂ reduction with an activation method employing a CH₄/O₂ mixture was investigated. The properties of catalysts were studied by N₂ physisorption, X-ray diffraction (XRD) and temperature programmed reduction (TPR). After activity tests, the catalysts were analyzed by scanning electron microscopy (SEM) and thermogravimetric analysis (TG/DTA). Ni supported on γ-Al₂O₃ was more active for H₂ production than the catalyst supported on -Al₂O₃. Metal loading did not affect the catalytic performance. The alternative activation method with CH₄/O₂ mixture affected differently the activity and stability of the Ni/γ-Al₂O₃ and the Ni/-Al₂O₃ catalyst. This activation method increased significantly the stability of Ni/-Al₂O₃ compared to H₂ reduction. SEM and TG/DTA analysis indicate the formation of filamentous carbon during the CH₄/O₂ activation step, which is associated with the increasing catalyst activity and stability. The effect of temperature on the type of carbon formed was investigated; indicating that filamentous coke increased activity while encapsulating coke promoted deactivation. A discussion about carbon formation and the influence on the activity is presented.     

Characterization of Pd-based FCC CO/NOx control additives by in situ FTIR and extended X-ray absorption fine structure spectroscopies

Pdⁿ⁺/Ceⁿ⁺/Na⁺/γ-Al₂O₃-type materials used as FCC additives for CO/NO_x control were characterized by extended X-ray absorption fine structure (EXAFS) spectroscopy and in situ FTIR. The EXAFS data indicate that in freshly prepared samples palladium is present in the form of highly dispersed PdO species. Reduction with H₂ at 500 °C leads to the formation of small Pd clusters incorporating on average approximately six to eight metal atoms at a Pd−Pd bond distance of 2.76 Å. All components of these materials can interact with NO and promote the formation of nitrate/nitrite species, essentially “trapping” NO_x species on the catalyst surface. However, the Na⁺ species dominate the surface chemistry and readily form sodium nitrates with a characteristic IR band at 1370–1385 cm⁻¹. Finally, hydroxyls from the support are also actively participating in the formation of HNO_x type compounds with characteristic stretching vibrations in the 3500–3572 cm⁻¹ region.     

K2CO3/γ-A12O3催化剂在棉籽油制备生物柴油中的应用

利用等体积浸渍法制备K₂CO₃/γ-A1₂O₃负载型固体碱催化剂,应用于棉籽油和甲醇酯交换反应制备生物柴油。对催化剂使用前的保存条件、水分、重复使用性能、游离脂肪酸影响以及失活和再生进行了分析。结果表明,固体催化剂K₂CO₃/γ-Al₂O₃具有较好的抗水性,酸度对催化剂影响明显,重复使用4次未经活化的催化剂,催化活性明显降低,催化剂应密封保存。K₂CO₃/γ-A1₂O₃负载型固体碱催化剂经济实惠且催化效果良好。