以短碳链含氟单体N-甲基全氟丁基磺酰胺基乙基丙烯酸酯(C4氟酯)、甲基丙烯酸十八烷基酯（SMA）、甲基丙烯酸甲酯(MMA)和偏二氯乙烯(VDC)为聚合单体,采用半连续种子乳液聚合法制备了短碳链全氟丁基丙烯酸酯（PC4FA）共聚物乳液,并将其应用于织物整理上。采用FTIR、XPS表征了共聚物的结构和表面元素组成,利用AFM、SEM观察了短碳链全氟丁基丙烯酸酯拒水剂整理前后棉织物的表面形态变化。考察了拒水剂中含氟单体用量、拒水剂质量分数、焙烘温度和焙烘时间对织物拒水效果的影响。优化的整理工艺为：拒水剂中含氟单体质量分数为51.02%,拒水剂质量分数1.8%,焙烘温度180℃,焙烘时间5min。经该工艺整理后的棉织物对水的接触角可达142.5°,拒水等级为100分。     

含氟丙烯酸酯共聚乳液合成及性能研究

以甲基丙烯酸甲酯（MMA）、丙烯酸丁酯（BA）和全氟烷基丙烯酸酯等为主要原料,丙二醇为分子量调节剂,采用非离子阴离子复合乳化剂、氧化还原引发体系、超声微乳化技术,不同的加料方式制备出系列含氟丙烯酸酯乳液,并利用衰减全反射红外光谱（ATR-FTIR）对含氟丙烯酸酯共聚乳液胶膜进行了表征。采用接触角测定方法研究了含氟共聚乳液对织物整理后的表面性能变化,结果显示：乳液整理后的纯棉无纺布的拒水拒醇性大大提高,对水的接触角达到127o左右,对醇的最大接触角达到112o。乳液整理后的PP无纺布拒醇性明显改善,接触角达到101o左右。但拒水性能未见明显提高。     

全氟丁基丙烯酸酯拒水剂的合成及应用

以N-甲基全氟丁基磺酰胺基乙基丙烯酸酯(C4氟酯)、甲基丙烯酸十八烷基酯(SMA)、甲基丙烯酸甲酯(MMA)和偏二氯乙烯(VDC)为聚合单体,采用半连续种子乳液聚合法制备了拒水剂短碳链全氟丁基丙烯酸酯(PC4FA)共聚物乳液,并将其应用于织物整理上。采用FTIR、XPS表征了共聚物的结构和表面元素组成,利用AFM、SEM观察了短碳链全氟丁基丙烯酸酯拒水剂整理前后棉织物的表面形态变化。考察了拒水剂中含氟单体用量、拒水剂质量分数、焙烘温度和焙烘时间对织物拒水效果的影响。优化的整理工艺为:拒水剂中含氟单体含量为51.02%(以单体的总质量为基准,下同),拒水剂质量分数为1.8%,焙烘温度180℃,焙烘时间5 min。经该工艺整理后的棉织物对水的接触角可达142.5°,拒水等级为100分。     

锦棉户外织物的拒水拒油整理

采用FCB15型拒水拒油整理剂对锦棉织物进行拒水、拒油整理,得出最佳的整理工艺:整理剂质量浓度20 g/L,烘焙温度160℃,烘焙时间3 min。经此工艺整理的织物,虽然织物强力和透气性有略微的下降,但并不影响织物的服用性能;织物具有优良的拒水拒油性能,且经过洗涤后织物仍然具有良好的拒水拒油性能。     

硅烷改性氟代聚丙烯酸酯乳液的合成及其应用

在阳/非离子表面活性剂及引发剂作用下,将甲基丙烯酸十二氟庚酯、甲基丙烯酸十二醇酯、丙烯酸羟丙酯、甲基丙烯酸二甲氨乙酯、乙烯基三乙氧基硅烷进行乳液共聚,制得了硅烷改性的阳离子氟代聚丙烯酸酯乳液(FL-HDV)。用红外光谱(FT-IR)和核磁共振氢谱(1H NMR)对FLHDV主组分的结构进行了表征,用X射线光电子能谱仪(XPS)对乳液的成膜表面成分进行分析和表征,并讨论了硅烷改性前后及不同的整理工艺对其在涤纶织物上应用性能的影响。结果表明,与未用硅烷改性的氟代聚丙烯酸酯乳液(FLDH)对比,硅烷改性可以提高含氟聚合物的交联度,进而增加织物的拒水拒油性。XPS分析和接触角测定结果表明,在涤纶纤维表面明显存在有FLHDV膜,使得纤维与空气的界面上富集着疏水的含氟链段,而硅氧基团与纤维表面结合,从而赋予涤纶良好的拒水拒油性。在不同的工艺条件下,一浸一轧工艺处理的织物具有更高的拒水拒油等级,且弯曲刚度略低,柔软度较好。     

间位芳纶基导电纤维多功能织物的后整理工艺

对间位芳纶基导电纤维多功能混纺棉织物进行了阻燃和拒水拒油整理,采用单因素试验,研究了整理剂质量浓度、烘焙温度和时间对织物性能的影响。试验得出:整理剂质量浓度的变化、烘焙温度的升高以及烘焙时间的延长,均对织物的阻燃性、拒水拒油性、抗静电性及白度有影响,提出了适合生产要求的后整理工艺,为开发出多功能织物提供了理论依据。     

含氟多功能织物整理剂的最新研究进展

含氟高分子呈现出的拒水拒油性、防污性和自洁性等各种表面特性在纺织工业和其他行业中的应用越来越广.从拒水拒油机理、含氟单体的合成、含氟聚合物的聚合方法及其应用等方面对含氟多功能织物整理剂的国内外最新研究进展进行了较详尽的综述.     

含氟防水防油防污织物整理剂概况

随着有机氟工业的发展和科学技术的进步,有机氟精细化学品和含氟高分子材料、含氟功能高分子材料并驾齐驱,成为新兴氟化学的一个分支。含氟织物整理剂则是有机氟精细化学品的代表之一。它的主要功能是赋于被整理的织物以优异的拒水、拒油、防污、抗静电、阻燃等性能,尤其以防水、防油、防污为突出。通常所使用的防水剂,是使被整理的织物在其表面形成一层拒水膜。经防水整理的织物     

热反应性含氟水性聚氨酯的制备及其应用性能

由聚醚三醇、自制的不同氟原子含量的含氟三醇、1,6-己二异氰酸酯(HDI)和亚硫酸氢钠等原料合成了一系列热反应性含氟水性聚氨酯(FWPU)。通过红外光谱及~(19)F-NMR谱对预聚体和FWPU膜的结构进行了表征;通过热失重分析(TGA)及AATCC标准对FWPU膜及FWPU整理的织物的热稳定性及拒水拒油性能进行了研究。结果表明,该类热反应性含氟聚氨酯膜的热稳定性非常好,膜及其整理的织物拒水拒油性能优异。     

梳型有机硅改性含氟丙烯酸酯乳液的制备及性能研究

通过八甲基环四硅氧烷、十八烷基甲基二甲氧基硅烷、γ-巯丙基甲基二甲氧基硅烷和氨基丙基甲基二甲氧基硅烷的反应合成了可反应性梳型聚硅氧烷(Si-SH),再用Si-SH与全氟己基乙基甲基丙烯酸酯(C6SFMA)、丙烯酸十八酯(SA)、N-羟丙基丙烯酰胺(NMA)乳液聚合,得到的梳型有机硅改性含氟丙烯酸酯乳液。当乳化剂用量为2.0%、C6SFMA用量为18.0%、SA与Si-SH的质量比为3:7、NMA用量为0.6%时综合性能最好,乳液整理过的棉织物具有优良的拒水拒油效果。     

氧杂含氟单体类聚合物织物防水防油剂的合成与应用

以氧杂含氟单体1,1-二氢-2,5-二(三氟甲基)-3,6-二氧杂-全氟-1-壬醇丙烯酸酯和1,1-二氢-2,5-二(三氟甲基)-3,6-二氧杂-全氟-1-壬醇烯丙基醚为防水防油功能单体,采用预乳化-均质-细乳液聚合的工艺制备了防水防油剂.测试结果表明,乳液稳定、性能优良,防水可达4.5级,防油可达3级;染整工厂应用试验表明,使用过程中无恶性泡沫与粘滚现象,用量少、成本低.该乳液不会产生持久性污染物,清洁、环保,符合防水防油剂乳液的发展方向.     

氟代聚丙烯酸酯无皂乳液整理剂的防水防油性能研究

本文采用无皂乳液聚合法,以全氟烷基酯（FEA）为功能单体,制备了一种氟代聚丙烯酸酯无皂乳液整理剂,并对其乳液颗粒粒径大小及分布和高分子溶液表面活性进行了研究。通过对棉织物进行防水防油整理应用实验,详细考察了该织物整理剂的使用质量百分数和烘焙温度对防水防油性能的影响,并测试了其他应用性能。结果表明,通过该防水防油剂处理的织物有优异的防水防油性能,处理后的织物表面动态防水性可达90分,防油性可达5级,对水的接触角可达142.5°,对石蜡油的接触角可达126?,并且有良好的耐水洗性和常规应用性能。     

含氟织物整理剂国内专利分析

含氟织物整理剂可使纺织品具备拒水、拒油、容易去污等功能。本文从专利技术的发展趋势、申请人、发明人以及技术分类构成等角度对国内含氟织物整理剂相关专利的发展情况进行了分析,并针对该领域的发展提出对策建议。     

含氟丙烯酸酯橡胶的合成及性能

以丙烯酸乙酯、丙烯酸丁酯、含氟丙烯酸酯为单体,采用半连续乳液聚合法合成了含氟丙烯酸酯橡胶(ACM),用傅里叶变换红外光谱表征了其微观结构,考察了含氟单体种类及用量对含氟ACM亲水性、玻璃化转变温度及硫化特性的影响,以及交联剂二乙烯基苯(DVB)用量对含氟ACM硫化胶拉伸性能的影响。结果表明,丙烯酸六氟丁酯或丙烯酸十二氟庚酯(简称G 05)的转化率均超过90%;随着含氟单体用量的增加,ACM乳液涂膜的接触角逐渐增大,当加入质量分数为5%的G 05时,涂膜变为疏水性表面;含氟ACM只有1个玻璃化转变温度,且随着含氟单体用量的增加而逐渐下降;含氟ACM的操作安全性高,在硫化初期具有良好的流动性能;当DVB质量分数为3%时,含氟ACM的拉伸强度达到11.2 MPa。     

Miniemulsion polymerization of fluorinated siloxane‐acrylate latex and the application as waterborne textile finishing agent

Fluorinated siloxane–acrylate polymer latex was synthesized via miniemulsion polymerization, which was carried out by pseudo one‐step method. In the synthesis protocol, the monomers of octamethylclotetrasiloxane (D₄), tetravinyltetramethylcyclotetrasiloxane (D₄^v), methyl methylacrylate, butyl acrylate, N‐methylol acrylamide, and dodecafluoroheptyl methacrylate (DFMA) were first mixed and homogenized into a miniemulsion, which was stabilized by dedecybenzene sulfonic acid. The ring‐opening polymerization of cyclosiloxane was then steadily performed under miniemulsion conditions and followed by the postaddition of radical initiators to initiate the polymerization of acrylate and DFMA monomers. The influences on the emulsion properties by acrylic monomer with different addition protocol were investigated in this work. In addition, the synthesized latexes were characterized by using dynamic laser scattering, transmission electron microscope, differential scanning calorimetry, and Fourier transform infrared spectroscopy. These results indicated that the introduction of D₄^v in the latex can successfully suppress the phase separation between the thermodynamically incompatible components for the formation of uniform hybrid latex particles. The further application of the as‐synthesized latex was investigated as a new kind of waterborne textile finishing agent. Moreover, the influences of the content of D₄^v and DFMA on the finishing properties, especially for the softness, the water repellence, and the antimoisture properties, were systematically studied in this work. With a proper design on the content of the D₄^v and DFMA, stable textile finishing emulsion was prepared, which can endow the fabric both desirable softness and excellent water resistances. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40161.     

含氟丙烯酸酯类单体合成技术进展

含氟丙烯酸酯聚合物具有许多特殊优异性能,成为新型含氟材料领域研究热点。在许多要求特殊性能领域获得广泛应用,如特殊涂料、纸张和皮革涂饰剂、织物整理剂等。阐述了含氟丙烯酸酯类单体合成技术进展,并对其研究开发提出一些建议。     

有机硅改性水性聚氨酯的合成及织物整理应用

以羟丙基硅油改性二苯基甲烷二异氰酸酯(MDI)型聚氨酯合成了一种有机硅改性聚氨酯预聚体,将预聚体乳化后制备了一种有机硅改性水性聚氨酯。确定了乳液最佳配方,讨论了各工艺条件对改性水性聚氨酯整理棉织物综合性能的影响。结果表明,原棉织物、聚氨酯乳液整理和改性水性聚氨酯整理的棉织物表面粗糙度(SMD)分别为2.625、2.605和2.190,弯曲刚度B分别为0.0894、0.0869和0.0464,可见聚氨酯乳液整理前后棉织物的表面特性和柔顺性变化不大,但经有机硅改性水性聚氨酯整理后棉织物的表面特性和柔顺性则大为改善。     

丙烯酸酯改性水性聚氨酯皮革涂饰剂研究进展

综述了近年来丙烯酸酯改性水性聚氨酯(PUA)皮革涂饰剂的改性方法,包括共混交联法、溶液聚合法、种子乳液聚合法和互穿网络聚合法。讨论了PUA复合乳液及漆膜结构与性能的关系,提出了水性皮革涂饰剂的发展趋势。     

Effect of different polymers on the efficiency of water‐borne methyl amine adduct as corrosion inhibitor for surface coatings

Styrene/acrylic emulsion copolymer and water‐based short oil urethane alkyd resin were used as binders to prepare water‐based, environmentally friendly paints by using 0.5% emulsified methylamine adduct as corrosion inhibitor. The choice of the two above‐mentioned binders was based on the fact that styrene/acrylic emulsion copolymer is a nonconvertible binder, whereas short oil urethane alkyd resin is a convertible binder. The physical, chemical, mechanical, and corrosion properties of the paint films were evaluated and compared with a commercially known anticorrosive water‐based paint. It was found that the prepared paints have unique desirable properties such as the following: they do not contain anticorrosive pigments (which contain heavy metals in their main chemical structure); they are solvent‐free; and they can be produced to match any color. Corrosion tests on the films of the formulated paints revealed that the short oil urethane alkyd resin is superior to the styrene/acrylic copolymer. Moreover, the corrosion inhibition properties of the paint films prepared from both binders are comparable with the commercially available paints containing anticorrosive pigments. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 85: 879–885, 2002