Crystallization and microstructural evolution of MgO–Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–SiO<Subscript>2</Subscript>–TiO<Subscript>2</Subscript>–La<Subscript>2</Subscript>O<Subscript>3</Subscript> glass-ceramics

Crystallization and microstructure of glasses with the molar compositions 1MgO·1.2Al₂O₃·2.8SiO₂·1.2TiO₂·xLa₂O₃ (x = 0.1 and 0.4) were thermally treated at different temperatures in the range from 950 to 1250 °C and then analyzed by X-ray diffraction and scanning electron microscopy, in combination with energy-dispersive X-ray spectroscopy and electron backscatter diffraction. It was found that the microstructure is first homogeneous with the precipitation of randomly distributed crystals and then indialite domains with embedded perrierite and rutile crystals are formed. For higher temperatures or prolonged times, more domains appear and expand into the bulk of the sample. Finally, the entire sample consists of the indialite domains and the boundaries that are enriched in rutile, perrierite, and magnesium aluminotitanate. Nevertheless, very distinct differences are observed between the samples with different La₂O₃ concentrations. For the sample with x = 0.4, the domains were detected at lower temperatures, while the quantity and size of the domains increase faster due to the promoted precipitation of indialite. For the sample with x = 0.1, in addition to the domain boundaries, secondary boundaries between the “regions” (assemblages of the domains) are observed in a larger length scale. The average size of the crystalline phases found between the “regions” is larger than that typically observed at the domain boundaries. The sizes of the crystals at the boundaries decrease with higher concentrations of La₂O₃, and the crystals (especially perrierite) within the domains become larger, resulting in a more homogeneous microstructure. This results in better dielectric properties, i.e., much higher quality factor for the sample with x = 0.4 in comparison to that with x = 0.1 after heat-treatment at 1150 or 1250 °C.     

In vitro dissolution behavior of SiO<Subscript>2</Subscript>–MgO–Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–K<Subscript>2</Subscript>O–B<Subscript>2</Subscript>O<Subscript>3</Subscript>–F glass–ceramic system

Herein, we report the results of the in vitro dissolution tests, which were carried out by immersing the selected glass-ceramic samples in artificial saliva (AS) for various time periods of up to 42 days. In our experiments, the SiO(2)-MgO-Al(2)O(3)-K(2)O-B(2)O(3)-F glass ceramics with different crystal morphology and crystal content were used and a comparison is also made with the baseline glass samples (without any crystals). The bioactivity of the samples was probed by measuring the changes in pH, ionic conductivity and ionic concentration of AS following in vitro dissolution experiments. High resistance of the selected glass-ceramic samples against in vitro leaching has been demonstrated by minimal weight loss (<1%) and insignificant density change, even after 6 weeks of dissolution in artificial saliva. While XRD analysis reveals the change in surface texture of the crystalline phase, FT-IR analysis weakly indicated the Ca-P compound formation on the leached surface. The experimental measurements further indicate that the leaching of F(-), Mg(2+) ions from the sample surface commonly causes the change in the surface chemistry. Furthermore, the presence of (Ca, P, O)-rich mineralized deposits on the leached glass-ceramic surface as well as the decrease in Ca(2+) ion concentrations in the leaching solutions (compared to that in the initial AS solution) provide evidences of the moderate bioactive or mild biomineralisation behaviour of investigated glass-ceramics.     

Evaluation of CaO–SiO<Subscript>2</Subscript>–P<Subscript>2</Subscript>O<Subscript>5</Subscript>–Na<Subscript>2</Subscript>O–Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> bioglass-ceramics for hyperthermia application

Magnetic bioglass ceramics (MBC) are being considered for use as thermoseeds in hyperthermia treatment of cancer. While the bioactivity in MBCs is attributed to the formation of the bone minerals such as crystalline apatite, wollastonite, etc. in a physiological environment, the magnetic property arises from the magnetite [Fe₃O₄] present in these implant materials. A new set of bioglasses with compositions 41CaO · (52 ? x)SiO₂ · 4P₂O₅  · xFe₂O₃ · 3Na₂O (2 ≤ x ≤ 10 mol% Fe₂O₃) have been prepared by melt quenching method. The as-quenched glasses were then heat treated at 1050°C for 3 h to obtain the glass-ceramics. The structure and microstructure of the samples were characterized using X-ray diffraction and microscopy techniques. X-ray diffraction data revealed the presence of magnetite in the heat treated samples with x ≥ 2 mol% Fe₂O₃. Room temperature magnetic property of the heat treated samples was investigated using a Vibrating Sample Magnetometer. Field scans up to 20 kOe revealed that the glass ceramic samples had a high saturation magnetization and low coercivity. Room temperature hysteresis cycles were also recorded at 500 Oe to ascertain the magnetic properties at clinically amenable field strengths. The area under the magnetic hysteresis loop is a measure of the heat generated by the MBC. The coercivity of the samples is another important factor for hyperthermia applications. The area under the loop increases with an increase in Fe₂O₃ molar concentration and the. coercivity decreases with an increase in Fe₂O₃ molar concentration The evolution of magnetic properties in these MBCs as a function of Fe₂O₃ molar concentration is discussed and correlated with the amount of magnetite present in them.     

Preparation and characterization of Li<Subscript>2</Subscript>O–CaO–Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–P<Subscript>2</Subscript>O<Subscript>5</Subscript>–SiO<Subscript>2</Subscript> glasses as bioactive material

The aim of the present investigation was to study the role of Al₂O₃ in the Li₂O–CaO–P₂O₅–SiO₂ bioactive glass for improving the bioactivity and other physico-mechanical properties of glass. A comparative study on structural and physico-mechanical properties and bioactivity of glasses were reported. The structural properties of glasses were investigated by X-ray diffraction, Fourier transform infrared spectrometry, scanning electron microscopy and the bioactivity of the glasses was evaluated by in vitro test in simulated body fluid (SBF). Density, compressive strength, Vickers hardness and ultrasonic wave velocity of glass samples were measured to investigate physical and mechanical properties. Results indicated that partial molar replacement of Li₂O by Al₂O₃ resulted in a significant increase in mechanical properties of glasses. In vitro studies of samples in SBF had shown that the pH of the solution increased after immersion of samples during the initial stage and then after reaching maxima it decreased with the increase in the immersion time. In vitro test in SBF indicated that the addition of Al₂O₃ up to 1.5 mol% resulted in an increase in bioactivity where as further addition of Al₂O₃ caused a decrease in bioactivity of the samples. The biocompatibility of these bioactive glass samples was studied using human osteoblast (MG-63) cell lines. The results obtained suggested that Li₂O–CaO–Al₂O₃–P₂O₅–SiO₂-based bioactive glasses containing alumina would be potential materials for biomedical applications.     

Catalytic combustion of methane over Pt and PdO-supported CeO<Subscript>2</Subscript>–ZrO<Subscript>2</Subscript>–Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>/γ-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> catalysts

Catalytic combustion of methane was investigated on Pt and PdO-supported CeO₂–ZrO₂–Bi₂O₃/γ-Al₂O₃ catalysts prepared by a wet impregnation method in the presence of polyvinylpyrrolidone. The catalysts were characterized by X-ray fluorescence analysis, X-ray powder diffraction, X-ray photoelectron spectra, transmission electron microscopy, and BET specific surface area measurements. The Pt/CeO₂–ZrO₂–Bi₂O₃/γ-Al₂O₃ and PdO/CeO₂–ZrO₂–Bi₂O₃/γ-Al₂O₃ catalysts were selective for the total oxidation of methane into carbon dioxide and steam, and no by-products such as HCHO, CO, and H₂ were obtained. The catalytic activities of the PdO/CeO₂–ZrO₂–Bi₂O₃/γ-Al₂O₃ catalysts were relatively higher than those of the Pt-supported catalysts, due to the facile re-oxidation of metallic Pd into PdO based on lattice oxygen supplied from the CeO₂–ZrO₂–Bi₂O₃ bulk. A decrease in the calcination temperature during the preparation process was found to be effective in enhancing the specific surface area of the catalysts, whereby particle agglomeration was inhibited. Optimization of the PdO amount and calcination temperature enabled complete oxidation of methane at temperatures as low as 320 °C on the 11.6 wt% PdO/CeO₂–ZrO₂–Bi₂O₃/γ-Al₂O₃ catalyst prepared at 400 °C.     

Compositional dependence of the structural and dielectric properties of Li<Subscript>2</Subscript>O–GeO<Subscript>2</Subscript>–ZnO–Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>–Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> glasses

(10Li₂O–20GeO₂–30ZnO–(40-x)Bi₂O₃–xFe₂O₃ where x = 0.0, 3, 6, and 9 mol%) glasses were prepared. A number of studies, viz. density, differential thermal analysis, FT-IR spectra, DC and AC conductivities, and dielectric properties (constant ε′, loss tan δ, AC conductivity, σ _ac, over a wide range of frequency and temperature) of these glasses were carried out as a function of iron ion concentration. The analysis of the results indicate that, the density and molar volume decrease with an increasing of iron content indicates structural changes of the glass matrix. The glass transition temperature T _g and onset of crystallization temperature T _x increase with the variation of concentration of Fe₂O₃ referred to the growth in the network connectivity in this concentration range, while glass-forming ability parameter ΔT decrease with increase Fe₂O₃ content, indicates an increasing concentration of iron ions that take part in the network-modifying positions. The FT-IR spectra evidenced that the main structural units are BiO₃, BiO₆, ZnO₄, GeO₄, and GeO₆. The structural changes observed by varying the Fe₂O₃ content in these glasses and evidenced by FTIR investigation suggest that the iron ions play a network modifier role in these glasses while Bi₂O₃, GeO₂, and ZnO play the role of network formers. The temperature dependence of DC and AC conductivities at different frequencies was analyzed using Mott’s small polaron hopping model and, the high temperature activation energies have been estimated and discussed. The dielectric constant and dielectric loss increased with increase in temperature and Fe₂O₃ content.     

Influence of Bi substitution on microwave dielectric properties of BaO–La<Subscript>2</Subscript>O<Subscript>3</Subscript>–Sm<Subscript>2</Subscript>O<Subscript>3</Subscript>–TiO<Subscript>2</Subscript> ceramics

The influences of Bi substitution on microwave dielectric properties of Ba₄(La_0.5Sm_0.5)_9.33Ti₁₈O₅₄ solid solutions were investigated. Dielectric ceramics with general formula Ba₄(La_(0.5−z)Sm_0.5Bi _z )_9.33Ti₁₈O₅₄, z = 0.0–0.2 were prepared by conventional solid state route. The structural analysis of all the samples was carried out by X-ray diffraction and scanning electron microscopy. The dielectric properties were investigated as a function of Bi contents using open-ended coaxial probe method in the frequency range 0.3–3.0 GHz at room temperature. Dielectric constant varies from 83 to 88 and loss tangent from 2.1 × 10⁻³ to 5.5 × 10⁻³ at 3 GHz with temperature coefficient of resonant frequency changing from 106.7 to −8.4 ppm/oC as Bi contents increases from z = 0.00–0.20. It has been found that dielectric constant and temperature coefficient of resonant frequency improve whereas loss tangent is adversely affected with increase in Bi substitution.     

Fabrication of Yb<Subscript>2</Subscript>O<Subscript>3</Subscript>–Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–P<Subscript>2</Subscript>O<Subscript>5</Subscript>–SiO<Subscript>2</Subscript> Optical Fibers with a Perfect Step-Index Profile by the MCVD Process

An all-vapor phase MCVD process has been proposed for the fabrication of fiber preforms with a Yb₂O₃–Al₂O₃–P₂O₅–SiO₂ multicomponent glass core. We have investigated the tubular preform collapse into a rod and demonstrated approaches capable of preventing P₂O₅ losses in the central part of the core during the collapse process. Preforms with a flat, perfect step-index profile have been fabricated.     

Frequency dependence of dielectric properties of CaO–SrO–Li<Subscript>2</Subscript>O–Ln<Subscript>2</Subscript>O<Subscript>3</Subscript>–TiO<Subscript>2</Subscript> ceramics

CaO–SrO–Li₂O–Ln₂O₃–TiO₂ ceramics were prepared by solid state reaction method, where Ln₂O₃ consists of equal proportions of Nd₂O₃ and Sm₂O₃. Dielectric properties and crystal structure were investigated with respect to the content of TiO₂. Single phase with an orthorhombic perovskites structure was formed within the composition range of investigation. The frequency dependence of dielectric properties of the present ceramics was extensively investigated. Dielectric constant was less sensitive to frequency. However, dielectric loss and temperature coefficients were both very sensitive to frequency and gradually decreased with increasing frequency, such as the variation was more than ten times between 1 MHz and several GHz. The relationship between the temperature coefficient and dielectric loss was also discussed at different frequencies. And the mechanism of the frequency dependence was discussed in term of the role of Li ions.     

Synthesis,bioactivity and preliminary biocompatibility studies of glasses in the system CaO–MgO–SiO<Subscript>2</Subscript>–Na<Subscript>2</Subscript>O–P<Subscript>2</Subscript>O<Subscript>5</Subscript>–CaF<Subscript>2</Subscript>

New compositions of bioactive glasses are proposed in the CaO–MgO–SiO₂–Na₂O–P₂O₅–CaF₂ system. Mineralization tests with immersion of the investigated glasses in simulated body fluid (SBF) at 37°C showed that the glasses favour the surface formation of hydroxyapatite (HA) from the early stages of the experiments. In the case of daily renewable SBF, monetite (CaHPO₄) formation competed with the formation of HA. The influence of structural features of the glasses on their mineralization (bioactivity) performance is discussed. Preliminary in vitro experiments with osteoblasts’ cell-cultures showed that the glasses are biocompatible and there is no evidence of toxicity. Sintering and devitrification studies of glass powder compacts were also performed. Glass-ceramics with attractive properties were obtained after heat treatment of the glasses at relatively low temperatures (up to 850°C).     

Investigation of solid solution of ZrP<Subscript>2</Subscript>O<Subscript>7</Subscript>–Sr<Subscript>2</Subscript>P<Subscript>2</Subscript>O<Subscript>7</Subscript>

In this study, ZrP₂O₇ was synthesized by the solid state reaction of ZrO₂ and NH₄H₂PO₄ at 900 °C. Then, in set 1; 10, 5, 1, 0.5, 0.1, 0.05, 0.03% previously prepared Sr₂P₂O₇ were doped into ZrP₂O₇, and Sr₂P₂O₇ slightly affect the unit cell parameter of cubic ZrP₂O₇ (a = 8.248(6)–8.233(8) Å). The reverse of this process was also applied to Sr₂P₂O₇ system (set 2). ZrP₂O₇ changes the unit cell parameters of orthorhombic Sr₂P₂O₇ in between a = 8.909(5)–8.877(5) Å, b = 13.163(3)–13.12(1) Å, and c = 5.403(2)–5.386(4) Å. Analysis of the vibrations of the P₂O ₇ ^4? ion and approximate band assignments for IR and Raman spectra are also reported in this work. Some coincidences in infrared and Raman spectra both sets were found and strong P–O–P bands were observed. Surface morphology, EDX analysis, and thermoluminescence properties of both sets were given the first time in this paper.     

Hardness properties and microscopic investigation of crack–crystal interaction in SiO<Subscript>2</Subscript>–MgO–Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–K<Subscript>2</Subscript>O–B<Subscript>2</Subscript>O<Subscript>3</Subscript>–F glass ceramic system

In view of the potential engineering applications requiring machinability and wear resistance, the present work focuses to evaluate hardness property and to understand the damage behavior of some selected glass–ceramics having different crystal morphologies with SiO₂–MgO–Al₂O₃–K₂O–B₂O₃–F composition, using static micro-indentation tests as well as dynamic scratch tests, respectively. Vickers hardness of up to 5.5 GPa has been measured in glass–ceramics containing plate like mica crystals. Scratch tests at a high load of 50 N in artificial saliva were carried out in order to simulate the crack–microstructure interaction during real-time abrasion wear and machining operation. The experimental observations indicate that the novel “spherulitic-dendritic” shaped crystals, similar to the plate like crystals, have the potential to hinder the scratching induced crack propagation. In particular, such potential of the ‘spherulitic-dendritic’ crystals become more effective due to the larger interfacial area with the glass matrix as well as the dendritic structure of each mica plate, which helps in crack deflection and crack blunting, to a larger extent. While modest damage tolerant behavior is observed in case of ‘spherulitic-dendritic’ crystal containing material, severe brittle fracture of plate like crystals were noted, when both were scratched at 50 N load.     

Spectroscopic characterisation of local structure in Y<Subscript>2</Subscript>O<Subscript>3</Subscript>–B<Subscript>2</Subscript>O<Subscript>3</Subscript>–Bi<Subscript>2</Subscript>O<Subscript>3</Subscript> glasses doped with gadolinium

Gadolinium doped bismuth borate glasses containing up to 30 mol% Y₂O₃ were prepared by fast melt quenching method. The effect of yttrium on the local order in 3B₂O₃ · Bi₂O₃ and B₂O₃ · Bi₂O₃ glass matrices, particularly on the bismuth sites, was investigated by infrared (IR) spectroscopy and electron paramagnetic resonance (EPR) of Gd³⁺ ions. The IR results show that the local structure is more ordered in the glass system with higher bismuth content and the progressive addition of yttrium increases the local disorder in both bismuth–borate glass matrices. The EPR results indicate that Gd³⁺ ions occupy both bismuth and yttrium sites and reflect the same structural disorder like that suggested by IR results.     

Phase Formation in Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–ZrO<Subscript>2</Subscript>–CeO<Subscript>2</Subscript> Nanopowders Modified with Calcium Cations

We have studied phase formation in calcium-modified Al₂O₃–ZrO₂–CeO₂ nanopowders during sol–gel synthesis. The results demonstrate that heat treatment of the nanopowders first leads to the formation of a zirconium dioxide-based solid solution stabilized with cerium cations. Raising the heat treatment temperature helps the crystallization of corundum, a stable phase of aluminum oxide, to reach completion. In the temperature range 1400–1550°C, we observe the formation of a second aluminum-containing phase: calcium cerium hexaaluminate consisting of long prismatic grains.     

Structure–property correlations in the SiO<Subscript>2</Subscript>–PbO–Bi<Subscript>2</Subscript>O<Subscript>3</Subscript> glasses

SiO₂–PbO–Bi₂O₃ glasses having the composition of 35SiO₂–xPbO–(65−x)Bi₂O₃ (where x = 5, 10, 15, 20, 25, 35, 45; in mol%) have been prepared using the conventional melting and annealing method. Density, molar volume and Vickers microhardness of the prepared glasses were measured. Infrared (IR) and UV–visible spectroscopic techniques were used for structural studies of these glasses. Density as well as the microhardness increase systematically and, conversely, the molar volume decreases with increasing the lead oxide content. This behavior can be explained by the correlation with the glass structure. Increasing the lead oxide content (≥20 mol%) increases the network former PbO₄ groups which can play an important role in increasing the connectivity and compactness of the glass matrix via increasing the cross-linking with the other constituent silicate and bismuthate structural units. The increased compactness may explain, in turn, the increase of the density and microhardness. IR spectra reinforce the idea that bismuth participates in the glassy network predominantly as BiO₆ octahedral structural units. UV–VIS optical absorption spectra revealed UV-charge transfer absorption bands related to the contribution of Pb²⁺ ions in the region 350–385 nm; in addition to the extrinsic absorption of trace iron impurities in the range 220–290 nm. In the visible region, three optical bands in the ranges 415–435, 605–650 and 880–890 nm were correlated with the contribution of electronic transitions in Bi³⁺ ions. Calculation of the optical mobility gap and the width of the energy tail of glass from the UV–VIS absorption indicated a slight increase followed by a decrease in their values. The behavior change occurred at the glass in which PbO content is 20 mol% where lead oxide starts to participate into the glassy matrix as a network former. The combination of analytical FTIR and UV–visible spectroscopy provided a consistent picture of structure–property relations in this glass system.     

Syntheses and proton conductivity of mesoporous Nd<Subscript>2</Subscript>O<Subscript>3</Subscript>–SiO<Subscript>2</Subscript> and NdOCl–SiO<Subscript>2</Subscript> composites

Two mesoporous oxide composites of Nd₂O₃–SiO₂ and NdOCl–SiO₂ were synthesized using SBA-15 as a template and neodymium nitrate or neodymium chloride as a precursor. The porous Nd₂O₃–SiO₂ with a SBA-15-like structure has amorphous walls and the porous NdOCl–SiO₂ with a replicated structure of SBA-15 has crystalline walls. These porous materials were characterized by X-ray diffraction, transmission electron microscopy and nitrogen adsorption/desorption. They exhibited significant proton conductivities in the presence of moisture at low temperatures and the highest conductivity observed was 4.55 × 10⁻⁴ S/cm at 47 °C in wet air (RH = 28.6%).     

Phytic acid derived bioactive CaO–P<Subscript>2</Subscript>O<Subscript>5</Subscript>–SiO<Subscript>2</Subscript> gel-glasses

The possibility of using phytic acid as a precursor to synthesize CaO–P₂O₅–SiO₂ glasses by sol–gel method has been explored and the pseudo ternary phase diagram has been established. It was shown that gel-glasses over a broader range of compositions could be prepared compared to other phosphorus precursors or melt-quenching method. Furthermore, phytic acid was found to assist calcium being incorporated into glass networks. In vitro tests in simulated body fluid (SBF) were performed on the above gel–glasses and it was found that they were bioactive over a much broader compositional range especially at high phosphate content, thus enabling one to design bioactive materials with various degradation rates by adjusting the phosphate content.     

Phase relations in the K<Subscript>2</Subscript>MoO<Subscript>4</Subscript>–Ln<Subscript>2</Subscript>(MoO<Subscript>4</Subscript>)<Subscript>3</Subscript>–Zr(MoO<Subscript>4</Subscript>)<Subscript>2</Subscript> (Ln = La–Lu,Y) systems

We have studied phase relations in the K₂MoO₄–Ln₂(MoO₄)₃–Zr(MoO₄)₂ (Ln = La–Lu, Y) systems by the method of “intersecting cuts,” identified pseudobinary joins in their composition triangles, and constructed their phase compatibility diagrams. The systems have been shown to contain new ternary molybdates with the general formula K₅LnZr(MoO₄)₆ (Ln = Dy–Lu and Y). The thermal characteristics of the synthesized compounds have been studied by differential scanning calorimetry in the temperature range 25–700°C. The new ternary molybdates crystallize in a trigonal structure (sp. gr. R\(\bar 3\)c, Z = 6).     

Structural investigation of V<Subscript>2</Subscript>O<Subscript>5</Subscript>–P<Subscript>2</Subscript>O<Subscript>5</Subscript>–K<Subscript>2</Subscript>O glass system with antibacterial potential

The xV₂O(1?x)[0.8 P₂O₅ ? 0.2 K₂O] glass system with 0 ≤ x ≤ 50 mol% was prepared and the structural changes induced in these glasses by increasing the vanadium oxide content were investigated by IR and ESR spectroscopies. The dual behaviour role of V₂O₅ oxide, as network modifier (for x ≤ 10 mol%) and the network former (x ≥ 20 mol%), as a consequence of phosphate network depolymerization and P–O–V and V–O–V linkages appearance was also highlighted. The antibacterial effect of the glasses with x ≤ 20 mol% V₂O₅ content was tested by optical density (OD) measurements. A linear correlation between the amount of vanadium and the antibacterial effect was evidenced.     

CaGa<Subscript>2</Subscript>Se<Subscript>4</Subscript>–GaSe system

The phase relations in the CaGa₂S₄–GaSe system have been studied using differential thermal analysis, X-ray diffraction, microstructural analysis, microhardness tests, and density measurements, and its T–x phase diagram has been mapped out. The CaGa₂S₄–GaSe system has been shown to be a pseudobinary join of the ternary system Ca–Ga–Se. The CaGa₂S₄–GaSe system has been found to contain limited solid solutions based on the constituent selenides. The electrical conductivity of CaGa₂S₄ has been measured and its current–light behavior and photoelectric properties have been studied.