A generalized micromechanical approach for the analysis of transverse crack and induced delamination in composite laminates

The previously developed micromechanical approaches for the analysis of transverse cracking and induced delamination are limited for laminates with specific lay-ups such as cross-ply and specific loading conditions. In this paper a new micromechanical approach is developed to overcome such shortcomings. For this purpose, a unit cell in the ply level of composite laminate including transverse cracking and delamination is considered. Then, the governing equations for the stress and displacement fields of the unit cell are derived. The obtained approximate stress field is used to calculate the energy release rate for the propagation of transverse cracking and induced delamination. To show the capability of the new method, it is employed for the analyses of general laminates with [0/90]_s, [45/−45]_s, [30/−30]_s and [90/45/0/−45]_s lay-ups under combined loadings to calculate the energy release rate due to the transverse cracking and induced delamination. It is shown that the obtained energy release rates for transverse cracking and delamination initiation are in good agreement with the available results in the literature and finite element method. Furthermore, the occurrence priority of further transverse cracks and/or delamination at each damage state of the laminates will be discussed.     

Damage Assessment of CFRP [90/±45/0] Composite Laminates over Fatigue Cycles

The present paper develops a stiffness-based model to characterize the progressive fatigue damage in quasi-isotropic carbon fiber reinforced polymer (CFRP) [90/±45/0] composite laminates with various stacking sequences. The damage model is constructed based on (i) cracking mechanism and damage progress in matrix (Region I), matrix-fiber interface (Region II) and fiber (Region III) and (ii) corresponding stiffness reduction of unidirectional plies of 90°, 0° and angle-ply laminates of ±45° as the number of cycles progresses. The proposed model accumulates damages of constituent plies constructing [90/±45/0] laminates by means of weighting factor η ₉₀, η ₀ and η ₄₅. These weighting factors were defined based on the damage progress over fatigue cycles within the plies 90°, 0° and ±45° of the composite laminates. Damage model has been verified using CFRP [90/±45/0] laminates samples made of graphite/epoxy 3501-6/AS4. Experimental fatigue damage data of [90/±45/0] composite laminates have fell between the predicted damage curves of 0°, 90° plies and ±45°, 0/±45° laminates over life cycles at various stress levels. Predicted damage results for CFRP [90/±45/0] laminates showed good agreement with experimental data. Effect of stacking sequence on the model of stiffness reduction has been assessed and it showed that proposed fatigue damage model successfully recognizes the changes in mechanism of fatigue damage development in quasi-isotropic composite laminates.     

Transverse crack growth behavior considering free-edge effect in quasi-isotropic CFRP laminates under high-cycle fatigue loading

The high-cycle fatigue characteristics focused on the behavior of the transverse crack growth up to 10⁸ cycles were investigated using quasi-isotropic carbon fiber reinforced plastic (CFRP) laminates whose stacking sequence was [−45/0/45/90]_s. To assess the fatigue behavior in the high-cycle region, fatigue tests were conducted at a frequency of 100 Hz in addition to 5 Hz. In this study, to evaluate quantitative characteristics of the transverse crack growth in the high-cycle region, the energy release rate considering the free-edge effect was calculated. Transverse crack growth behavior was evaluated based on a modified Paris law approach. The results revealed that transverse crack growth was delayed under the test conditions of the applied stress level of σ_max/σ_b = 0.2.     

Notched strength of carbon fibre/epoxy composite laminates with a circular hole

This paper improves the two stress fracture criteria proposed by Whitney and Nuismer (known as the point stress criterion and the average stress criterion) to predict the strength of composite laminates with a circular hole. In the point stress criterion, it is assumed that the failure occurs when the stress over some distance (d ₀) away from the notch is equal to or greater than the unnotched laminate strength. In the average stress criterion it is assumed that failure occurs when the average stress over some distance (a ₀) ahead of the notch equals the unnotched laminate strength. Both stress fracture criteria are two parameter models based on the unnotched strength (σ₀) and a characteristic dimension (d ₀ or a ₀). A simple relation is used for the characteristic length to improve the accuracy while evaluating the notched strength of carbon/epoxy composite laminates. The analytical results are compared well with the existing test results of AS4-carbon/948 A1 epoxy [0/90]_{4 s} and [0/±45/90]_{2 S} composite laminates with various hole diameters and specimen widths.     

Notched strength of carbon fibre/epoxy composite laminates with a circular hole

This paper improves the two stress fracture criteria proposed by Whitney and Nuismer (known as the point stress criterion and the average stress criterion) to predict the strength of composite laminates with a circular hole. In the point stress criterion, it is assumed that the failure occurs when the stress over some distance (d ₀) away from the notch is equal to or greater than the un-notched laminate strength. In the average stress criterion it is assumed that failure occurs when the average stress over some distance (a ₀) ahead of the notch equals the unnotched laminate strength. Both stress fracture criteria are two parameter models based on the unnotched strength (σ ₀) and a characteristic dimension (d ₀ ora ₀). A simple relation is used for the characteristic length to improve the accuracy while evaluating the notched strength of carbon/epoxy composite laminates. The analytical results are compared well with the existing test results of AS4-carbon/948 Al epoxy [0/90]_4s and [0/ ± 45/90]_2S composite laminates with various hole diameters and specimen widths.     

Damage mechanics characterization of transverse cracking behavior in quasi-isotropic CFRP laminates with interlaminar-toughened layers

Microscopic damage behavior in quasi-isotropic CFRP laminates with interlaminar-toughened layers under tensile fatigue loading is investigated. Damage observation is conducted using an optical microscope and soft X-ray radiography. The material used is CFRP with interlaminar-toughened layers, T800H/3900-2. The laminate configurations are quasi-isotropic [45/0/−45/90]_s, [0/45/−45/90]_s and [45/−45/0/90]_s to discuss the effect of stacking sequence on microscopic fatigue damages. A damage mechanics analysis is used to obtain the energy release rate for transverse cracking which is correlated to the transverse crack density growth rate. The modified Paris-law analysis proves to be valid for characterization of transverse crack multiplication when the effect of other damage is small.     

Toughness,flexural, damping and interfacial properties of hybridized GFRE composites with MWCNTs

As the improved damping in fiber-reinforced composites can affect the other mechanical properties, therefore, the aim of this work is to investigate the effect of multiwall carbon nanotube (MWCNT) on the interfacial bond strength, flexural strength and stiffness, toughness and damping properties of hybridized glass-fiber reinforced epoxy (GFRE) composites. Nanophased epoxy resin was used to hybridize unidirectional and quasi-isotropic GFRE composites with [0/±45/90]_s and [90/±45/0]_s stacking sequences. Results from the interfacial characterizations of the hybridized composites showed improvement up to 30% compared to the control laminates. Hybridization of GFRE laminates with MWCNTs leads to decreasing the flexural and storage moduli, increasing flexural strength, toughness, natural frequencies and damping ratio. A high correlation coefficient of 0.9985 was obtained between static flexural and dynamic storage moduli. The highest flexural strength, flexural and storage moduli and natural frequency of quasi-isotropic laminate were observed for [0/±45/90]_s stacking sequence and vice versa for damping ratio.     

Damage response of stitched cross-ply laminates under impact loadings

The impact response of stitched graphite/epoxy laminates was examined with the aim of evaluating the efficiency of stitching as a reinforcing mechanism able to improve the delamination resistance of laminates. The investigation, which focussed on two classes of cross-ply stacking sequences ([0₃/90₃]_s and [0/90]_3s), showed that the role of stitches in controlling damage progression of laminates and their capability to reduce the impact sensitivity of specimens are greatly dependent on the impact behaviour of base (unstitched) laminates. In [0₃/90₃]_s laminates, in particular, stitching is able to reduce damage area, on condition that the impact energy is higher than a threshold level and delaminations are sufficiently developed. In [0/90]_3s laminates, on the other hand, stress concentration regions generated by the stitching process appear to promote the initiation and propagation of fibre fractures, thereby inducing a decrease in the penetration resistance of the laminate.     

Fatigue life prediction of carbon/epoxy laminates by stochastic numerical simulation

A three dimensional (3D) finite element model is developed to predict the progressive fatigue damage and the life of a plain carbon/epoxy laminate (AS4/3501-6) based on the longitudinal, transverse and in-plane shear fatigue characteristic. The model takes into account stress analysis, fatigue failure analysis, random distribution and material property degradation. Different cross- and angle-ply laminates including [0₈], [90₈], [0/90₂]_s, [0/90₄]_s, [0₂/90₂]_s, [30₁₆], [45/−45]_2s with the available experimental data are considered for the fatigue life simulation. In order to consider the random distribution of the laminate’s properties from element to element in the model, the laminate’s stiffness, and strength are randomly generated using a Gaussian distribution function. Sudden and gradual material properties degradation are considered during the fatigue simulation. The progressive fatigue damage and failure analysis is implemented in ABAQUS through user subroutines UMAT (user-defined material) and USDFLD (user-defined field variables). The predicted fatigue life of the simulation for different laminates is in good agreement with the experimental results.     

Damage evolution of angle-ply SCS-6/Ti composites under static and fatigue loading

The effect of fibre orientation and laminate stacking sequence on the tensile and fatigue behaviour of SCS-6/Ti 15-3 composites were investigated. The laminates used in this study were: (90)₆, (0/ ± 45)_s, (0/90)_s, and (90/ +-45)_s. The initiation and progression of microstructural damage at various stress levels was thoroughly characterized. It was found that fatigue life at high applied stresses were controlled by fibre fracture; progressive damage involving fibre fracture, interfacial debonding and matrix cracking became dominant at low applied stresses. Observation of the damage mechanisms in the angle-ply laminates under cyclic loading suggests that increasing the fibre-matrix bonding strength may improve the load carrying capability and fatigue life of laminates containing off-axis plies.     

Fatigue life estimation of graphite/epoxy laminates under consideration of delamination growth

A closed form approach to the assessment of the fatigue life of graphite/epoxy laminates under cyclic tension–compression loading has been developed. The model is mechanistic and uses cyclic energy release rates for prediction of delamination growth and of critical delamination sizes which induce buckling and the final failure of the laminates. Tests performed with graphite/epoxy specimens of stacking order [0_n, ?_m]_s with severed central plies [?], and of stacking order [0₂, +45, 0₂, ?45, 0, 90]_s with a central unloaded hole, indicate good correlation between estimated values and observed delamination growth, critical buckling strength of separated plies and load cycles to failure.     

An investigation into the damage development and residual strengths of open-hole specimens in fatigue

An extensive experimental program was carried out to investigate and understand the sequence of damage development throughout the life of open-hole composite laminates loaded in tension–tension fatigue. Quasi-isotropic carbon/epoxy laminates, with stacking sequence [45₂/90₂/−45₂/0₂]_S, [45/90/−45/0]_2S and [45/90/−45/0]_4S were examined. These were selected on the basis that under quasi-static loading the [45₂/90₂/−45₂/0₂]_S configuration exhibited a delamination dominated mode of failure whilst the [45/90/−45/0]_2S and [45/90/−45/0]_4S configurations showed a fibre dominated failure mode, previously described as “pull-out” and “brittle” respectively. Specimens were fatigue loaded to 1 × 10⁶ cycles or catastrophic failure, which ever occurred first. A number of tests were interrupted at various points as the stiffness dropped with increasing cycles, which were inspected using X-ray computed tomography (CT) scanning. A static residual strength program was carried out for run-out specimens of each configuration.     

Effects of laminate carbon/epoxy composite patches on the strength of double-strap adhesive joints: Experimental and numerical analysis

In this study, mechanical properties of double-strap joints with aluminum or composite patches of different orientation angles at their overlap area were investigated under tensile loading. For this purpose, AA2024-T3 aluminum was used as adherend, while patches were either AA2024-T3 aluminum or 16-ply laminate of carbon/epoxy composite with five different orientation angles ([0]₁₆, [90]₁₆, [0/90]₈, [45/−45]₈, [0/45/−45/90]₄). A two-part paste adhesive (DP 460) was used to bond adherend and patches. Six different types of joint samples were subjected to tensile loading. The effect of patch material on failure load and stress distribution was examined experimentally and numerically. As a result, it was concluded that the data obtained from 3-D finite element analysis were coherent with experimental results and additional to that fiber orientation angles of the patches markedly affected the failure load of joints, failure mode and stress distributions appeared in adhesive and composite.     

Simulation of fatigue performance of cross-ply composite laminates

The fatigue life of cross-ply composite laminates was evaluated using a statistical model. A modified shear-lag analysis was applied to describe the cycle-number-dependent stiffness reduction and consequent stress redistribution processes in the laminates resulted from both progressive transverse matrix cracking in transverse plies and local delamination at tips of transverse cracks. From the strength degradation behaviour and the static strength distribution of 0° plies as well as the fatigue behaviour of 90° plies, the fatigue life of cross-ply laminates with various types of lay-up can be simulated from the model. Predictions of fatigue performance are compared with experimental data for [0/90₂] _s , [02/90₂] _s and [0₂/90₄] _s graphite/epoxy cross-ply laminates: good agreements are obtained.     

Postbuckling strengths of composite laminate with various shaped cutouts under in-plane shear

The aim of present investigation is to study the buckling and postbuckling response and strengths under positive and negative in-plane shear loads of simply-supported composite laminate with various shaped cutouts (i.e., circular, square, diamond, elliptical-vertical and elliptical-horizontal) of various sizes using finite-element method. The FEM formulation is based on the first order shear deformation theory which incorporates geometric nonlinearity using von Karman’s assumptions. The 3-D Tsai-Hill criterion is used to predict the failure of a lamina while the onset of delamination is predicted by the interlaminar failure criterion. The effect of cutout shape, size and direction of shear load on buckling and postbuckling responses, failure loads and failure characteristics of quasi-isotropic [i.e., (+45/−45/0/90)_2s] laminate has been discussed. In addition, the effect of composite lay-up [i.e., (+45/−45/0/90)_2s, (45/−45)_4s and (0/90)_4s] has also been reported. It is observed that the cutout shape has considerable effect on the buckling and postbucking behaviour of the quasi-isotropic laminate with large size cutout. It is also observed that the direction of shear load and composite lay-up have substantial influence on strength and failure characteristics of the laminate.     

Numerical Modeling of Combined Matrix Cracking and Delamination in Composite Laminates Using Cohesive Elements

Sub-laminate damage in the form of matrix cracking and delamination was simulated by using interface cohesive elements in the finite element (FE) software ABAQUS. Interface cohesive elements were inserted parallel to the fiber orientation in the transverse ply with equal spacing (matrix cracking) and between the interfaces (delamination). Matrix cracking initiation in the cohesive elements was based on stress traction separation laws and propagated under mixed-mode loading. We expanded the work of Shi et al. (Appl. Compos. Mater. 21, 57–70 2014) to include delamination and simulated additional [45/?45/0/90]_s and [0₂/90_n]_s {n?=?1,2,3} CFRP laminates and a [0/90₃]_s GFRP laminate. Delamination damage was quantified numerically in terms of damage dissipative energy. We observed that transverse matrix cracks can propagate to the ply interface and initiate delamination. We also observed for [0/90_n/0] laminates that as the number of 90° ply increases past n?=?2, the crack density decreases. The predicted crack density evolution compared well with experimental results and the equivalent constraint model (ECM) theory. Empirical relationships were established between crack density and applied stress by linear curve fitting. The reduction of laminate elastic modulus due to cracking was also computed numerically and it is in accordance with reported experimental measurements.     

High-cycle fatigue characteristics of quasi-isotropic CFRP laminates over 10 cycles (Initiation and propagation of delamination considering interaction with transverse cracks)

High-cycle fatigue features of over 10⁸ cycles, particularly the initiation and propagation of edge delamination considering the effects of transverse cracks, were investigated using quasi-isotropic carbon-fiber-reinforced plastic (CFRP) laminates with a stacking sequence of [45/0/−45/90]_s in this study. In the relationship between a transverse crack density and initiation and growth of edge delamination, it was found that fatigue damage growth behavior varied depending on applied stress. It was observed that edge delamination initiated and grew at parts where transverse cracks were dense at ordinary applied stress, whereas it was observed that edge delamination grew before or simultaneously with transverse crack propagation at a low applied stress and high-cycle loading. In addition, the critical transverse crack density where delamination begins growing was calculated to evaluate the interaction between transverse crack and edge delamination growth.     

Study of critical buckling loads and modes of cross-ply laminated annular plates

Buckling of composite annular plates under uniform internal and external radial edge loads have been investigated using energy method. Trefftez rule is used in the stability equations. The symmetric buckling of symmetric cross-ply laminates is considered. In this paper, buckling behavior for the three laminates (90/0)_2s, (90/0₂/90)_s and (90₂/0₂)_s are studied. Influence of some parameters such as thickness, stacking sequence, type of supports and the ratio of hole to sheet radius on buckling loads and modes are investigated. The results of the energy method are compared with the results of numerical method. Based on the results, in the plates with clamped boundary conditions the symmetric buckling assumption is not accurate, contrary to other boundary conditions.     

Bearing damage evolution of a pinned joint in CFRP laminates under repeated tensile loading

A mechanical pinned joint in the CFRP laminates such as [0/±45/90]_3S, [90/±45/0]_3S, [0/±45/90]_2S and [90/±45/0]_2s is loaded statically and cyclically to finally obtain the critical condition for fatigue. It is derived that in the static loading, the critical damage that yields shear matrix crack is kink and the critical condition to the final failure is the appearance of kink in every inner 0° layer and that in the fatigue loading within the moderate load, the critical damage that yields shear matrix crack is almost always kink-like damage along the collapse front and at high load it is rather kink. Next, the non-elastic elongation of a joint at the maximum load subtracted by the one at 10th cycle is focused on and its capability is figured out for various stacking sequences. The critical value U_NE,F^* for the elongation rate change to the final fatigue failure is around 50–65 μm in the present material. The critical condition to the final fatigue failure and corresponding to U_NE,F^* is roughly the appearance of mostly kink-like damage in every inner 0° layer.