Pyroelectric properties of BST/PLT composite thick films with addition of xPbO–(1 − x)B2O3 glass

The Ba_xSr_1−xTiO₃ (BST)/Pb_1−xLa_xTiO₃ (PLT) composite thick films (20 μm) with 12 mol% amount of xPbO–(1 − x)B₂O₃ glass additives (x = 0.2, 0.35, 0.5, 0.65 and 0.8) have been prepared by screen-printing the paste onto the alumina substrates with silver bottom electrode. X-ray diffraction (XRD), scanning electron microscope (SEM) and an impedance analyzer and an electrometer were used to analyze the phase structures, morphologies and dielectric and pyroelectric properties of the composite thick films, respectively. The wetting and infiltration of the liquid phase on the particles results in the densification of the composite thick films sintered at 750 °C. Nice porous structure formed in the composite thick films with xPbO–(1 − x)B₂O₃ glass as the PbO content (x) is 0.5 ≥ x ≥ 0.35, while dense structure formed in these thick films as the PbO content (x) is 0.8 ≥ x ≥ 0.65. The volatilization of the PbO in PLT and the interdiffusion between the PLT and the glass lead to the reduction of the c-axis of the PLT phase. The operating temperature range of our composite thick films is 0–200 °C. At room temperature (20 °C), the BST/PLT composite thick films with 0.35PbO–0.65B₂O₃ glass additives provided low heat capacity and good pyroelectric figure-of-merit because of their porous structure. The pyroelectric coefficient and figure-of-merit F_D are 364 μC/(m² K) and 14.3 μPa^−1/2, respectively. These good pyroelectric properties as well as being able to produce low-cost devices make this kind of thick films a promising candidate for high-performance pyroelectric applications.     

Influence of A-site nonstoichiometry on sintering, microstructure and electrical properties of (Bi0.5Na0.5)TiO3 ceramics

Lead-free (Bi_0.5Na_0.5)_1+xTiO₃ ceramics (x = −0.02, −0.01, −0.005, 0, 0.005 and 0.01) were prepared by ordinary sintering. The effect of A-site stoichiometry on the densification, microstructure, dielectric properties, high-temperature impedances, and piezoelectric properties was explored. It was found that the high conductivity of (Bi_0.5Na_0.5)TiO₃ (BNT) ceramics should be mainly attributed to the formation of A-site cation vacancies during sintering. Improved physical and electrical properties can be achieved in the sample with A-site cation excess. The control of the stoichiometry proves to be an effective way to improve BNT ceramics for possible application.     

Sintering behavior and microwave dielectric properties of Bi3(Nb1−xTax)O7 solid solutions

Solid solutions of Bi₃(Nb_1−xTa_x)O₇ (x = 0.0, 0.3, 0.7, 1) were synthesized using solid state reaction method and their microwave dielectric properties were first reported. Pure phase of fluorite-type could be obtained after calcined at 700 °C (2 h)⁻¹ between 0 ≤ x ≤ 1 and Bi₃(Nb_1−xTa_x)O₇ ceramics could be well densified below 990 °C. As x increased from 0.0 to 1.0, saturated density of Bi₃(Nb_1−xTa_x)O₇ ceramics increased from 8.2 to 9.1 g cm⁻³, microwave permittivity decreased from 95 to 65 while Q_f values increasing from 230 to 560 GHz. Substitution of Ta for Nb modified temperature coefficient of resonant frequency τ_f from −113 ppm °C⁻¹ of Bi₃NbO₇ to −70 ppm °C⁻¹ of Bi₃TaO₇. Microwave permittivity, Q_f values and τ_f values were found to correlate strongly with the structure parameters of fluorite solid solutions and the correlation between them was discussed in detail. Considering the low densified temperature and good microwave dielectric proprieties, solid solutions of Bi₃(Nb_1−xTa_x)O₇ ceramics could be a good candidate for low temperature co-fired ceramics application.     

Characterization and microstructure of highly preferred oriented lead barium titanate thin films on MgO (100) by sol-gel process

Highly preferred oriented lead barium titanate (Pb_1−x,Ba_x)TiO₃ thin film, with particular emphasis on (Pb_0.5,Ba_0.5)TiO₃, can be obtained by spin-coating on MgO (100) substrate by using the precursor sol, which was synthesized from acetylacetone chelating with titanium isopropoxide and ethylene glycol as a solvent, in the sol-gel process. Film thickness, pyrolysis temperature and heating rate were studied systemically to investigate their influences on the formation of preferred oriented thin films. The highly preferred (001)/(100) oriented thin film could be obtained by the pyrolysis of wet film at 500 °C and annealing at 600 °C at a slow heating rate of 5 °C/min. It is confirmed that the tetragonal perovskite structure of the titanate ceramic decreases with an increase of Ba content in (Pb_1−x,Ba_x)TiO₃. The (001)/(100) oriented films were synthesized from all compositions between x = 0.2 and x = 0.8, at a crystallization temperature of 600 °C. In particular, for the Ba content in the range of x = 0.50.6, highly preferred (001)/(100) planes were observed.     

Optical and electrical properties of p-type AgInSnxS2−x (x = 0–0.04) thin films prepared by spray pyrolysis

AgInSn_xS_2−x (x = 0–0.2) polycrystalline thin films were prepared by the spray pyrolysis technique. The samples were deposited on glass substrates at temperatures of 375 and 400 °C from alcoholic solutions comprising silver acetate, indium chloride, thiourea and tin chloride. All deposited films crystallized in the chalcopyrite structure of AgInS₂. A p-type conductivity was detected in the Sn-doped samples deposited at 375 °C, otherwise they are n-type. The optical properties of AgInSn_xS_2−x (x < 0.2) resemble those of chalcopyrite AgInS₂. Low-temperature PL measurements revealed that Sn occupying an S-site could be the responsible defect for the p-type conductivity observed in AgInSn_xS_2−x (x < 2) thin films.     

Physical properties of (La,Sr)Ti(O,N)3 thin films grown by pulsed laser deposition

Thin films of La_xSr_1−xTiO_3+x/2 (x = 0, 0.25, 0.5, 0.75, 1) were grown by laser ablation on two different kinds of substrates (SrTiO₃ (STO) and MgO) and were subsequently ammonolysed to yield the corresponding oxynitrides La_xSr_1−xTi(O,N)₃. For both substrates all films were found to grow epitaxially to the (1 0 0) direction of the cubic perovskite structure, except for x = 0.5 that grew parallel to the (1 1 0) direction. For some of the films TiN was detected as impurity phase. Scanning electron microscopy revealed that the films are dense and homogeneous with thicknesses around 350 nm. Atomic force microscopy showed that the surface roughness of the films varied between 4.2 and 14.1 nm. The employed substrate had a strong influence on the electrical properties. Films grown on STO exhibited a metallic behaviour, in contrast to the films grown on MgO, which were insulating.     

Synthesis and humidity sensitive properties of nanocrystalline Ba1−xSrxTiO3 thick films

Nanocrystalline Ba_1−xSr_xTiO₃ (x=0, 0.2, 0.4, 0.6, 0.8 and 1.0) precursors were synthesized using the stearic acid gel method. After the precursors had been calcined at 600–950°C for 0.5–1 h, nanocrystalline powders with the cubic perovskite structure were obtained and these were made into thick films. The powder samples were characterized by differential thermal analysis, X-ray diffraction and transmission electron microscopy, and the thick film samples were characterized by scanning electron microscopy and X-ray diffraction. The humidity-sensitive properties of the nanocrystalline Ba_1−xSr_xTiO₃ thick films were investigated. The results show that these nanocrystalline thick films possess higher humidity sensitivity and lower resistance than those of conventional materials.     

Growth of lithium doped silver niobate single crystals and their piezoelectric properties

Lithium doped silver niobate (Ag_1−xLi_xNbO₃, 0 < x < 0.1) is one of the candidate materials for lead-free piezoelectric materials. In this study, Ag_1−xLi_xNbO₃ single crystals were successfully grown by a slow cooling method. Crystal structure was assigned to perovskite-type orthorhombic (monoclinic) phase. Dielectric properties were measured as a function of temperature. As a result, with increasing lithium contents, the phase transition at around 60 °C was shifted to lower temperature while the phase transition at around 400 °C was shifted to higher temperature. On the basis of these peak shifts, the lithium contents in Ag_1−xLi_xNbO₃ single crystals were determined. Moreover, P–E hysteresis measurement revealed that pure silver niobate crystal was weak ferroelectrics with P_r of 0.095 μC/cm² while Ag_0.9Li_0.1NbO₃ (ALN10) crystal was normal ferroelectrics with P_r of 10.68 μC/cm². About this ALN10 crystal, polling treatment was performed and finally piezoelectric properties were measured. As a result, high electromechanical coupling coefficient k₃₁ over 70% was observed.     

Thermal nonlinear refraction in the dye-doped sol–gel xTiO2 · (100 − x)SiO2 system

The build-up time of the thermal lens effect induced by a Gaussian beam in the DO3-doped sol–gel system xTiO₂ · (100 − x)SiO₂ at different compositions, both in the liquid and gel phases has been measured in a Z-scan geometry. While the pure titania samples show a minimum of the thermal diffusivity, a maximum is found for x ≈ 30. The sol to gel transformation leads to an increase of the build-up times at all compositions.     

Polar nanodomains and relaxor behaviour in (1 − x)Pb(Mg1/3Nb2/3)O3–xPbTiO3 crystals with x = 0.3–0.5

Phase transitions and dielectric properties of the (1 − x)Pb(Mg_1/3Nb_2/3)O₃–xPbTiO₃ crystals with x = 0.3–0.5 are studied. The solid solutions in this composition range are shown to be relaxor ferroelectrics. The crystals with low x demonstrate a diffused maximum in the temperature dependences of the dielectric permittivity at T_m. T_m varies with frequency according to the Vogel–Fulcher law. The polarizing microscopy investigations reveal a first-order phase transition from the relaxor phase to the low-temperature ferroelectric phase at T_C, which is several degrees below T_m. The permittivity peak in the crystals with x = 0.5 is sharp, and T_m is equal to T_C and does not depend on frequency, as is typical of the transition from a ferroelectric to an ordinary paraelectric phase. Nevertheless, the relaxor, but not the paraelectric, phase is observed at T > T_m. This conclusion is confirmed by the observation of the temperature behaviour of complex dielectric permittivity at T > T_m, which is typical of relaxors and related to the existence of polar nanodomains.     

Spectroscopic ellipsometry analysis of GaAs1 − xNx layers grown by molecular beam epitaxy

In this work, we present the effect of nitrogen incorporation on the dielectric function of GaAsN samples, grown by molecular beam epitaxy (MBE) followed by a rapid thermal annealing (for 90 s at 680 °C). The GaAs_1 − xN_x samples with N content up to 1.5% (x = 0.0%, 0.1%, 0.5%, 1.5%), are investigated using room temperature spectroscopic ellipsometry (SE). The optical transitions in the spectral region around 3 eV are analyzed by fitting analytical critical point line shapes to the second derivative of the dielectric function. It was found that the features associated with E₁ and E₁ + Δ₁ transitions are blue-shifted and become less sharp with increasing nitrogen incorporation, in contrast to the case of E₀ transition energy in GaAs_1 − xN_x. An increase of the split-off Δ₁ energy with nitrogen content was also obtained, in agreement to results found with MOVPE GaAs_1 − xN_x grown samples.     

Piezoelectric and dielectric properties of PZT–PZN–PMS ceramics prepared by molten salt synthesis method

Piezoelectric powders and ceramics with the composition of Pb_0.95Sr_0.05(Zr_0.52Ti_0.48)O₃–Pb(Zn_1/3Nb_2/3)O₃–Pb(Mn_1/3Sb_2/3)O₃ (PZT–PZN–PMS) were prepared by molten salt synthesis (MSS) and conventional mixed-oxide (CMO) methods, respectively. The influence of synthesis process on the properties of powders and ceramics were investigated in detail. The results show that the MSS method significantly improved the sinterability of PZT–PZN–PMS ceramics, resulting in an improvement of dielectric and piezoelectric properties compared to the CMO method. The optimum values of MSS samples are as follows: _r = 1773; tan δ = 0.0040; T_c = 280 °C; d₃₃ = 455 pC/N; k_p = 0.70; Q_m = 888; E_c = 10.3 kV/cm; and P_r = 28.2 μC/cm², at calcination of 800 °C and sintering of 1120 °C temperature.     

Optical properties of a-(Se70Te30)100−x(Se98 Bi2)x thin films

Measurements of optical constants (absorption coefficient, refractive index, extinction coefficient, real and imaginary part of the dielectric constant) have been made on a-(Se₇₀Te₃₀)_100−x (Se₉₈Bi₂)_x thin films (where x=0, 5, 10, 15 and 20) of thickness 2000 Å in the wavelength range 450–1000 nm. It is found that the optical bandgap decreases with the increase of Se₉₈Bi₂ concentration in the a-(Se₇₀Te₃₀)_100−x(Se₉₈Bi₂)_x system. The value of refractive index (n) decreases, while the extinction coefficient (k) increases with increasing photon energy. The results are interpreted in terms of concentration of localized states varying effective Fermi level.     

Preparation and optical properties of sol–gel derived Er-doped Al2O3–Ta2O5 films

Thin films of the system xAl₂O₃–(100 − x)Ta₂O₅–1Er₂O₃ were prepared by a sol–gel method and a dip-coating technique. The influences of the composition and the crystallization of the films on Er³⁺ optical properties were investigated. Results of X-ray diffraction indicated that the crystallization temperature of Ta₂O₅ increased from 800 to 1000 °C with increased values of x. In crystallized films, the intensities of the visible fluorescence and upconversion fluorescence tend to decrease with an increase in x values, due to the high phonon energy of Al₂O₃; the strongest fluorescence is observed in a crystallized film for x = 4 heat treated at 1000 °C. In amorphous films obtained by heat treatment at relatively low temperatures the Er³⁺ fluorescence could not be observed because strong fluorescence from organic residues remaining in the films thoroughly covered the Er³⁺ fluorescence. On the other hand, the Er³⁺ upconversion fluorescence in the amorphous films was observed to be stronger than that in the crystallized films. The strongest upconversion fluorescence is observed in an amorphous film for x = 75 heat treated at 800 °C.     

YNixMn1−xO3 thin films by pulsed laser deposition: Structure and magnetic properties

Highly oriented YNi_xMn_1−xO₃ thin films on SrTiO₃ (100) substrates were achieved by using pulsed laser deposition for x = 0.33 and x = 0.50. We used a combination of X-ray diffraction, scanning electron microscopy, atomic force microscopy, and magnetic-property measurements. The magnetic transition temperatures (T_c) of the as-grown films are higher than the corresponding bulk values (typically 85 K instead of 80 K, for x = 0.5, and 60 K instead of 50 K, for x = 0.33). Our magnetic measurements also suggest a spin-glass characteristic in the x = 0.33 films, while a cluster glasslike behavior is observed for the films with x = 0.5, which is quite different from that of the bulk samples. Finally, the influence of post-deposition heat treatment on the magnetic properties of the as-grown films is discussed.     

Mechanical characterization of Ni1−xZnxFe2O4 prepared by non-conventional methods

The mechanical properties like hardness, H_v and compressive strength, σ of Ni_1−xZn_xFe₂O₄ (x = 0.2, 0.3, 0.4 and 0.5) prepared by the non-conventional flash combustion and citrate-gel decomposition techniques are studied and reported. It is observed that there is an increase in hardness with zinc content as well as sintering temperature. The hardness in the order of 2.0–3.63 GPa and compressive strength in the order of 150–240 MPa are obtained for Ni–Zn ferrites prepared by these non-conventional techniques. The influence of density, porosity and microstructure on hardness and compressive strength of Ni–Zn ferrites with respect to sintering temperature was studied.     

In situ co-precipitation synthesis and photoluminescence of YxGd1−xVO4:Tm microcrystalline phosphors by hybrid precursors

Y_xGd_1−xVO₄:Tm³⁺ (5 mol%) phosphors were prepared by in situ co-precipitation technology with the different content ratio of Y/Gd (x = 0.2, 0.3, 0.4, 0.5, 0.6, 0.8, respectively). During the process, rare earth coordination polymers with o-hydroxylbenzoate were used as precursors, composing with polyethylene glycol (PEG) as dispersing media. After heat-treatment of the resulting multicomponent hybrid precursors at 900 °C, the samples were obtained. SEM indicated the particles present good crystalline state, whose crystalline grain sizes were about 0.2–2 μm. Under the excitation of 257 nm, all the materials show the characteristic emission of Tm³⁺ which is the strong blue emission centered at 475 nm originating from ¹G₄ → ³H₆ of Tm³⁺. Besides this, concentration quenching appears in the system of YVO₄:Tm³⁺ and GdVO₄:Tm³⁺. And when x reaches 0.5, the system of Y_xGd_1−xVO₄:Tm³⁺ shows the strongest blue emission.     

Anelastic spectroscopy measurements of nanoscale charge and magnetic structures in cuprates and manganites

Many perovskites and perovskite related materials exhibit electronic phase separation phenomena at nanometer scales, which are thought to concur to important electric and magnetic properties, like high-T_c superconductivity or colossal magnetoresistence (CMR). Recent and new anelastic spectroscopy experiments are presented, which supply information on the dynamics of such inhomogeneities in the superconductors of the La_2−xSr_xCuO₄ (LSCO) family and on the magnetic perovskite La_1−xCa_xMnO₃. In La_2−xSr_xCuO₄, a relaxation process at liquid He temperatures is identified as due to the motion of the hole stripes, acting as walls between antiferromagnetic (AF) domains. Another process is identified as the depinning of these stripes from defects in the disordered phase. In La_1−xCa_xMnO₃ a glassy dynamic response below the ferromagnetic (FM) transition is attributed to the insulating nanodomains coexisting with the ferromagnetic background.     

Characterization of CuIn1 − xAlxS2 thin films prepared by thermal evaporation

Ingots containing single crystals of the quaternary alloys CuIn_1 − xAl_xS₂ (CIAS) were grown by a horizontal Bridgman method for compositions with x = 0, 0.2 and x = 0.4. (CIAS) thin films were prepared by thermal evaporation technique on to glass substrates. Structural and optical properties of the films were studied in function of the Al content. Band gap, and absorption coefficients were determined from the analysis of the optical spectra (transmittance and reflectance as a function of wavelength) recorded by a spectrophotometer. The samples have direct bandgap energies of 1.95 eV (x = 0), 2.06 eV (x = 0,2) and 2.1 eV (x = 0,4). These optical results were correlated with the structural analysis by X-Ray diffraction.     

Effect of B-doping on the structural, magnetotransport and magnetocaloric properties of La0.67Ca0.33MnO3 compounds

In this study, the effect of Mn site substitution of B on the structural, electrical and magnetocaloric properties of manganites was investigated. Polycrystalline manganites with the chemical composition La_0.67Ca_0.33Mn_1−xB_xO₃ (x = 0, 0.1, 0.2 and 0.3) were prepared by the standard solid-state process. It was found that the magnetisation, the Curie temperature and the maximum value of the magnetic entropy change |ΔS_m| decrease with increasing concentration of B.