FGH95粉末镍基合金的组织结构与蠕变断裂特征

通过对不同工艺处理FGH95合金进行组织形貌观察及持久性能测试,研究了组织结构对合金持久性能的影响规律。结果表明:经1150℃固溶和时效处理后,合金中有粗大γ′相在较宽的边界区域不连续分布,其周围存在γ′相贫化区;经1160℃固溶及时效处理后,合金中粗大γ′相完全溶解,在晶内弥散分布高体积分数的γ′相,并有粒状(Cr,Nb)23(C,B)6硼碳化合物在晶内及沿晶界不连续析出;经1165℃固溶和时效后,合金的晶粒尺寸明显长大,并有硬而脆的碳化物膜沿晶界连续析出。在650℃、1034MPa条件下,经1160℃固溶和时效合金具有较高蠕变抗力和较长持久寿命,蠕变期间的变形机制是位错以Orowan机制饶过γ′相、或位错剪切γ′相,其中晶界处不连续析出的粒状碳化物可有效阻碍位错滑移,是使合金具有较好蠕变性能的主要原因。蠕变后期,合金的变形特征是晶内发生单取向滑移,随蠕变进行位错在晶界处塞积,并引起应力集中,致使裂纹在晶界处萌生及扩展是合金的蠕变断裂机制。     

固溶温度对DZ951镍基高温合金组织和持久性能的影响

采用光学显微镜、扫描电镜和透射电镜研究了固溶温度对定向凝固DZ951镍基高温合金组织和持久性能的影响.结果表明:合金经固溶处理后,枝晶偏析降低,合金强度增加.碳化物由铸态时的骨架状变成块状,呈不连续状分布在晶界,对裂纹的萌生和扩展都有抑制作用.γ′相经固溶处理后,尺寸变小,分布更加均匀.合金在1100℃/60MPa的持久性能得到提高.在1300℃固溶处理时,合金元素分布更加均匀,γ′相体积分数增加,使DZ951合金具有较高的持久寿命.     

固溶处理对GH4169G合金蠕变的影响

研究了固溶处理温度对GH4169G合金晶粒组织、晶界析出和蠕变的影响。结果表明,随着固溶处理温度的提高(由980℃提高到1020℃)GH4169G合金的晶粒尺寸明显增大,晶界d相的尺寸和数量明显减少,晶内g″相的析出变化不大;合金的650℃/700 MPa稳态蠕变速率明显降低,表观蠕变激活能明显增大,蠕变断裂寿命显著延长。固溶处理温度对680℃/725 MPa的蠕变性能有相同的影响趋势,但其程度减弱。孪晶的形成是GH4169G合金的重要蠕变机制。提高固溶处理温度使晶界d相的析出减少,晶界滑动蠕变速率降低;同时使晶粒度增大,形成孪晶的阻力增大,晶粒蠕变速率降低。     

热处理对Ti-35V-15Cr-0.15Si-0.05C合金热稳定性能的影响

通过对Ti-35V-15Cr-0.15Si-0.05C合金轧制环件取样进行热处理和热稳定性能实验,研究了850℃和950℃固溶处理和950℃固溶后在600℃和700℃实效后的热稳定性能和微观组织。结果表明:合金仅经过固溶处理α相析出不明显,而经过固溶加时效处理后α相在晶界和晶内大量析出,在热稳定性能测试时,经过540℃100h热暴露后,α相进一步析出。合金α相是影响合金拉伸性能的主要因素,在晶界析出的连续α相导致合金塑性急剧下降;通过850℃固溶热处理能够获得较好的室温拉伸和热稳定性能。     

热处理制度对GH706高温合金持久性能的影响

不同热处理制度对GH706高温合金持久性能影响的研究结果表明,固溶加低温时效的两段热处理使合金中析出的η相呈胞状紧密排列于晶界,强化晶界,获得较长的持久寿命。增加稳定化处理的三段热处理合金,晶界η相以长针状析出,并在其周围形成γ′、γ″相贫化区,贫化区强度较低,弱化了晶界,使得裂纹易于萌生,且易于连通形成扩展通道,降低了持久寿命。直接时效(DA)处理的合金中η相在晶界呈短捧状分散排列,可以起到强化晶界的作用,而η相间的无析出区可以钝化裂纹的萌生和扩展,从而获得最长的持久寿命和最高的持久塑性。     

热轧态Inconel690合金中碳化物的溶解和析出

研究了热轧态690合金中碳化物的溶解和析出行为及其结构,结果表明:在热轧态合金中存在的碳化物多数沿晶界长条状分布,少量呈颗粒状分布于晶内,类型为M_(23)C_6.热轧态合金的晶界和晶内碳化物的完全固溶温度分别为1050℃、1080℃,在低固溶温度下未完全溶解的残余晶界碳化物直接导致后续TT处理晶界不再析出碳化物;将合金完全固溶处理后,在后续TT处理的晶界上会重新析出细小、半连续的碳化物.     

GH4720Li镍基合金混晶组织对高温持久性能的影响

GH4720Li镍基合金具有优良的高温力学性能,被广泛地用于制造航空发动机热端部件。在实际生产过程中GH4720Li合金容易得到含有局部粗晶的混晶组织。利用高温持久实验和扫描电子显微镜技术,研究了680℃/830 MPa与730℃/530 MPa条件下混晶组织对GH4720Li合金持久性能的影响规律,结果表明680℃/830 MPa条件下合金的持久失效机制以晶内位错运动为主,持久寿命随着粗晶数量增加而缩短。混晶中的粗晶含量相同时,晶界滑移机制也会起到一定作用,粗晶尺寸增大可以有效延长持久寿命。730℃/530 MPa条件下合金的持久失效机制以晶界滑移机制为主,持久寿命随着粗晶数量增加而延长。混晶中的粗晶含量相同时,持久寿命随着粗晶尺寸增大而缩短。     

单晶镍基合金的热处理及对蠕变性能的影响

根据差热曲线分析制定出合金的热处理工艺,结合蠕变性能测试及组织形貌观察,研究了固溶温度对一种含Re单晶镍基合金蠕变性能的影响.结果表明:铸态合金组织中存在明显的成分偏析,其中元素Cr,Co,Re富集于枝晶干,元素Al,Ta,W等富集于枝晶间.采用不同温度固溶处理,合金具有不同的蠕变寿命.当固溶温度提高到1320℃时,可使合金成分的均匀化程度提高,难溶元素得到充分扩散,降低合金的枝晶干/间成分偏析,并抑制合金中TCP相的析出,可显著提高合金的蠕变抗力.与1300℃固溶处理相比较,合金经1320℃高温固溶处理后,其在1072℃,137MPa条件下的蠕变寿命由37h提高到230h.     

显微组织对HK40钢光滑和缺口试样持久性能的影响

HK40钢是石油化工厂合成氨、乙烯等大量使用的高温材料。采用高温固溶处理模拟焊接热影响区组织,研究显微组织对光滑和缺口试样持久性能的影响具有实际意义。本工作采用铸态直接时效和1250℃固溶后时效两种热处理工艺,时效温度为600、800、871和950℃,时效时间为200h,研究了晶界和晶内碳化物对持久寿命和持久延性的影响。     

热处理对Ti-6Mo-5V-3Al-2Fe-2Zr合金拉伸性能的影响

研究了固溶+单级时效处理、固溶+双级时效处理、固溶+随炉冷却处理对新型亚稳β钛合金Ti-6Mo-5V-3Al-2Fe-2Zr的显微组织和拉伸性能的影响。结果表明：与固溶+单级时效处理相比,固溶+双级时效处理析出的晶内次生α相间距减小和体积分数增大而使合金的强度提高。两种热处理都使合金中生成连续的晶界α相,导致合金的塑性降低;与上述两种热处理相比,固溶+随炉冷却处理使合金中析出的晶内次生α相的间距明显减小且沿晶界生成向晶内生长的α_wgb相,使合金的强度和塑性显著提高,其抗拉强度达到1421 MPa,断后伸长率为7.7%;与次生α相的体积分数相比,其间距是影响合金强度的主要因素。随着次生α相间距的减小,合金的强度提高。     

Estimation of Parameters of Universal Distribution of Moments of Failure of Products

A method is proposed for estimating the parameters of a mixture of exponential and Weibull distributions for which the accuracy of preliminary estimates obtained by graphical analysis is refined in accordance with the criterion of maximum likelihood. The efficiency of the proposed method is supported by the results of statistical modeling.     

Analysis of the rate of propagation of the wave of change of boiling modes

An approximate analytical expression is derived for the velocity of the front of the wave of change of boiling modes on a rod and on a plate. The impact of the Thomson effect and of the heater orientation in the gravity field is included. Adequate agreement is demonstrated between the derived relations and experimental data.     

Evaluation of optical properties of highly scattering media by moments of distributions of times of flight of photons

A novel method for the determination of the optical properties of tissue from time-domain measurements is presented. The data analysis is based on the evaluation of the first moment and the second centralized moment, i.e., the mean time of flight and the variance of the measured distribution of times of flight (DTOF) of photons injected by short (picosecond) laser pulses. Analytical expressions are derived for calculation of absorption and of reduced scattering coefficients from these moments by application of diffusion theory for infinite and semi-infinite homogeneous media. The proposed method was tested on experimental data obtained with phantoms, and results for absorption and reduced scattering coefficients obtained by the proposed method are compared with those obtained by fitting of the same data with analytical solutions of the diffusion equation. Furthermore, the accuracy of the moment analysis was investigated for a range of integration limits of the DTOF. The moment analysis may serve as a comparatively fast method for evaluating optical properties with sufficient accuracy and can be used, e.g., for on-line monitoring of optical properties of biological tissue.     

可燃气体检测报警器测量结果的不确定度评定

本文详细介绍了可燃气体检测报警器示值误差测量结果的不确定度评定方法。     

水三相点复现的不确定度评定

水三相点是开尔文热力学温度的唯一基准点，也是ITS-90国际温标重要的定义固定点。因此，水三相点不确定度分析对整个温标的建立、温度量值传递起着至关重要的作用。近3年来，中国计量科学研究院研制出一系列高质量的水三相点容器，加强了水三相点的研究，为不确定度的分析提供了更为可靠的实验依据。同时，不确定度的分析也是客观评价新研制容器性能的一个重要指标。因此，根据实验结果对新研制容器所复现的水三相点进行了不确定度评定。评定结果表明，其扩展不确定度为0．16mK(k=2．69，P=0．99)。     

心电图机电压测量示值误差测量值的不确定度评定

本文介绍了心电图机电压测量示值误差测量值的不确定度评定与表示方法。     

Estimation of potentialities of methods of summation of direct measurement errors

Conventional methods for summation of direct measurement errors are considered. Conditions under which these methods provide consistent results are stated. It is proposed to utilize for characteristic of the total error, its interval estimator or the half-sum of the value obtained by adding up its arithmetic and geometric random errors.Translated from Izmeritel'naya Tekhnika, No. 4, pp. 10–12, April, 1995.