Effect of BiScO3 and LiNbO3 on the Piezoelectric Properties of (Na0.5K0.5)NbO3 Ceramics

Lead-free potassium sodium niobate-based piezoelectric ceramics (1− y )(Na_{0.5−0.5 x} K_{0.5−0.5 x} Li _x )NbO₃− y BiScO₃ (  y =0.01, x= 0–0.06) have been prepared by an ordinary sintering process. The XRD analysis showed that the structure changes from orthorhombic to tetragonal with the increase of x (at y =0.01, abbreviated as KNNBSL100 x ). At room temperature, the polymorphic phase transition from the orthorhombic to the tetragonal phase was identified at approximately 0.02≤ x ≤0.04. The piezoelectric and ferroelectric properties were significantly enhanced. The temperature dependences of the relative permittivity revealed that the Curie temperature was increased with the addition of LiNbO₃. These solid solution ceramics are promising as potential lead-free candidate materials.     

Phase Structure and Electrical Properties of (K0.48Na0.52)(Nb0.95Ta0.05)O3-LiSbO3 Lead-Free Piezoelectric Ceramics

(1− x )(K_0.48Na_0.52)(Nb_0.95Ta_0.05)O₃– x LiSbO₃ [(1− x )KNNT− x LS] lead-free piezoelectric ceramics were prepared by the conventional solid-state sintering method. A morphotropic phase boundary (MPB) between orthorhombic and tetragonal phases was identified in the composition range of 0.03< x <0.05. The ceramics near the MPB exhibit a strong compositional dependence and enhanced electrical properties. The (1− x )KNNT– x LS ( x =0.04) ceramics exhibit good electrical properties ( d ₃₃=250 pC/N, k _p=45.1%, k _t =46.3%, T _c=348°C, T _{o − t} =74°C, P _r=25.9 μC/cm², E _c=10.7 kV/cm, ɛ_r∼1352, tan δ∼3%). These results show that (1− x )KNNT– x LS ceramic is a promising lead-free piezoelectric material.     

Synthesis and Properties of Multiferroic La-Modified BiFeO3 Ceramics

Multiferroic Bi_{(1− x )}La _x FeO₃ was synthesized by a modified Pechini approach. Optimal conditions for the synthesis of single-phase Bi_{(1− x )}La _x FeO₃ powder were reported. A conventional sintering process was used to fabricate Bi_{(1− x )}La _x FeO₃ ceramics. Ferroelectric and magnetic loops measured at room temperature indicate the coexistence of ferroelectricity and magnetism. The La modification of BiFeO₃ has a beneficial effect on the ferroelectric and magnetic properties. The ceramic samples show a stable dielectric constant and quite low dielectric loss between 100 Hz and 10 MHz. The piezoelectric constants of Bi_{(1− x )}La _x FeO₃ ceramics were first reported.     

Structural and Dielectric Properties of Ag(Nb0.8Ta0.2)1−xSbxO3 (x≤0.08) Ceramics

Sb₂O₅ were selected to substitute (Nb_0.8Ta_0.2)₂O₅ and the effects of Sb substitution on the dielectric properties of Ag(Nb_0.8Ta_0.2)O₃ ceramics were studied. The perovskite Ag(Nb_0.8Ta_0.2)_{1− x} Sb _x O₃ ceramics showed no obvious change with x value being no more than 0.08, and the pseudoperovskite unit cell parameters a = c , b and monoclinic angle β decrease with Sb concentration increasing. The dielectric properties of Ag(Nb_0.8Ta_0.2)_{1− x} Sb _x O₃ ceramics were found to be affected greatly by the substitution of Sb for Nb/Ta. The ɛ value of Ag(Nb_0.8Ta_0.2)_{1− x} Sb _x O₃ ceramics sintered at their densified temperature increased from 480 to 825 with x from 0 to 0.08, the tan δ value decreased sharply from 0.0065 to 0.0023 (at 1 MHz) with x increasing from 0 to 0.04, and then kept a stable lower tan δ value ∼0.0024 with x to 0.08. The temperature coefficient of capacitance values continuously decreased from a positive value of 1450 ppm/°C for x =0 to a negative value of −38.52 ppm/°C for x =0.08.     

Ferroelectric and Piezoelectric Properties of Na1−xBaxNb1−xTixO3 Ceramics

Piezoelectric ceramics Na_{1− x} Ba _x Nb_{1− x} Ti _x O₃ with low BaTiO₃ concentrations x have been prepared by the solid-state reaction method, and their ferroelectric and piezoelectric properties have been studied. The ceramics are classic ferroelectrics when x ≤0.10, and the ferroelectric–paraelectric phase transition becomes diffusive when x ≥0.15. A low doping level of BaTiO₃ changes the NaNbO₃ ceramics from antiferroelectric to ferroelectric. With the increase in BaTiO₃ doping level, the Curie temperature of ceramics decreases linearly and the remnant polarization and coercive field also decrease, while their dielectric constant increases. Na_0.9Ba_0.1Nb_0.9Ti_0.1O₃ ceramics show the largest piezoelectric constant d ₃₃ (147 pC/N) and good sinterability, suggesting that it is a good candidate for lead-free piezoelectric ceramics.     

Microstructure and Piezoelectric Properties of (1−x)(Na0.5K0.5)NbO3–xLiNbO3 Ceramics

(1− x )(Na_0.5K_0.5)NbO₃– x LiNbO₃ [(1− x )NKN– x LN] ceramics were produced by the conventional solid-state sintering method, and their microstructure and piezoelectric properties were investigated. The formation of the liquid phase and K₆Li₄Nb₁₀O₃₀ second phase that were observed in the (1− x )NKN– x LN ceramics was explained by the evaporation of Na₂O during the sintering. A morphotropic phase boundary (MPB) was observed in the specimens with 0.05< x <0.08. Promising piezoelectric properties were obtained for the specimens with x =0.07. Therefore, the piezoelectric properties of this 0.93NKN–0.07LN ceramic were further investigated and were found to be influenced by their relative density and grain size. In particular, grain size considerably affected the d ₃₃ value. Two-step sintering was conducted at different temperatures to increase the grain size. Piezoelectric properties of d ₃₃=240 (pC/N) and k _p=0.35 were obtained for the 0.93NKN–0.07LN ceramics sintered at 1030°C and subsequently annealed at 1050°C.     

High-Q Microwave Dielectrics in the (Mg1−xCox)2TiO4 Ceramics

The microwave dielectric properties and the microstructures of (Mg_{1− x} Co _x )₂TiO₄ ceramics prepared by the conventional solid-state route were investigated. Lattice parameters were also measured for specimens with different x . The formation of solid solution (Mg_{1− x} Co _x )₂TiO₄ ( x =0.02–0.1) was confirmed by the X-ray diffraction patterns, energy dispersive X-ray analysis, and the lattice parameters measured. By increasing x from 0 to 0.05, the Q × f of the specimen can be tremendously boosted from 150 000 GHz to a maximum of 286 000 GHz. A fine combination of microwave dielectric properties (ɛ_r∼15.7, Q × f ∼286 000 GHz at 10.4 GHz, τ_f∼−52.5 ppm/°C) was achieved for (Mg_0.95Co_0.05)₂TiO₄ ceramics sintered at 1390°C for 4 h. Ilmenite-structured (Mg_0.95Co_0.05)TiO₃ was detected as a second phase. The presence of the second phase would cause no significant variation in the dielectric properties of the specimen because it possesses compatible properties compared with that of the main phase. In addition, only a small deviation in the dielectric properties was monitored for specimens with x =0.04–0.05 at 1360°–1420°C. It not only provides a wide process window but also ensures an extremely reliable material proposed as a very promising dielectric for low-loss microwave and millimeter wave applications.     

Phase Transformation and Tunable Piezoelectric Properties of Lead-Free (Na0.52K0.48−xLix)(Nb1−x−ySbyTax)O3 System

Lead-free (Na_0.52K_{0.48− x} )(Nb_{1− x − y} Sb _y )O₃- x LiTaO₃ (NKNS–LT) piezoelectric ceramics have been fabricated by ordinary sintering. A special attention was paid to the composition design through which the dielectric and piezoelectric properties of the (Li, Ta, Sb) modified NKN systems were significantly promoted. A property spectrum was generated with a particular discussion on the relationship between the Sb content, the LT content, the polymorphic phase transition, and the electrical properties and their temperature stability. Excellent and tunable electrical properties of d ₃₃=242–400 pC/N, k _p=36%–54%,     , and T _c=230°–430°C demonstrate a tremendous potential of the compositions studied for device applications.     

The Li2O–Nb2O5–TiO2 Composite Microwave Dielectric Ceramics with Adjustable Permittivities

A group of new y M-phase/(1− y ) Li_{2+ x} Ti_{1−4 x} Nb_{3 x} O₃ composite ceramics with adjustable permittivities for low-temperature co-fired ceramic applications was initially investigated in the study. The 0.5 M-phase/0.5 Li_{2+ x} Ti_{1−4 x} Nb_{3 x} O₃ ( x =0.01, 0.02, 0.04, 0.06, 0.081) composite ceramics were first investigated to find the appropriate "Li₂TiO₃ss" composition ( x value). The best dielectric properties of ɛ_r=40.1, Q × f values up to 9318 GHz, τ_f=25 ppm/°C, were obtained for the ceramics composites at x =0.02. Based on the good dielectric properties, the suitable "Li₂TiO₃ss" composition with x =0.02 was mixed with the Li_1.0Nb_0.6Ti_0.5O₃ powder as the ratio of y "M-phase"/(1− y ) "Li₂TiO₃ss" ( y =0.2, 0.4, 0.5, 0.6, 0.8). By adjusting the y values, the group of composite ceramics could exhibit largely are adjustable permittivities varying from ∼20 to ∼60, while Q × f and τ_f values relatively good. Nevertheless, in this study, because there are interactions between the M-phase and Li₂TiO₃ss during sintering process, their microwave dielectric properties could not be predicted precisely by the empirical model.     

Microstructure and Electrical Properties of [(K0.50Na0.50)0.95−xLi0.05Agx](Nb0.95Ta0.05)O3 Lead-Free Ceramics

[(K_0.50Na_0.50)_{0.95− x} Li_0.05Ag _x ](Nb_0.95Ta_0.05)O₃ (KNLNANT- x ) lead-free piezoelectric ceramics were prepared by normal sintering. Effects of the Ag content on the microstructure and electrical properties of KNLNANT- x ceramics were systematically investigated. It is found that the ceramics with x =0.03 exhibit relatively good electrical properties along with high Curie temperature: ( d ₃₃∼252 pC/N, T _c∼438°C, k _p∼45.4%, P _r∼30.1 μC/cm², E _c∼13.8 kV/cm, ɛ_r∼1030, and tan δ∼2.6%). The related mechanism for enhanced electrical properties of the ceramics was also discussed. These results show that KNLNANT-0.03 ceramic is a promising candidate material for high temperature lead-free piezoelectric ceramics.     

Piezoelectric Properties of (1−x)(Na0.5K0.5)NbO3–xAgSbO3 Lead-Free Ceramics

(1− x )(Na_0.5K_0.5)NbO₃– x AgSbO₃ lead-free piezoelectric ceramics were prepared by normal sintering. The effects of the AgSbO₃ on the phase structure and piezoelectric properties of the ceramics were systematically studied. These results show that the AgSbO₃-modified (K_0.50Na_0.50)NbO₃ lead-free piezoelectric ceramics form stable solution with orthorhombic structure, and the Curie temperature and the polymorphic phase transition of the ceramics decreased with increasing AgSbO₃. The result shows that the piezoelectric properties of the ceramics strongly depend on the AgSbO₃. The ceramics with x =0.05 possess optimum properties ( d ₃₃=192 pC/N, k _p=43%, T _c=348°C, T _o−t =145°C, ɛ_r∼632, and tan δ∼3.5%). These results indicate that the ceramic is a promising candidate material for lead-free piezoelectric ceramics.     

Effects of La on Dielectric and Piezoelectric Properties of Pb1−xLa2x/3(Nb0.95Ti0.0625)2 O6 Ceramics

Ceramics with the chemical compositions of Pb_{1− x} La_{2 x /3}(Nb_0.95Ti_0.0625)₂O₆ (0≤ x ≤0.060) (PLTN) were prepared by the conventional solid-state reaction method. X-ray diffraction analysis indicated that Ti and La doping not only decreased the rhombohedral–tetragonal phase transformation temperature, but also stabilized the orthorhombic phase of PLTN ceramics. All ceramics sintered at 1190°–1250°C had shown the pure orthorhombic ferroelectric phase. La doping suppresses grain growth and inhibits the formation of pores and cracks, resulting in an increase in relative density up to 97%. The amount of La doping to PLTN ceramics obviously affect ceramics' piezoelectric constant ( d ₃₃) and dielectric loss (tanδ). The sample with x =0.015 possesses high Curie temperature ( T _c=560°C), low dielectric loss (tanδ=0.0054), and excellent piezoelectric constant ( d ₃₃=92 pC/N), presenting a high potential to be used in high-temperature applications as piezoelectric transducers.     

Microwave Dielectric Properties of CaTiO3-CaAl1/2Nb1/2O3 Ceramics Doped with Li3NbO4

The microwave dielectric properties of CaTi_{1− x} (Al_1/2Nb_1/2) _x O₃ solid solutions (0.3 ≤ x ≤ 0.7) have been investigated. The sintered samples had perovskite structures similar to CaTiO₃. The substitution of Ti⁴⁺ by Al³⁺/Nb⁵⁺ improved the quality factor Q of the sintered specimens. A small addition of Li₃NbO₄ (about 1 wt%) was found to be very effective for lowering sintering temperature of ceramics from 1450–1500° to 1300°C. The composition with x = 0.5 sintered at 1300°C for 5 h revealed excellent dielectric properties, namely, a dielectric constant (ɛ_r) of 48, a Q × f value of 32 100 GHz, and a temperature coefficient of the resonant frequency (τ_f) of −2 ppm/K. Li₃NbO₄ as a sintering additive had no harmful influence on τ_f of ceramics.     

A Novel Temperature-Compensated Microwave Dielectric (1−x)(Mg0.95Ni0.05)TiO3−xCa0.6La0.8/3TiO3 Ceramics System

The microstructure and microwave dielectric properties of a (1− x )(Mg_0.95Ni_0.05)TiO₃− x Ca_0.6La_0.8/3TiO₃ ceramics system have been investigated. The system was prepared using a conventional solid-state ceramic route. In order to produce a temperature-stable material, Ca_0.6La_0.8/3TiO₃ was added for a near-zero temperature coefficient (τ_f). With partial replacement of Mg²⁺ by Ni²⁺, the dielectric properties of the (1− x )(Mg_0.95Ni_0.05)TiO₃− x Ca_0.6La_0.8/3TiO₃ ceramics can be promoted. The microwave dielectric properties are strongly correlated with the sintering temperature and the composition. An excellent Q × f value of 118,000 GHz can be obtained for the system with x =0.9 at 1325°C. For practical application, a dielectric constant (ɛ_r) of 24.61, a Q × f value of 102,000 GHz, and a temperature coefficient of resonant frequency (τ_f) of −3.6 ppm/°C for 0.85(Mg_0.95Ni_0.05)TiO₃−0.15Ca_0.6La_0.8/3TiO₃ at 1325°C are proposed. A parallel-coupled line band-pass filter is designed and simulated using the proposed dielectric to study its performance.     

BiScO3 Doped (Na0.5K0.5)NbO3 Lead-Free Piezoelectric Ceramics

Lead-free potassium sodium niobate-based piezoelectric ceramics (1− x )(Na_0.5K_0.5)NbO₃– x BiScO₃ (KNN–BS) ( x =0∼0.05) have been prepared by an ordinary sintering process. Single perovskite phase of KNN–BS exhibits an orthorhombic symmetry at x <0.015 and pseudocubic symmetry at x >0.02, separating by a MPB at 0.015≤ x ≤0.02. Piezoelectric and ferroelectric properties are significantly enhanced in the MPB, which are as follows: piezoelectric constant d ₃₃=203 pC/N, planar coupling coefficient k _p=0.36, remnant polarization P _r=24.4 μC/cm². These solid solution ceramics look promising as a potential lead-free candidate materials.     

Effect of V2O5 Doping on the Sintering and Dielectric Properties of M-Phase Li1+x−yNb1−x−3yTix+4yO3 Ceramics

The effect of the addition of V₂O₅ on the structure, sintering and dielectric properties of M -phase (Li_{1+ x − y} Nb_{1− x −3 y} Ti _x +4 _y )O₃ ceramics has been investigated. Homogeneous substitution of V⁵⁺ for Nb⁵⁺ was obtained in LiNb_{0.6(1− x )}V_{0.6 x} Ti_0.5O₃ for x ≤ 0.02. The addition of V₂O₅ led to a large reduction in the sintering temperature and samples with x = 0.02 could be fully densified at 900°C. The substitution of vanadia had a relatively minor adverse effect on the microwave dielectric properties of the M -phase system and the x = 0.02 ceramics had [alt epsilon]_r= 66, Q × f = 3800 at 5.6 GHz, and τ_f= 11 ppm/°C. Preliminary investigations suggest that silver metallization does not diffuse into the V₂O₅-doped M -phase ceramics at 900°C, making these materials potential candidates for low-temperature cofired ceramic (LTCC) applications.     

Modification of MgAl2O4 Microwave Dielectric Ceramics by Zn Substitution

MgAl₂O₄ microwave dielectric ceramics were modified by Zn substitution for Mg, and their dielectric characteristics were evaluated, along with their structures. Dense (Mg_{1− x} Zn _x )Al₂O₄ ceramics were obtained by sintering at 1550°–1650°C in air for 3 h, and the (Mg_{1− x} Zn _x )Al₂O₄ solid solution was determined in the entire composition range. With Zn substitution for Mg, the dielectric constant ɛ of MgAl₂O₄ just varied from 7.90 to 8.56, while the Q × f value had significantly improved up to a maximal value of 106 000 GHz at x =1.0. Moreover, the τ_f of MgAl₂O₄ ceramics had declined from −73 to −63 ppm/°C.     

Sintering Behavior, Phase Evolution, and Microwave Dielectric Properties of Bi(Sb1−xTax)O4 Ceramics

Sintering behavior, phase evolution, and microwave dielectric properties of Bi(Sb_{1− x} Ta _x )O₄ ceramics (0.05≤ x ≤0.60) were studied and their relationships were discussed in detail. Phase studies revealed that a pure monoclinic phase could be formed when x ≤0.20 and a pure orthorhombic phase could be obtained when x ≥0.50. As the x value increased from 0.05 to 0.60, the densified temperature of Bi(Sb_{1− x} Ta _x )O₄ ceramics decreased from 1050° to about 960°C whereas the density increased from 8.07 to 8.41 g/cm³. The microwave dielectric constant increased from 20.5 to 34 whereas the Q × f value decreased from 60 000 to 29 000 GHz. In the monoclinic phase region, the temperature coefficients of resonant frequency shifted linearly from −58 to −45 ppm/°C as the x value increased from 0.05 to 0.2 and then remained constant at about −12 ppm/°C when x ≥0.40. The Bi(Sb_{1− x} Ta _x )O₄ ceramics are promising for application of low-temperature cofired ceramics technology.     

K/Na Ratio Dependence of the Electrical Properties of [(KxNa1−x)0.95Li0.05](Nb0.95Ta0.05)O3 Lead-Free Ceramics

[(K _x Na_{1− x} )_0.95Li_0.05](Nb_0.95Ta_0.05)O₃ (K _x NLNT) ( x= 0.40–0.60) lead-free piezoelectric ceramics were prepared by conventional solid-state sintering. The effects of K/Na ratio on the dielectric, piezoelectric, and ferroelectric properties of the K _x NLNT ceramics were studied. The experimental results show that the electrical properties strongly depend on the K/Na ratio in the K _x NLNT ceramics. The K _x NLNT ( x =0.42) ceramics exhibit enhanced properties ( d ₃₃∼242 pC/N, k _p∼45.7%, k _t∼47%, T _c∼432°C, T _o−t =48°C, ɛ_r∼1040, tanδ∼2.0%, P _r∼26.4 μC/cm², E _c∼10.3 kV/cm). Enhanced electrical properties of the K _x NLNT ( x =0.42) ceramics could be attributed to the polymorphic phase transition near room temperature. These results show that the K _x NLNT ( x =0.42) ceramic is a promising lead-free piezoelectric material.     

Effects of Ca/Ti Cosubstitution upon Microwave Dielectric Characteristics of CaSmAlO4 Ceramics

(Ca_{1+ x} Sm_{1− x} )(Al_{1− x} Ti _x )O₄ (0≤ x ≤0.4) ceramics were synthesized by solid-state reaction method and their microstructures and microwave dielectric properties were investigated. X-ray diffraction analysis and energy-dispersive X-ray analysis indicated that the matrix phase was a solid solution with a composition represented by the chemical formula (Ca_{1+ x} Sm_{1− x} ) (Al_{1− x} Ti _x )O₄ and minor amount of (Ca,Sm)(Al,Ti)O₃ secondary phase was detected. Ca/Ti cosubstitution could significantly improve the microwave dielectric characteristics of CaSmAlO₄ ceramics, and the excellent microwave dielectric characteristics were obtained in the modified ceramics as ɛ_r=19–23, Q × f =49 100–118 700 GHz, and τ_f=−15–15 ppm/°C.