Formation of LiNi0.5Co0.5VO4 nano-crystals by solvothermal reaction

LiNi_0.5Co_0.5VO₄ nano-crystals were solvothermally prepared using a mixture of LiOH·H₂O, Ni(NO₃)₂·6H₂O, Co(NO₃)₂·6H₂O and NH₄VO₃ in isopropanol at 150–200 °C followed by 300–600 °C calcination to form powders. TGA curves of the solvothermal products show weight losses due to evaporation and decomposition processes. The purified products seem to form at 500 °C and above. The products analyzed by XRD, selected area electron diffraction (SAED), energy dispersive X-ray (EDX) and atomic absorption spectrophotometer (AAS) correspond to LiNi_0.5Co_0.5VO₄. V–O stretching vibrations of VO₄ tetrahedrons analyzed using FTIR and Raman spectrometer are in the range of 620–900 cm⁻¹. A solvothermal reaction at 150 °C for 10 h followed by calcination at 600 °C for 6 h yields crystals with lattice parameter of 0.8252 ± 0.0008 nm. Transmission electron microscope (TEM) images clearly show that the solvothermal temperatures play a more important role in the size formation than the reaction times.     

Synthesis and electrochemical performance of LiNi0.5Mn1.5O4 spinel compound

Spinel compound LiNi_0.5Mn_1.5O₄ was synthesized by a chemical wet method. Mn(NO₃)₂, Ni(NO₃)₂·6H₂O, NH₄HCO₃ and LiOH·H₂O were used as the starting materials. At first, Mn(NO₃)₂ and Ni(NO₃)₂·6H₂O reacted with NH₄HCO₃ to produce a precursor, then the precursor reacted with LiOH·H₂O to synthesize product LiNi_0.5Mn_1.5O₄. The product showed a single spinel phase under appropriate calcination conditions, and exhibited a high voltage plateau at about 4.6-4.8 V in the charge/discharge process. The LiNi_0.5Mn_1.5O₄ had a discharge specific capacity of 118 mAh/g at about 4.6 V and 126 mAh/g in total in the first cycle at a discharge current density of 2 mA/cm². After 50 cycles, the total discharge capacity was above 118 mAh/g.     

Preparation of ZrO2/Gd2O3 composite ceramic materials by coprecipitation method

High burnup is a goal for further development of advanced nuclear power in the future. However, along with the increase of burnup, it becomes more diffidult to control reactor reactivity, which affects the operation safety of the nuclear reactor. Al₂O₃/B₄C burnable poison materials widely used in pressurized water reactor currently will not meet the requirements of burnable poison materials in high burnup nuclear power. Because of the better performance of ZrO₂/Gd₂O₃ burnable poison materials than that of Al₂O₃/B₄C, this paper studies the preparation of ZrO₂/Gd₂O₃ composite ceramic materials by the coprecipitation method. The experimental results show that at the sintering temperature of 1500–1650 °C, ZrO₂/Gd₂O₃ composite ceramic grains are small, compact and uniform with the generation of homogeneous solid solution. At 1600 °C, ZrO₂–10%Gd₂O₃ has the highest density and mechanical strength.     

Deposition behavior and characteristics of hydroxyapatite coatings on Al2O3, Ti,and Ti6Al4V formed by a chemical bath method

A simple chemical bath method was used to deposit hydroxyapatite (HA) coatings on Al₂O₃, Ti, and Ti6Al4V substrates at ambient pressure by heating to 65–95 °C in an aqueous solution prepared with Ca(NO₃)₂·4H₂O, KH₂PO₄, KOH, and EDTA. The deposition behavior, morphology, thickness, and phase of the coatings were investigated using scanning electron microscopy and X-ray diffractometry. The bonding strength of the coatings was measured using an epoxy resin method. The HA coatings deposited on the three kinds of substrates were fairly dense and uniform and exhibited good crystallinity without any additional heat treatment. A coating thickness of 1–1.8 μm was obtained for the samples coated once. By repeating the coating process three times, the thickness could be increased to 4.5 μm on the Al₂O₃ substrate. The bonding strength of these coatings was 18 MPa.     

Soft template synthesis of mesoporous Co3O4/RuO2·xH2O composites for electrochemical capacitors

Co₃O₄/RuO₂·xH₂O composites with various Ru content (molar content of Ru = 5%, 10%, 20%, 50%) were synthesized by one-step co-precipitation method. The precursors were prepared via adjusting pH of the mixed aqueous solutions of Co(NO₃)₂·6H₂O and RuCl₃·0.5H₂O by using Pluronic123 as a soft template. For the composite with molar ratio of Co:Ru = 1:1 annealed at 200 °C, Brunauer-Emmet-Teller (BET) results indicated that the composite showed mesoporous structure, and the specific surface area of the composite was as high as 107 m² g⁻¹. The electrochemical performances of these composites were measured in 1 M KOH electrolyte. Compared with the composite prepared without template, the composite with P123 exhibited a higher specific capacitance. When the molar content of Ru was rising, the specific capacitance of the composites increased significantly. It was also observed that the crystalline structures as well as the electrochemical activities were strongly dependent on the annealing temperature. A capacitance of 642 F/g was obtained for the composite (Co:Ru = 1:1) annealed at 150 °C. Meanwhile, the composites also exhibited good cycle stability. Besides, the morphologies and textural characteristic of the samples were also investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM).     

Single crystal nanobelts of V3O7·H2O: A lithium intercalation host with a large capacity

In this study, single crystal V₃O₇·H₂O nanobelts were successfully synthesized using a simple hydrothermal route, in which templates or catalysts were absent. The synthesized V₃O₇·H₂O nanobelts are highly crystalline and have lengths up to several tens of micrometers. The width and thickness of the nanobelts are found to be about 30-50 and 30 nm, respectively. A lithium battery using V₃O₇·H₂O nanobelts as the positive electrode exhibits a high initial discharge capacity of 409 mAh g⁻¹, corresponding to the formation of Li_xV₃O₇·H₂O (x = 4.32). Such a high degree of electrochemical performance is attributed to the intrinsic properties of the single-crystalline V₃O₇·H₂O nanobelts.     

Low temperature sintering and microwave dielectric properties of Ce2(WO4)3 ceramics

Ce₂(WO₄)₃ ceramics have been synthesized by the conventional solid-state ceramic route. Ce₂(WO₄)₃ ceramics sintered at 1000 °C exhibited ?_r = 12.4, Qxf = 10,500 GHz (at 4.8 GHz) and τ_f = −39 ppm/°C. The effects of B₂O₃, ZnO–B₂O₃, BaO–B₂O₃–SiO₂, ZnO–B₂O₃–SiO₂ and PbO–B₂O₃–SiO₂ glasses on the sintering temperature and microwave dielectric properties of Ce₂(WO₄)₃ were investigated. The Ce₂(WO₄)₃ + 0.2 wt% ZBS sintered at 900 °C/4 h has ?_r = 13.7, Qxf = 20,200 GHz and τ_f = −25 ppm/°C.     

Effects of HCl concentration on the growth and negative thermal expansion property of the ZrW2O8 nanorods

A kind of negative thermal expansion ZrW₂O₈ nanorods were synthesized using a hydrothermal method, followed with a post-annealing at 570 °C for 2 h. Effects of HCl concentration on the microstructure, morphology and negative thermal expansion property in resulting ZrW₂O₈ powders were investigated by X-ray diffraction (XRD) and transmission electron microscope (TEM). Results indicate that the formation of the precursor ZrW₂O₇(OH)₂(H₂O)₂ significantly depends on the HCl concentration, and the precursors ZrW₂O₇(OH)₂(H₂O)₂ can form in the 2-8 mol/L HCl solution. With increasing the concentration of the HCl solutions from 2 to 8 mol/L, the rod-like ZrW₂O₈ particles become more homogeneous, and the average dimension change from 10 μm × 0.5 μm to 700 nm × 50 nm. All the ZrW₂O₈ powders obtained in different conditions exhibit negative thermal expansion property, and the average negative thermal expansion coefficients from 15 °C to 600 °C decrease gradually with the increasing HCl concentration.     

RuO2·xH2O/NiO composites as electrodes for electrochemical capacitors: Effect of the RuO2 content and the thermal treatment on the specific capacitance

RuO₂·xH₂O/NiO composites having RuO₂ contents in the range 0-100 wt.% have been prepared by a co-precipitation method. Structural, microstructural and textural transformations after heating the as-prepared composites at 200 and 600 °C have been followed by X-ray diffraction, scanning electron microscopy (SEM) and nitrogen adsorption/desorption isotherms. At 200 °C the composites are made of micrometric particles in which nanometric crystallites of the two oxides are aggregated. The composites show microporosity (0.02-0.10 cm³/g), mesoporosity (0.07-0.12 cm³/g) and relatively high specific surface area (62-309 m²/g). At 600 °C the composites are fully dehydrated and RuO₂ has crystallized and segregated. Microporosity and mesoporosity as well as specific surface area are strongly decreased. Specific capacitance and specific surface area of the composites heated at 200 and 600 °C have been measured and discussed on the basis of the RuO₂ content. For comparison the specific capacitance and specific surface area of mixtures of NiO and RuO₂·xH₂O (or RuO₂) have been taken as references. The higher specific capacitance of the 200 °C-heated composites compared to the 600 °C-heated ones is due to the higher specific surface area of the former and the higher pseudocapacitance of RuO₂·xH₂O compared to RuO₂. The discussion reported in this work can be applied to other composites such as RuO₂·xH₂O/carbon and RuO₂·xH₂O/other oxides.     

Large-scale synthesis of WO3 nanoplates by a microwave-hydrothermal method

Tungsten oxide (WO₃) nanoplates were synthesized by a 270 W microwave-hydrothermal reaction of Na₂WO₄·2H₂O and citric acid (C₆H₈O₇·H₂O) in deionized water. X-ray diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), and selected area electron diffraction (SAED) were used to reveal the synthesis of WO₃ complete rectangular nanoplates in the solution of 0.2 g citric acid for 180 min, with O-W-O FTIR stretching modes at 819 and 741 cm⁻¹, and two prominent O-W-O Raman stretching modes at 804 and 713 cm⁻¹. The 2.71 eV indirect energy gap, and 430-460 nm blue emission wavelength range of WO₃ complete rectangular nanoplates were determined using UV-visible and photoluminescence (PL) spectrometers. The formation mechanism was also proposed according to the experimental results.     

V-doped In2O3 nanofibers for H2S detection at low temperature

Pristine and vanadium-doped In₂O₃ nanofibers were fabricated by electrospinning and their sensing properties to H₂S gas were studied. X-ray diffractometry (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to investigate the inner structure and the surface morphology. The H₂S-sensing performances were characterized at different temperatures ranging from 50 to 170 °C. The sensor based on 6 mol% V-doped In₂O₃ nanofibers exhibit the highest response, i.e. 13.9–50 ppm H₂S at the relatively low temperature of 90 °C. In addition, the fast response (15 s) and recovery (18 s) time, and good selectivity were observed.     

Sintering of glass-added BaZn1/3Nb2/3O3 ceramics

The complex perovskite oxide Ba(Zn_1/3Nb_2/3)O₃ (BZN) has been studied for its attractive dielectric properties which place this material interesting for applications as multilayer ceramics capacitors or hyperfrequency resonators. This material is sinterable at low temperature with combined glass phase–lithium salt additions, and exhibits, at 1 MHz very low dielectric losses combined with relatively high dielectric constant and a good stability of this later versus temperature. The 2 wt.% of ZnO–SiO₂–B₂O₃ glass phase and 1 wt.% of LiF-added BZN sample sintered at 900 °C exhibits a relative density higher than 95% and attractive dielectric properties: a dielectric constant ?_r of 39, low dielectrics losses (tan(δ) < 10⁻³) and a temperature coefficient of permittivity τ_? of 45 ppm/°C⁻¹. The 2 wt.% ZnO–SiO₂–B₂O₃ glass phase and 1 wt.% of B₂O₃-added BZN sintered at 930 °C exhibits also attractive dielectric properties (?_r = 38, tan(δ) < 10⁻³) and it is more interesting in terms of temperature coefficient of the permittivity (τ_? = −5 ppm/°C). Their good dielectric properties and their compatibility with Ag electrodes, make these ceramics suitable for L.T.C.C applications.     

Effect of CeO2 addition on densification and microstructure of Al2O3-YSZ composites

Alumina (Al₂O₃) and alumina-yttria stabilized zirconia (YSZ) composites containing 3 and 5 mass% ceria (CeO₂) were prepared by spark plasma sintering (SPS) at temperatures of 1350-1400 °C for 300 s under a pressure of 40 MPa. Densification, microstructure and mechanical properties of the Al₂O₃ based composites were investigated. Fully dense composites with a relative density of approximately 99% were obtained. The grain growth of alumina was inhibited significantly by the addition of 10 vol% zirconia, and formation of elongated CeAl₁₁O₁₈ grains was observed in the ceria containing composites sintered at 1400 °C. Al₂O₃-YSZ composites without CeO₂ had higher hardness than monolithic Al₂O₃ sintered body and the hardness of Al₂O₃-YSZ composites decreased from 20.3 GPa to 18.5 GPa when the content of ZrO₂ increased from 10 to 30 vol%. The fracture toughness of Al₂O₃ increased from 2.8 MPa m^1/2 to 5.6 MPa m^1/2 with the addition of 10 vol% YSZ, and further addition resulted in higher fracture toughness values. The highest value of fracture toughness, 6.2 MPa m^1/2, was achieved with the addition of 30 vol% YSZ.     

Microwave dielectric properties of SnO2-doped CaSiO3 ceramics

SnO₂-doped CaSiO₃ ceramics were successfully synthesized by a solid-state method. Effects of different SnO₂ additions on the sintering behavior, microstructure and dielectric properties of Ca(Sn_1−xSi_x)O₃ (x=0.5–1.0) ceramics have been investigated. SnO₂ improved the densification process and expanded the sintering temperature range effectively. Moreover, Sn⁴⁺ substituting for Si⁴⁺ sites leads to the emergence of Ca₃SnSi₂O₉ phase, which has a positive effect on the dielectric properties of CaO–SiO₂–SnO₂ materials, especially the Qf value. The Ca(Sn_0.1Si_0.9)O₃ ceramics sintered at 1375 °C possessed good microwave dielectric properties: ε_r =7.92, Qf =58,000 GHz and τ_f=−42 ppm/°C. The Ca(Sn_0.4Si_0.6)O₃ ceramics sintered at 1450 °C also exhibited good microwave dielectric properties of ε_r=9.27, Qf=63,000 GHz, and τ_f=−52 ppm/°C. Thus, they are promising candidate materials for millimeter-wave devices.     

Grass blade-like microparticle MnPO4·H2O prepared by a simple precipitation at room temperature

Grass blade-like microparticle MnPO₄·H₂O was synthesized by a simple precipitation at room temperature using a mixture of manganese sulphate monohydrate, phosphoric acid and water at pH = 7. The thermogravimetric study indicates that the synthesized compound is stable below 500 °C and its final decomposed product is Mn₂P₂O₇. The pure monoclinic phases of the synthesized MnPO₄·H₂O and its final decomposed product Mn₂P₂O₇ are verified by XRD data. FTIR spectra indicate the presences of the PO₄³⁻ ion and water molecules in the MnPO₄·H₂O structure and the P₂O₇⁴⁻ ion in the Mn₂P₂O₇ structure. The thermal stability, crystallite size, and grass blade-like microparticle of MnPO₄·H₂O in this work are different from previous reports, which may be caused by the starting reagents and reaction condition for the precipitation.     

Mechanochemical synthesis of MgTa2O6 ceramic

MgTa₂O₆ powders were prepared by mechanochemical synthesis from MgO and Ta₂O₅ in a planetary ball mill in air atmosphere using steel vial and steel balls. High-energy ball milling gave nearly single-phase MgTa₂O₆ after 8 h of milling time. Annealing of high-energy milled powder at various temperatures (700–1200 °C) indicated that high-energy milling speed up the formation and crystallization of MgTa₂O₆ from the amorphous mixture. The powder derived from 8 h of mechanical activation gave a particle size of around 28 nm. Although at low-annealing temperatures the grain size was almost the same as-milled powder, the grain size increased with annealing temperature reaching to around 1–2 μm after annealing at 1200 °C for 8 h.     

Synthesis and characterization of ZnxMg1 − xGa2O4:Co fabricated by low-temperature burning method

A series of Zn_xMg_1 − xGa₂O₄:Co²⁺ spinels (x = 0, 0.25, 0.5, 0.75, and 1.0) was successfully produced through low-temperature burning method by using Mg(NO₃)₂·4H₂O, Zn(NO₃)₂·6H₂O, Ga(NO₃)₃·6H₂O, CO(NH₂)₂, NH₄NO₃, and Co(NO₃)₂·6H₂O as raw materials. The product was characterized by X-ray diffraction, transmission electron microscopy, and photoluminescence spectroscopy. The product was not merely a simple mixture of MgGa₂O₄ and ZnGa₂O₄; rather, it formed a solid solution. The lattice constant of Zn_xMg_1 − xGa₂O₄:Co²⁺ (0 ≤ x ≤ 1.0) crystals has a good linear relationship with the doping density, x. The synthesized products have high crystallinities with neat arrays. Based on an analysis of the form and position of the emission spectrum, the strong emission peak around the visible region (670 nm) can be attributed to the energy level transition [⁴T₁(⁴P) → ⁴A₂(⁴F)] of Co²⁺ in the tetrahedron. The weak emission peak in the near-infrared region can be attributed to the energy level transition [⁴T₁(⁴P) → ⁴T₂(⁴F)] of Co²⁺ in the tetrahedron.     

Characterization of electrodeposited WO3 films and its application to electrochemical wastewater treatment

WO₃ films have been prepared on to IrO₂-coated Ti substrate by cathodic deposition, and as-deposited and annealed films have been characterized using XRD, TEM, Raman and FT-IR spectroscopy. The as-deposited film consists of nanocrystalline, orthorhombic WO₃·H₂O and this phase transforms to amorphous WO₃ by annealing at 250 °C and to monoclinic WO₃ by annealing at and above 350 °C. The as-deposited and annealed films have been used as anodes for electrochemical decomposition of phenol in aqueous solutions with and without chloride ions. The monoclinic WO₃ anodes prepared by annealing at 350 and 400 °C show relatively high electrochemical activity in the chloride-containing solution. In addition, the anodes possess high chemical and physical stabilities: very low dissolution rate of WO₃ during the electrolysis and good adhesion to the substrate. Thus, WO₃ anodes may be promising materials for anodic oxidation of bio-refractory organics in wastewater, although further improvement of electrochemical activity is needed for more effective decrease in total organic carbons in wastewater.     

Synthesis of LiFePO4/C by solid-liquid reaction milling method

LiFePO₄/C was synthesized by the method of solid-liquid reaction milling, using FeCl₃·6H₂O, Li₂CO₃ and (NH₄)₂HPO₄ and glucose, which was used as reductant (carbon source). The samples were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), TG-DTA analysis, infrared absorption carbon-sulfur analysis and electrochemical performance test. The sample synthesized at 680 °C for 8 h showed, at initial discharge, a capacity of 155.8, 153.2, 148.5, 132.7 mAh g^− 1 at 0.2 °C, 0.5 °C, 1 °C and 3 °C rate respectively. The sample also showed an excellent capacity retention as there was no significant capacity fade after 10 cycles.     

Thermal conductivity in mullite/ZrO2 composite coatings

Mullite-based multilayered structures have been suggested as promising environmental barrier coatings for Si₃N₄ and SiC ceramics. Mullite has been used as bottom layer because its thermal expansion coefficient closely matches those of the Si-based substrates, whereas Y–ZrO₂ has been tried as top layer due to its stability in combustion environments. In addition, mullite/ZrO₂ compositions may work as middle layers to reduce the thermal expansion coefficient mismatch between the ZrO₂ and mullite layers. Present work studies the thermal behaviour of a flame sprayed mullite/ZrO₂ (75/25, v/v) composite coating. The changes in crystallinity, microstructure and thermal conductivity of free-standing coatings heat treated at two different temperatures (1000 and 1300 °C) are comparatively discussed. The as-sprayed and 1000 °C treated coatings showed an almost constant thermal conductivity (K) of 1.5 W m⁻¹ K⁻¹. The K of the 1300 °C treated specimen increased up to twice due to the extensive mullite crystallization without any cracking.