Effect of Fe2O3 Loading Amount on Catalytic Properties of Monolithic Fe2O3/Ce0.67Zr0.33O2 -Al2O3 Catalyst for Methane Combustion

Ce0.67Zr0.33O2-Al2O3 solid solution was prepared by the co-precipitation method. Fe2O3-based catalysts supported on the solid solution were obtained by the impregnation method. The article revealed that the optimal loading amount of Fe2O3 on Ce0.67Zr0.33 O2-Al2O3 in our experimental condition for catalytic combustion of methane was 8% （ mass fraction）. The prepared catalysts were characterized by BET, TPR, XRD analyses, and their catalytic activity was investigated after being calcined at 873 K and after being aged in water gas at 1273 K. When the loading amount of Fe203 was 8% （ mass fraction）, the catalyst held the highest activity, and the best temperature speciality and thermal stability. The complete-conversion temperature of methane for fresh and aged sample was 788 and 838 K, respectively. The range between the light-off temperature and the complete-conversion temperature was only 15 K. The characterization results of XRD indicated that Fe2O3 was well dispersed on the Ce0.67Zr0.33O2-Al2O3 matrix. The results of BET and TPR were in good harmony with the catalytic activity results.     

Catalytic combustion of diesel soot over K2NiF4-type oxides La2-xKxCuO4

Nanostructure K2NiF4 type oxides La2-xKxCuO4 complex oxides were prepared using the Sol-Gel method, characterized by X-Ray Diffraction （XRD）, Fourier Transform Infrared （FT-IR）, and Scanning Electron Microscopy （SEM）. The catalytic activity for soot combustion was evaluated by the Temperature-Programmed Reaction （TPO） technique. The results demonstrated that the substitution quality of K^＋ for La^3＋ at the A-site would increase the catalytic activities of La2-xKxCuO4 for soot combustion greatly; the substitution quality affected the structure and catalytic activity obviously. The La1.8K0.2CuO4 complex oxides with tetrahedral structures had the best catalytic activity for soot combustion, and the ignition temperature of soot combustion was lowered from 490 to 320 ℃.     

Catalytic performance for methane combustion of supported Mn-Ce mixed oxides

A series of supported Mn-Ce mixed oxide catalysts were prepared by the impregnation method and used for the oxidation of methane. The catalysts were characterized by N2 adsorption （BET）, X-ray diffraction （XRD）, laser Raman spectrum （LRS）, and temperature programmed reduction （TPR） techniques. The XRD and LRS results confirmed the high dispersion of active components or formation of solid solution between manganese and cerium oxides in the bulk and on the surface of mixed oxide catalysts. The reducibility was remarkably promoted by the stronger synergistic interaction between the two oxides from H2-TPR measurements. As expected, all the experimental mixed oxide catalysts showed excellent activity for methane combustion at low temperature. Especially, for the catalyst with Mn-Ce ratio 3：7, methane conversion reached 92% at a temperature as low as 470 ℃.     

Partial oxidation of methane on Ni/CeO2-ZrO2/γ-Al2O3 prepared using different processes

The influences of CeO2-ZrO2 and γ-Al2O3 mixing methods on the catalytic activity and stability of partial oxidation of methane （POM） were investigated over Ni/Ce0.7Zr0.3O2-Al2O3 catalysts. The catalysts were characterized by XRD, TPR, H2-chemsorption, and TG-DTA. For fresh catalysts, the results showed that the salt precursor mixing catalyst （ATOM） presented better performance than the catalysts prepared by the precipitator mixing method （MOL） and the powder mechanically mixing method （MECH）. The result of XRD suggested that the interaction between CeO2-ZrO2 and Al2O3 in ATOM sample was stronger than the others, which led to more lattice defects and thereby better initial activity. Moreover, the MECH sample had the best stability and the least coke deposition in 24 h stability tests. The results of TPR and H2-chemsorption indicated that the intimate contact of Ni-Al in MECH sample enhanced the ability of resisting coke deposition and metal sintering.     

O2/N2与O2/CO2气氛下Fe2O3与K2CO3对无烟煤催化燃烧反应性的影响

利用综合热分析仪研究了O2/N2与O2/CO2气氛下Fe2O3与K2CO3对无烟煤催化燃烧反应性的影响。结果表明,在O2/CO2气氛下,Fe2O3与K2CO3均可以催化无烟煤粉的燃烧,但其催化作用要弱于O2/N2气氛,且在低氧气浓度的O2/CO2气氛下对Fe2O3与K2CO3的抑制作用大于高氧气浓度。氧气浓度为20%~80%时,K2CO3在O2/N2气氛下催化煤粉前期燃烧使燃烧由反应控制转变为扩散控制,Fe2O3则只在氧气浓度为20%时能改变煤粉前期燃烧的控制步骤;而Fe2O3与K2CO3在O2/CO2气氛下均只能在氧气浓度为20%时改变煤粉前期燃烧的控制步骤,由反应控制转变为扩散控制。     

Influence of Al_2O_3/CeZrAl composition on the catalytic behavior of Pd/Rh catalyst

Al2O3 and Ce-Zr mixed oxides are important components of the automobile three-way catalyst.Various contents modifying A12O3(GAL) was physically introduced into Ce-Zr-Al mixed oxides(CZA) to form series of GAL/CZA composition.The Pd/Rh catalyst samples were prepared by different GAL/CZA support loading Pd/Rh,then aged at 950 oC for 6 h.The catalytic behavior of different Pd/Rh catalyst samples was studied.Surface area,oxygen storage capacity(OSC) and H2 adsorption capacity(TPR) of fresh and aged samples were...     

Effect of Novel Supporter on Catalytic Combustion of Methane

A new catalyst support, Ce-Mg-O, was prepared in a novel way macromolecule surfactant modified method and was used as a catalyst support for low-temperature methane combustion. The results indicate that the new type of FeOx/Ce- Mg-O catalyst exhibits high activity in low-temperature methane combustion, such that the T90 at which 90% conversion of methane occurs can be obtained at 560 ℃. The structure of the catalyst and the effect of the supporter on catalytic activity were characterized by transmission electronic microscopy （TEM）, X-ray diffraction （XRD）, and temperature-programmed reduction （TPR）. The results indicate that the high catalytic activity of FeOx/Ce-Mg-O over methane combustion is strongly dependent on the particle size, typical crystal phase of the Ce-Mg-O, and the interaction of FeOx and Ce-Mg-O.     

Effect of different mixing ways in palladium/ceria-zirconia/alumina preparation on partial oxidation of methane

The effect of the mixing ways of Ce0.7Zr0.3O2-Al2O3 mixed oxides on the partial oxidations of methane （POM） was investigated over Pd/Ce0.7Zr0.3O2-Al2O3 catalysts, the mixing ways including salt precursor mixing （ATOM）, precipitator mixing （MOL）, and powder mechanically mixing （MECH）, respectively. The test results indicated that among the three samples, Pd/ATOM had the best catalytic activity while Pd/MOL had the best stability in the stability test. Both the activity sequences of the fresh and used samples were consistent with the order of Pd dispersion. According to the X-ray diffraction （XRD） and BET characterization, the interaction of Ce^4＋, Zr^4＋, and Al^3＋ in the ATOM mixed oxide was in favor of performing higher catalytic activity and thermal stability. The stability test indicated that Pd/MOL had the highest Pd dispersion and least coke formation on the active sites calculated by the Hz-chemisorption and TG results, which was considered to relate to its superior activity of POM to other catalysts.     

A rationale for the development of thermally stable nanostructured CeO2-ZrO2-containing mixed oxides

CeO2-ZeO2 solid solutions are extensively used as oxygen storage promoters in the current automotive three-way catalysts. High thermal stability of the textural properties is one of the most important requirements for practical application since temperatures up to 1273 K are easily experienced by these materials under real working conditions. In the present paper, we investigated how hydrothermal treatments applied to cakes of doped and undoped ZrO2-rich CeO2-ZrO2 precursors might improve the thermal stability of the final CeO2-ZrO2 solid solution. A rationale was developed that allowed to correlate the morphology of the hydrothermaUy treated cake with the thermal stability at 1273 K of the final product, which did not depend on the composition of the mixed oxides.     

Catalytic Performance of Ce／Zr Oxides Catalysts for Soot Combustion

Catalytic performances of a series Ce/Zr oxides(CexZr1-xO2 )for soot combustion were investigated. The catalytic activities for soot combustion were affected by both the Ce/Zr ratio and the oxygen storageinvestigated. Thecapability of Ce/Zr oxides. O2-TPD and TG-DTA results indicate that CexZr1-xO2 can release its lattice oxygen continuously and promote soot combustion even no oxygen occurs in the reaction atmosphere. Among these Ce/Zr oxides, Ce0.5Zr0.5O2 has the best catalytic activity, and the ignition temperature of soot combustion was about 410℃, which is close to the practical exhaust temperature of the diesel engine.     

CuO-CeO2/Al2O3/FeCrAl monolithic catalysts prepared by in situ combustion synthesis method for preferential oxidation of carbon monoxide

This work described in situ combustion synthesis method for depositing CuO-CeO2 on the FeCrAl honeycomb supports.The in-fluence of the solution concentration and the role of the additive were studied and analyzed by scanning electron microscopy (SEM),X-ray diffractometer (XRD),and temperature programmed reduction (TPR) techniques.The results showed that 200 g/L of the active solution was the most appropriate concentration for preparing the monolithic catalysts,and the additives of praseodymium and lanthanum...     

Preparation and Characterization of Cex Th1-xO2 Solid Solutions Prepared by Sol-Gel Method

Ceriumoxidehasbeenwidelystudiedinrecent yearsbecauseofitsusefulnessindifferentareasof chemistry.Incatalyticfield,forexample,CeO2has beenusedasanimportantcomponentofautomotive three waycatalystsforreducingtheexhaust.The mainroleofceriainthree waycatalystsi…     

Partial oxidation of methane on Ni/CeO2-ZrO2/γ-Al2O3 prepared using different processes

The influences of CeO2-ZrO2 and γ-Al2O3 mixing methods on the catalytic activity and stability of partial oxidation of methane (POM) were investigated over Ni/Ce0.7Zr0.3O2-Al2O3 catalysts. The catalysts were characterized by XRD, TPR, H2-chemsorption, and TG-DTA. For fresh catalysts, the results showed that the salt precursor mixing catalyst (ATOM) presented better performance than the catalysts prepared by the precipitator mixing method (MOL) and the powder mechanically mixing method (MECH). The result of XRD suggested that the interaction between CeO2-ZrO2 and Al2O3 in ATOM sample was stronger than the others, which led to more lattice defects and thereby better initial activity. Moreover, the MECH sample had the best stability and the least coke deposition in 24 h stability tests. The results of TPR and H2-chemsorption indicated that the intimate contact of Ni-Al in MECH sample enhanced the ability of resisting coke deposition and metal sintering.     

Catalytic Partial Oxidation of Methane over Ni/CeO2-ZrO2-Al2O3

Nickel catalysts supported on CeO2-ZrO2-CeO2,ZrO2-Al2O3 and Al2O3 were prepared and characterized by means of X-ray diffraction（XRD）,BET areas,H2 temperature-programmed reduction（H2-TPR）,and X-ray photoelectron spectroscopy（XPS）.Through the test of catalytic partial oxidation of methane（CPOM）,Ni/CeO2-ZrO2-Al2O3 displayed the highest activity,which resulted from its largest BET area and best NiO dispersion.Furthermore,Ni/CeO2-ZrO2-Al2O3 maintained a long-time stability in CPOM,which was attributed to its best coking resistance among all the prepared catalysts.     

Thermal Stability and Reductive Property of Cex Zr1-xO2 Solid Solution Doped Simultaneously by Fe, Mn or Fe, Cu

CeO2 findswideapplicationsinfuelcells ,andasapromoterinthree waycatalyst(TWC)forautomotiveexhaustcontrol.Thestabilityandoxygenstorageca pacityofCeO2 makeitanidealpromoterinTWCfo rmulations[1,2 ] .Ithasbeenreported[3 ] thatmicrostruc turalstabilityofCeO2 i…     

Promotional effect of CeO2 and Y2O3 on CuO/ZrO2 catalysts for methane combustion

Catalytic combustion of methane was conducted by using a Cu-based catalyst prepared by the plasma-assisted impregnation method. The properties of the catalysts were surveyed by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and temperature-programmed reduction (H2-TPR). The results showed that the activity of CuO/ZrO2 with the CeO2 and Y2O3 was obviously increased compared with the CuO/ZrO2 catalyst, which was examined in relation to the structure and surface characteristics and might be correlated with their surface oxygen species and redox properties. Among the investigated catalysts, the Ce-CuO/ZrO2 sample exhibited the highest activity for methane combustion.     

La-Hexaaluminate Catalyst Preparation and Its Performance for Methane Catalytic Combustion

The La-hexaaluminate catalysts with high performance ration method with the buffer solution of NH4HCO3 and NH4OH were synthesized by the modified controllable co-precipimixture as the precipitation agent. The physicochemical properties of catalysts were characterized by the means of BET, XRD, and TPR techniques. With methane catalytic combustion as the probe reaction, the catalytic performances were also tested on a fixed bed, continual flow system. The resuits show that it is a good method to obtain chemical homogeneous hexaaluminate materials by the buffer solution as the precipitation agent. The La-hexaaluminate can be formed at low temperatures ranging from 1050 to 1200 ℃. The cerium introduction plays a great role in the methane catalytic combustion on La-Mn hexaaluminate because of its high oxygen storage capacity property and the well synergic effect between Ce and Mn. However, the CeO2 appears in hexaaluminate through the XRD pattern, which reveals that Ce can not enter the crystal lattice position. Mn introduction improves the methane catalytic activity to a large extent due to its high redox property. When Mn atomic substitution amount for A1 is 2, the hexaaluminate shows the highest activity, and the catalyst possesses good H2 consumption and redox performance. Mn can easily occupy the hexaaluminate crystal position, which reveals that the Mn substitute La-hexaaluminate is a promising high temperature methane combustion catalyst with high activity and good stability.     

Preparation, Characterization of CuO／CeO2 and Cu／CeO2 Catalysts and Their Applications in Low-Temperature CO Oxidation

CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were examined by means of a microreactor-GC system, HRTEM, XRD, TPR and XPS techniques. The results show that CuO has not catalytic activity and the activity of CeO2 is quite low for CO oxidation. However, the catalytic activity of CuO/CeO2 and Cu/CeO2 catalysts increases significantly. Furthermore, the activity of CuO/CeO2 is higher than that of Cu/CeO2 catalysts.     

Performance of Pd/CeO2-ZrO2-Al2O3 catalyst for motorcycle

The Pd-only catalysts for motorcycle were prepared by impregnating CeO2-ZrO2-Al2O3 and CeO2-ZrO2+Al2O3 with PdCl2 aque-ous solution and characterized by X-ray diffraction (XRD), oxygen storage capacity (OSC) and H2-temperature-programmed reduction (H2-TPR) methods. The XRD result indicated that the CeO2-ZrO2-Al2O3 compound prepared by co-precipitation formed a single solid solu-tion and had good thermal stability, and Pd phase was not observed in all catalysts. The TPR results showed that the reduction temperature of Pd/CeO2-ZrO2-Al2O3 catalyst was lower than that of Pd/CeO2-ZrO2+Al2O3 catalyst whether they were fresh or aged catalysts. The Pd/CeO2-ZrO2-Al2O3 exhibited high three-way catalytic activity at low temperature, high thermal stability, and wide working window, sug-gesting a great potential for applications.     

Lanthanum Modified Ni/γ-Al2O3 Catalysts for Partial Oxidation of Methane

La modified Ni/γ-Al2O3 catalysts prepared by co-precipitation method using NaOH-Na2CO3 as a precipitator show high activity and selectivity for the partial oxidation of methane (POM). Meanwhile, the addition of La is beneficial for the formation of an active component and stability of support. We investigated some factors including calcining temperature, nickel content, and space velocity, which turned out to have a strong influence on catalytic activity and selectivity. By XRD and TPR, it is concluded that Ni0 reduced from amorphous NiAl2O4 is the major active component for POM.