共查询到20条相似文献,搜索用时 15 毫秒
1.
DIBK-TBP体系萃取分离锆铪的机理 总被引:5,自引:0,他引:5
为了解二异丁基甲酮(DIBK)-TBP体系萃取锆铪的化学行为,分别采用斜率法和饱和容量法研究DIBK和TBP在HSCN介质中协同萃取锆铪的性能及机理,结果表明:DIBK-TBP体系萃取分离锆铪时优先萃取铪,萃取反应机理为溶剂化机理,萃合物中Zr4+(Hf4+)、TBP、DIBK的摩尔比为1:1:1,其萃合物组成分别为Zr(SCN)4.TBP.DIBK和Hf(SCN)4.TBP.DIBK,并通过对负载有机相进行红外光谱分析进一步确定了萃合物可能的结构式;DIBK和TBP协同使用可以改善HSCN介质下锆铪的萃取分离效果。 相似文献
2.
3.
采用置氢TC21钛合金粉末模压成形+保护气氛烧结工艺,研究置氢TC21钛合金粉末模压成形-烧结合金的组织性能的变化规律.结果表明:置氢量0.22%(质量分数,下同)和0.39%的TC21粉末烧结体组织较细,致密化程度也较高,置氢量0.39%的TC21粉末烧结体退火后的抗压强度和屈服强度最高.随着置氢量的增加,置氢TC21钛合金粉末模压成形烧结体片层组织尺寸变薄、针状的组织变细,晶粒尺寸变小;置氢TC21钛合金粉末模压成形烧结体退火后组织较退火前发生了明显的均匀化和细化;烧结体真空退火后氢含量达到安全状态,其中,置氢量0.39%的TC21钛合金粉末烧结体致密效果较好、综合力学性能较高. 相似文献
4.
5.
6.
SHUWangen ZHOUZhongcheng LIXiong 《稀有金属(英文版)》2002,21(1):1-6
The research progress in trialkyl compounds of gallium and indium was discussed from two aspects, one was the chemical synthesis of the compounds and the other was the purification of them. There are three synthesis routes being reported in the first aspect, i.e. the route staring from pure metal, the route starting from the pure metal trihalides, and the electrochemical route. In the second aspect, the purifying methods of decomposition-distillation and zone refining were reviewed. 相似文献
7.
渗硼工艺研究与应用现状及发展 总被引:1,自引:0,他引:1
渗硼能够显著提高金属表面的性能,目前的研究方向主要是降低渗硼温度。多元复合渗硼改善渗层显微组织、显微硬度、脆性和耐磨性,以及渗硼共晶化使渗层与基体呈冶金结合,从而改善以往的渗硼层脆性大、容易剥落等问题。 相似文献
8.
9.
1 INTRODUCTIONDespitetheabundantdepositofbauxitesinChi na ,ofthosepredominantisthediasporictypewithhighalumina ,highsilicaandlowferricoxides .Thebauxitedeposit,withthemassratioofaluminatosil ica(A/S)between 4and 8,accountsfor 80 %ofallthebauxitedeposit.Thenatureofhighsilicacontentdeterminesthatthemainlyadoptedtechniquetopro ducealuminainChinashouldbeBayer sinteringcom binationprocessorevenpuresinteringprocess .Althoughadramaticadvancementinaluminaproductionhasbeenachievedandthetechnolo… 相似文献
10.
回顾了静压造型的发展历史,通过典型机型的介绍,对其优缺点进行了分析,指出目前静压造型机存在的主要问题,提出高生产率、柔性化、少人(无人)操控的高可靠性静压造型线是今后发展的方向。 相似文献
11.
采用化学成分分析、着色渗透探伤分析、电子探针分析、显微组织分析、力学性能及高温持久性能分析等方法,对大型合成氨一段炉竖琴管排运行1.0×105h的转化管进行综合分析和评估。结果表明:转化管化学成分符合技术要求,宏观组织正常,显微组织形态良好,内外表面轻微腐蚀;经高温持久性能在L-M曲线中拟合外推,该管的剩余寿命远大于2.2×104h;炉管虽使用1.0×105h满足了工艺要求,但壁厚太大,影响热效率,同时内径小,限制了触媒和流量;因此,为提高效率,建议在今后的设计中采用性能较好的材料ZG50Ni35Cr25NbM。 相似文献
12.
13.
目的 通过等比例添加石英与长石,提高低碳钢搪瓷涂层的摩擦磨损性能.方法 采用一次浸搪法在Q235低碳钢表面制备等比例添加石英与长石的搪瓷涂层.采用SEM、HSR-2M型高速往复摩擦试验机,研究了不同石英与长石添加量的搪瓷涂层的组织形貌及摩擦磨损性能.结果 未添加石英与长石的搪瓷涂层硬度高、韧性差,且大气孔对裂纹形核扩展阻力小,摩擦时气孔边缘易脆性断裂.随着石英与长石添加量的增加,致使烧结体系的熔点和黏度降低,气孔形核位点增多,促进熔体扩散和气体排出,表层韧性和塑性提高,且小尺寸气孔阻碍裂纹扩展,磨屑填充气孔形成转移膜,显著降低了涂层脆性断裂倾向,发生轻微磨粒磨损和粘着磨损.然而当长石添加量过多(6%)时,Na2O的断网作用明显,致使更多Si─O键断裂,降低小气孔对裂纹扩展的阻力,因而导致涂层的耐磨性变差.结论 等比例添加石英与长石可降低涂层气孔率、提高涂层韧性,进而提高涂层的摩擦磨损性能. 相似文献
14.
15.
16.
The oxidation of nickel by atomic oxygen at pressures from 6×10–3 to 0.33 Torr between 1050 and 1250 K has been investigated. In these ranges, the oxidation was found to follow the parabolic rate law, viz.k
p
= 1.14×10–5 exp(–13410/T)g2 cm–4sec–1 for films of greater than 1 m thickness and was pressure-independent. The activation enthalpy for the oxidation reaction was 27±3 kcal mole–1. Of a number of possible mechanisms and defect structures considered, it was shown that, based on reaction activation enthalpies, impurity effects, pressure independence, and magnitudes of the rates, the most likely was a saturated surface defect model for atomic oxidation. A possible model judged somewhat less likely was one having equilibrium concentrations of doubly ionized cationic defects rate-controlling in both atomic and molecular oxygen. From comparisons of the appropriate processes, the following enthalpy values were derived: H* (Ni diffusion in NiO) = 26.5 ± 8 kcal mole–1 and H
f
0
(doubly ionized cation vacancies in NiO from atomic oxygen) = – 2.1 ± 6.0 kcal mole–1. The recombination coefficient of atomic oxygen on oxidized nickel was determined to be 0.14 ± 0.06 in the temperature range 985 to 1100 K. 相似文献
17.
18.
Large grain, low-dislocation, high-quality single crystals of various Pb-salt compounds have been grownreproducibly by the Horizontal Unseeded Vapor Growth (HUVG) technique. The Tunable Diode Lasers withbetter performance have been made with such crystals. The annealing feature, dislocations and diffusion in thecrystals have also been investigated. 相似文献
19.
采用定量金相及化学分析方法研究了B,Sr联合处理对亚共晶Al-7Si合金凝固组织的影响.Al-7Si合金熔体经B,Sr联合处理时,Sr对合金的细化处理效果无明显影响.而B的出现减少了熔体中有效Sr含量,降低了合金的变质处理效果.在此基础上,结合冷却曲线模式识别技术研究了合金熔体状态与冷却曲线凝固段整体形状的关系.随着表征曲线相似程度的综合偏差值仃趋近于零,相应的变质级别差值及晶粒尺寸差值也同时向零收敛.冷却曲线凝固段的整体形状可以表征B,Sr联合处理后合金的熔体状态.通过建立基于大量实验结果累积的数据库,有望实现B,Sr联合处理Al-7Si合金细化变质效果的在线评测. 相似文献
20.
采用力学性能测试、X射线衍射物相分析、SEM背散射扫描和能谱分析、金相试验技术,研究了时效工艺对固溶-冷拉处理过程中,用Sn和Bi微合金化对无Pb易切削Al-Mg-Si合金棒材显微组织结构特征和力学性能的影响。结果表明,其最佳的时效热处理工艺为170℃×8h。单独添加Sn的合金的物相组成除了Al基体,还有低熔点Mg2Sn和AlMnSi相,而联合添加Sn,Bi的合金组织由Al基体,低熔点Mg3Bi2与少量Sn和Bi单质以及AlMnSi相组成。 相似文献