Radiation grafting of α,β,β-trifluoroethylenesulfonyl fluoride onto low-density polyethylene film by simultaneous irradiation method. I. Kinetic study of simultaneous-irradiation grafting

α,β,β-Trifluoroethylenesulfonyl fluoride (TFESF) was grafted onto polyethylene (PE) film by a simultaneous-irradiation method. The influences of the grafting conditions were analyzed kinetically. The dependencies of the grafting rate on the dose rates and monomer concentrations ranging from 10 to 75% were found to be of 1 and 0 order, respectively. The overall activation energy for the graft polymerization was 2.05 × 10⁴ J/mol. The grafting rate was found to be independent of the film thicknesses ranging from 25 to 100 μm.     

Radiation grafting of α,β,β-trifluorostyrene onto poly(ethylene-tetrafluoroethylene) film by preirradiation method. II. Properties of cation-exchange membrane obtained by sulfonation and hydrolysis of the grafted film

A Study was made on certain properties of the cation-exchange membranes obtained by the preirradiation grafting of α,β,β-trifluorostyrene (TFS) noto poly(ethylene-tetrafluoroethylene) (ETFE), followed by sulfonation and hydrolysis of the grafted film. Swelling, water uptake, electric conductivity, and transport number of the membranes were measured as a function of ino-exchange capacity. Thermal and chemical stability were also investigated. These properties were found to be mainly dependent on ion-exchange capacity. The stable membrane properties were established due to a homogeneous ion-exchange group distribution in the membrane, as confirmed by x-ray imcroscopy analysis of the membrane cross sections. In addition, the membranes showed good electrochemical, thermal, and chemical properties, and were found to be scceptable for practical use as cation-exchange membranes.     

Radiation grafting of α,β,β-trifluorostyrene onto poly(ethylene–tetrafluoroethylene) film by preirradiation method. III. Properties of anion-exchange membrane obtained by chloromethylation and quaternization of the grafted film

A study was made of certain properties of the anion-exchange membranes obtained by the preirradiation grafting of α,β,β-trifluorostyrene (TFS) onto poly(ethylene–tetrafluoroethylene) (ETFE), followed by chloromethylation and quaternization of the grafted film. Swelling, water uptake, electric conductivity, and transport number of the membranes were measured as a function of ion-exchange capacity. Thermal and chemical stability were also investigated. These properties were found to be mainly dependent on ion-exchange capacity. The stable membrane properties were established due to a homogeneous ion-exchange group distribution in the membrane, as confirmed by X-ray microscopy analysis of the membrane cross sections. In addition, the membranes showed good electrochemical, thermal, and chemical properties, and were found to be acceptable for practical use as anion-exchange membranes.     

Radiation-induced copolymerization of α,β,β-trifluoroacrylonitrile with α-olefin

Homopolymerization and copolymerization of α,β,β-trifluoroacrylonitrile (FAN) with γ-olefins were carried out in bulk by γ-ray irradiation at 25°C. FAN gives very small quantities of brown and greasy low molecular weight polymer. Cyano groups in FAN polymer were found to be readily hydrolyzed to acid amide groups in the atmosphere. FAN was found to copolymerize with ethylene, propylene, and isobutylene via a radical mechanism to form equimolar copolymers in a wide range of monomer compositions. The polymerization rate increases linearly with FAN fraction in the monomer mixture. These copolymers are also hydrolyzed in the atmosphere, and the hydrolysis proceeds with more difficulty for the copolymer with higher α-olefin. The reactivity ratios r₁ (FAN) and r₂ (α-olefin) were determined to be 0.01 and 0.12 for the FAN/ethylene copolymerization and 0.01 and 0.07 for the FAN/propylene copolymerization. These results confirm that an alternating copolymerization takes place in the FAN/α-olefin system.     

HPLC and 13C-NMR study of carboxymethyl-β-(1 → 6)-D-gluco-β-(1 → 3)-D-glucan derived from saccharomyces cerevisiae

Sodium salt of carboxymethyl-β-(1 → 6)-D-gluco-β-(1 → 3)-D-glucan (CMG-Na) was prepared from β-D-glucan isolated from baker's yeast (Saccharomyces cerevisiae). Three samples, Fractions I, II, and III, were further separated from the crude CMG-Na derivative. For the physicochemical characterization of the separated fractions, the methods of high-performance liquid chromatography (HPLC) in the size-exclusion mode and carbon?13 nuclear magnetic resonance (¹³C-NMR) spectroscopy were applied. The HPLC method revealed that the molecular weights, M_n, M_w, and M_z averages, of Fraction II were 9.71 × 10⁴, 2.27 × 10⁵, and 3.59 × 10⁵ Da, respectively, whereas those of Fraction III were 1.52 × 10⁴, 2.13 × 10⁴, and 3.57 × 10⁴ Da, respectively. The ¹³C-NMR spectra of Fraction II showed a ratio of 3 : 1 for β?(1 → 3) / β?(1 → 6), whereas for Fraction III, the content of β-(1 → 3) units was smaller. © 1993 John Wiley & Sons, Inc.     

One‐pot synthesis of a polysaccharide‐based graft copolymer with an efficient redox pair (Fe2+/BrO3−)

A graft copolymer based on a polysaccharide (sodium salt of carboxymethylcellulose) and a vinyl monomer (acrylamide) has been synthesized in a nitrogen atmosphere, and its reaction conditions have been optimized for a better yield with ferrous sulfate and potassium bromate as a redox initiator. The effects of ferrous ion, bromate ion, hydrogen ion, sodium carboxymethylcellulose, and acrylamide along with the reaction time and temperature have been studied through the determination of the grafting parameters: the grafting ratio, add‐on, conversion, efficiency, homopolymer, and rate of grafting. The maximum yield has been found to occur when the acrylamide concentration is 8.0 × 10^?2 mol/dm³, whereas the maximum conversion occurs at a minimum concentration of acrylamide, that is, at 3.0 × 10^?2 mol/dm³. The grafting parameters have been found to increase with an increasing concentration of the redox initiator (Fe²⁺, from 2.0 × 10^?3 to 10.0 × 10^?3 mol/dm³; BrO, from 2.2 × 10^?3 to 4.0 × 10^?3 mol/dm³). The maximum efficiency occurs with a reaction time of 210 min. The rate of grafting has been found to be maximum up to 60 min; after that, it decreases rapidly. In this article, it is shown that the hydrogen ion leads to a very clear decrease in the grafting parameters as its concentration increases from 2.1 × 10^?3 to 11.3 × 10^?3 mol/dm³. Grafted gum and ungrafted gum have been characterized with Fourier transform infrared spectroscopy and thermogravimetric analysis. A probable mechanism has been suggested for graft copolymerization. It has been observed that the graft copolymer is thermally more stable than the parent backbone. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Polymerization of α,β-unsaturated carbonyl monomers initiated by 9-borabicyclo [3.3.1] nonane

9-Borabicyclo[3.3.1]nonane (9-BBN) initiated the polymerization of α,β-unsaturated carbonyl monomers such as ethyl acrylate (EA) without an oxidant at low temperatures (to −90°C) under argon. Hydroquinone and 2,6-di-tert-butyl-p-cresol had little effect on the polymerization, indicating that the propagating chain end is not a free radical. The rate of polymerization was found to be proportional to [9-BBN]^1.0 and [EA]^1.5. Electron spin resonance measurements using 5,5-dimethyl-1-pyrroline-N-oxide as a spin trap showed the absence of any radical species under polymerization conditions. No copolymerization of EA with styrene occurred. On the basis of the results obtained, this polymerization was assumed to proceed via a non-radical mechanism.     

Graft copolymerization of 2‐acrylamido‐2‐methyl‐1‐propanesulphonic acid onto carboxymethylcellulose (sodium salt) using bromate/thiourea redox pair

Unreported graft copolymer of 2‐acrylamido‐2‐methyl‐1‐propanesulphonic acid (AMPS) with sodium carboxymethylcellulose (Na‐CMC) was synthesized and reaction conditions were optimized using a bromate/thiourea redox pair under an inert atmosphere at 40°C. Grafting ratio, add on, and conversion increase as the concentration of thiourea and [H⁺] increases up to 3.6 × 10^?3 and 0.6 × 10^?2 mol dm^?3, respectively, while on increasing the concentration of bromate ion and Na‐CMC, grafting ratio, add on, and conversion decrease. The samples of Na‐CMC and grafted Na‐CMC with AMPS were subjected to thermogravimetric analysis, with the objective of studying the effect of grafting of AMPS on the thermal stability of graft copolymer. The graft copolymer was found to be more thermally stable than pure Na‐CMC. Comparing the IR spectra of pure with grafted Na‐CMC confirm the evidence of grafting. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 100: 26–34, 2006     

The β‐δ‐Phase Transition and Thermal Expansion of Octahydro‐1,3,5,7‐Tetranitro‐1,3,5,7‐Tetrazocine

Phase behavior of octahydro‐1,3,5,7‐tetranitro‐1,3,5,7‐tetrazocine (HMX) is investigated by X‐ray powder diffraction (XRD). The XRD patterns at elevated temperature show that there is a co‐existing temperature range of β‐ and δ‐phase during the phase transition process. Additionally, mechanical forces can catalyze the conversion from δ‐ back to β‐phase. Based on the diffraction patterns of β‐ and δ‐phase at different temperatures, we calculate the coefficients of thermal expansion by Rietveld refinement. For β‐HMX, the linear coefficients of thermal expansion of a‐axis and b‐axis are about 1.37×10⁻⁵ and 1.25×10⁻⁴ °C⁻¹. A slight decrease in c‐axis with temperature is also observed, and the value is about −0.63×10⁻⁵ °C⁻¹. The volume coefficient of thermal expansion is about 1.60×10⁻⁴ °C⁻¹, with a 2.2% change from 30 to 170 °C. For δ‐HMX, the linear coefficients of thermal expansion of a‐axis and c‐axis are found to be 5.39×10⁻⁵ and 2.38×10⁻⁵ °C⁻¹, respectively. The volume coefficient of thermal expansion is about 1.33×10⁻⁴ °C⁻¹, with a 2.6% change from 30 to 230 °C. The results indicate that β‐HMX has a similar volume coefficient of thermal expansion compared with δ‐HMX, and there is about 10.5% expansion from β‐HMX at 30 °C to δ‐HMX at 230 °C, of which about 7% may be attributed to the reconstructive transition.     

Atom‐transfer radical polymerization of methyl methacrylate with α,α′‐dichloroxylene/CuCl/N,N,N′,N″,N″‐pentamethyldiethylenetriamine initiation system under microwave irradiation

The atom‐transfer radical polymerization (ATRP) of methyl methacrylate (MMA), using α,α′‐dichloroxylene as initiator and CuCl/N,N,N′,N″,N″‐pentamethyldiethylenetriamine as catalyst was successfully carried out under microwave irradiation (MI). The polymerization of MMA under MI showed linear first‐order rate plots, a linear increase of the number‐average molecular weight with conversion, and low polydispersities, which indicated that the ATRP of MMA was controlled. Using the same experimental conditions, the apparent rate constant (k) under MI (k = 7.6 × 10^?4 s^?1) was higher than that under conventional heating (k = 5.3 × 10^?5 s^?1). © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 92: 2189–2195, 2004     

Graft polymerization of acrylic acid onto polyethylene film by preirradiation method. I. Effects of preirradiation dose,monomer concentration,reaction temperature,and film thickness

Low-and high-density polyethylenes were irradiated by electron beams with dose of 2–50 Mrad and then immersed in aqueous solution of acrylic acid (monomer concentration from 30 to 100 wt %) for 10 min?5 h at a temperature of 25–40°C. The degree of grafting increases with time and levels off. High density polyethylene shows lower grafting rate and higher final % grafting in compared with low-density polyethylene. Both grafting rate and final % grafting increase with total dose of preirradiation, but show some saturation at high doses. The highest grafting rate was observed at 60 wt % of monomer concentration where the grafted polyethylene swells to the largest extent in the monomer mixture. Apparent activation energies for the grafting are 19.6 and 27.3 kcal/mol for low- and high-density polyethylenes, respectively, reflecting the proces of monomer diffusion in the film. Grafting rate decreases with increasing film thickness. Graft polymerization starts on the surface of the film and proceeds to the inner part with monomer diffusion through the grafted layer.     

Modification of dextran through the grafting of N‐vinyl‐2‐pyrrolidone and studies of physicochemical phenomena in terms of metal‐ion uptake,swelling capacity,and flocculation

The optimum conditions for grafting N‐vinyl‐2‐pyrrolidone onto dextran initiated by a peroxydiphosphate/thiourea redox system were determined through the variation of the concentrations of N‐vinyl‐2‐pyrrolidone, hydrogen ion, potassium peroxydiphosphate, thiourea, and dextran along with the time and temperature. The grafting ratio increased as the concentration of N‐vinyl‐2‐pyrrolidone increased and reached the maximum value at 24 × 10^?2 mol/dm³. Similarly, when the concentration of hydrogen ion increased, the grafting parameters increased from 3 × 10^?3 to 5 × 10^?3 mol/dm³ and attained the maximum value at 5 × 10^?3 mol/dm³. The grafting ratio, add‐on, and efficiency increased continuously with the concentration of peroxydiphosphate increasing from 0.8 × 10^?2 to 2.4 × 10^?2 mol/dm³. When the concentration of thiourea increased from 0.4 × 10^?2 to 2.0 × 10^?2 mol/dm³, the grafting ratio attained the maximum value at 1.2 × 10^?2 mol/dm³. The grafting parameters decreased continuously as the concentration of dextran increased from 0.6 to 1.4 g/dm³. An attempt was made to study some physicochemical properties in terms of metal‐ion sorption, swelling, and flocculation. Dextran‐g‐N‐vinyl‐2‐pyrrolidone was characterized with infrared spectroscopy and thermogravimetric analysis. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

A study toward the physicochemical properties of graft copolymer (partially carboxymethylated guar gum‐g‐N,N′‐dimethylacrylamide): Synthesis and characterization

Unreported graft copolymer of N,N′‐dimethylacrylamide (DMA) with partially carboxymethylated guar gum (CmgOH) has been synthesized and the reaction conditions have been optimized for affording maximum grafting using a potassium peroxymonosulphate (PMS)/thiourea (TU) redox initiators under nitrogen atmosphere. The study of graft copolymerization has been performed to observe maximum value of grafting parameters except percentage of homopolymer by varying the concentrations of DMA, PMS, and TU. The grafting parameters increase continuously on increasing the concentration of DMA from 8 × 10^?2 to 24 × 10^?2 mol dm^?3, PMS from 5 × 10^?3 to 21 × 10^?3 mol dm^?3, and TU from 1.6 × 10^?3 to 4.8 × 10^?3 mol dm^?3. The optimum temperature and time for grafting of DMA onto CmgOH were found to be 35°C and 120 min, respectively. The water‐swelling capacity of graft copolymer is investigated. Flocculation property for both coking and noncoking coals is studied for the treatment of coal mine waste water. The graft copolymer is characterized by Fourier transform infrared spectroscopy and thermogravimetric analysis. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Graft copolymerization of 2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid onto carboxymethylcellulose (sodium salt) by H2O2/Fe+2 redox pair

The effect of the reaction conditions on the grafting parameters during grafting of 2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid onto sodium carboxymethylcellulose using H₂O₂/Fe⁺² redox pair are studied at 30°C. The grafting ratio, add on, and conversion initially increase with the H₂O₂ concentration in the range of (10.0–15.0) × 10^?2 mol dm^?3. Thereafter, these parameters decrease with the H₂O₂ concentration. The grafting ratio, add on, and conversion increase when increasing the ferrous ion concentration from (0.5 to 4.0) × 10^?2 mol dm^?3 and decrease with a further increase in the concentration. It is observed that the grafting ratio and add on increase with the monomer concentration, whereas the conversion decrease. The hydrogen ions seem to be facilitating the grafting reaction up to a certain concentration and after this concentration seem to be retarding the process. The grafting ratio, add on, and conversion decrease with the sodium carboxymethylcellulose concentration. When increasing the time period from 60 to 90 min, the grafting parameters increase but decrease thereafter. Similarly, when increasing the temperature from 25 to 30°C, the grafting parameters increase and decrease thereafter. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 4819–4825, 2006     

Synthesis,characterization of poly‐2‐ (2‐hydroxybenzylideneamino)‐6‐phenyl‐4,5,6, 7‐tetrahydrobenzo[b]thiophene‐3‐carbonitrile: Investigation of antibacterial activity and optical properties

The oxidative polycondensation reaction conditions of 2‐(2‐hydroxybenzylideneamino)‐6‐phenyl‐4,5,6,7‐tetrahydrobenzo[b]thiophene‐3‐carbonitrile were examined. The magnitude of the reflectance of the polymer decreases sharply with increasing of wavelength up to 524 nm, then reflectance of the polymer increases slowly with increasing of wavelength. The refractive index values of the polymer vary from 1.474 to 2.350. The E_p and E_d values of the polymer were found to be 4.56 and 7.068 eV, respectively. Absorption coefficient K of the polymer is of the order 817.062–1434.77 m^?1. Angle values of incidence and refraction of the polymer vary from 57.36 to 66.95° and from 23.05 to 32.65°, respectively. The film‐phase thickness of the polymer increases with increasing photon energy. The thickness, d, of the polymer was of the order 439.3–4184.7 Å for 190 and 1100 nm, respectively. The real part of dielectric constant of the polymer decreases slowly with increasing of frequency up to about 600 THz, then the real part of dielectric constant of the polymer increases sharply with increasing of frequency. The real and imaginary parts of dielectric constant of the polymer vary from 2.17 to 5.52 and from 5.81 × 10^?5 to 3.58 × 10^?4, respectively. Finally, polymer was tested for antibacterial activities against some bacteria. POLYM. ENG. SCI., 2012. © 2012 Society of Plastics Engineers     

Behaviour of poly(β-hydroxybutyric acid) in dilute solution

The refractive indices of poly(β-hydroxybutyric acid) (PHB) at four wavelengths have been determined via different procedures. Viscometric and light scattering measurements have been made on solutions of eight samples of PHB (M_w = 20·9 × 10³?929 × 10³ g mol^?1) in 2,2,2-trifluoroethanol. From the dependences of intrinsic viscosity and of radius of gyration on molar mass, the conformation of PHB in dilute solution is shown to be that of a random coil. The findings are discussed in relation to existing conflicting evidence on the conformation of this polymer.     

Poly‐α,β‐(3‐hydroxypropyl)‐DL‐aspartamide: A new drug carrier

Poly‐α,β‐(3‐hydroxypropyl)‐DL ‐aspartamide (PHPA) was synthesized by the ring‐open reaction of polysuccinimide (PSI) and 3‐hydroxypropylamine. The polymer was characterized by ¹H‐NMR, ¹³C‐NMR, FTIR, and GPC. Mark–Houwink coefficients were obtained from viscometry and GPC measurements, K = 5.53 × 10⁻³ and α = 0.78 in water. The acute toxicity of PHPA was examined and it revealed no death in ICR mice up to the dose treated of 15.3 kg/kg, and hematological parameters showed no significant difference between treated and control animals. The potential use of PHPA as a drug carrier was also investigated. In a typical case, a contraceptive drug, norethindrone (NET), was bonded to PHPA, and the drug sustained released as long as 120 days an in vitro test. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 77: 2411–2417, 2000     

Radiation‐induced graft copolymerization of 2‐vinylpyridine and styrene onto isotactic polypropylene fiber

Isotactic polypropylene fiber (IPP) was graft‐copolymerized using 2‐vinyl pyridine (2‐VP) and styrene (sty) as the monomers by the mutual irradiation method in air. The percentage of grafting was determined as a function of various reaction parameters and it was found that the maximum grafting of 2‐VP (114%) and sty (76%) was obtained at an optimum dose of 1.08 × 10⁴ and 0.64 × 10⁴ Gy using 1.8 × 10⁻² mol of 2‐VP and 4.3 × 10⁻² mol of sty, respectively. The graft copolymers were characterized by differential scanning calorimetric analysis and isolation of the grafted chains from the grafted iPP samples. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 73: 2959–2969, 1999     

Effects of β-α transformation on the static and dynamic tensile behavior of isotactic polypropylene

It was demonstrated that the mechanical stress-induced βα-transformation in isotactic polypropylene (iPP) is associated with considerable toughness enhancement. This toughness improvement depends on the test conditions (loading frequency). The toughness of β-iPP was superior to the α-iPP by 13% under static (characterized by a load frequency of ca. 5 × 10⁻⁴ Hz) and 70% under dynamic (tensile impact with a loading frequency in the range of ca. 3 × 10²…10³ Hz) conditions, respectively. By applying the essential work of fracture (EWF) concept to single-edge notched tensile (SEN-T) specimens it was shown that for the toughness upgrading observed, energy dissipation in the enlarged plastic zone is responsible. The occurrence of the βα-transformation was evidenced by differential scanning calorimetry (DSC). Based on DSC measurements it was found that the degree of βα-trans-formation depends on the local strain. At high strain values the βα-conversion is complete (at elogation at break in uniaxial static tensile test), while this transformation is only partial at lower strains (at tensile impact). In addition, in the plastic (or deformation) zone the βα-conversion changed locally, and can be used for mapping of this region. © 1996 John Wiley & Sons, Inc.     

Studies of methyl methacrylate-methyl α-chloroacrylate,copolymers and poly(methyl α-chloroactylate) as electron sensitive positive resists

Poly(methyl α-chloroacrylate) (PMCA) and the copolymers of methyl methacrylate and methyl α-chloroacrylate (poly(MMA-co-MCA)) have been reported recently to be more susceptible to radiation degradation than poly(methyl methacrylate) (PMMA). In this paper we report our studies of PMCA and poly(MMA-co-MCA) as electron-sensitive positive resists. It has been found that both PMCA and the copolymers are more sensitive than PMMA. Using mixtures of dimethylformamide and 2-propanol as developers, the sensitivities of PMCA and poly(MMA-co-MCA) (38 mole percent MCA) have been found to be 1 × 10^?5 and 6 × 10^?6 coulomb/cm², respectively. It has also been found that crosslinking predominates in PMCA when the electron dose exceeds 6 × 10^?4 coulomb/cm².