硫化镍试金预富集-ICP-AES测定矿石中的Pt、Pd、Ir、Au

详细研究了硫化镍试金预富集－ICP－AES测定矿石中的Pt,Pd,Ir,Au的多种影响因素，结果表明硫化镍扣用盐酸溶解，多孔玻砂坩埚过滤溶液，盐酸和双氧水溶解残渣是比较理想的分析方案，硫化镍扣溶解过程中，Pt,Pd的损失可忽略。Au的损失相当高，仅能半定量，对于μg/g级的样品，Pt,Pd,Ir,Au的平均回收率在96－99％之间，相对标准偏差为1．7％－6．8％（n=5)，拟定的方法已用于矿石、精矿的分析。     

基于XRD的薄膜界面结合强度试验研究

利用X射线衍射技术（XRD）分析了薄膜结合界面应力及其变化规律，通过对薄膜界面结合状态的检测，建立了X衍射法测量薄膜界面结合强度的原理、方法与过程。其检测界面结合强度方法可对薄膜试样进行非接触检测，适用于晶体或多晶体薄膜的界面结合强度测量，是一种研究无损检测薄膜结合强度的试验新方法。     

Determination of the accuracy of phase analysis measurements on spherical surfaces through X-ray diffraction

This research analyzes the effect on measurement accuracy when taking X-ray diffraction (XRD) measurements on spherical rather than flat surfaces in the assessment of the proportion of retained austenite and martensite phases. By calculating the difference in X-ray absorption paths between a flat surface and spherical surface, this study demonstrates that only in spherical surfaces of small diameter (0.381 cm) will the difference in X-ray absorption path affect the accuracy of measurements derived from XRD. To improve the accuracy of such measurements, the research presents a model for quantifying the absorption path that X-rays follow when measuring spherical surfaces.     

Ti6Al4V零件铣削加工表面等效残余应力与作用深度的测量及其有限元分析

金属零件在切削加工后,其被加工表面会形成一残余应力层,其所引起零件的变形是影响精密弱刚性零件精度的重要的因素。为了预测Ti6Al4V零件因铣削加工表面残余应力而引起的变形,本文介绍一种测量表面等效残余应力及其作用深度的方法而达到此目的。通过对被加工面的对面进行两次腐蚀去除材料的操作使得零件的厚度和中性层的位置发生变化,测量此过程中零件挠度和表面应变的变化,进而计算得铣削加工引起的零件表面等效残余应力及其作用深度值。通过有限元分析验证该方法得到的结果,发现有限元计算得到的零件挠度和应变的变化与实际测量值非常吻合,因此可以断定该方法得到的结果是正确的,其可以正确评估铣削加工引起的表面残余应力性质和大小并能准确预测零件铣削加工后因表面残余应力而引起的工件的变形量,从而可以预测零件是否满足精度要求。     

PS 微球的制备及表面镀镍工艺研究

以聚乙烯吡咯烷酮为分散剂,偶氮二异丁腈为引发剂,无水乙醇为分散介质,通过分散聚合,制备出表面光滑、分散均匀的聚苯乙烯(PS)微球。在PS微球表面化学镀Ni,制得具有较好导电性能的PS/Ni复合粒子。研究了PS微球表面镀Ni前后的表观形貌及晶相变化,并分析了制备工艺对复合粒子导电性能的影响。分析表明,PS微球表面镀Ni的优化工艺为:PS/NiCl2·6H2O质量比4∶7,络合剂用量2 g,NH3·H2O用量30mL。     

Effect of varying blends of finished RO, surface and ground waters on solid lead surfaces

PbO, PbCO₃, and Pb₃(OH)₂(CO₃)₂ were identified as primary corrosion products on lead coupons following three months of exposure to finished RO, surface and ground water by XRD and XPS. Based on these results, a Pb₃(OH)₂(CO₃)₂ solid phase equilibrium model was used as a function of water quality, was modified using diffusion theory and accurately predicted lead release for a majority of field observations. SEM photographs revealed sulfate and chloride affected the surface structure of corrosion scales and lead release.     

金诺芬的晶体结构研究

用X射线粉末衍射方法 (XRD)对 3种不同熔点的金诺芬 (C2 0 H34AuO9PS)的晶体结构进行研究。结果表明 ,熔点为 1 1 2～ 1 1 4℃的金诺芬属于单斜晶系 ,晶胞参数是a =1 0 30 6nm ,b =0 82 30nm ,c =1 61 62nm ,β =1 0 5 31 6° ;熔点为 1 1 8～ 1 2 0℃的金诺芬属于六方晶系 ,晶胞参数是a =1 462 4 ( 4 )nm ,c =1 1 367( 3)nm ,β =1 2 0° ;熔点为 1 1 4～ 1 1 8℃的金诺芬是单斜晶系和六方晶系晶体组成的混合物。     

薄壁Ti6Al4V管件采用不同车削参数加工引起的表面残余应力的测量

切削加工引起的金属零件的表面残余应力,其性质和大小对零件的服役性能产生很重要的影响。在测量车削加工Ti6Al4V薄壁管件引起的表面残余过程中,由于边缘效应的存在,使得零件的长度对测量精度有严重的影响。由于管件的壁厚很薄,当去除一应力层时会对剩余部分的残余应力的重新分布产生重要的影响,因此必须对剥层后X射线法测得的应力值进行修正补偿才能得到其初始应力值。传统的修正方法其计算比较复杂,对零件和应力都有特别的要求,而且在某些情况下其修正精度还达不到要求。同时考虑测量精度、测量可行性以及节约材料诸多方面的问题,本文运用有限元验证的方法确定零件合适的长度。同时本文运用精度较高的基于有限元分析的修正方法结合X射线法测量Ti6Al4V管件车削加工引起的表面残余应力,分析不同切削参数以及退火处理对表面残余应力的影响。结果显示：切削速度、进给量以及切削深度在指定范围内增大时会导致表面切削和进给方向的压应力增大,退火处理会使得表面两个方向的残余应力减小将近85%。     

QT600球墨铸铁激光淬火相变层残余应力测试研究

利用CO2激光器对QT600球墨铸铁进行了激光淬火处理试验,用X-350A型X射线应力仪测定QT600激光淬火后的表面及其断面残余应力规律,分析了QT600激光淬火后的残余应力形成机理。试验结果表明,在CO2激光工艺参数为输出功率P=800-1200W、光斑直径=3.5-4.0mm、扫描速度V=6-8mm/s的条件下,QT600激光淬火后的残余应力均为压应力,其值在-250MPa以上。在QT600材料表面及断面上测定了Ψ=0°4、5°和90°方向上的残余应力,其值的变化范围小,表明淬火后材料组织结构比较均匀,无明显织构,有利于提高材料的使用寿命。