ASP工艺下Ti-IF钢微观织构演变规律研究

利用X射线衍射三维取向分布函数(ODF),对济钢"ASP+罩式退火工艺"下生产的Ti-IF钢的热轧、冷轧及退火、平整试样的织构演变规律进行研究。结果表明:济钢Ti-IF钢热轧板形成了较强的{111}面织构,在冷轧和退火后γ纤维织构强度显著增强;经罩式退火后,{111}110织构强度减弱,{111}112织构强度增强,V({111})/V({100})增大;经平整工序后高斯织构强度略有增强;随着碳含量的增加,Ti-IF钢在各生产工序的有利织构{111}减少,有害织构{100}增加,成形性能变差。     

精轧温度对超纯21%Cr铁素体不锈钢织构演变和成形性能的影响

研究了超纯21%Cr铁素体不锈钢精轧温度对织构演变规律和成形性能的影响。将粗轧板坯切块并在900~750℃范围内进行精轧,随后经相同的热轧退火、酸洗、冷轧及退火处理,系统研究了试样的宏观织构、显微织构和成形性能的变化规律。结果表明:精轧温度对铁素体不锈钢的织构演变有重要影响,降低热轧精轧温度有利于增加热轧退火板中{111}再结晶织构组分;冷轧及冷轧退火板的织构分布具有明显的遗传性,热轧板中较高的{111}再结晶织构组分,促进了冷轧退火板中{111}再结晶织构的生成,从而提高了铁素体不锈钢的成形性能。     

JSP-双机可逆冷轧条件下IF钢织构研究

针对济钢现场工艺条件下生产的Ti-IF钢,利用X’Pert ProxX射线衍射宏观织构分析方法,研究了中薄板坯热连轧轧制及随后的冷轧、退火工艺过程中织构的变化规律。IF钢冷硬板主要织构类型为{111}〈110〉、{111}〈112〉和{001}〈110〉,其中{111}〈110〉织构强度达到12;再结晶退火后的IF钢退火板,主要织构类型为{111}〈110〉和{111}〈112〉,{111}〈110〉织构强度提高到15.37。济钢生产的Ti-IF钢获得了对板材成形最有利的{111}//ND织构。     

低碳铝镇静汽车钢板有利织构{111}的形成及发展

本文对大工业生产的低碳铝镇静汽车钢板的有利织构{111}<110>的形成和发展作了初步的研究。研究表明:从热轧、冷轧、退火和平整一系列工序后的反极图有利织构因子 Rx 来看,{111}<110>有利织构逐渐由弱到强地发展,而不利织构{001}<100>逐渐减弱。而且这种有利织构的形成和发展又与AlN 颗粒的形成和沉淀直接有关。同时还证明了:平整工序对有利织构的发展也有重要贡献。     

CSP工艺0.04C钢热轧板冷轧-退火织构的演变

通过实验室4辊轧机和保护气氛管式退火炉，对0．04C钢CSP工艺生产的3姗热轧板进行冷轧（至0．8mm）和退火试验，并用蚀坑法对退火试样进行织构分析；同时对包钢薄板厂CSP3mm热轧板冷轧的1．2姗板卷退火试样进行了X-射线检测。结果表明，1．2mm SPCC冷轧板退火织构表层有较弱的{111}织构组分，中心层没有发现有利于提高钢的深冲性能的{111}织构。1．2mm板卷退火试样{111}／{100}取向密度比为2．0～3．0，与实验室蚀坑法的试验结果一致。     

冷轧压下率对IF钢织构的影响

采用CSP工艺生产厚度为3.5 mm的IF热轧钢板,分析了冷轧压下率对冷轧织构、退火织构、各组分含量、{111}/{100}比值的影响。结果表明,采用71.4%的冷轧压下率生产的IF钢{111}织构占比最大,最有利于冲压性能的提高。     

热轧板初始组织对冷轧无取向硅钢织构演变的影响

研究了27.5 mm热轧板的初始组织(热轧态,850℃退火、950℃退火)对冷轧态和870℃退火的0.5mm冷轧无取向硅钢50W600薄板(/%:0.004C、0.33Si、0.38Mn、0.099P、0.007S、0.32Al)织构演变的影响。结果表明,经冷轧后冷轧板织构中{100}〈011〉和{112}〈110〉织构密度明显增大,末退火热轧板轧成的冷轧板织构密度较退火热轧板轧成的冷轧板强;经未退火热轧板冷轧成的薄板再结晶退火后的织构中主要为{100}〈011〉、{110}〈011〉和{111}〈112〉,退火热轧板冷轧成的薄板再结晶退火后的织构除{100}〈011〉和{110}〈011〉外还有密度较强的高斯织构。     

无取向硅钢50W600组织和织构演变规律的研究

利用光学显微镜(OM)和X射线衍射仪(XRD)研究了铸坯、热轧板、冷轧板和退火板的组织和织构,采用磁性能测试仪测试磁性能。结果表明,通过使用电磁搅拌可使连铸坯中心等轴晶率达到44.5%,采用高温卷取工艺使热轧钢板表面组织发生完全再结晶,平均晶粒尺寸为28.5μm,热轧板中心位置组织由再结晶晶粒和长条带状组织交错组成,退火板平均晶粒尺寸为74.2μm。热轧板厚度方向织构分布不均匀,表层织构主要为黄铜织构和高斯织构,1/4层织构主要为{100}和{112}组分,中心织构主要为{100}和{110}组分,退火板织构主要由{111}面织构和较弱的{100}面织构组成。随机抽取成品样板采用爱泼斯坦方圈法测量磁性能,结果满足用户要求。     

退火工艺对DC04汽车板再结晶组织和织构的影响

以酒钢CSP工艺DC04冷轧汽车板为原料,通过实验室模拟退火工艺,采用OM、EBSD、ODF技术,研究退火工艺对其组织和织构特征的影响。结果表明,DC04汽车板退火组织为铁素体和少量渗碳体,575℃退火1h再结晶开始,730℃退火1h后再结晶较为充分,并随着退火时间的延长,铁素体晶粒长大。不同压下率的DC04冷轧板和退火板中,主要织构均为bcc金属中典型的α(<110>//RD)纤维织构和γ（<111>//ND）纤维织构。随着压下率增加,{111}<112>织构的取向密度明显大于{111}<110>织构的取向密度。730 ℃退火后,低压下率67%的退火板织构中有微弱的{001}<110>取向,但随着压下率增大,这种织构逐渐消失,而形成较强的{111}<112>、{111}<110>有利织构。增加变形量有利于获得有利的{111}织构而抑制不利{001}织构的生成,从而提高DC04的深冲性能。     

50W600正常晶粒长大过程中再结晶织构演化研究

运用EBSD技术研究了50W600无取向硅钢再结晶晶粒正常长大过程中织构的演化机理。结果表明:再结晶晶粒长大过程中织构演化源于不同织构组分长大速率不同;晶粒尺寸不是唯一决定某取向晶粒长大的因素;晶粒与其周围其它晶粒取向差角分布是影响该晶粒长大的重要参数;{111}<112>与{111}<110>取向晶粒长大过程中的相互竞争导致{111}面织构取向锋锐度交替变化;950℃退火时,随退火时间延长,{100}<120>织构、{100}<310>织构减弱,{110}<001>增强;恒定退火时间3.5 min,随退火温度升高,{110}<001>、{100}<120>、{100}<310>织构均增强;温度对不同取向晶粒取向差角分布有较大影响。     

Evolution of Through-Thickness Texture in Ultra Purified 17%Cr Ferritic Stainless Steels

 Texture inhomogeneity usually takes place in ferritic stainless steels due to the lack of phase transformation and recrystallization during hot strip rolling, which can deteriorate the formability of final sheets. In order to work out the way of weakening texture inhomogeneity, conventional hot rolling and warm rolling processes have been carried out with an ultra purified ferritic stainless steel. The results showed that the evolution of through-thickness texture is closely dependent on rolling process, especially for the texture in the center layer. For both conventional and warm rolling processes, shear texture components were formed in the surface layers after hot rolling and annealing; sharp α-fiber and weak γ-fiber with the major component at {111}<110> were developed in both cold rolled sheet surfaces, leading to the formation of inhomogeneous γ-fiber dominated by {111}<112> after recrystallization annealing. In the center layer of conventional rolled and annealed bands, strong α-fiber and weak γ-fiber textures were formed; the cold rolled textures were comprised of sharp α-fiber and weak γ-fiber with the major component at {111}<110>, and inhomogeneous γ-fiber dominated by {111}<112> was formed after recrystallization annealing. By contrast, in the centre layer of warm rolled bands, the texture was comprised of weak α-fiber and sharp γ-fiber, and γ-fiber became the only component after annealing. The cold rolled texture displayed a sharp γ-fiber with the major component at {111}<112> and the intensity of γ-fiber close to that of α-fiber, resulting in the formation of a nearly homogeneous γ-fiber recrystallization texture in the center layer of the final sheet.     

一次再结晶法取向硅钢超薄带的冷轧塑性变形行为北大核心CSCD

以市场上购买的取向硅钢成品板为原料,经不同压下率冷轧至0.23~0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量,利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征,分析了硅钢超薄带的塑性变形行为。结果发现,在平面压缩应力下,{112}<111>滑移系的取向因子较大。随冷轧压下率的增加,Goss织构的含量逐渐减少,{212}<141>织构组分的含量先增加后减少,{111}<112>织构组分的含量逐渐增加,织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶,其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。     

CSP制无取向硅钢热轧、常化、冷轧织构的演变

运用EBSD和X射线衍射技术,研究了模拟CSP流程生产无取向硅钢在热轧-常化-冷轧过程中织构的演变。热轧板沿板厚方向应力场和温度场的差异导致由表至中织构锋锐度增高,织构类型存在明显变化,表层主织构为B类纤维织构,次表层为A类纤维织构,中心层为旋转立方织构{001}<110>。常化过程削弱了这种差异性,但中心层仍保留了一定强度的立方织构{001}<100>。冷轧板表层及中心层的主织构均为{112}<110>、{111}<112>,表层织构锋锐度较中心层的强。分析表明热轧、常化、冷轧织构的演变与基体初始织构、组织密切相关。表层、次表层热轧板织构经常化演化成散漫、分布较均匀的织构,中心层主要织构由{001}<-1-10>绕RD逆时针旋转45°演化至{001}<0-10>。冷轧后织构演变为以{223}<110>为主的B类织构和以{111}<112>为主的A类织构。     

再结晶阶段加热速度对低碳冷轧板罩式退火过程组织和织构的影响

在实验室条件下模拟CSP热轧板为基板生产的低碳冷轧板罩式退火过程,研究再结晶阶段加热速度对冷轧板罩式退火过程组织和织构的影响。结果表明,压下率83.3%的冷轧板,随着再结晶阶段加热速度的增加,会使试样再结晶温度降低,再结晶过程提前完成,{001}110织构变强,{111}110织构先减少后增加,{111}112织构先减少后增加出现峰值,当加热速度超过50℃/h时又减小。在加热速度30~40℃/h间变形织构{112}110有较低的密度值。再结晶阶段加热速度40℃/h的退火工艺成品组织为饼形晶粒,{001}110织构密度较低,{111}110和{111}112密度较强,密度值接近。     

基于CSP工艺稀土冷轧板罩式退火中组织织构演变

 采用金相显微镜和X射线衍射仪对CSP(Compact Strip Production)稀土板热轧、冷轧及退火3个阶段的组织和织构进行了检测和分析,并结合文献讨论了稀土板组织织构的演变规律。结果表明：稀土冷轧板以{223}<110>、{001}<110>、{112}<110>为主要织构,退火后形成了以{223}<110>和{111}<110>为主的再结晶织构,织构密度均达8. 5以上,{223}<110>和{111}<110>取向差为10°。稀土板开始再结晶需要的温度较高,并且再结晶完成需要的时间较长。再结晶初期织构变化比后期小。试验稀土板退火后{111}/{001}值极大,{111}<011>织构与{111}<211>织构密度差约为6。     

取向硅钢板坯加热温度对热轧及冷轧板织构的影响

 采用取向分布函数及取向线分析方法对取向硅钢高温和低温板坯加热工艺的热轧及冷轧钢板织构进行了研究。结果表明：低温与高温板坯加热工艺的热轧板及冷轧板织构组分有明显不同。低温板坯加热热轧板中{100}<001>及{110}<110>织构较强,但经冷轧后{001}<110>织构最强。