热成形钢22MnB5的Q&P工艺

采用盐浴法对热成形钢22MnB5进行了Q&P工艺(quenching and partitioningprocess)处理,研究了淬火终点温度、分配温度和分配时间对试验钢的显微组织、力学性能和残余奥氏体含量的影响。结果表明:Q&P工艺处理22MnB5钢的显微组织主要为马氏体和残余奥氏体组织,同时有一定量的碳化物析出,随着淬火终点温度和分配温度的升高或分配时间的延长,马氏体和碳化物的微观形貌会发生变化;在淬火终点温度和分配温度为325℃,分配时间为60s时得到的试样强塑积最高,达到20435MPa.%;试样的拉伸断口都显示出良好的韧性断裂特征;XRD分析表明,在Q&P工艺处理后试验钢的残余奥氏体含量可达5.5%。     

一种多元低合金高碳钢的热处理组织及硬度的研究

对一种低合金高碳钢(0.81C,0.65Cr,0.89W,0.54Mo,0.23V)热处理组织及硬度研究表明,该钢退火具有多类型碳化物(M3C,M7C3,M23C6,M6C和MC),在800～840℃区间退火,处于γ相低温区原碳化物部分溶解和新碳化物重新形核生长过程,使碳化物颗粒超细化,平均尺寸0.33～0.34 μm.淬火时,因M3C、M23C6溶解于奥氏体的速度较快,在840～860℃淬火时,硬度可达HRC63～65;未溶碳化物M6C和MC(VC)有利于马氏体细化,但因其数量较少,淬火最高温度不易超过880℃.该钢在低温和中温回火有较好的抗回火性能,并能有效地促进残余奥氏体转变.该钢热处理过程组织结构特征能较好地以相平衡热力学计算结果进行解释.     

Q＆P钢塑性变形机制及组织-性能研究

研究淬火和碳再分配(Q&P)热处理工艺对低碳硅-锰系Q&P钢的显微组织及精细结构的影响,并和常规工艺实验进行对比.通过SEM,TEM分析,经Q&P工艺热处理后的钢板可获得板条马氏体和残余奥氏体两相组织,残余奥氏体呈膜状.利用XRD技术并结合软件编程的手段对残余奥氏体进行了定量分析.采用MTS万能拉伸机测定了其力学性能并进行了断口观察,拉伸试样纤维区为比较典型的韧窝状形貌,体现出良好的韧性断裂特征.结果表明:Q&P工艺处理后的钢板具有高的抗拉强度(1000MPa以上)和良好的塑性,残余奥氏体在组织中起到了相变诱发塑性的作用.     

奥氏体化温度对超强耐热齿轮轴承钢显微组织和强韧性的影响EI北大核心

新型超强耐热齿轮轴承钢具有优越的强韧性。通过改变钢的淬火加热温度,结合拉伸、冲击、断裂韧度等力学性能测试以及TEM,SEM,EDS等微观分析技术,研究不同奥氏体化温度下钢的显微组织与力学性能。结果表明:1060℃奥氏体化后,钢中存在未溶碳化物M_(6)C,冲击功和断裂韧度较低;1080~1100℃奥氏体化后,M_(6)C碳化物固溶,冲击功和断裂韧度显著增加。在1060~1100℃奥氏体化后,抗拉强度和塑性变化不大,规定塑性延伸强度随奥氏体化温度的增加略有降低。M_(6)C碳化物加速裂纹的萌生与扩展,导致韧性下降。在1080~1100℃奥氏体化后,超强耐热齿轮轴承钢可获得超高强度和高韧性,抗拉强度不小于2000 MPa,规定塑性延伸强度不小于1800 MPa,断裂韧度不小于100 MPa·m^(1/2)。     

原位研究M2高速钢微裂纹的萌生和扩展

使用扫描电子显微镜(SEM)内的原位加载台对M2高速钢进行了原位拉伸实验。结果表明：在M2高速钢的原位拉伸过程中,微裂纹主要在大尺寸共晶碳化物与基体的界面处萌生和扩展。与回火马氏体相比,裂纹更容易在残余奥氏体上萌生。碳化物的尺寸、形状和种类,对微裂纹的萌生和扩展也有重要的影响。减少块状残余奥氏体、一次共晶碳化物和MC碳化物的数量、减小碳化物的尺寸和改善碳化物形状,可减缓微裂纹的萌生和扩展。     

前驱体对含Cu低碳钢I&Q&P处理后组织性能的影响

采用IQP工艺和EPMA、SEM和XRD等手段,研究了3种前驱体对含Cu低碳钢残余奥氏体含量及力学性能的影响。结果表明,双相区保温初期试验钢奥氏体长大由C配分控制,后期由合金元素Mn、Cu配分控制;双相区保温奥氏体化后,双相区配分后形成弥散分布的局部高浓度Mn、Cu区域仍保留富集效果,在随后的淬火-碳配分阶段易于形成残余奥氏体。经IQP处理后,前驱体为P+F的钢室温组织中马氏体板条较粗,原始奥氏体晶界并不明显;前驱体为F+M钢得到的马氏体板条有序细密;前驱体为M的钢室温组织中马氏体板条更加细密。其中,前驱体组织为M的钢中残余奥氏体量最高,延伸率为24.1%,强塑积可达25 338 MPa·%,综合性能最好。     

600 MPa级相变诱导塑性钢的动态力学性能

目的研究相变诱导塑性钢不同应变速率下的力学性能,尤其是动态力学性能。方法对600 MPa级相变诱导塑性钢进行了准静态至动态6种不同应变速率下的力学性能测试,并对各试样断口处残余奥氏体含量进行了测试比对。0.001~0.01 s~(-1)准静态测试在ZWICK Z050万能试验机上完成,0.1,1,10,100 s~(-1)动态测试在ZWICK HTM5020液压伺服高速拉伸试验机上完成。结果力学测试结果表明,TRIP600具有明显的应变速率效应。在较高速率下,随应变速率的升高材料屈服强度、抗拉强度及伸长率都有一定程度的提高。结论断口处残余奥氏体含量在较高速率下无明显差别,表明较动态条件下应变速率对残余奥氏体转变影响不明显。     

回火温度对0Cr16Ni5Mo马氏体不锈钢组织和性能的影响

通过光学显微镜(OM)、扫描电镜(SEM)、X射线衍射分析(XRD)和力学性能测试,研究了回火温度对0Cr16Ni5Mo马氏体不锈钢组织和性能的影响。结果表明,试验钢在450—700℃温度区间回火处理后的组织均为回火马氏体+残余奥氏体+δ-铁素体,随着回火温度的升高,韧化相残余奥氏体含量先增加后降低,在600℃其含量达到最大值29.8%。其强度则随着回火温度的升高先降低然后回升,在600℃回火后强度最低,而伸长率变化趋势与强度相反;不同温度回火后的冲击断口均呈韧窝状,撕裂棱清晰可见,断裂方式均为韧性断裂。     

回火温度对两相区退火海工钢组织和性能的影响

对690 MPa级海工钢进行“淬火+两相区退火+回火”三步热处理,研究了回火温度对其组织和性能的影响、分析了力学性能变化与组织演变和残余奥氏体体积分数之间的关系。结果表明：回火后实验钢的显微组织为回火贝氏体/马氏体、临界铁素体和残余奥氏体的混合组织。随着回火温度的提高贝氏体/马氏体和临界铁素体逐渐分解成小尺寸晶粒,而残余奥氏体的体积分数逐渐增加;屈服强度由787 MPa降低到716 MPa,塑性和低温韧性明显增强,断后伸长率由20.30%增至29.24%,-40℃下的冲击功由77 J提升至150 J。残余奥氏体体积分数的增加引起裂纹扩展功增大,是低温韧性提高的主要原因。贝氏体/马氏体的分解和残余奥氏体的生成,引起组织细化、晶粒内低KAM值位错的比例逐渐提高和小角度晶界峰值的频率增大,使材料的塑性和韧性显著提高。     

轧辊用高速钢中碳化物研究

本文利用扫描电镜、能谱分析对三种轧辊用高速钢的组织中碳化物进行了研究,并分析了VC形态与高速钢化学成分之间的关系。结果表明：轧辊用高速钢组织包括马氏体基体,残余奥氏体和各种类型碳化物,如粒状或小块状的MC型碳化物,网状的M7G型碳化物,鱼骨状的M6C型碳化物以及其他复合型碳化物,各种碳化物含有的合金元素以及显微硬度不同;在研究范围内（Weq≤10）,晶粒尺寸是随钨当量的升高而变小;根据V含量不同,VC会出现不同形貌进而影响高速钢性能。     

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

From Industry 4.0 to Research 4.0. Development of High Performance Fibers in the Light of Digitization

We associate a variety of innovations with the term ＂Industry 4.0＂. The pioneer of many 4.0 modifications forms the basisfor the trend towards the integrated di...     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Refrigerators Enter a New Era of Health Preservation Frestech initiates the establishment of China's first standard for household sterilization refrigerators

On November 30, 2007, the China Association for Standardization (CAS) held a press conference at Beijing Diaoyutai State Guest House. Leaders from the China Household Electric Appliance Research Institute, the China Household Electric Appliance Association, and the China Consumers' Association attended and made speeches.……     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

Roman iron and steel: A review

ABSTRACT

The production of ferrous metal increased during the Roman Late Republican period, Principate and Empire. The direct bloomery process was used to extract the metal from its ores using slag-tapping and slag-pit furnaces. The fuel was charcoal and an air blast was introduced by bellows-operated tuyères. Iron formed as a bloom, often as a spongy mass of metal, which contained impurities from the smelting process, including unreacted ore, fuel, slag and fragments from the furnace walls, while the metal was often inhomogeneous with varied carbon contents. Blooms were either smithed directly into bars or ingots or they were broken up, which also allowed the removal of gross impurities and a selection of pieces with similar properties to be made. These could then be forge-welded together and formed into characteristically shaped ingots. Making steel in the furnace seems to have been achieved: it depended on the ore and the furnace and conditions within it. Surface carburization was also carried out. Iron and steel were used extensively in construction and for tools and weapons. Fire welding was often used to add pieces of steel to make the edges of tools and weapons, which could be heat-treated by quenching to harden them.     

A study of centrifugal cast high boron high speed steel

In the present study a high‐boron high speed steel (HSS) roll material was designed. Many expensive alloy elements have been substituted by cheap boron alloy, and high‐boron high speed steel roll has been manufactured by centrifugal casting method. The microstructures, mechanical properties and wear resistance of centrifugal casting high‐boron high speed steel roll have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and X‐ray diffraction (XRD) analysis, hardness test, impact test and wear test. The results indicated that the solidification microstructures of high‐boron high speed steel roll consisted of M₂(B,C), (W,Mo)₂(B,C), M₃(B,C), M₂₃(B,C)₆ type borocarbides and martensite, a small amount of retained austenite. Borocarbides were continuously distributed over the grain boundary. After quenching from 1050 °C, local broken network appeared in partial borocarbides, and fine secondary borocarbide precipitated from the matrix. After tempering from 525 °C, the amount of precipitated borocarbide increased significantly. After heat treatment, the hardness of high‐boron high speed steel roll excelled 60 HRC, and its impact toughness excelled 8.0 J/cm². The single groove steel rolling amount of high‐boron high speed steel rolls increases by 500% than that of bainite cast iron roll, when the rolls are used in K₁ mill housing of bar mill.     

Thixotropy of Systems with Shear Thinning and Plastic Flow Behavior

The definition of the thixotropy is a decrease in viscosity with time in shear and a subsequent recovery of viscosity after the shear deformation is removed.We ...