Microstructure and thermal stability behavior of a rapidly solidified Al—Ti—Fe—Cr alloy

A rapidly solidified Al-2.5Ti-2.5Fe-2.5Cr(mass fraction in%) alloy was prepared by melt spinning.Asquenched and as-annealed microstructures were studied by X-ray diffractometry(XRD),transmission electron microseopy(TEM),high-resolution transmission electron microscopy(HREM) and energy dispersive spersive spectrum(EDS) analysis,The microhardness of the alloy at different annealing temperatures was measured.The results obtained indicate that the microhardness of the rapidly solidified Al-2.5Ti-2.5Fe-2.5Cr alloy does not vary with differnet annealing temperatures.The as-quenched microstructure of the alloy includes two kinds of dispersed primary phases:Al3Ti and Al13(Cr,Fe)2,After annealing at 400℃ for 10h,the stable phase Al13Fe4 appears in the microstructure.     

退火处理对Al3CoCrCu1/2FeMoNiTi高熵合金激光涂层组织和性能的影响

目的研究Al_3CoCrCu_(1/2)FeMoNiTi高熵合金涂层的退火时效硬化及其强化机理。方法使用激光熔覆设备,在40Cr钢上制备了Al_3CoCrCu_(1/2)FeMoNiTi高熵合金涂层,对涂层进行了退火处理。使用X射线衍射仪、扫描电子显微镜和显微硬度计对涂层进行了分析。结果涂覆态涂层为BCC单相结构,经300℃和500℃退火,涂层仍然为BCC单相;700℃退火后,涂层析出了NiTi金属间化合物相;900℃退火后,涂层由FCC相及NiTi金属间化合物组成。涂覆态和经300~700℃退火的涂层为胞粒状,经900℃退火后,涂层为板条状。经300℃退火,涂层硬度下降,但超过300℃退火,硬度比涂覆态的高。700℃退火合金硬度达到最大值924HV。退火温度升到900℃后,硬度比700℃退火的低。NiTi析出相促进了硬度提高,位错强化机制能较好解释该高熵合金的固溶强化现象。结论Al_3CoCrCu_(1/2)FeMoNiTi合金涂层具有明显的时效硬化效应,700℃退火可获得最佳的时效硬化效果。     

退火工艺对3003铝合金板微观组织与力学性能的影响

研究了退火工艺对3003铝合金板微观组织与力学性能的影响。试验结果表明,3003铝合金板退火后第二相粒子主要为Al₆(Mn, Fe)、Al₆Mn以及在位错或者亚晶界等缺陷处形成的α-Al(Fe, Mn)Si相。随退火温度升高和保温时间延长,第二相粒子发生粗化,并出现了少量的弥散第二相。当退火温度为450 ℃时,第二相又重新固溶到基体。随退火温度升高,3003铝合金板硬度稳定在31.0 HV0.5 左右,抗拉强度整体上呈下降趋势,伸长率呈增加趋势。     

热处理对快速凝固ZK60镁合金薄带组织和硬度的影响

采用单辊甩带法制备了ZK60镁合金薄带,研究了不同条件热处理薄带的组织和显微硬度。结果表明,薄带由晶粒尺寸8μm的等轴α-Mg、球状β′2相和少量杆状β′1相组成;热处理温度300℃时,晶粒无长大;温度300℃时,晶粒显著长大。原始薄带显微硬度约为50HV,300℃×2h热处理后显微硬度值最大约为80HV;β′1和β′2相的弥散强化作用是薄带硬度提高的内在原因。     

RECRYSTALLIZATION OF SWAGED W-Ni-Fe HEAVY ALLOY DURING ANNEALING TREATMENT

ＲＥＣＲＹＳＴＡＬＬＩＺＡＴＩＯＮＯＦＳＷＡＧＥＤＷ－Ｎｉ－ＦｅＨＥＡＶＹＡＬＬＯＹＤＵＲＩＮＧＡＮＮＥＡＬＩＮＧＴＲＥＡＴＭＥＮＴ￥Ｚ．Ｌｉ;Ｙ．Ｌ．Ｙａｎｄ;Ｊ．ＫＸｉ;Ｊ．Ｘ．ＱｕａｎｄＨ．Ｓ．Ｓｈａｏ（ＤｅｐａｒｔｍｅｎｔｏｆＭａｔｅｒｉａｌ...     

铝含量和退火温度对锆铝合金相组成和力学性能的影响

利用非自耗电弧炉熔炼了Al含量为6.0%,7.0%,8.0%(质量分数)的锆铝二元合金,通过退火过程中的包析反应得到了不同相组成的Zr3Al基合金,借助光学显微镜、XRD分析研究了合金的金相组织和相组成,进行了显微硬度测定和拉伸试验。结果表明:铸态的锆铝合金显微硬度随着铝含量的增加而增大;退火可得到组织均匀的Zr3Al基合金,其显微硬度和抗拉强度主要与相组成和基体晶粒大小有关,而与第二相的形态无关;合金的显微硬度、抗拉强度随着Zr3Al相的增多而增大,延伸率随着Zr3Al相的增多而减小;合金的显微硬度、抗拉强度和延伸率随着Zr3Al晶粒的细化而不同程度地增大。     

Al-Cu-Ce合金的微观组织与力学性能

采用X射线衍射、金相显微镜、扫描电镜、能谱分析及拉伸性能测试等方法,研究3种成分Al-Cu-Ce合金的显微组织与力学性能。结果表明:铸态Al-14Cu-7Ce合金由α-Al+Al8CeCu4片状共晶组成,而Al-10Cu-5Ce、Al-18Cu-9Ce合金中除含有α-Al+Al8CeCu4共晶组织外,还分别含有α-Al和Al8CeCu4初生相。铸态Al-14Cu-7Ce合金具有优良耐热性能,即使550℃×3 h退火后仍能保持约360 MPa的抗拉强度,退火导致合金强度下降的主要原因是高温下共晶Al8CeCu4相的球化。经充分球化退火后,Al-Cu-Ce合金能获得良好的热轧、冷轧变形能力,并且变形态合金也具有良好的耐热性能,因而Al-Cu-Ce合金有望成为一种兼具铸造和变形两用的新型耐热铝合金。     

退火对AlCoCrFeMnTi高熵合金相组成与显微形貌的影响

为了研究退火温度对AlCoCrFeMnTi高熵合金的物相结构、显微组织及硬度的影响,分别采用X射线衍射仪、光学显微镜、扫描电镜和显微硬度计对不同退火温度下AlCoCrFeMnTi合金进行了测试。结果表明:铸态AlCoCrFeMnTi高熵合金物相结构是由bcc主相和fcc相双相组成,且其各相衍射峰普遍较宽,这是由于原子半径差较大和冷却速度快引起的晶格畸变所致。600 ℃退火后,合金中形成了新的hcp相,当退火温度为800 ℃和1000 ℃时,合金衍射峰的峰形并未再发生显著变化。铸态和退火后的AlCoCrFeMnTi合金均为典型的树枝晶结构,1000 ℃退火后的扫描电镜照片中发现了典型的调幅分解组织。合金硬度值在铸态最大,达到了750 HV0.5,随着退火温度升高硬度逐步降低。在经过1000 ℃退火后,一方面由于合金中出现调幅分解组织,使得过饱和的原子大量析出,降低了晶格畸变程度,导致硬度下降;另一方面,由于退火温度的升高,加速了原子的扩散能力,降低了合金内部的内应力,此时合金硬度下降到604.9 HV0.5。     

热处理对Fe80Zr5Nb4B11非晶合金的结构及磁性能影响

采用单辊快淬法制备Fe80Zr5Nb4B11合金,并在不同温度下对其进行退火,研究热处理对该合金的结构和磁性能的影响。利用X射线衍射（XRD）和透射电镜（TEM）表征合金的结构,利用振动样品磁强计（VSM）测量合金的磁性能。结果表明：随着退火温度的增加,α-Fe晶体相从非晶基体中析出;晶粒尺寸逐渐增大;Fe80Zr5Nb4B11合金的比饱和磁化强度（Ms）在300℃下降,之后保持持续上升的趋势;而矫顽力（Hc）的变化相对复杂,呈现先上升→下降→上升的趋势,这些特征与其微观结构密切相关。     

Fe79Zr9B12和Fe76Zr9B15合金的晶化行为和磁性能

采用单辊快淬法制备Fe79Zr9B12和Fe76Zr9B15非晶合金薄带,并对两合金进行不同温度下热处理。利用差热分析仪(DTA)、X射线衍射仪(XRD)和振动样品磁强计(VSM)研究Fe79Zr9B12合金和Fe76Zr9B15合金的晶化行为和磁性能。结果表明,Fe79Zr9B12合金和Fe76Zr9B15合金的晶化激活能分别为404.42 kJ/mol和370.75 kJ/mol。晶化初期,有α-Mn型相和α-Fe相从Fe79Zr9B12非晶合金基体中析出,Fe23B6型相和α-Fe相从Fe76Zr9B15非晶合金基体中析出。α-Mn型相和Fe23B6型相均为亚稳相,进一步高温热处理后,α-Mn型相转变为α-Fe相,Fe23B6型相转变为α-Fe相、Fe2B相和Fe3B相。Fe79Zr9B12合金的矫顽力(Hc)在600℃退火后突然增大,继续高温退火,Hc下降;Fe76Zr9B15合金的Hc随着退火温度的升高持续增大。两种合金矫顽力随退火温度的变化与退火后合金的微观结构密切相关。     

退火温度对挤压态细晶钨合金性能及组织演变的影响

采用稀土微合金化和液相强化烧结技术制备细晶93W-4.9Ni-2.1Fe+0.03%Y合金。研究在快速热挤压形变强化后,时效热处理对挤压态细晶93W-4.9Ni-2.1Fe+0.03%Y合金显微硬度和组织演变的影响,并与相应条件的传统钨合金进行对比。结果表明,随着退火温度的升高,2种钨合金钨相的显微硬度大大降低。EDS分析表明,随着退火温度的升高,钨合金粘结相中钨含量逐渐增加,其中细晶钨合金经过1200 ℃退火处理后,粘结相钨含量高达26.11%,而传统钨合金在1350 ℃退火处理后含量最高,达到28.14%。显微组织观察表明,退火有利于降低W-W连接度和细化钨颗粒;与传统钨合金相比,高温退火后,细晶钨合金的粘结相体积比更高且分布更为均匀     

Microstructures of Ti–Ni–Fe wire after severe cold-drawing and annealing

The microstructures and mechanical properties of Ti–47 at%Ni–3 at%Fe shape memory alloy wire under the condition of severe cold-drawing at room temperature and different postdeformation annealing processes were intensively investigated using transmission electron microscope(TEM),X-ray diffraction(XRD),Vickers microhardness tester and electron tensile tester.It is indicated that the structure of the alloy evolves into a predominant amorphous structure with a trace of nanocrystalline B2 phase after the cold-drawing of 76%areal reduction.Postdeformation annealing process exerted significant influence on the microstructure and mechanical properties.Crystallization occurs when the cold-drawn wire was annealed at 300℃ for 30 min.The ultimate tensile strength and ductility as well as the superelasticity of the wire are improved significantly by cold-drawing plus postdeformation annealing.     

NANOCRYSTALLINE STRUCTURE AND INITIAL PERMEABILITY OF ANNEALED Fe_（73．5）Cu_1W_3Si_（13．5）B_9 Alloy

ＮＡＮＯＣＲＹＳＴＡＬＬＩＮＥＳＴＲＵＣＴＵＲＥＡＮＤＩＮＩＴＩＡＬＰＥＲＭＥＡＢＩＬＩＴＹＯＦＡＮＮＥＡＬＥＤＦｅ_（７３．５）Ｃｕ_１Ｗ_３Ｓｉ_（１３．５）Ｂ_９ＡｌｌｏｙＺＨＡＮＧＸｉａｎｇｙｉ,ＺＨＡＮＧＪｉｎｇｗｕａｎｄＺＨＥＮＧＹａｎｇｚｅ?..     

退火时间对BAg45CuZn钎料组织和性能的影响

以制冷、工具等行业常用钎料BAg45CuZn为对象,分析了退火时间对其组织和性能的影响。结果表明:BAg45CuZn钎料合金主要相组成为Cu(铜固溶体)、Ag(银固溶体)、Ag-Zn、Cu-Zn化合物;在580 ℃保温不同时间,钎料的组成相并未发生变化,而各相的比例和形态发生部分改变;其中以共晶组织尤为明显,随着保温时间的延长,其由细小的共晶组织转变为粗大的共晶组织;共晶组织中Cu-Zn、Ag-Zn化合物的硬度较高,致使整个基体的显微硬度明显提高,脆性增大,钎料加工性能变差;580 ℃保温不同时间钎料流铺性和接头强度均发生明显变化,对钎焊工艺性造成较大影响。     

真空退火处理对掺Cr类石墨碳膜力学和摩擦学性能的影响

采用闭合场非平衡磁控溅射离子镀技术制备了掺Cr类石墨镀层,研究了真空退火温度对镀层的硬度、结合强度、摩擦系数和比磨损率的影响规律,通过X射线衍射(XRD)分析了镀层结构随退火温度的变化.结果表明:随退火温度的升高,镀层有新相生成,镀层的膜基结合强度降低,镀层硬度随温度的升高先增加后降低,退火温度为500℃时,镀层显微硬度最大;随退火温度的升高镀层摩擦系数呈现出先降低后升高的变化趋势,比磨损率逐渐增大.     

固溶时效处理对Ti-5.43Al-3.11Mo-1.41V合金显微组织和力学性能的影响

对BT14钛合金(Ti-5.43Al-3.11Mo-1.41V)进行不同温度固溶+时效热处理,研究了固溶温度对合金的显微组织、元素分布和硬度和压缩性能的影响。结果表明,在β相转变温度以下固溶后,随固溶温度上升,初生α相含量不断减少,初生α相和基体相(α′、α″或亚稳β相)中的Al含量均增加,Mo和V含量均下降,显微硬度上升。890、940、990 ℃固溶+540 ℃×6 h时效处理后,基体相分解形成弥散细小的α+β相,起到显著的强化作用,导致显微硬度整体提高,且随着固溶温度的升高,显微硬度和压缩屈服强度提高。     

化学沉积 Ni-Mo-P 和 Ni-P 镀层退火晶化组织及耐蚀性

目的研究化学沉积Ni-4.11%Mo-6.50%P和Ni-9.19%P合金镀层退火晶化转变特征,通过定量表征镀层的晶化程度、晶粒尺寸及结晶相的质量分数,建立显微组织与耐蚀性的关联。方法采用XRD衍射技术和Jade软件分析,定量表征镀层的晶化组织特征,由SEM/EDS测试确定镀层的成分及表面形貌,通过浸泡腐蚀实验及金相显微观察,对比两种镀层的耐蚀性。结果 Ni-Mo-P镀层在低于400℃退火时,只有Ni相结晶;在≥400℃退火时,发生Ni3P晶化反应,同时伴有Ni-Mo固溶体的形成,600℃时的晶化程度为88.13%。相比之下,Ni-P镀层中Ni3P相开始析出的温度降至300℃,600℃时的晶化程度达到91%。在相同温度进行热处理时,Ni-Mo-P镀层晶粒尺寸小于Ni-P镀层。在发生Ni3P晶化反应的温度下,两种镀层中Ni3P的晶粒尺寸总是大于Ni相。在0.5 mol/L的H2SO4中,对于Ni-Mo-P镀层,除300℃外,其他温度下的热处理均能显著改善其耐蚀性;而对于Ni-P镀层,镀态下具有最好的耐蚀性能。在10%的HCl溶液中,退火温度为600℃时,Ni-Mo-P镀层的耐点蚀性能更好;而Ni-P合金则相反,镀态及低温200℃退火后的耐点蚀性能最好。结论 Mo的共沉积提高了Ni-Mo-P镀层Ni3P的析出温度,降低了镀层的晶化程度及晶粒尺寸;与Ni-P镀层相比,高温退火的Ni-Mo-P镀层表现出了优异的耐点蚀性能,但耐硫酸均匀腐蚀的性能较差。     

退火温度对MAO-TC4钛合金表面组织及腐蚀性能的影响

通过微弧氧化技术(Micro-arc oxidation, MAO)对TC4合金进行表面处理,随后采用X射线衍射仪、场发射扫描电镜、激光共聚焦显微镜、硬度测试以及电化学腐蚀等方法研究不同退火温度下MAO-TC4合金的表面氧化膜层形貌、厚度、硬度、相结构以及电化学腐蚀行为。结果表明:随着退火温度的升高,MAO-TC4合金表面氧化膜层的显微硬度亦随之增大,当退火温度为850 ℃时,其最高显微硬度为592 HV0.2。450~850 ℃退火温度范围内,随退火温度升高,MAO-TC4合金的膜层耐腐蚀性先增加后降低;当退火温度为650 ℃时,膜层的自腐蚀电流密度为0.125 μA/cm²,耐腐蚀性能最佳。     

微合金化元素Zr对5083铝合金组织和性能的影响

在实验室中用井式坩埚炉熔炼铸造了5083和5083+0.1Zr两种铝合金,轧制后在100～450℃范围内退火。通过金相显微镜、显微硬度计、扫描电镜、电子万能试验机、透射电镜对合金的铸态组织、板材纤维组织、力学性能、耐蚀性能、第二相粒子成分进行了分析,研究了微量元素Zr对5083铝合金组织性能的影响。结果表明,添加微量元素Zr能够细化合金组织,与未添加Zr相比,添加0.1Zr的5083合金的铸态晶粒尺寸从123μm降至73μm,并使第二相粒子Al₆Mn(Fe)尺寸变小;同时使晶间腐蚀坑变小,合金耐蚀性得到提高。添加微量元素Zr还能抑制合金板材再结晶,300℃退火1 h无明显再结晶现象;尤其是5083+0.1Zr合金经250℃退火1 h,抗拉强度为389.50 MPa,屈服强度为215.62 MPa,伸长率为18.2%,仍完全满足使用要求。     

大块非晶Nd_(60)Fe_(20)Co_(10)Al_(10)合金在晶化过程中磁粘滞行为的研究

通过铜模吸铸法制备出了Nd_(60)Fe_(20)Co_(10)Al_(10)大块非晶合金,研究了该合金在晶化过程中的结构与磁性能,并利用等待时间法研究了其在晶化过程中的磁粘滞行为,结果表明:在453~783 K温度退火时,合金的磁性能变化不大。当退火温度高于783 K时,合金的剩余磁化强度(M_r)、饱和磁化强度(M_s)和矫顽力(_iH_c)的值均急剧降低,在803K退火后,合金完全晶化,铁磁性消失。当合金在703和753 K退火后,合金的激活体积v_a和激活直径Da的数值变化不大,而合金的扰动场H_f则呈现先上升后下降的现象,并且在703 K时达到最大值,这是因为703 K样品中存在的亚稳相造成了扰动场的增加。此外,还讨论了这些微观磁性参数与合金宏观磁性能的关联性。