摘要:本文主要研究了CR232/NBR4155共混以及硫化体系、补强体系对硫化胶料物理机械性能的影响,经研究发现:NBR4155/CR232=100:40、氧化锌:氧化镁:硫磺:DM硫化促进剂=6:6:4:0.6、碳黑N550为50份物理机械性能最好。 相似文献
2.
3.
研究硫化体系、硫化时间和补强体系对氯丁橡胶(CR)2442在深海环境下性能的影响。结果表明:硫化时间为60min时胶料的拉伸强度最大;增加1份炭黑N550或白炭黑能使CR2442胶料的硬度增大0. 5或0. 4度左右;最终优化配方为CR2442 100,炭黑N550 20,白炭黑10,氧化锌4,氧化镁2,芳烃油14,硬脂酸0. 5,防老剂RD 1,防老剂4010 2,硫黄2,促进剂DM 0. 15,相应胶料性能满足深海环境水密接插件性能要求。 相似文献
4.
5.
采用硫化特性参数、溶胀指数和DSC谱图等表征了聚氨酯橡胶(PUR)/氯丁橡胶(CR)共混胶的共硫化性能,并研究了PUR/CR的共混比、补强体系与软化体系等对共混胶的硫化特性的影响.结果表明,采用过氧化二异丙苯/氧化镁(DCP/MgO)复合硫化体系,可以使PUR/CR共混胶达到共硫化;增加PUR和炭黑的用量,减少软化剂的用量,则共混胶料的转矩增大;增加PUR用量,可以加快共混胶料的硫化速度,其它因素对硫化速度的影响不明显.当PUR/CR共混比为20/80、DCP 3份、MgO 4份、炭黑N550 30份、软化剂聚异丁烯(PIB)5份时,共混硫化胶有较好的综合性能. 相似文献
6.
7.
探讨补强剂种类和用量对酚醛树脂硫化BIIR胶料性能的影响。结果表明,炭黑N330、N660和气相法白炭黑对酚醛树脂硫化BIIR胶料均有较好的补强效果。补强剂用量为60份时BIIR胶料的综合物理性能较好;炭黑N330补强BIIR胶料的耐热老化和抗溶胀性能最好。 相似文献
8.
9.
10.
以天然橡胶(NR)为基体,选取20份N774、N550和白炭黑分别与40份N990协同补强NR,并借助Ding-Leonov硫化动力学模型考察相同填料用量水平下纯N990填充体系和填料替代体系对硫磺硫化NR复合材料硫化过程和硫化返原行为的影响。结果表明:Ding-Leonov硫化动力学模型能较好描述硫磺硫化体系硫化NR的硫化行为,交联键分解反应对温度的依赖性要高于硫化先驱体分解产生交联中间体的反应,采用低粒径炭黑以及白炭黑部分替代N990均使硫磺硫化NR混炼胶的高温硫化返原现象加剧。与仅用N990填充胶料相比,随着替代炭黑粒径的降低,NR混炼胶的硫化程度和硫化速率均提高,NR硫化胶的拉伸强度相近,硬度和定伸应力不同程度提高;而用20份白炭黑替代等量N990,硫化程度变化不大,硫化速率增大,硫化胶回弹性略有下降,但具有较高的拉断伸长率。 相似文献
11.
通过配位反应制备得到双金属硫化促进剂二乙基二硫代氨基甲酸锌镧配合物(ZnLaDC),在不添加传统活化体系氧化锌(ZnO)/硬脂酸(SA)的情况下,考察了ZnLaDC用量对丁苯橡胶(SBR)/天然橡胶(NR)胎面胶复合材料硫化特性及物理机械性能的影响,并与传统硫化体系二乙基二硫代氨基甲酸锌(ZnDC)/ZnO/SA制备的硫化胶性能进行了对比。结果表明,随着ZnLaDC用量的增加,SBR/NR胎面胶复合材料的硫化特性、压缩疲劳生热性能及耐磨性得到有效提高,当ZnLaDC用量为5份时,复合材料的综合性能最佳。与传统硫化体系ZnDC/ZnO/SA制备的硫化胶相比,采用ZnLaDC制备的硫化胶具有更优异的静态力学性能及耐切割性。 相似文献
12.
摘要:本文主要研究了不同牌号的碳黑对氯丁橡胶硫化胶料物理机械性能的影响以及不同牌号的碳黑在氯丁橡胶与黄铜粘合中的应用。通过研究发现:采用碳黑N330或者碳黑N550时能够得到具有良好物理机械性能的硫化胶料。无论是物理粘合法还是化学粘合法,采用碳黑N550的配方其初始抽出力、耐老化抽出力以及耐水腐蚀后抽出力均最大。 相似文献
13.
14.
用填充炭黑的异戊橡胶(IR)和天然橡胶(NR)分别研究其硫化特性、力学性能、热空气老化性能和动态力学性能。结果表明,异戊橡胶比天然橡胶的硫化速度慢,焦烧时间长。随着炭黑用量的增多,IR和NR的300%定伸应力增大,拉伸强度和拉断伸长率都下降,撕裂强度出现了峰值。炭黑用量增加到40份时,IR的拉伸强度下降最缓慢,耐老化性能最好;而NR随炭黑用量增加,其拉伸强度下降加快,耐老化性能变差。0℃时IR的损耗因子大于NR的损耗因子;60℃时,IR的损耗因子小于NR的损耗因子。 相似文献
15.
16.
17.
The effects of carbon black on polymer-filler interaction, technical properties and fracture mode of carboxylated nitrile rubber (XNBR) cured by different curing systems have been studied. Technical properties show improvement in all cases with increase of filler loadings. At lower loadings of filler, a marked difference in physical properties was observed among different curing systems whereas this difference is minimized at higher loadings when polymer-filler interaction overshadows the effect of the crosslinking system. Scanning electron microscope studies of tensile fracture surfaces have been made. While filler has marked effect on fracture mode, crosslinking system seems to have little effect. Unfilled (gum) and carbon-black (N 550) filled XNBR vulcanizates show different fracture patterns irrespective of the curing system. This is true in the case of sulphur, metal oxide and metal oxide-sulphur mixed crosslinking systems. But the dicumyl peroxide cured system shows a different fracture pattern and the difference is more in the case of gum vulcanizates. 相似文献
18.
Z. A. Mohd Ishak P. Y. Wan P. L. Wong Z. Ahmad U. S. Ishiaku J. Karger‐Kocsis 《应用聚合物科学杂志》2002,84(12):2265-2276
Hygrothermally decomposed polyurethane (HD‐PUR) was mixed up to 20 phr in epoxidized natural rubber (with 50 mol % epoxidation; ENR50) recipes, and the curing and mechanical behaviors were studied. Mechanical testing of the ENR50/HD‐PUR vulcanizates determined the tensile, tear, compression‐set, hardness, abrasion, hysteresis, and resilience properties. No significant changes were observed in the tensile properties with the incorporation of HD‐PUR. The ENR50 compounds showed an increase in compression set with increasing HD‐PUR content. Rubbers cured by a semi‐efficient vulcanization system gave the best overall performance. A further improvement in curing and mechanical properties was achieved by the carbon black grade N330 being replaced with a more active grade (N375). © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 2265–2276, 2002 相似文献