Comprehensive Analysis of Microalloying Element V Improving Hydrogen Embrittlement Resistance of 1300MPa Bolt Steel

Metallurgical and Materials Transactions A - In this study, the effect of vanadium addition (0.14 wt pct) on microstructure and hydrogen embrittlement (HE) susceptibility were...     

Hydrogen Embrittlement of a 1500-MPa Tensile Strength Level Steel with an Ultrafine Elongated Grain Structure

A deformation of a tempered martensitic structure (i.e., tempforming) at 773 K (500 °C) was applied to a 0.6 pct C-2 pct Si-1 pct Cr steel. The hydrogen embrittlement (HE) property of the tempformed (TF) steel was investigated by a slow strain rate test (SSRT) and an accelerated atmospheric corrosion test (AACT). Hydrogen content within the samples after SSRT and AACT was measured by thermal desorption spectrometry (TDS). The tempforming at 773 K (500 °C) using multipass caliber rolling with an accumulative are reduction of 76 pct resulted in the evolution of an ultrafine elongated grain (UFEG) structure with a strong 〈110〉//rolling direction (RD) fiber deformation texture and a dispersion of spheroidized cementite particles. The SSRT of the pre-hydrogen-charged notched specimens and the AACT demonstrated that the TF sample had superior potential for HE resistance to the conventional quenched and tempered (QT) sample at a tensile strength of 1500 MPa. The TDS analysis also indicated that the hydrogen might be mainly trapped by reversible trapping sites such as grain boundaries and dislocations in the TF sample, and the hydrogen trapping states of the TF sample were similar to those of the QT sample. The QT sample exhibited hydrogen-induced intergranular fracture along the boundaries of coarse prior-austenite grains. In contrast, the hydrogen-induced cracking occurred in association with the UFEG structure in the TF sample, leading to the higher HE resistance of the TF sample.     

Effect of High-Pressure Torsion Processing and Annealing on Hydrogen Embrittlement of Type 304 Metastable Austenitic Stainless Steel

The effect of high-pressure torsion (HPT) and annealing on hydrogen embrittlement (HE) of a type 304 stainless steel was studied by metallographic characterization and tensile test after hydrogen gas charging. A volume fraction of ~78 pct of the austenite transformed to α′ martensite by the HPT processing at an equivalent strain of ~30. Annealing the HPT-processed specimen at a temperature of 873 K (600 °C) for 0.5 hours decreased the α′ martensite to ~31 pct with the average grain size reduced to ~0.43 μm through the reverse austenitic transformation. Hydrogen charge into the HPT-processed and the HPT+annealed specimens in the hydrogen content of ~10 to 20 ppm led to no severe HE but appeared in the solution-treated specimen. Especially the 873 K (600 °C) annealed specimen had the ~1.4 GPa tensile strength and the ~50 pct reduction of area (RA) despite the hydrogenation.     

Tempered martensite embrittlement in SAE 4340 steel

The toughness of SAE 4340 steel with low (0.003 wt pct) and high (0.03 wt pct) phosphorus has been evaluated by Charpy V notch (CVN) impact and compact tension plane strain fracture toughness (K _1c) tests of specimens quenched and tempered up to 673 K (400°C). Both the high and low P steel showed the characteristic tempered martensite embrittlement (TME) plateau or trough in room temperature CVN impact toughness after tempering at temperatures between 473 K (200°C) and 673 K (400°C). The CVN energy absorbed by low P specimens after tempering at any temperature was always about 10 J higher than that of the high P specimens given the same heat treatment. Interlath carbide initiated cleavage across the martensite laths was identified as the mechanism of TME in the low P 4340 steel, while intergranular fracture, apparently due to a combination of P segregation and carbide formation at prior austenite grain boundaries, was associated with TME in the high P steel.K _IC values reflected TME in the high P steels but did not show TME in the low P steel, a result explained by the formation of a narrow zone of ductile fracture adjacent to the fatigue precrack during fracture toughness testing. The ductile fracture zone was attributed to the low rate of work hardening characteristic of martensitic steels tempered above 473 K (200°C).     

Effect of welding consumables and processes on dynamic fracture toughness (J 1d) of armour grade Q&T steel joints

Abstract

Austenitic stainless steel (ASS) welding consumables are being used for welding armour grade Q&T steels, as they have higher solubility for hydrogen in the austenitic phase, to avoid hydrogen induced cracking (HIC). Even with austenitic stainless steel consumables under high dilution, the risk of HIC prevailed. In recent years, the developments of low hydrogen ferritic steel (LHF) consumables that contain no hygroscopic compounds are utilised for welding Q&T steels. The use of ASS fillers for welding armour grade Q&T steels creates a duplex microstructure (austenite and δ ferrite) in the welds, which drastically reduces the joint efficiency (ratio of ultimate tensile strength of the joint and the base metal). On the other hand, the weld made using LHF fillers exhibited superior joint efficiency due to the preferential ferrite microstructure in the welds. The use of ASS and LHF consumables for armour grade Q&T steels will lead to formation of distinct microstructures in their respective welds. This microstructural heterogeneity will have a drastic influence on the dynamic fracture toughness of the armour grade Q&T steel welds. Hence, in this investigation an attempt has been made to study the influence on the welding consumables and processes on the dynamic fracture toughness properties of armour grade Q&T steel joints. Shielded metal arc welding (SMAW) and flux cored arc welding (FCAW) processes were used for fabrication of the joints using ASS and LHF welding consumables. The joints fabricated by SMAW process using ASS consumables exhibited superior dynamic fracture toughness values compared to all other joints.     

Hydrogen degradation of spheroidized AISI 1090 steel

Spheroidized AISI 1090 steel was mechanically tested after precharging or dynamically charging with hydrogen at high fugacity. The degradation of properties was greater for plane-strain tensile tests or notched bend tests than for tensile tests of round bars. In precharged specimens the degradation was manifested as an early onset of plastic instability in the form of shear bands leading to premature fracture. In dynamically charged specimens, hydrogen caused brittle fracture in a mode I manner. The results are compared with those in other hydrogen embrittlement studies and discussed in relation to theories for the onset of plastic instability. Formerly Graduate Student, The Ohio State University     

Evaluation of Carbon Partitioning in New Generation of Quench and Partitioning (Q&P) Steels

Quenching and partitioning (Q&P) and a novel combined process of hot straining (HS) and Q&P (HSQ&P) treatments have been applied to a TRIP-assisted steel in a Gleeble®3S50 thermomechanical simulator. The heat treatments involved intercritical annealing at 800 °C and a two-step Q&P heat treatment with a partitioning time of 100 seconds at 400 °C. The “optimum” quench temperature of 318 °C was selected according to the constrained carbon equilibrium (CCE) criterion. The effects of high-temperature deformation (isothermal and non-isothermal) on the carbon enrichment of austenite, carbide formation, and the strain-induced transformation to ferrite (SIT) mechanism were investigated. Carbon partitioning from supersaturated martensite into austenite and carbide precipitation were confirmed by means of atom probe tomography (APT) and scanning transmission electron microscopy (STEM). Austenite carbon enrichment was clearly observed in all specimens, and in the HSQ&P samples, it was significantly greater than in Q&P, suggesting an additional carbon partitioning to austenite from ferrite formed by the deformation-induced austenite-to-ferrite transformation (DIFT) phenomenon. By APT, the carbon accumulation at austenite/martensite interfaces was observed, with higher values for HSQ&P deformed isothermally (≈ 11 at. pct), when compared with non-isothermal HSQ&P (≈ 9.45 at. pct) and Q&P (≈ 7.6 at. pct). Moreover, a local Mn enrichment was observed in a ferrite/austenite interface, indicating ferrite growth under local equilibrium with negligible partitioning (LENP).

     

Quench embrittlement of hardened 5160 steel as a function of austenitizing temperature

Charpy V-notch (CVN) specimens from experimental heats of 5160 steel containing 0.001 and 0.034 mass pct phosphorus were austenitized at temperatures between 830 °C and 1100 °C, quenched to martensite, and tempered at temperatures between 100 °C and 500 °C. Scanning electron microscopy (SEM) was used to characterize the fracture surfaces of tested CVN specimens and carbide formation on prior austenite grain boundaries. Quench embrittlement, the susceptibility to intergranular fracture in as-quenched and low-temperature tempered high-carbon steels due to cementite formation as affected by phosphorus segregation on austenite grain boundaries, developed readily in specimens of the high phosphorus steel austenitized at all temperatures. The low phosphorus steel developed quench embrittlement only after austenitizing at 1100 °C. Intergranular fractures correlated with low room-temperature CVN impact toughness. The results are discussed with respect to the dissolution of carbides during austenitizing and the effect of phosphorus on grain boundary, carbide formation, and stability.     

Development of Multiphase Microstructure with Bainite, Martensite, and Retained Austenite in a Co-Containing Steel Through Quenching and Partitioning (Q&P) Treatment

The quenching and partitioning (Q&P) treatment of steel aims to produce a higher fraction of retained austenite by carbon partitioning from supersaturated martensite. Q&P studies done so far, relies on the basic concept of suppression of carbide formation by the addition of Si and/or Al. In the present study Q&P treatment is performed on a steel containing 0.32 C, 1.78 Mn, 0.64 Si, 1.75 Al, and 1.20 Co (all wt pct). A combination of 0.64 Si and 1.75 Al is chosen to suppress the carbide precipitation and therefore, to achieve carbon partitioning after quenching. Addition of Co along with Al is expected to accelerate the bainite transformation during Q&P treatment by increasing the driving force for transformation. The final aim is to develop a multiphase microstructure containing bainite, martensite, and the retained austenite and to study the effect of processing parameters (especially, quenching temperature and homogenization time) on the fraction and stability of retained austenite. A higher fraction of retained austenite (~13 pct) has indeed been achieved by Q&P treatment, compared to that obtained after direct-quenching (2.7 pct) or isothermal bainitic transformation (9.7 pct). Carbon partitioning during martensitic and bainitic transformations increased the stability of retained austenite.     

Effect of Hydrogen on Tensile Properties of Ultrafine-Grained Type 310S Austenitic Stainless Steel Processed by High-Pressure Torsion

This study addresses a hydrogen effect on the tensile properties of a type 310S austenitic stainless steel with ultrafine-grained structures produced by high-pressure torsion (HPT) and subsequent annealing. The mean grain size was reduced to ~85 nm by the HPT processing. The grain size was increased by the post-HPT annealing, but the grain size of ~265 nm was retained after annealing at 1023 K (750 °C). The tensile strength of ~1.2 GPa, which is approximately twice as much as that of the solution-treated specimen, was attained in the 1023 K (750 °C) post-HPT-annealed specimen. The elongation to failure was restored up to ~15 pct by the post-HPT annealing, although it was still insufficient in comparison with the ~55 pct elongation of the solution-treated specimen. There was no change in the tensile strength of the HPT-processed specimens and the post-HPT-annealed specimens by hydrogen charging with the hydrogen content in the range of ~20 to 40 mass ppm. The HPT-processed and the 773 K (500 °C) post-HPT-annealed specimens exhibited a ductility loss through the fully shear type fracture. The hydrogen charge into higher temperature post-HPT-annealed specimens with σ-FeCr precipitates led to a mild hydrogen embrittlement.     

A study of the hydrogen-induced degradation of two steels differing in sulfur content

Two steels with different sulfur contents: 0.003 and 0.024 wt pct, were cathodically charged under three different conditions and brought to fracture in tension immediately after charging or after aging at room temperature. All hydrogen charged specimens showed embrittlement, with a little higher loss of ductility in the high sulfur steel. The hydrogen embrittlement was reversible in both steels when specimens were charged in arsenic-free sulfuric acid solution at room temperature but was irreversible when charged in arsenic-containing acid at the same temperature. After charging in molten salts at 200 °C, some of the low sulfur steel specimens exhibited irreversible hydrogen damage with the appearance of quasicleavage fractures, while all high sulfur steel specimens were restored to the uncharged ductility by aging at room temperature. These results are interpreted by assuming that an increased sulfur content in steel increases the density of trapping sites for hydrogen at the sulfide/matrix interfaces. These traps are inactive above 150 °C and become operative after cooling. Therefore, at the same hydrogen content in steel after cooling, the greater content of sulfur results in a decreased activity of the lattice dissolved hydrogen, hence in reduced embrittlement.     

Effect of welding consumables on hydrogen induced cracking of armour grade quenched and tempered steel welds

Abstract

Armour grade quenched and tempered (Q&T) steels are susceptible to hydrogen induced cracking (HIC) in the heat affected zone after welding. Austenitic stainless steel (ASS) consumables are selected for welding Q&T steels as they have higher solubility for hydrogen in the austenitic phase and it is the most beneficial method for controlling HIC in Q&T steel welds. Recent studies reveal that high nickel steel and low hydrogen ferritic steel consumables can be used to weld Q&T steels, which can give very low hydrogen levels in the weld deposits. In this investigation, an attempt has been made to study the effect of welding consumables on hydrogen induced cracking of Q&T steel welds by implant testing. Shielded metal arc (SMAW) welding process has been used for making welds using three different consumables, namely austenitic stainless steel, low hydrogen ferritic steel (LHF) and high nickel steel (HNS) to assess HIC by implant testing. The high nickel steel consumables exhibited a higher value of lower critical stress (LCS) and thus they offered a greater resistance to hydrogen induced cracking of armour grade Q&T steel welds than other consumables. The diffusible hydrogen content and the value of the LCS meets the specified limit for armour grade Q&T steel welds and hence, the LHF consumables can be accepted as an alternative to the to the traditionally used ASS consumables and the proposed HNS consumables.     

The effect of hydrogen on mechanical properties in Ti-10V-2Fe-3Al

The effect of hydrogen on the mechanical properties of the metastable β alloy Ti-10V-2Fe-3Al was examined. The material was beta annealed and water quenched (B/WQ) to yield a nominally all-β microstructure, with a small volume fraction of athermal omega present. Tensile and notched bend bar tests were performed with differing levels of hydrogen concentration (~0 to >30 at. pct) obtained by Sieverts (gaseous) charging prior to beta annealing. The β phase was transformed to orthorhombic alpha double prime martensite (β") upon deformation. The volume fraction and morphology of the alpha double prime depended on the hydrogen concentration. The deformation-induced martensitic transformation changed from being stress-induced to being strain-induced with increased hydrogen concentration. High hydrogen concentrations also resulted in changes in fracture mode. At high hydrogen concentrations, where little or no martensite formed upon deformation, “intrinsic” (i.e., independent of microstructural modification) hydrogen effects were observed in the β phase. These intrinsic hydrogen effects, deleterious in nature, were taken to be evidence of hydrogen embrittlement in the body-centered cubic β phase. Formerly at Carnegie Mellon University.     

Effect of hydrogen on fracture behavior of a quenched and tempered medium-carbon steel

This work examined the effects of hydrogen on fracture of quenched and tempered 1045 steel. Tests were made at room temperature on tensile, Charpy impact, and 4-point notched bend specimens. This steel exhibits tempered martensite embrittlement (TME) for tempering temperatures between 300 and 375 °C. Thus hydrogen in most cases affected fracture by increasing the amount of intergranular fracture. In bend specimens, hydrogen also induced quasicleavage (QC) fracture at points of maximum normal stress below the notch root, points which appeared to be the locations of crack initiation. Tear ridges on theseQC surfaces were at martensite lath packet boundaries. Crack orientations were largely mode I in uncharged specimens, with mode II appearing at the notch root in most hydrogen-charged specimens. These observations are in general agreement with earlier work on martensitic steel. Formerly graduate student, Carnegie-Mellon University     

Comparative Study of Hydrogen Embrittlement of Three Heat-resistant Cr-Mo Steels Subjected to Electrochemical and Gaseous Hydrogen Charging

Hydrogen embrittlement (HE) behaviors of low carbon steel and three heat-resistant Cr-Mo steels having different Cr contents were compared through tensile testing, silver decoration, and blistering observation after electrochemical hydrogen charging and hardness testing after gaseous hydrogen charging. It was observed that higher Cr content caused a longer suppression in charging hydrogen into the steels. However, under hydrogen supersaturation conditions, the higher the strength of the heat-resistant steels, the poorer the HE resistance after electrochemical charging. In contrast, the higher the Cr content, the better the HE resistance under high-temperature gaseous charging conditions.

     

Hydrogen embrittlement of dual-phase steels

Reversible hydrogen embrittlement (HE) is usually only found in quenched and tempered steels with yield stresses in excess of 1035 MPa (150 ksi). A study of the HE phenomena in two dual-phase steels with tensile strengths of about 690 MPa (100 ksi) has shown that these steels are susceptible to the presence of hydrogen. HE results in a reduction in fracture strength, although no preyield failures are observed, and a change in fracture mode from ductile dimpling to transgranular cleavage. After prestraining and HE, it is found that the greater the prestrain the higher is the fracture stress. It is concluded that the presence of the 15 to 20 pct high carbon (0.6 pct C) high strength martensite in the dual-phase steels is responsible for the HE; tempering studies give results consistent with this idea. Delayed failure tests on notched specimens showed that for the as-received condition, the run-out stress (stress for no failures in 50 to 100 h) to be above the macroscopic flow stress. A condition for HE failure in dual-phase steels appears to be considerable macroscopic deformation.     

Application of Quenching and Partitioning (Q&P) Processing to Press Hardening Steel

Press hardening steel (PHS) has been increasingly used for the manufacture of structural automotive parts in recent years. One of the most critical characteristics of PHS is a low residual ductility related to a martensitic microstructure. The present work proposes the application of quenching and partitioning (Q&P) processing to improve the ductility of PHS. Q&P processing was applied to a Si- and Cr-added Q&P-compatible PHS, leading to a press hardened microstructure consisting of a tempered martensite matrix containing carbide-free bainite and retained austenite. The simultaneous addition of Si and Cr was used to increase the retained austenite fraction in the Q&P-compatible PHS. The Q&P processing of the PHS resulted in a high volume fraction of C-enriched retained austenite, and excellent mechanical properties. After a quench at 543 K (270 °C) and a partition treatment at 673 K (400 °C), the PHS microstructure contained a high volume fraction of retained austenite and a total elongation (TE) of 17 pct was achieved. The yield strength (YS) and the tensile strength were 1098 and 1320 MPa, respectively. The considerable improvement of the ductility of the Q&P-compatible PHS should lead to an improved in-service ductility beneficial to the passive safety of vehicle passengers.     

Crack paths,microstructure, and fatigue crack growth in annealed and cold-rolled AISI 304 stainless steels

To assist in the understanding of micromechanisms for corrosion fatigue crack growth in metastable austenitic steels, the relationships between the crack paths and the underlying microstructure were investigated for annealed and cold-rolled (CR) 304 stainless steels that had been tested in a deaerated 3.5 pct NaCl solution, air, and vacuum. Corrosion fatigue in the deleterious environments (3.5 pct NaCl and air) was brittle and occurred primarily by {001}_γ and other unidentified, quasi-cleavage (QC), accompanied by preferential cracking along {111}_γ twin and grain boundaries. In contrast, fatigue cracking in vacuum was ductile, fully transgranular, and noncrystallographic. Transformation to alpha prime (α′-) martensite by fatigue was found to be essentially complete in the CR steel, which contained ε-martensite, and in the annealed steel tested in vacuum, but was substantially less in the annealed steel tested in air and 3.5 pct NaCl solution. These results, taken in conjunction with the crack growth and electrochemical reaction data, support hydrogen embrittlement (HE) as the mechanism for corrosion fatigue crack growth in 304 stainless steels in 3.5 pct NaCl solution. Martensitic transformation appears not to be the only responsible factor for embrittlement. Other microstructural components, such as twin and grain boundaries, slip bands, and cold work-induced lattice defects, may play more important roles in enhancing crack growth rates.     

Quenched and Partitioned Microstructures Produced <Emphasis Type="Italic">via</Emphasis> Gleeble Simulations of Hot-Strip Mill Cooling Practices

Previous researchers reported on quenched and partitioned (Q&P) microstructures produced via carbon partitioning from martensite into austenite during isothermal annealing after quenching to develop a partially martensitic initial structure. However, the thermal profile used in previous studies is not well suited to creating Q&P microstructures directly from a hot-strip mill. In this work, the commonly employed Q&P thermal profile (i.e., having an isothermal partitioning step) was modified to evaluate nonisothermal partitioning that might instead occur during cooling of a wound coil. Thus, it was possible to assess the potential for creating Q&P microstructures and properties directly off of the hot mill. Gleeble thermal simulations representative of a hot-strip mill cooling practice were used to create dual-phase, Q&P, transformation-induced plasticity (TRIP), and conventional microstructures by varying the quench/coiling temperatures (CTs) using a 0.19C-1.59Mn-1.63Si (wt pct) steel. Microstructural and mechanical property data indicate that hot rolling might be a viable processing route for high-strength Q&P steels.