焊后热处理对异种合金摩擦焊件组织与性能的影响

用金相观察、SEM分析和拉伸试验等方法研究不同的焊后热处理制度对异种合金(Ti2AlNb/TC11)线性摩擦焊接件显微组织与力学性能的影响。结果表明:仅进行时效热处理时,随着保温时间的延长或热处理温度的提高,焊缝两侧热影响区条状α/O相析出量不断增加,焊接接头强度也相应得到提高;固溶及时效热处理后,TC11合金侧热影响区在晶界上析出大量粗条状α相,Ti2AlNb合金侧热影响区晶界主要由条状O相构成,焊接接头强度超出母材TC11合金的强度。     

Effect of post weld heat treatment on properties of variable polarity TIG welded AA2219 aluminium alloy joints

AA2219 aluminium alloy joints were fabricated by variable polarity tungsten inert gas (VPTIG) welding process and the effects of post weld heat treatment (PWHT) on the tensile properties, microstructure and fatigue behaviour of the welded joints were investigated. The VPTIG welding process was adopted because it could meet the need of cathode cleaning and meanwhile it could reduce the deterioration of tungsten electrode furthest. The welded samples were divided into as-welded (AW) sample and PWHT sample. The PWHT method used on the samples was solution treatment (535 °C, 30 min), water quenching and artificial aging (175 °C, 12 h). The experimental results show that, compared with the AW samples, the microstructure characteristics and mechanical properties of the AA2219 joints after PWHT were significantly improved. The improvement of yield strength, ultimate tensile strength, and fatigue strength are 42.6%, 43.1% and 18.4%, respectively.     

GH3230合金的焊后热处理

分析测试了GH3230合金氩弧焊接后经不同焊后热处理制度处理后的显微组织、显微硬度和拉伸性能.试验结果表明:GH3230合金焊接板材经1140～1180℃保温10 min焊后热处理,既能使焊后残余应力得到充分释放,又能保证组织稳定,满足合金力学性能要求.     

焊后热处理对2219-T6铝合金搅拌摩擦焊接头力学性能的影响

采用搅拌摩擦焊方法对2219-T6铝合金进行焊接,对焊接接头的宏观形貌、显微组织、拉伸强度、显微硬度进行了分析。结果表明,焊核区组织为细小的晶粒,热机影响区组织为弯曲变形的晶粒,热影响区组织出现了明显粗化。接头室温拉伸强度可以达到母材的75%左右,接头强度低于母材的原因主要归结为金属的塑性损伤、缺陷的产生和热影响区的软化。通过固溶及时效方法并兼顾再结晶过程的热处理工艺可以回复接头塑性、消除软化,达到改善接头性能的目的。     

预热与焊后退火对T24钢焊接接头力学性能的影响

在不同焊前预热与焊后热处理配合工艺条件下,对SA-213 T24(以下简称T24)钢管对接接头的力学性能进行了对比试验。结果表明,T24钢管具有优良的焊接性能,在焊接工艺控制合适的情况下,可不进行焊前预热及焊后热处理,是700℃参数超超临界机组锅炉水冷壁用钢管的优选材料。     

热处理对双FCC相CoCrFeNiCu高熵合金组织与性能的影响

用真空感应熔炼法制备了CoCrFeNiCu高熵合金,研究了不同退火温度对合金组织及力学性能的影响.结果表明,铸态CoCrFeNiCu合金具有双FCC相结构,分别为富Cu相和贫Cu相,而且相分离现象随热处理温度的升高逐渐明显.铸态合金的组织形貌为典型树枝晶组织,随热处理温度的升高,富铜相增多,枝晶间隙变宽,且出现了大量纳...     

焊后热处理对复杂结构件完整性的影响

通过考虑热处理前后δ_CTOD值和残余应力变化,研究了焊后热处理对复杂结构件完整性的影响. 对厚板(80 mm)对接接头进行了焊态和热处理态的残余应力测量和断裂韧性(CTOD)试验. 相对厚板对接接头焊态,热处理态的残余应力有效降低,焊缝δ_CTOD值基本不变,热影响区δ_CTOD值有较大幅度下降;对带拘束和装配应力复杂焊接结构进行局部热处理并测试焊态和热处理态的残余应力. 结果表明,残余应力降低不明显,有的部位残余应力水平反而上升. 基于以上试验结果,对多种情况进行结构完整性的评估,发现了局部热处理并不能够改善复杂结构的安全性.     

热处理对CoCrFeNiMo高熵合金组织与硬度的影响

用真空电弧熔炼法制备了CoCrFeNiMo高熵合金,研究了退火温度对合金组织及硬度的影响。结果表明,铸态合金的晶体结构以FCC为主,同时夹杂Cr9Mo21Ni20和CrFe4少量金属间化合物;铸态合金的组织形貌为树枝晶组织,在枝晶间分布着类似于共晶组织的片层状结构,随退火温度升高,合金中FCC相逐渐减少,共晶相逐渐增多,最终形成了类似于过共晶的组织形貌;合金的硬度随退火温度的升高先增大后减小,但铸态与退火态的合金的硬度相差不大,说明此合金具有较高的热稳定性以及较好的高温使用性能。     

焊后时效处理和固溶处理对接头组织和性能的影响

通过以2519高强铝合金为研究对象,研究了单独时效处理和固溶再时效处理对接头组织和性能的影响.结果表明,时效处理对接头的强度提升有一定的帮助,当时效温度为150 ℃时接头的抗拉强度达到最大;固溶再时效处理能使接头的抗拉强度显著增加,且随着固溶温度的增加,接头的抗拉强度随之增加,但当固溶温度达到540 ℃时,接头中容易产生液化裂纹,接头强度反而降低.采用强化固溶的方法,可以将固溶温度提升至540 ℃,显著提升接头的强度.     

热处理对含Ag耐热铝合金组织与性能影响

通过铸锭冶金及形变热处理,制备了一种含0.6Ag的Al-5.3Cu-0.8Mg-0.6Mn耐热铝合金.采用光学显微镜、扫描电子显微镜、差热分析及力学性能测试,研究了热处理工艺(包括均匀化处理、固溶及人工时效处理)对合金的组织与性能影响,并推导了其均匀化动力学过程.结果表明,理想的热处理工艺是均匀化制度为500℃×12h,固溶温度为525℃,人工时效制度为185℃×8h.通过优化热处理工艺,合金的室温抗拉强度达570MPa,伸长率在10%以上.     

Microstructures and mechanical properties of a welded CoCrFeMnNi high-entropy alloy

The response of the CoCrFeMnNi high-entropy alloy to weld thermal cycles was investigated to determine its applicability as an engineering structural material. Two processes were used: high-energy-density, low-heat-input electron beam (EB) welding and low-energy-density, high-heat-input gas tungsten arc (GTA) welding. Weldability was determined through comprehensive microstructural and mechanical property characterisation of the welds. The welds did not develop solidification cracking or heat-affected zone cracks. The microstructures in weld fusion zones are similar to that in the as-cast materials, consisting of large columnar grains with dendrite. The dendrite arm spacing and the extent of elemental segregation were less in the welds than in the cast ingot, and also were less pronounced in the EB weld than in the GTA weld. Compositional microsegregation between dendritic cores and interdendritic regions of the welds was insignificant. Both welds exhibited slightly higher yield strengths than the base metal. The EB weld possessed comparable tensile strength and ductility to that of the base metal. In comparison, the GTA weld maintained ～80% of the base metal’s tensile strength and 50% of the ductility.     

焊后热处理对DH36钢焊接接头断裂韧性的影响

文中对DH36钢埋弧焊焊接接头进行了焊后热处理,并根据BS7448标准对焊缝和热影响区进行裂纹尖端张开位移CTOD测试,研究焊后热处理对断裂韧性的影响.结果表明,焊后热处理对焊缝断裂韧性的影响并不一定是好的效果,热处理后,焊缝δ值有的升高有的降低;焊后热处理对热影响区粗晶区的断裂韧性有不利影响,热处理后,热影响区粗晶区的δ值均有所下降.经过焊后热处理,90 mm厚焊缝试样的δ值略有下降,60mm厚焊缝试样的δ值明显升高;90mm厚热影响区试样的δ值明显下降,60mm厚热影响区试样的δ值略有下降.     

高熵合金涂层制备工艺的研究现状

利用激光熔覆技术在Q235基体表面制备CoCrFeNiTi_0.8Nb_y(y = 0.25,0.5,0.75,1.0)涂层.采用光学显微镜、X射线衍射仪、扫描电子显微镜、能谱分析仪等方法分析涂层的相结构和微观组织等;用显微维氏硬度计、摩擦磨损试验机测试涂层的硬度与耐磨性能.结果表明,组织中呈现典型的树枝晶结构,加入Nb元素,涂层微观组织的尺寸减小,增加Nb元素含量时,高熵合金涂层的晶体结构由体心立方相(body-centered cubi,BCC)、少量的面心立方相(face-centered cubic,FCC)和Fe₂(Ti,Nb)型的Laves相组成;在细晶强化、固溶强化和第二相强化的共同作用下提高了涂层的显微硬度;中间相的存在一定程度上可以阻碍犁削切削过程的进行,进而提高了涂层的耐磨性能;CoCrFeNiTi_0.8Nb_0.75涂层的硬度和耐磨性最好,硬度为710 HV,约为基体的4倍,涂层的磨损量最小,磨痕较为平整.

     

2195铝锂合金电子束焊接头的焊后热处理

采用光学显微镜、扫描电镜、能谱仪及X射线衍射仪等微观分析手段,研究不同热处理工艺条件下2195铝锂合金电子束焊接头焊缝区的显微组织演变,探讨接头的焊后热处理强化机制。结果表明,焊后热处理可显著改善接头区域的显微组织,促进强化相的析出,有利于提高接头的力学性能。经过焊后固溶+双级时效热处理,焊态下接头熔合线附近存在的等轴细晶区消失,β′、θ′和T₁等强化相在接头焊缝区析出,与单级时效处理工艺相比,双级时效处理的析出强化效果更为显著。力学性能测试表明,经过双级时效热处理后,接头的抗拉强度达到492.5 MPa,为母材强度的90.4%。接头拉伸断口表面存在许多小韧窝,并伴随出现解理面,接头呈韧-脆混合型断裂特征。     

ASME MC级部件焊后热处理

探讨ASME锅炉及压力容器规范第Ⅲ卷第Ⅰ册NE分卷MC级部件焊后热处理温度范围,模拟焊后热处理的目的意义。结合焊后热处理的预期目的、材料特性、结构特点、工程建造等综合考虑制定焊后热处理的工艺参数及加热方式,并提出局部焊后热处理加热方式可借鉴ASME第Ⅷ卷第Ⅰ册。     

热处理工艺对TC16合金棒材组织和性能的影响

TC16钛合金在780、800、850、900℃下固溶热处理30 min,分别以水淬、空冷、炉冷方式进行冷却,再分别在520、560和600℃保温2、4、8、16 h空冷进行时效处理,利用OM和室温拉伸性能测试等方法,研究了不同热处理工艺对TC16钛合金棒材组织和性能的影响。结果表明,固溶温度对TC16钛合金塑性影响不大,相同的固溶时效处理制度下,随时效时间增加和温度的提高,合金强度和塑性都增加。TC16钛合金较合理的固溶时效处理工艺为:(780±20)℃固溶处理,保温2 h,炉冷至550℃以下后空冷,后在560℃下时效8 h,空冷,如此能获得要求的室温拉伸性能及良好的综合性能。     

焊后热处理对Al-Zn-Mg-Cu合金MIG焊接接头组织与性能的影响

采用ER5356焊丝对Al-4.6Zn-1.5Mg-0.15Cu合金板材进行熔化极钨极氩弧焊试验,并对焊接接头进行了不同的焊后热处理。借助光学显微镜(OM)、扫描电镜(SEM)研究不同焊后热处理试样的组织变化规律,并进行了显微硬度测试与拉伸试验。结果表明:经固溶加时效处理后,焊接接头抗拉强度与显微硬度得到明显提升,抗拉强度与焊缝硬度均值分别提高至304 MPa与85 HV,相比焊后未处理的263 MPa与66 HV,增幅分别达15.6%与28.8%。焊接接头经时效处理后,组织的不均匀性及强化相的分布得到改善;而经重新固溶后,第二相发生回溶,再经时效处理将使得一部分不稳定的过饱和固溶体重新析出且弥散分布。     

热处理工艺对Al0.5CoCrCuFeNi高熵合金显微组织与硬度的影响

采用水冷铜坩埚真空感应悬浮熔炼制备了多组元高熵合金Al_0.5CoCrCuFeNi,研究了不同热处理工艺对合金的显微组织和硬度的影响规律。结果表明,Al_0.5CoCrCuFeNi高熵合金相结构简单,在铸态下由两种不同成分的FCC相组成,枝晶处为贫Cu的FCC1相,枝晶间为富Cu的FCC2相,显微组织为树枝晶形貌,存在一定的枝晶偏析。合金制备态的硬度为255 HV0.5。合金具有良好的热稳定性,随着热处理温度的升高,合金的相结构和硬度均无太大的变化。冷却方式对合金的显微组织和相结构影响不大,但炉冷后合金的硬度比空冷和水冷时高。     

热处理工艺对2.25Cr-1Mo-0.25V钢焊缝组织和力学性能的影响

采用光学金相显微镜、扫描电镜观察,测试力学性能,研究不同焊后热处理对2.25Cr-1Mo-0.25V钢焊缝力学性能、夏比冲击吸收能量和显微组织的影响。结果表明,回火参数增加,焊缝力学性能提高。焊态硬度最高,冲击吸收能量最小,组织主要为板条贝氏体,贝氏体粗大且板条平行;最小焊后热处理后硬度下降,冲击吸收能量提高,组织为板条贝氏体和粒状贝氏体;最大焊后热处理后焊缝硬度和母材近似相同,冲击吸收能量均在153 J以上,板条贝氏体细化,粒状贝氏体增加,焊缝的力学性能相对最好。     

热处理对ZG34Cr2Ni2Mo低合金钢力学性能的影响

采用光学显微镜、扫描电镜、电子万能试验机和显微硬度仪等研究了正火+回火+调质热处理工艺对ZG34Cr2Ni2Mo低合金钢显微组织及力学性能的影响.结果表明:正火(870℃×3 h)+回火(600℃×5 h)+调质(淬火860℃×3 h+回火600℃×5 h)的热处理工艺有助于提高ZG34Cr2Ni2Mo低合金钢的力学性...