Very fast H2 production from the methanolysis of NaBH4 by metal‐free poly(ethylene imine) microgel catalysts

The polyethyleneimine (PEI) microgels prepared via microemulsion polymerization are protonated by hydrochloric acid treatment (p‐PEI) and quaternized (q‐PEI) via modification reaction with methyl iodide and with bromo alkanes of different alkyl chain lengths such as 1‐bromoethane, 1‐bromobutane, 1‐bromohexane, and 1‐bromooctane. The bare p‐PEI and q‐PEI microgels are used as catalysts directly without any metal nanoparticles for the methanolysis reaction of sodium borohydride (NaBH₄). Various parameters such as the protonation/quaternization reaction on PEI microgels, the amount of catalyst, the amount of NaBH₄, and temperature are investigated for their effects on the hydrogen (H₂) production rate. The reaction of self‐methanolysis of NaBH₄ finishes in about 32.5 min, whereas the bare PEI microgel as catalyst finishes the methanolysis of NaBH₄ in 22 min. Surprisingly, it is found that when the protonated PEI microgels are used as catalyst, the same methanolysis of NaBH₄ is finished in 1.5 min. The highest H₂ generation rate value is observed for protonated PEI microgels (10 mg) with 8013 mL of H₂/(g of catalyst.min) for the methanolysis of NaBH₄. Moreover, activation parameters are also calculated with activation energy value of 23.7 kJ/mol, enthalpy 20.9 kJ/mol, and entropy ?158 J/K.mol. Copyright © 2016 John Wiley & Sons, Ltd.     

Poly(2-aminoethyl methacrylate) based microgels catalyst system to be used in hydrolysis and methanolysis of NaBH4 for H2 generation

The poly(2-aminoethyl methacrylate) (p(AEM)) microgels were synthesized by microemulsion polymerization technique and used for in situ metal nanoparticle preparation to render as p(AEM)-M (M: Co or Ni) microgel composites and were used in p(AEM) based poly ionic liquid (PIL) microgels. Next, these p(AEM)) based microgel materials were used as catalysts for hydrogen (H₂) production from both hydrolysis and methanolysis reactions of sodium borohydride (NaBH₄). It was found that the catalytic hydrolysis of the NaBH₄ reaction, catalyzed by p(AEM)-Co microgel composite was completed in 140 min, whereas the methanolysis of NaBH₄ methanolysis catalyzed by the PIL of p(AEM)⁺Cl⁻ microgels was completed in 5 min both with 250 ± 2 mL H₂ production. Furthermore, p(AEM)-Co microgel composite catalysts maintained 80% catalytic activity after 5 consecutive uses in NaBH₄ hydrolysis. On the other hand, p(AEM)⁺Cl⁻ microgels were found to afford more than 50% catalytic activity even after 20 repetitive use in NaBH₄ methanolysis due to superior regeneration ability. Moreover, activation energy values for p(AEM)-Co microgel composites catalyzed NaBH₄ hydrolysis reaction were calculated as 38.9 kJ/mol in comparison to 37.3 kJ/mol activation energy of p(AEM)⁺Cl⁻ microgel catalyzed methanolysis reaction.     

Catalytic decomposition of hydrogen iodide over pre-treated Ni/CeO2 catalysts for hydrogen production in the sulfur–iodine cycle

The Ni/CeO₂ catalysts with successive oxidization, reduction and re-oxidization have been tested for hydrogen production in sulfur–iodine (SI or IS) cycle. The samples were characterized by BET, XRD, TEM, TPR and XPS. The oxidative/reductive atmosphere affected the structure and performance of the catalysts. It was suggested that a migration of Ce⁴⁺ from the bulk to the surface occurred during the reductive treatment. The diffusion process was reversed when the atmosphere was changed to an oxidative one. The reduced and re-oxidized samples seemed to be similar all the time and showed better catalytic activity in comparison with the as-received and oxidized samples. For the re-oxidized sample, the strongest interaction compared with other samples occurred between Ni and CeO₂ and oxygen vacancies transferred from bulk to surface, which led to form more surface sites and oxygen vacancies. The metal Ni was found only on the surface of the reduced sample. The active site of metal Ni besides the surface site and oxygen vacancy were assumed to play an important role for hydrogen production.