Low-Temperature Sintering and Piezoelectric Properties of CuO-Added 0.95(Na0.5K0.5)NbO3–0.05BaTiO3 Ceramics

The sintering temperature of 0.95(Na_0.5K_0.5)NbO₃–0.05BaTiO₃ (NKN–BT) ceramics needs to be decreased below 1000°C to prevent Na₂O evaporation, which can cause difficulties in poling and may eventually degrade their piezoelectric properties. NKN–BT ceramics containing CuO were well sintered at 950°C with grain growth. Poling was easy for all specimens. Densification and grain growth were explained by the formation of a liquid phase. The addition of CuO improved the piezoelectric properties by increasing the grain size and density. High piezoelectric properties of d ₃₃=230 pC/N, k _p=37%, and ɛ₃^T/ɛ₀=1150 were obtained from the specimen containing 1.0 mol% of CuO synthesized by the conventional solid-state method.     

Effect of CuO on the Sintering Temperature and Piezoelectric Properties of (Na0.5K0.5)NbO3 Lead-Free Piezoelectric Ceramics

When a small amount of CuO was added to (Na_0.5K_0.5)NbO₃ (NKN) ceramics sintered at 960°C for 2 h, a dense microstructure with increased grains was developed, probably due to liquid-phase sintering. The Curie temperature slightly increased when CuO exceeded 1.5 mol%. The Cu²⁺ ion was considered to have replaced the Nb⁵⁺ ion and acted as a hardener, which increased the E _c and Q _m values of the NKN ceramics. High piezoelectric properties of k _p=0.37, Q _m=844, and ɛ₃ ^T /ɛ₀=229 were obtained from the specimen containing 1.5 mol% of CuO sintered at 960°C for 2 h.     

Piezoelectric Properties of (1−x)(Na0.5K0.5)NbO3–xAgSbO3 Lead-Free Ceramics

(1− x )(Na_0.5K_0.5)NbO₃– x AgSbO₃ lead-free piezoelectric ceramics were prepared by normal sintering. The effects of the AgSbO₃ on the phase structure and piezoelectric properties of the ceramics were systematically studied. These results show that the AgSbO₃-modified (K_0.50Na_0.50)NbO₃ lead-free piezoelectric ceramics form stable solution with orthorhombic structure, and the Curie temperature and the polymorphic phase transition of the ceramics decreased with increasing AgSbO₃. The result shows that the piezoelectric properties of the ceramics strongly depend on the AgSbO₃. The ceramics with x =0.05 possess optimum properties ( d ₃₃=192 pC/N, k _p=43%, T _c=348°C, T _o−t =145°C, ɛ_r∼632, and tan δ∼3.5%). These results indicate that the ceramic is a promising candidate material for lead-free piezoelectric ceramics.     

Low-Temperature Sintering and Piezoelectric Properties of (Na0.5K0.5)NbO3 Lead-Free Piezoelectric Ceramics

(Na_0.5K_0.5)NbO₃ (NKN) ceramic with 1.5 mol% CuO added (NKNC) was well sintered even at a low temperature of 900°C with the addition of ZnO. Most of the ZnO reacted with the CuO and formed the liquid phase that assisted the densification of the specimens at 900°C. A few Zn²⁺ ions entered the matrix of the specimens and increased the coercive field ( E _c) and Q _m values of the specimens. High-piezoelectric properties of k _p=0.37, Q _m=755, and ɛ₃ ^T /ɛ₀=327 were obtained from the NKNC ceramics containing 1.0 mol% ZnO sintered at 900°C for 2 h.     

Enhanced Piezoelectric Properties in Mn-Doped 0.98K0.5Na0.5NbO3–0.02BiScO3 Lead-Free Ceramics

Mn-doped 0.98K_0.5Na_0.5NbO₃–0.02BiScO₃ (0.98KNN–0.02BS) lead-free piezoelectric ceramics have been prepared by a conventional sintering technique and the effects of Mn doping on the phase structure and piezoelectric properties of the ceramics have been studied. Our results reveal that a small amount of Mn can improve the densification of the ceramics effectively. Because of the high densification, fine grain, and Mn doping effects, the piezoelectric and dielectric properties of the ceramics are improved considerably. Very good piezoelectric and dielectric properties of d ₃₃=288 pC/N, k _p=0.46, ɛ_r=1591, and T _C=328°C were obtained for the 0.98KNN–0.02BS ceramics doped with 0.8 mol% Mn. Therefore, the 0.98KNN–0.02BS ceramics containing a small amount of Mn are a good candidate material for lead-free piezoelectric ceramics.     

Microstructural Evolution of Crystalline-Oriented (K0.5Na0.5)NbO3 Piezoelectric Ceramics with a Sintering Aid of CuO

The microstructural development of crystalline-oriented (K_0.5Na_0.5)NbO₃ (KNN)-based piezoelectric ceramics during sintering was investigated. The addition of CuO as a sintering aid was found to be effective for fabricating highly oriented and dense KNN ceramics. KNN specimens containing 0.5–1.0 mol% CuO sintered at 1100°C for 1 h were found to have relative densities and pseudo-cubic {100} orientation degrees of 95% or higher. In the early stages of sintering, KNN is formed in the reaction between complementary reactants NaNbO₃ and KNbO₃, after which oriented grain growth proceeds at a relative density of more than 90%. In addition, the results of transmission electron microscopy observation showed that textured KNN ceramics have a unique pectinate-like domain structure with domain walls consisting of {101} planes.     

Microstructure and Piezoelectric Properties of (1−x)(Na0.5K0.5)NbO3–xLiNbO3 Ceramics

(1− x )(Na_0.5K_0.5)NbO₃– x LiNbO₃ [(1− x )NKN– x LN] ceramics were produced by the conventional solid-state sintering method, and their microstructure and piezoelectric properties were investigated. The formation of the liquid phase and K₆Li₄Nb₁₀O₃₀ second phase that were observed in the (1− x )NKN– x LN ceramics was explained by the evaporation of Na₂O during the sintering. A morphotropic phase boundary (MPB) was observed in the specimens with 0.05< x <0.08. Promising piezoelectric properties were obtained for the specimens with x =0.07. Therefore, the piezoelectric properties of this 0.93NKN–0.07LN ceramic were further investigated and were found to be influenced by their relative density and grain size. In particular, grain size considerably affected the d ₃₃ value. Two-step sintering was conducted at different temperatures to increase the grain size. Piezoelectric properties of d ₃₃=240 (pC/N) and k _p=0.35 were obtained for the 0.93NKN–0.07LN ceramics sintered at 1030°C and subsequently annealed at 1050°C.     

Ferroelectric and Piezoelectric Properties of Fine-Grained Na0.5K0.5NbO3 Lead-Free Piezoelectric Ceramics Prepared by Spark Plasma Sintering

Lead-free piezoelectric ceramics have received attention because of increasing interest in environmental protection. Niobate ceramics such as NaNbO₃ and KNbO₃ have been studied as promising Pb-free piezoelectric ceramics, but their sintering densification is fairly difficult. In the present study, highly dense Na_0.5K_0.5NbO₃ ceramics were prepared using spark plasma sintering (SPS). Although the SPS temperature was as low as 920°C, the density of the Na_0.5K_0.5NbO₃ solid solution ceramics was raised to 4.47 g/cm³ (>99% of the theoretical density). After post-annealing in air, reasonably good ferroelectric and piezoelectric properties were obtained in the Na_0.5K_0.5NbO₃ ceramics with submicron grains. The crystal phase of the Na_0.5K_0.5NbO₃ has an orthorhombic structure. The Curie temperature is 395°C and the piezoelectric parameter ( d ₃₃) of the Na_0.5K_0.5NbO₃ ceramics reached 148 pC/N.     

Sintering and Electrical Properties of Lead-Free Na0.5K0.5NbO3 Piezoelectric Ceramics

Lead-free Na_0.5K_0.5NbO₃ (NKN) piezoelectric ceramics were fairly well densified at a relatively low temperature under atmospheric conditions. A relative density of 96%–99% can be achieved by either using high-energy attrition milling or adding 1 mol% oxide additives. It is suggested that ultra-fine starting powders by active milling or oxygen vacancies and even liquid phases from B-site oxide additives mainly lead to improved sintering. Not only were dielectric properties influenced by oxide additives, such as the Curie temperature ( T _c) and dielectric loss ( D ), but also the ferroelectricity was modified. A relatively large remanent polarization was produced, ranging from 16 μC/cm² for pure NKN to 23 μC/cm² for ZnO-added NKN samples. The following dielectric and piezoelectric properties were obtained: relative permittivity ɛ ^T ₃₃/ɛ ₀ =570–650, planar mode electromechanical coupling factor, k _p=32%–44%, and piezoelectric strain constant, d ₃₃=92–117 pC/N.     

Microstructure, Piezoelectric, and Ferroelectric Properties of Bi2O3-Added (K0.5Na0.5)NbO3 Lead-Free Ceramics

Lead-free piezoelectric (K_0.5Na_0.5)NbO₃– x wt% Bi₂O₃ ceramics have been synthesized by an ordinary sintering technique. The addition of Bi₂O₃ increases the melting point of the system and improves the sintering temperature of (K_0.5Na_0.5)NbO₃ ceramics. All samples show a pure perovskite phase with a typical orthorhombic symmetry when the Bi₂O₃ content <0.7 wt%. The phase transition temperature of orthorhombic–tetragonal ( T _{O − T} ) and tetragonal–cubic ( T _C) slightly decreased when a small amount of Bi₂O₃ was added. The remnant polarization P _r increased and the coercive field E _c decreased with increasing addition of Bi₂O₃. The piezoelectric properties of (K_0.5Na_0.5)NbO₃ ceramics increased when a small amount of Bi₂O₃ was added. The optimum piezoelectric properties are d ₃₃=140 pC/N, k _p=0.46, Q _m=167, and T _C=410°C for (K_0.5Na_0.5)NbO₃–0.5 wt% Bi₂O₃ ceramics.     

Phase Structure and Electrical Properties of (K0.48Na0.52)(Nb0.95Ta0.05)O3-LiSbO3 Lead-Free Piezoelectric Ceramics

(1− x )(K_0.48Na_0.52)(Nb_0.95Ta_0.05)O₃– x LiSbO₃ [(1− x )KNNT− x LS] lead-free piezoelectric ceramics were prepared by the conventional solid-state sintering method. A morphotropic phase boundary (MPB) between orthorhombic and tetragonal phases was identified in the composition range of 0.03< x <0.05. The ceramics near the MPB exhibit a strong compositional dependence and enhanced electrical properties. The (1− x )KNNT– x LS ( x =0.04) ceramics exhibit good electrical properties ( d ₃₃=250 pC/N, k _p=45.1%, k _t =46.3%, T _c=348°C, T _{o − t} =74°C, P _r=25.9 μC/cm², E _c=10.7 kV/cm, ɛ_r∼1352, tan δ∼3%). These results show that (1− x )KNNT– x LS ceramic is a promising lead-free piezoelectric material.     

Influence of Sintering Temperature on Grain Growth and Phase Structure of Compositionally Optimized High-Performance Li/Ta-Modified (Na,K)NbO3 Ceramics

Microstructure characteristics, phase transition, and electrical properties of (Na_0.535K_0.485)_0.926Li_0.074(Nb_0.942Ta_0.058)O₃ (NKN-LT) lead-free piezoelectric ceramics prepared by normal sintering are investigated with an emphasis on the influence of sintering temperature. Some abnormal coarse grains of 20–30 μm in diameter are formed in a matrix consisting of about 2 μm fine grains when the sintering temperature was relatively low (980°C). However, only normally grown grains were observed when the sintering temperature was increased to 1020°C. On the other hand, orthorhombic and tetragonal phases coexisted in the ceramics sintered at 980°–1000°C, whereas the tetragonal phase becomes dominant when sintered above 1020°C. For the ceramics sintered at 1000°C, the piezoelectric constant d ₃₃ is enhanced to 276 pC/N, which is a high value for the Li- and Ta-modified (Na,K)NbO₃ ceramics system. The other piezoelectric and ferroelectric properties are as follows: planar electromechanical coupling factor k _p=46.2%, thickness electromechanical coupling factor k _t=36%, mechanical quality factor Q _m=18, remnant polarization P _r=21.1 μC/cm², and coercive field E _c=1.85 kV/mm.     

K/Na Ratio Dependence of the Electrical Properties of [(KxNa1−x)0.95Li0.05](Nb0.95Ta0.05)O3 Lead-Free Ceramics

[(K _x Na_{1− x} )_0.95Li_0.05](Nb_0.95Ta_0.05)O₃ (K _x NLNT) ( x= 0.40–0.60) lead-free piezoelectric ceramics were prepared by conventional solid-state sintering. The effects of K/Na ratio on the dielectric, piezoelectric, and ferroelectric properties of the K _x NLNT ceramics were studied. The experimental results show that the electrical properties strongly depend on the K/Na ratio in the K _x NLNT ceramics. The K _x NLNT ( x =0.42) ceramics exhibit enhanced properties ( d ₃₃∼242 pC/N, k _p∼45.7%, k _t∼47%, T _c∼432°C, T _o−t =48°C, ɛ_r∼1040, tanδ∼2.0%, P _r∼26.4 μC/cm², E _c∼10.3 kV/cm). Enhanced electrical properties of the K _x NLNT ( x =0.42) ceramics could be attributed to the polymorphic phase transition near room temperature. These results show that the K _x NLNT ( x =0.42) ceramic is a promising lead-free piezoelectric material.     

Microstructure and Piezoelectric Properties of 0.95(Na0.5K0.5)NbO3–0.05SrTiO3 Ceramics

The 0.95(Na_0.5K_0.5)NbO₃–0.05SrTiO₃ (0.95NKN–0.05ST) ceramics formed in this study had a porous microstructure with small grains and low piezoelectric properties due to their low density. However, when a small amount of Na₂O was intentionally subtracted from the 0.95NKN–0.05ST ceramics, a liquid phase was formed, which led to increased density and grain size. Piezoelectric properties were also improved for the Na₂O-subtracted 0.95NKN–0.05ST ceramics. The increased density and grain size were responsible for the enhancement of the piezoelectric properties. In particular, the 0.95(Na_0.49K_0.5)NbO_2.995–0.05ST ceramics showed high piezoelectric properties of d ₃₃=220, k _p=0.4, Q _m=72, and ɛ₃^T/ɛ_o=1447, thereby demonstrating their promising potential as a candidate material for application to lead-free piezoelectric ceramics.     

Properties of Modified Lead Zirconate Titanate Ceramics Prepared at Low Temperature (800°C) by Hot Isostatic Pressing

High-density lead zirconate titanate (PZT) ceramics were fabricated for the first time at a temperature as low as 800°C via the hot isostatic pressing (HIP) of a PZT powder with a modified composition of 0.92Pb(Zr_0.53Ti_0.47)O₃—0.05BiFeO₃—0.03Ba(Cu_0.5W_0.5)O₃ that contained 0.5 mass% MnO₂. The resultant PZT ceramics exhibited a microstructure that was denser and finer than that of PZT sintered at 935°C, which is the lowest temperature for the densification of the same composition via normal sintering. The relevant dielectric and piezoelectric properties of the HIPed PZT ceramics were as follows: coefficient of electromechanical coupling ( K ₃₁), 31.8%; mechanical quality factor ( Q _m), 1364; piezoelectric constant ( d ₃₁), −73.7 × 10⁻¹² C/N; relative dielectric constant (ɛ₃₃^T/ɛ₀), 633; dielectric loss factor (tan δ), 0.5%; Curie temperature ( T _c), 285°C; and density (ρ), 8.06 g/cm³. In addition to these reasonably good piezoelectric properties, the HIPed PZT exhibited better mechanical properties—particularly, higher fracture strength—than the normally sintered PZT.     

Microwave Dielectric Properties of CaTiO3-CaAl1/2Nb1/2O3 Ceramics Doped with Li3NbO4

The microwave dielectric properties of CaTi_{1− x} (Al_1/2Nb_1/2) _x O₃ solid solutions (0.3 ≤ x ≤ 0.7) have been investigated. The sintered samples had perovskite structures similar to CaTiO₃. The substitution of Ti⁴⁺ by Al³⁺/Nb⁵⁺ improved the quality factor Q of the sintered specimens. A small addition of Li₃NbO₄ (about 1 wt%) was found to be very effective for lowering sintering temperature of ceramics from 1450–1500° to 1300°C. The composition with x = 0.5 sintered at 1300°C for 5 h revealed excellent dielectric properties, namely, a dielectric constant (ɛ_r) of 48, a Q × f value of 32 100 GHz, and a temperature coefficient of the resonant frequency (τ_f) of −2 ppm/K. Li₃NbO₄ as a sintering additive had no harmful influence on τ_f of ceramics.     

Double Precursor Solution Coating Approach for Low-Temperature Sintering of [Pb(Mg1/3Nb2/3)O3]0.63[PbTiO3]0.37 Solids

Lead-based piezoelectric ceramics typically require sintering temperatures higher than 1000°C at which significant lead loss can occur. Here, we report a double precursor solution coating (PSC) method for fabricating low-temperature sinterable polycrystalline [Pb(Mg_1/3Nb_2/3)O₃]_0.63-[PbTiO₃]_0.37 (PMN–PT) ceramics. In this method, submicrometer crystalline PMN powder was first obtained by dispersing Mg(OH)₂-coated Nb₂O₅ particles in a lead acetate/ethylene glycol solution (first PSC), followed by calcination at 800°C. The crystalline PMN powder was subsequently suspended in a PT precursor solution containing lead acetate and titanium isopropoxide in ethylene glycol to form the PMN–PT precursor powder (second PSC) that could be sintered at a temperature as low as 900°C. The resultant d ₃₃ for samples sintered at 900°, 1000°, and 1100°C for 2 h were 600, 620, and 700 pm/V, respectively, comparable with the known value. We attributed the low sintering temperature to the reactive sintering nature of the present PMN–PT precursor powder. The reaction between the nanosize PT and the submicrometer-size PMN occurred roughly in the same temperature range as the densification, 850°–900°C, thereby significantly accelerating the sintering process. The present PSC technique is very general and should be readily applicable to other multicomponent systems.     

Phase Transitional Behavior and Piezoelectric Properties of Lead-Free (Na0.5K0.5)NbO3–(Bi0.5K0.5)TiO3 Ceramics

(1− x )(Na_0.5K_0.5)NbO₃–(Bi_0.5K_0.5)TiO₃ solid solution ceramics were successfully fabricated, exhibiting a continuous phase transition with changing x at room temperature from orthorhombic, to tetragonal, to cubic, and finally to tetragonal symmetries. A morphotropic phase boundary (MPB) between orthorhombic and tetragonal ferroelectric phases was found at 2–3 mol% (Bi_0.5K_0.5)TiO₃ (BKT), which brings about enhanced piezoelectric and electromechanical properties of piezoelectric constant d ₃₃=192 pC/N and planar electromechanical coupling coefficient k _p=45%. The MPB composition has a Curie temperature of 370°–380°C, comparable with that of the widely used PZT materials. These results demonstrate that this system is a promising lead-free piezoelectric candidate material.     

Microstructures and Piezoelectric Properties in the Li2O-Excess 0.95(Na0.5K0.5)NbO3–0.05LiTaO3 Ceramics

As a candidate for lead-free piezoelectric materials, Li₂O-excess 0.95(Na_0.5K_0.5)NbO₃–0.05LiTaO₃ (NKN–5LT) ceramics were developed by a conventional sintering process. The sintering temperature was lowered by adding Li₂O as a sintering aid. Abnormal grain growth in NKN–5LT ceramics was observed with varying Li₂O content. This grain-growth behavior was explained in terms of interface reaction-controlled nucleation and growth. In the 1 mol% Li₂O excess NKN–5LT samples sintered at 1000°C for 4 h in air, the electromechanical coupling factor and the piezoelectric constant of NKN–5LT ceramics were found to reach the highest values of 0.37 and 250 pC/N, respectively.     

Enhancing Electrical Properties in NBT–KBT Lead-Free Piezoelectric Ceramics by Optimizing Sintering Temperature

Conventional sintering of (Na_{1− x} K _x )_0.5Bi_0.5TiO₃ (abbreviated as NKBT x , x =18–22 mol%) lead-free piezoelectric ceramics was investigated to clarify the optimal sintering temperature for densification and electrical properties. Both sintered density and electrical properties were sensitive to sintering temperature; particularly, the piezoelectric properties deteriorated when the ceramics were sintered above the optimum temperature. The NKBT20 and NKBT22 ceramics synthesized at 1110°–1170°C showed a phase transition from tetragonal to rhombohedral symmetry, which was similar to the morphotropic phase boundary (MPB). Because of such MPB-like behavior, the highest piezoelectric constant ( d ₃₃) of about 192 pC/N with a high electromechanical coupling factor ( k _p) of about 32% were obtained in the NKBT22 ceramics sintered at 1150°C.