86CrMOV7钢动态再结晶行为

用THERMECMASTOR－Z热模拟试验装置研究了86CrMoV7钢热变形时奥氏体的动态再结晶行为，结果表明，在较高温度条件下，动态再结晶为晶界形核长大机制；在较低温度时，由于碳化物的动态析出，动态软化机制向亚晶独立形核再结晶及动态回复转变。其转析温度约在970－1000℃之间，在此温度上下，变形激活能亦不同，在1050℃以上热变形激活能为386kJ/mol，在950℃以下变形时激活能为452kJ/mol。     

稀土Ce对T91钢高温塑性变形和动态再结晶的影响

为了研究含0. 016%稀土Ce的T91钢的高温变形行为,采用Gleeble-1500D热模拟机进行热圧缩测试,测定该材料在变形温度T为1 100～1 250℃和应变速率为0. 5～5. 0 s-1时变形的应力-应变曲线,采用ZenerHollomon参数法构建高温塑性变形的本构方程,然后计算材料的能量耗散图,并且对高温变形组织在光学显微镜下进行研究。结果表明:添加稀土Ce的T91钢的应力-应变曲线没有出现双峰特性,存在动态再结晶现象;通过流变应力模型计算的热变形激活能为559. 46 k J·mol-1,说明稀土Ce的添加增加了T91钢的热变形激活能;结合能量耗损图和微观组织可知,稀土Ce推迟了T91钢的动态再结晶过程,在高温和小应变速率下,动态再结晶容易发生。     

钒对直接切削用非调质钢动态再结晶的影响

 在Gleeble-3800热模拟试验机上进行热变形试验,研究不同钒质量分数的直接切削用非调质钢在变形温度为950～1 150 ℃,应变速率为0.1～10 s-1,变形量为60%的单道次压缩的奥氏体再结晶过程,计算得出V1钢的动态再结晶激活能[Qd]比V2钢提高了79.617 kJ/mol,增加钒质量分数具有抑制奥氏体动态再结晶发生的作用。根据试验模拟结果并结合实际生产情况,确定V1钢和V2钢最佳的热加工工艺参数。     

T91钢的高温塑性变形及动态再结晶行为

采用Gleeble-1500热模拟试验机进行了T91钢的压缩试验,研究了变形温度为1100~1250℃、应变速率为0.01~1 s^-1时该钢的变形行为,分析了流变应力与应变速率和变形温度之间的关系,计算了高温变形时应力指数和变形激活能,并采用Zener-Hollomon参数法构建该钢高温塑性变形的本构关系,绘制了动态再结晶图和热加工图.结果表明:在试验变形条件范围内,其真应力-真应变曲线呈双峰特征;钢中发生了明显的动态再结晶,且再结晶类型属于连续动态再结晶.T91钢的热变形激活能为484 kJ.mol^-1,利用加工图确定了热变形的流变失稳区,结合力学性能,可以优先选择的变形温度为1200~1 250℃,应变速率不高于0.1 s^-1.     

稀土元素对Al-Zn-Mg合金动态再结晶行为的影响

本文通过在透射电子显微镜下对比观察Al-Zn-Mg-RE和Al-Zn-Mg两种合金的动态再结晶现象,发现在其各自的最佳超塑性条件下,Al-Zn-Mg合金的动态再结晶晶粒随着应变的增加而粗化,而Al-Zn-Mg-RE合金在超塑变形的过程中随形变量的增加其晶粒反而细化。从而使Al-Zn-Mg-RE合金的超塑性大大优于Al-Zn-Mg合金。并分析了稀土元素细化Al-Zn-Mg合金动态再结晶晶粒并改善其超塑性的机理。     

钒质量分数对S30432钢回复再结晶行为的影响

采用Gleeble-3500热模拟机,对低质量分数钒和高质量分数钒的S30432耐热钢在900～1100℃及0.001～0.100 s-1变形条件下进行了热压缩试验,研究钒的质量分数对S30432钢动态回复再结晶的影响及作用机理。结果表明,添加质量分数0.18%钒后S30432钢的峰值流变应力增高,再结晶激活能从498增加到562 kJ/mol。在1000和1050℃,钒对S30432钢的动态回复再结晶的阻碍作用最显著。高质量分数钒的S30432钢中由于析出细小的Z相,它具有强烈钉扎作用,能有效阻碍动态回复再结晶的发生。此外,高质量分数钒钢中固溶原子的增加对动态回复再结晶也有一定的阻碍作用。     

稀土对微合金钢奥氏体再结晶行为的影响

设计了系列热模拟压缩实验,通过对热变形后的实验钢进行保温,结合理论计算,分析了等温过程稀土对奥氏体再结晶组织演变的影响规律。结果表明,随着保温时间的延长,再结晶晶粒不断粗化长大,含有稀土元素的实验钢在再结晶后期晶粒长大速度显著加快。基于变形储能和钉扎力对再结晶晶粒长大驱动力的影响分析,讨论了理论计算预测结果与实际晶粒变化情况的关系,预测分析与实验观察结果均显示,在再结晶保温初期,实验钢晶粒长大并不明显,40 s后晶粒迅速长大,其中含有稀土的实验钢晶粒长大更为明显。     

AH60C高强钢热变形下动态再结晶行为研究

采用Gleeble-3800热模拟机进行单道次压缩试验,研究了AH60C高强钢在变形温度850℃、950℃、1050℃,应变速率0.1 s^-1、1s^-1、10s^-1条件下的动态再结晶行为。采用Zener-Hollomon参数的正弦函数计算出材料参数值α、n、A以及AH60C高强钢热变形激活能Q,并且利用加工硬化原理来计算动态再结晶临界条件。结果表明:随着变形温度的升高,流变应力降低,随着应变速率的增大,流变应力增大,并且变形温度越高,应变速率越低,动态再结晶越彻底;计算出的AH60C高强钢热变形激活能Q为293 305.163 J/mol;临界应变随着变形温度的升高而降低,随着应变速率的增大而增大,且在本次试验条件下,AH60C高强钢动态再结晶临界应变预测模型为ε_c=3.04×10⁽(-4))Z^{1.889 75}。     

钒对低碳钢动态再结晶的影响规律研究

为研究钒对低碳钢动态再结晶的影响规律,选取4种对比成分的钒氮微合金化钢,测量动态再结晶的流变应力曲线,获得了峰值应力σ_p、应变速率ε及变形温度T的对应关系,分析了变形温度、V及N含量对流变应力曲线的影响。建立了钒氮微合金化钢及对比钢的热变形动态再结晶Avrami模型,回归得到其动态再结晶名义激活能。结果表明:V对动态再结晶临界温度提高有限,V和N复合后对动态再结晶临界温度提高明显,延迟再结晶能力增强。     

贝氏体非调质紧固件用钢动态再结晶行为分析

 为研究贝氏体非调质紧固件用钢的动态再结晶行为,在Gleeble-3500热模拟试验机上进行了单道次压缩试验,并分析了压缩变形应力-应变曲线。研究表明,奥氏体热变形激活能较一般C-Mn钢要高,为427.065kJ/mol;再结晶开始时间与温度曲线在1000℃左右出现明显的转折点,温度低于1000℃时,动态再结晶发生困难。     

Effect of rare earths on oxidation resistance of heat resistant steel

The application of rare earths(RE) in the Ni saving heat resistant steel was studied by metalloscopy,scanning electron microscopy(SEM),energy dispersive spectrometer(EDS),X-ray difference(XRD).Because the diffusion of chromium was promoted by RE,a dense and adhesive Cr2O3 layer could form rapidly at the early oxidation stage,which played a effective protection role;the pinning effect of silicon dioxide was enhanced by RE in the internal oxidation layer,which had a block effect on the diffusion of metal ions and oxygen ions at later stage of oxidation and resulted in that the high temperature oxidation rate of RE heat resistant steel was decreased.     

Influence of rare earths on eutectic carbides in AISI M2 high speed steel

The effect of rare earths on the morphology and microstructure of eutectic carbides in M2 high speed steel was studied. The results showed that rare earths promoted the formation of fishbone-like M6C eutectic carbides, compared to plate-like M2C carbides in ingots without modification. The formation of M6C was expected to be caused by rare earth inclusions which acted effectively as the substrate for nucleation of M6C carbides during solidification. M2C and M6C eutectic carbides exhibited different stability during heating. M2C eutectic carbides were much less stable than M6C carbides, and decomposed at high temperatures, favoring the spheroidization and refinement of carbides in high speed steels.     

铌含量对低碳微合金钢回复再结晶行为的影响

采用应力松弛实验研究了低C含Nb微合金钢奥氏体热变形过程中的析出及再结晶动力学过程,通过实验及理论模型分析了析出/溶质拖曳对回复和再结晶行为的影响.结果显示:随Nb含量的增加,析出动力学曲线的鼻尖温度上升,但鼻尖温度对应的时间变化不大,约为20~30s;析出可明显抑制再结晶的发生,增加Nb含量将使非再结晶温度升高;Nb溶质通过拖曳作用阻碍晶界运动,减小了晶界迁移率,最终减慢再结晶过程的发生;对于低C含Nb实验钢,拟合得到再结晶激活能与Nb质量分数的0.5次方成正比.     

铌对低温取向硅钢初次再结晶行为的影响

以含铌取向硅钢铸坯低温加热制备高磁感取向硅钢为研究目标,通过研究铌对低温取向硅钢初次再结晶行为的影响,达到获得有利于二次再结晶发展的初次再结晶组织目的,采用OM和EBSD技术主要对比了 0.055％铌和不含铌对低温取向硅钢中间退火板的初次再结晶组织、织构和晶界特征的影响.结果表明,铌的加入,使硅钢基体中形成了细小弥散的...     

Influence of adding various rare earths on microstructures and corrosion resistance of chromizing coatings prepared via pack cementation on P110 steel

In order to improve the corrosion resistance and increase the service lifetime of P110 steel during operation,four chromizing coatings were formed onto its surface with/without addition of rare earths via pack cementation process.The surface morphologies and microstructures of the chromizing coatings were observed using scanning electron microscopy(SEM),and the phase constitutions were investigated by X-ray diffraction(XRD).Electrochemical corrosion behavior of the chromizing coatings in simulated oilfield ...     

GCr15轴承钢静态再结晶行为

在Gleeble-3800热模拟实验机上利用双道次热压缩的实验方法,获得了GCr15轴承钢在不同实验条件下的应力-应变曲线,研究了该钢种在高温变形道次间隔时间内的静态软化行为以及再结晶规律,模拟材料热加工组织性能,为制定合理的轧制工艺提供实验基础和理论依据。分析了变形温度、应变速率和道次间隔时间对其静态再结晶行为的影响,建立了GCr15钢静态再结晶动力学模型,相应的静态再结晶激活能约为118.72kJ/mol。结果表明:静态再结晶体积分数随变形温度的升高、应变速率的提高或道次间隔时间的延长而增大。     

钇基稀土对E36钢板显微组织及冲击性能的影响

运用扫描电镜及能谱等分析手段研究了钇基稀土对E36钢中夹杂物的变质作用以及对显微组织和冲击性能的影响.研究表明,钇基稀土改善了E36钢的显微组织,减少了珠光体的片间距和含量.加入钇基稀土后,E36钢的冲击断口由典型的解理断口变为准解理+韧窝型断口,韧窝中细小球状的稀土夹杂是其转变的主要原因.加入少量的钇基稀土显著改善了E36钢的冲击韧性,尤其是低温冲击性能.在-60℃情况下,E36Re钢的纵向冲击功较E36钢提高了33.5%,横向冲击功提高了113.7%.并且,钇基稀土显著改善了E36钢纵横向冲击性能的差异性,未加稀土E36钢的纵、横冲击比均大于1.70,-60℃条件下达到2.77,而E36Re钢的纵、横冲击比为1.51~1.73.     

904L不锈钢动态再结晶行为

采用单道次热压缩试验,研究了904L钢在不同变形温度、不同应变速率下的真应力-应变曲线以及组织形貌,阐明了热加工过程中热变形参数对其在变形过程中发生的动态再结晶行为及微观组织演变规律的影响,揭示了其相应的软化机制。结果表明:变形温度越高,流变应力越小,动态再结晶体积分数越高,晶粒尺寸越大;同温度下,变形速率越小,应力峰值越小,晶粒尺寸越大且晶界越平直化;904L钢的动态再结晶行为随着变形温度的升高,应变速率的减小,应变量的增大而进行得越充分且较高的变形温度有利于动态再结晶的进行。