预备热处理对AMS 6308钢组织及性能的影响

 采用SEM、TEM和力学性能测试等手段,研究了预备热处理对AMS 6308钢组织及性能的影响。结果表明,980 ℃以下正火,随着温度的提高,M6C碳化物逐渐溶解,晶粒细小,淬火后马氏体板条均匀细小,碳化物呈球状或椭球状弥散分布在板条界和晶界上,碳化物体积分数和位错密度较高,强度和冲击值逐渐增加。980 ℃以上正火,M6C碳化物溶解增多,晶粒开始长大,淬火后马氏体板条束尺寸也长大,碳化物体积分数和位错密度下降,强度和冲击值降低。推荐的预备热处理制度：正火温度为980～1 010 ℃,回火温度为680～700 ℃,经性能热处理后,AMS 6308钢体现出良好的强韧性匹配。     

热处理对Q1030钢的亚结构及析出物的影响机理

Q1030钢是低合金高强钢。利用两相区轧制的方式,再经过淬火和回火处理后,力学性能有了较大的提高。经分析得出,200℃回火后,低于5°的小角度晶界频率比较多;经400℃回火后,θ-碳化物沿着马氏体的{112}面析出和{111}面析出,在马氏体板条内呈梭子状弥散分布,对马氏体内位错起到有效的钉扎作用,从而阻碍了位错的运动和螺纹的扩展。此外,200℃到400℃回火后,屈服强度、延伸率和屈强比与淬火态的相比都明显升高,但抗拉强度变化不明显。     

回火温度对1500MPa级直接淬火钢组织与性能的影响

设计了一种新型1500MPa级Si-Mn-Cr-Ni-Mo多组元系低合金、超高强度工程结构钢,研究了回火温度对直接淬火钢组织与力学性能的影响.结果表明,抗拉强度随回火温度的升高而不断降低,屈服强度随回火温度升高先升高后下降,延伸率和冲击功均随回火温度升高呈现先升高、后降低、再升高的变化趋势.分析认为,回火过程组织演变的物理机制一方面包括板条马氏体和位错亚结构的回复、再结晶软化过程,另一方面包括残余奥氏体的分解与马氏体中过饱和碳的脱溶及析出第2相的强化机制综合作用.250℃回火后,板条马氏体内析出ε碳化物;400℃回火后ε碳化物明显粗化,产生回火脆性;600℃回火后部分析出相在奥氏体中形核,在马氏体基体内长大和粗化,最终形态为近似球形,另一部分析出相在马氏体内形核、生长,呈现椭球形或矩形.     

回火温度对不同自回火程度的中碳马氏体钢组织和拉伸性能的影响

为探究不同自回火程度的中碳马氏体钢在回火过程中的组织演化及其对材料力学性能的影响，采用水淬与油淬2种方式淬火，研究了2种自回火程度存在明显差异的马氏体组织在不同回火温度区间内的组织演化，并对比分析了2种淬火态及回火后板料的拉伸性能。结果表明：在淬火及低温回火过程中，马氏体组织内析出的ε-碳化物会明显改善材料的塑韧性。水淬马氏体组织中的ε-碳化物是在温度为200℃的回火过程中析出。油淬马氏体组织中的ε-碳化物则是在淬火过程中析出，而在低温回火过程中，淬火态组织中的亚稳ε-碳化物会发生分解。当回火温度为300和400℃时，2种淬火态组织的演化依次为残余奥氏体的分解以及渗碳体的形成，马氏体组织中的位错密度均逐渐降低。     

406钢回火过程的初步探讨

通过透射电镜观察和鉴别了406钢在回火过程中的力学性能变化规律和马氏体精细结构特征,碳化物种类、形态、分布及它们之间的关系。结果表明:406钢淬火并300℃回火后具有较高的强度和韧性,是高位错密度的板条马氏体和马氏体内大量的与基体高度共格的ε-碳化物弥散析出,及马氏体板条周围2～3％的残留奥氏体网状薄膜的贡献。同时钢中含有1.5％Si和0.5％Mo,提高了ε-碳化物和残留奥氏体的稳定性,从而推迟并减缓了马氏体回火脆性凹,改善了断裂形貌。360～500℃回火脆性是由于渗碳体在板条边界析出和杂质元素在晶界偏聚的结果。     

高钴,镍超高强度钢的二次硬化行为

利用透射电子显微术（ＴＥＭ）研究了一种高钴、镍超高强度钢不同时效温度下的碳化物的析了过程及钢的二次硬化机制。研究结果表明，马氏体板条内和板条间开始析出合金碳化物Ｍ２Ｃ的初始回火温度为４００℃左右；４４０℃温度回火钢的二次硬化行为是由于合金碳化物Ｍ２Ｃ对尚未回复和再结晶的位错型马氏体板条弥散强化的结果；６５０℃过时效后在钢的回火组织中还发现了一种正交结构的碳化物相，其点阵常数α＝０．４４８ｎｍ，ｂ＝     

25Co15Ni11Cr2MoE钢回火过程中析出相的演变规律

采用透射电子显微镜(TEM)和X射线衍射仪(XRD)等试验方法对一种高Co-Ni二次硬化钢25Co15Ni11Cr2MoE淬火后经300~660℃温度范围回火后析出的合金碳化物和韧化相逆转变奥氏体的析出演变规律进行系统研究。结果表明:25Co15Ni11Cr2MoE经300~660℃温度范围回火后,随回火温度升高,钢中析出的合金碳化物依次为:弥散的ε-碳化物→片状的合金渗碳体→弥散的M2C碳化物→粗化的M23C6碳化物。经495℃回火后,钢中板条马氏体基体上析出大量细小弥散的M2C碳化物,回火早期析出的粗大片状渗碳体全部回溶,并在马氏体板条间析出薄膜状韧化相逆转变奥氏体。回火温度提高至530℃后,逆转变奥氏体含量继续增加,但其形貌逐渐由薄膜状转变为条、块状,回火温度提高到600℃时,钢中的逆转变奥氏体含量达到极大值。     

回火温度对07MnMoVR钢微观组织的影响

研究了07MnMoVR钢910℃保温1 h淬火后,不同的回火温度对微观组织的影响。试验钢在回火过程中伴随着铁素体回复与再结晶及碳化物的聚集长大。回复过程中板条贝氏体板条合并,位错密度降低,并重新排列形成条状或网状分布。当回火温度高于600℃时,铁素体再结晶形成位错密度很低的等轴铁素体取代淬火组织中的板条铁素体晶粒。析出的碳化物逐渐与铁素体脱离共格关系而迅速聚集长大并粗化。本文对07MnMoVR钢在不同回火温度下贝氏体转变、残余奥氏体的分解和碳化物的转变等规律的研究结果,为现场制定合理的回火工艺制度提供了重要的理论依据。     

回火对C-Si-Mn系双相钢组织与性能的影响

在实验室研究了回火温度对C-Si-Mn双相钢力学性能与显微组织的影响.力学性能测定结果表明,250℃以下的低温回火,对改善双相钢的伸长率具有良好作用,但是其它力学性能的变化不明显.高于300℃的高温回火对改善双相钢的延性作用不大,但会引起双相钢的屈服强度升高,抗拉强度、加工硬化与烘烤硬化值降低,使双相钢性能恶化.扫描电镜与透射电镜的观察结果表明,低温回火双相钢的显微组织变化不明显,马氏体为板条状,马氏体前沿的铁素体基体中分布着大量的可动位错,高温回火双相钢的显微组织则有较大变化,马氏体分解,边界变得模糊,岛内出现碳化物颗粒,铁素体中的位错密度减小,位错线附近出现粗大的析出物.高温回火后,马氏体的分解软化以及铁素体中位错密度减小是导致双相钢性能恶化的主要原因.     

加热温度对热成形中锰钢氢脆敏感性的影响

对0.1C–5Mn中锰钢在不同温度(850、950和1000℃)加热后进行热成形处理,利用电化学预充氢、慢应变速率拉伸及氢渗透实验等研究了加热温度对其氢脆敏感性的影响.结果表明,试验钢在不同温度加热后进行热成形处理,其组织全部为马氏体,同时因自回火而生成一定量的ε-碳化物,且随着加热温度的升高,原奥氏体晶粒尺寸增加,而试验钢的强度和塑性逐渐降低.当加热温度为850℃时获得了较好的强度与塑性配合,强塑积为22 GPa·%.随着加热温度升高,充氢样中的可扩散氢含量明显降低而非可扩散氢含量有所增加,而以相对缺口抗拉强度损失表征的氢脆敏感性指数及有效氢扩散系数呈现先升高后显著降低的变化趋势,当加热温度为1000℃时,氢脆敏感性最低.进一步断口分析表明,试验钢充氢断口起裂区均为沿着原奥氏晶界的沿晶断裂.试验钢的这种氢脆断裂行为主要与热成形中锰钢的强度水平及自回火析出的ε-碳化物有关.与常用的传统热成形钢22MnB5相比,试验钢的氢脆敏感性较高,这主要与其M_s点(马氏体转变开始温度)较低而使得自回火程度较低等有关.     

回火温度对Cu-Cr-Ti马氏体耐磨钢组织及强韧性的影响

摘要：矿山机械用耐磨钢构件服役环境恶劣而常常出现磨损失效,研究适用于复杂工况下的高耐磨钢成分、工艺与组织性能的关系,有利于提高耐磨构件的服役寿命并降低经济损失。利用SEM、TEM、洛氏硬度计、万能拉伸试验机及冲击试验机等,研究了160～400℃不同回火温度下Cu-Cr-Ti马氏体耐磨钢的组织形貌、强度硬度及-20℃冲击韧性的变化。结果表明,试验钢淬火态组织主要为板条马氏体,当回火温度为160℃时,马氏体板条依然清晰,但随回火温度升高到400℃,马氏体板条界渐渐消失,基体中出现大量片状或粒状渗碳体。EDS分析发现样品钢基体中含有纳米级Ti、Nb的碳氮化物。随回火温度升高,基体组织演变导致强化机制发生变化,回火温度为300℃,综合力学性能最佳,其抗拉强度为1500MPa,屈服强度1100MPa,伸长率为15.5%。随回火温度升高,-20℃冲击韧性由60J/cm2逐渐降低到36.3J/cm2。     

Relationship Among Microstructure and Properties and Heat Treatment Process of Ultra-High Strength X120 Pipeline Steel

 The variation of heat treatments including directed quenching and tempering off-line after controlled rolling (DQT) and quenching off-line and tempering off-line after controlled rolling (RQT) with microstructure and mechanical properties of a low-carbon microalloyed steel was compared and analyzed. For DQT, the quenched steel was obviously banded microstructure, with increasing tempering temperature, lath martensite coarsened, the cusp carbide precipitated at grain boundaries, the yield strength fluctuated slightly, and the fracture-separation was obvious. The impact toughness was better in the steel tempered at 500 ℃ for 1 h. In RQT, with increasing tempering temperature, lath martensite degenerated, intragranular and intergranular finer precipitations with smaller than 30 nm precipitated and grew up and were distributed dispersedly, the stripe-like carbides were distributed at grain boundaries, and the yield strength and tensile strengthen decreased obviously. The impact toughness of RQT process was much better than that of DQT process, and the comprehensive mechanical properties were better for the steel tempered at 500 ℃ for 1 h of RQT process.     

Influence of Heat Treatment Temperature on Micro-structure and Property of 00Cr13Ni5Mo2 Su-permartensitic Stainless Steel

The microstructural evolution and mechanical property of 00Cr13Ni5Mo2supermartensitic stainless steel(SMSS)subjected to different heat treatments were investigated.Room tensile tests,hardness tests,scanning electron microscopy,transmission electron microscopy and X-ray diffraction were conducted on the heat-treated steels.It is found that the microstructure of the heat-treated steel is composed of tempered lath martensite,retained austenite andδ-ferrite.The austenitizing temperature and tempering temperature have a significant effect on the microstructural changes,which leads to the complex variations of mechanical properties.The fine tempered lath martensite and more dispersed reversed austenite in the microstructure facilitate improving the comprehensive mechanical properties of the studied steel.The optimal heat treatment process of 00Cr13Ni5Mo2SMSS is obtained by austenitizing at 1 000℃for 0.5h+air cooling followed by tempering at 630℃for 2h+air cooling,where the excellent combination of tensile strength,elongation and hardness can be achieved.     

800MPa级水电用钢的微观组织和力学性能研究

采用控轧控冷与调质工艺相结合的方法,开发了一种力学性能满足要求的800 MPa级高强度水电用钢,并利用组织观察和性能测试手段研究了该水电用钢的显微组织和力学性能。结果表明：经调质处理后,该水电用钢的显微组织为回火索氏体＋回火马氏体,抗拉强度达880 MPa,断后延伸率为18.5%,40℃的冲击功为126 J。微观组织观察表明,该实验钢中碳化物在回火索氏体中分布均匀,在回火马氏体中主要分布在马氏体板条界处。     

直接淬火石油储罐用钢N610E的回火组织与力学性能

 N610E级石油储备罐用钢(12MnNiVR)常用加热调质处理工艺生产。利用OM、TEM等试验方法,研究了石油储罐用钢N610E直接淬火后,不同回火温度对组织和力学性能的影响。结果表明：直接淬火钢经655℃回火,钢板具有最佳综合力学性能,其抗拉强度640MPa,屈服强度570MPa,伸长率22%,－20℃冲击功273J,不同回火温度的N610E钢韧脆?湮露染冢?0℃以下。随回火温度的升高,板条贝氏体回复作用逐渐加强,位错通过运动、合并、重组,相邻板条合并,组织粗化;回火后钢的力学性能变化趋势的非单调性,归因于回火过程贝氏体中位错亚结构的回复软化与碳的脱溶及第二相的析出强化机制综合作用。     

22SiMn2TiB钢淬火与回火过程中的组织演变

以超高强度钢 22SiMn2TiB 为对象,研究了在淬火、回火和配分状态下组织的演变规律.采用光学金相显微镜(OM)、扫描电镜(SEM)和 X 射线衍射技术(XRD)研究了不同处理状态下组织的演变规律.实验表明,回火或配分温度低于 320 ℃,板条马氏体组织形貌没有明显变化,且不随回火和配分时间的变化而变化;在此温度以上进行配分,不论配分时间的长短,组织皆转变为回火组织.表明 320 ℃为该钢材的临界回火、配分温度.随着回火温度的升高,位错密度下降;且 320 ℃以下温度回火或配分,马氏体衍射峰的半峰宽 FWHM 只是略有减少,表明虽然板条马氏体的组织形貌没有明显变化,但板条内的位错密度和内应力降低.     

Influence of Tempering Process on Mechanical Properties of 00Cr13Ni4Mo Supermartensitic Stainless Steel

To investigate the influence of tempering process on microstructural evolutions and mechanical properties of 00Cr13Ni4Mo supermartensitic stainless steel(SMSS),specimens were tempered in the temperature range of 520-720 ℃ for 3 h followed by air cooling and an optimized tempering temperature was chosen to prolong holding time from 3 to 12 h.After heat treatments,microstructure examination was conducted by scanning electron microscope,X-ray diffraction examinations,hardness measurements and tensile tests.The results revealed that the superior mechanical properties were achieved by quenching at 1040 ℃ for 1 h+water cooling and tempering at 600 ℃ for 3 h+air cooling.Increasing isothermal tempering time could improve the toughness notably.It was believed that the property was correlated with the microstructure of tempered lath martensite and retained austenite.More retained austenite content is beneficial to the higher toughness of the SMSS.     

热处理工艺对海洋工程用高强度耐低温H型钢组织及性能影响

摘要：以热轧耐低温H型钢为研究对象,采用光学显微镜、扫描电镜、透射电镜分析和力学性能测试等手段,研究了完全淬火和亚温淬火对试验钢微观组织和力学性能的演变规律。结果表明,试验型钢经780℃亚温淬火+600℃回火处理后,形成回火索氏体+铁素体的网状组织;试验型钢900℃淬火+600℃回火处理后,转变得到具有马氏体位向的回火索氏体,碳化物分布更加细小均匀,位错密度下降。2种热处理工艺制备H型钢综合力学性能优良,屈服强度均达到500MPa以上,900℃淬火+600℃回火处理后钢的屈服强度和抗拉强度更高。-40℃低温冲击韧性比热轧状态下出现大幅度提高,随着淬火温度升高冲击功更加稳定。     

1800MPa级低合金超高强度工程机械用钢显微组织与力学性能

 设计了一种新型的超高强度工程机械用钢,在中试轧机上进行了不同工艺模拟轧制,对比研究了工艺1（80%变形量+直接淬火+250℃回火）、工艺2（90%变形量+层流冷却快冷至650℃/1h+空冷+250℃回火）和工艺3（90%变形量+空冷至650℃/1h+空冷+250℃回火）3种不同控轧控冷工艺对试验用钢的显微组织和力学性能的影响。结果表明：工艺1条件下试验钢的抗拉、屈服强度最高,塑韧性最好,分别可达到1816,1473MPa,伸长率为9.5%,断面收缩率为45%,室温冲击功为28J,-40℃冲击功为21J,硬度值达到50HRC,认为获得的是板条马氏体+残余奥氏体的复相组织和析出的复合微合金碳化物、ε-碳化物强韧化机制的综合作用;工艺2,3分别得到的是板条马氏体+块状贝氏体+残余奥氏体、板条马氏体+针状铁素体+片层状珠光体+残余奥氏体,力学性能下降明显;第二相析出物主要是Nb,V,Ti的复合析出颗粒。     

屈服强度785 MPa低碳含铜船板钢的组织和性能

 研究了一种屈服强度大于785 MPa的船板钢,测试了其动态连续冷却相变曲线（CCT）,研究了试验钢经控制轧制+直接淬火+回火（DQ- T）工艺处理后的组织性能。结果表明,直接淬火（DQ）钢板组织为板条马氏体（LM）,回火后铜、铌元素呈弥散析出。经500 ℃回火钢板的强度最高,冲击韧性（KV2）最低。钢板经710 ℃回火,其组织为二次马氏体（SLM）+铁素体,屈服强度（Re）为810 MPa,抗拉强度（Rm）为 1 066 MPa,伸长率（A）为17%,在-80 ℃下KV2为97 J,达到最佳强韧性匹配。