稀土对羊毛的抗菌及染色性能研究

研究将羊毛织物用稀土铈离子进行抗菌整理,探讨了各种工艺因素,如稀土金属离子浓度、温度、时间、pH值、交联剂等对Ce3 在羊毛织物上吸附量的影响,得到了Ce3 处理羊毛的最佳工艺条件.然后在最佳工艺条件下,用弱酸性染料对抗菌羊毛进行染色.结果表明:经Ce3 处理并染色后,羊毛对金黄色葡萄球菌和大肠杆菌的抗菌率均达到90%以上,断裂强力增大,染色速率和上染百分率都显著提高.     

稀土铈化合物对羊毛织物染色性能的影响

文章主要对稀土铈化合物在改善羊毛染色性能方面进行研究,通过实验探讨稀土铈化合物用量、染色温度和保温时间对羊毛染色上染百分率的影响,确定最佳染色工艺;探讨稀土铈化合物对羊毛低温染色性能的影响;对稀土染色羊毛织物的匀染性和各项色牢度进行测定分析.结果表明,染色浴中加入一定量的稀土铈化合物,可提高羊毛的上染百分率;在85℃较低染色温度下可获得理想的上染百分率;匀染性良好,皂洗牢度和耐摩擦色牢度满足使用要求.     

壳聚糖在羊毛表面的吸附性能研究

研究了将羊毛用壳聚精的醋酸溶液处理,探讨了各种处理条件对壳聚糖在羊毛纤维上吸附率的影响。结果表明：壳聚精浓度、溶液pH值以及羊毛表面性能对壳聚格吸附率的影响最大。     

壳聚糖在羊毛表面的吸附性能研究

研究了将羊毛用壳聚糖的醋酸溶液处理,探讨了各种处理条件对壳聚糖在羊毛纤维上吸附率的影响。结果表明：壳聚糖浓度、溶液ｐＨ值以及羊毛表面性能对壳聚糖吸附率的影响最大。     

稀土在活性染料染羊毛及抗菌整理中的应用

研究了用稀土Ce3 处理羊毛织物后,再用活性染料染色的新工艺.探讨了预处理及染色工艺条件对上染百分率的影响,确定了最佳预处理及染色工艺,并测定了染色羊毛的色牢度、断裂强力及抗菌性能.结果表明:羊毛经稀土Ce3 处理并染色后,各种染色性能优良,且具有一定的抗菌性.     

稀土Ce3+在羊毛染色及抗菌整理中的应用

研究了用稀土Ce3 对羊毛进行预处理,再用酸性媒介染料染色的新工艺.结果表明:羊毛织物经Ce3 处理并用酸性媒介染料染色后,染色性能好,实现了无铬或低铬染色的目的,使酸性媒介染料染色的皂洗牢度及染色上染百分率都得到了提高.经测试,稀土处理后的羊毛织物抗菌性能良好.     

叶绿素铜钠盐吸附羊毛织物的动力学研究

基于能上染绿色的天然染料很少,文章研究了叶绿素铜钠盐吸附羊毛织物的动力学过程。研究表明,在70～100℃染色温度范围内,叶绿素铜钠盐在染色初期上染羊毛速率很高,随着染色时间增加到20 min后,上染速率降低,60 min后上染百分率、织物上的染料量基本不变,上染达到平衡;叶绿素铜钠盐染后羊毛织物的颜色特征值表观深度与时间的关系与上染百分率趋势基本一致,当染色时间达到120 min后,织物K/S值不再随时间增加而提高;随着染色温度的提高,叶绿素铜钠盐上染羊毛的平衡上染百分率提高,扩散系数提高;准二级动力学模型能很好地描述叶绿素铜钠盐染羊毛织物的染色动力学,该吸附过程以化学吸附为主。     

羊毛纤维对Cu(Ⅱ)的吸附规律

从Cu2+初始摩尔浓度、溶液pH值、处理时间、处理温度以及羊毛纤维前处理工艺(丙酮处理、剥鳞处理、巯基乙酸处理)等因素人手,以吸附量为指标,研究了羊毛纤维对Cu2+的吸附规律.通过比较处理前后羊毛纤维的力学性能,分析处理后纤维的损伤情况,发现由于Cu2的进入,羊毛纤维的强力有所降低.通过傅里叶红外光谱对Cu2+—羊毛纤...     

羊毛纤维对Cu(Ⅱ)的吸附规律

从Cu2+初始摩尔浓度、溶液pH值、处理时间、处理温度以及羊毛纤维前处理工艺(丙酮处理、剥鳞处理、巯基乙酸处理)等因素入手,以吸附量为指标,研究了羊毛纤维对Cu2+的吸附规律。通过比较处理前后羊毛纤维的力学性能,分析处理后纤维的损伤情况,发现由于Cu2+的进入,羊毛纤维的强力有所降低。通过傅里叶红外光谱对Cu2+—羊毛纤维进行结构表征,探讨羊毛纤维对Cu2+的吸附结合位置,表明Cu2+主要与羊毛纤维中的—COO-发生结合。     

羊毛织物的生态防缩整理

研究和开发有利于环保的羊毛防缩加工技术、寻找无污染的整理剂成为羊毛防毡缩研究的发展趋势。文章就蛋白酶处理、等离子体技术、天然聚合物壳聚糖的应用、臭氧处理、液氨整理、纳米材料的应用进行了阐述和展望。     

毛织物机可洗整理

从羊毛的结构与性能出发,介绍了毛织物产生毡缩的原因,并探讨了毛织物机可洗整理的方法和机理,最后介绍了几种机可洗整理后的效果评价方法。     

引澳血细羊毛的主要性能分析

通过对内蒙古引澳血细毛羊与前苏联、澳大利亚美利国毛羊羊毛主要性能指标细度、长度、净毛率及净毛量的对比分析，说明了内蒙古自治区引血后改良羊羊毛的性能已接近澳美羊的中等水平，超过了前苏联细毛羊，可取代外毛，满足纺高支纱、生产高档精纺面料的要求。     

Microwave-Assisted Bleaching of Wool Fabrics

Microwave irradiation was used to reduce consumption of energy and time during bleaching of wool fabrics with hydrogen peroxide. The effect of some reaction conditions; viz. hydrogen peroxide concentration, treatment time, presence of stabilizer, on degree of whiteness imparted to bleached wool, was studied systematically. Comparative study between bleaching of wool using microwave irradiation and conventional heating was undergone. The effect of bleaching of wool on its morphological structure was assigned by scanning electron microscopy. The change in some chemical and physicomechanical characteristics of bleached wool was monitored; namely whiteness index, alkali solubility, wettability, critical surface area, tensile strength, and elongation at break, of the treated as well as untreated fabrics were measured. The microwave-assisted bleaching of wool resulted in improved degree of whiteness comparable to that is obtained using conventional heating method. However, the microwave-assisted bleached wool shows lower degree of deterioration than that of conventionally bleached wool. The COD and BOD of the wool bleaching effluents were determined.     

羊毛/仪纶混纺产品开发

文章介绍了仪纶纤维的特性,以适当的比例与羊毛混纺,开发短顺大衣呢、斜纹大衣呢等新型面料。对产品规格设计、短纤染色、和毛纺纱、织造上机、后整理等生产过程进行了探讨,对实际试制过程中遇到的问题及解决办法进行了阐述。通过评审测试,成品手感细腻柔软、亲肤舒适,主要物理指标符合GB/T 26378—2011《粗梳毛织品》质量标准要求。为仪纶纤维在新风格毛纺产品中的应用,降低成本,扩大市场空间提供了思路。     

五倍子染料的提取及其在羊毛织物上的染色性能研究

本文侧重以五倍子染料染得更深、牢度更好的毛织物为出发点,研究了五倍子染液的提取方法以及染色工艺参数对其染色效果的影响。结果表明,五倍子可选择在100℃提取,五倍子提取液在100℃沸水中能稳定存在2h,其耐酸较好,但耐碱性差;五倍子染料染毛织物的优化工艺为：铁离子媒染剂浓度7．5％（omf）,植物染料用量为50％（omf）,Ph4,染色温度100℃。     

毛织物在中国元素服装中的创新应用

为了提升中国元素服装市场竞争力,使中国原创服装档次进一步提升,同时使我国生产的毛织物用途更广泛。文章提出将毛织物应用于中国元素服装:结合实例从毛织物与中国元素相结合的设计、缂毛工艺的运用、毛织物和刺绣工艺的结合、毛织物面料的再塑造、毛织物的优良性能、毛织物的织物风格、视觉感受等方面研究了毛织物在中国元素服装中的创新应用。     

弹性体对蚕丝和丝／毛混纺织物折皱性影响

采用阳离子型、非离子型改性聚硅氧烷和阴离子型水溶性聚氨基甲酸乙酯磺酸盐等弹性体处理蚕丝、蚕丝和羊毛混纺织物,研究处理方法对织物折皱性、吸湿性和耐磨性的影响.采用“热板法”测定织物的折皱弹性;差热分析法(DSC)、扫描电镜(SEM)和酸碱水解法探明弹性聚合体提高蚕丝和丝/毛混纺织物折皱回复性的原因。     

羊毛蛋白溶液后整理对棉针织物性能的影响

经过羊毛蛋白溶液整理后的纯棉针织物的折皱弹性、耐磨性、顶破强力和毛细效应都得到了改善,而处理后织物的刚柔性、悬垂性和透气性变差。     

低温等离子体对羊毛织物防毡缩性能的影响

文章讨论了低温等离子体对羊毛织物防毡缩性能的影响,分析了低温等离子体处理时间和功率对羊毛织物的毡缩率及断裂强力的影响,比较了树脂整理与低温等离子对羊毛织物防毡缩性能的影响,得出了最佳工艺:处理时间:3 min,压强:1 MPa,处理功率100 W,树脂用量:40 g/L。