再生骨料缺陷对再生混凝土力学性能与渗透性的影响

对高、低2种水胶比(0.255和0.586)再生混凝土(RAC)的力学性能和渗透性进行试验研究.再生骨料由同样2种水胶比的原生混凝土破碎而成,采用热处理方法去除再生骨料(RA)表面附着砂浆,对骨料进行吸水率和压碎指标试验,对RAC和天然骨料混凝土(NAC)进行抗压强度、劈裂抗拉强度、断裂能和渗透性试验.结果表明,石子损伤和附着砂浆均对RA吸水率和压碎指标有显著影响;同配合比下,RAC的力学性能比NAC有明显降低;在低水胶比下,附着砂浆的去除导致RAC力学性能降低,但在高水胶比下,附着砂浆的去除则使RAC力学性能提高;在受压荷载作用下,RAC的氯离子渗透性与NAC有所不同,这可能是RA缺陷导致的,对其机理有待进一步研究.     

骨料缺陷对再生混凝土力学性能的影响

将2种普通混凝土破碎加工成再生粗骨料(RA),经620℃高温处理,剔除RA上的附着砂浆,得到再生粗骨料H-RA,然后配制再生骨料混凝土(RAC),测定其抗压强度、劈裂抗拉强度和断裂能.结果表明:RAC的力学性能显著下降,这归因于RA破碎加工导致的石子损伤及其表面的附着砂浆;在低水胶比条件下,RA中的石子损伤是导致RAC力学性能下降的主要因素,而在高水胶比条件下,导致RAC力学性能下降的主要因素则是石子表面的附着砂浆;吸水率与断裂能可敏锐反映RA的缺陷特征.     

再生骨料改性后对混凝土性能影响的试验研究

文章以3种粗骨料(粗骨料NA(natural aggregate)、普通再生粗骨料RA(recycled aggregate)、经掺入新材料(KA粉)的水泥浆液浸泡处理的再生粗骨料RA-KA)为研究对象,然后分别配制成混凝土NAC、RAC、RAC-KA,并测试在不同水胶比条件下(W/B=0.26与0.60)配置成的混凝土的力学性能,通过试验数据对比分析,26RAC-KA和26RAC对比发现,26RAC-KA的抗压强度、劈裂抗拉强度、断裂能和弹性模量都有所提高;60RAC-KA与60RAC对比发现,再生混凝土断裂能有较大提高,劈裂抗拉强度和弹性模量有小幅提高,但抗压强度略有下降。     

碱激发再生骨料纤维混凝土的工作性和力学性能研究

研究了碱激发剂浓度（2%、5%、8%）和再生粗骨料取代率（0、25%、50%、75%、100%）对PVA纤维混凝土坍落度、抗压强度、劈裂抗拉强度和轴心抗压强度的影响,建立了碱激发再生骨料纤维混凝土的力学指标换算式。结果表明：随着再生粗骨料取代率和碱激发剂浓度的增加,混凝土拌合物的坍落度降低;试件的抗压强度、劈裂抗拉强度和轴心抗压强度均随着再生粗骨料取代率的增加而减小,随着碱激发剂浓度的增加而增大;建立的抗压强度分别与劈裂抗拉强度和轴心抗压强度的换算式具有较高的拟合精度。     

不同取代率再生粗骨料混凝土的力学性能

采用人工破碎的方式,把某路面废弃的C25混凝土破碎后,参照普通混凝土配合比设计规范配制再生混凝土,设计了30个不同再生粗骨料取代率标准试块进行抗压强度和劈裂抗拉强度试验,并以普通混凝土为基准进行比较分析,试验结果表明:再生粗骨料的取代率为50%时,抗压强度相对较高;再生混凝土的劈裂抗拉强度与普通混凝土较为相似。     

再生废砖粗骨料混凝土基本力学性能研究

进行了再生废砖粗骨料混凝土基本力学性能的试验,主要研究了与普通混凝土强度等级相同条件下再生废砖粗骨料混凝土的立方体抗压强度、轴心抗压强度、劈裂抗拉强度、弹性模量。试验结果表明:再生砖粗骨料混凝土的立方体抗压强度、轴心抗压强度、劈裂抗拉强度、弹性模量均要低于普通混凝土,其主要原因可能为再生砖粗骨料强度较低;再生砖粗骨料混凝土的立方体抗压强度、轴心抗压强度和劈裂抗拉强度与普通混凝土的破坏形式相类似。     

再生混凝土基本力学性能试验研究

设计并完成了再生粗骨料已使用年限分别为0、10、40年和取代率分别为0、30%、50%、70%、100%的C30级再生混凝土的立方体抗压强度、劈裂抗拉强度和抗折强度相关试验,并以天然骨料混凝土作为基准进行对比分析.试验结果表明:再生混凝土立方体抗压强度、劈裂抗拉强度和抗折强度破坏过程和破坏形态与普通混凝土基本一致,在水灰比相同的情况下,再生混凝土立方体抗压强度高于普通混凝土,劈裂抗拉强度低于普通混凝土,抗折强度基本接近普通混凝土;另外,还表明再生粗骨料的寿命对再生混凝土强度有一定影响.     

再生混凝土力学性能试验研究

将收集的3种不同龄期来源的废弃混凝土制备成再生粗骨料(RA-Ⅰ、RA-Ⅱ、RA-Ⅲ ),利用正交试验设计选择合理的再生混凝土配合比,通过对不同取代率和不同使用寿命骨料再生混凝土(RAC)的抗压强度、劈裂抗拉强度和抗折强度进行了试验研究。研究结果表明:对于立方体、轴心抗压强度,在不同取代率的情况下均超过普通混凝土对应的强度;对于劈裂抗拉强度,RA-Ⅰ随着取代率的增加而相继增加,最大增幅达9.58%;RA-Ⅱ和RA-Ⅲ随着取代率的增加呈现先增加后降低的趋势;对于抗折强度,随着取代率的增加呈现先降低后持续增高的趋势。     

再生混凝土力学性能试验研究

通过对三种不同配合比的再生混凝土进行强度试验,研究了再生粗骨料取代率分别为0、40%、70%、100%时,再生混凝土的抗压强度与劈裂抗拉强度变化规律,提出了劈裂抗拉强度与抗压强度的关系式。研究结果表明,随着取代率的增大,混凝土抗压强度与劈裂抗拉强度均呈下降趋势,但当取代率为70%时,强度反而有一定上升。     

无机聚合物轻骨料混凝土基本力学性能试验研究

通过试验研究了无机聚合物轻骨料混凝土(Inorganic Polymer Lightweight Aggregate Concrete,简称IPLAC)的立方体抗压强度、劈裂抗拉强度、轴心抗压强度和弹性模量等力学性能,分析了水胶比、砂率、预吸水对无机聚合物轻骨料混凝土的力学性能和表观密度的影响。试验结果表明:水胶比大于0.38时,无机聚合物轻骨料混凝土抗压强度、劈裂抗拉强度、弹性模量随着水胶比的降低而增加,水胶比小于0.38时其影响不再明显;砂率存在最优砂率为40%;轻骨料经预吸水处理的无机聚合物轻骨料混凝土28 d抗压强度较高;本试验的无机聚合物轻骨料混凝土的表观密度为1 834~1 893 kg/m~3,比强度为18.21~23.57((N/m~2)/(g/m~3))。     

正交法分析再生粗骨料混凝土的基本性能

采用正交法试验分析了再生粗骨料掺量、聚丙烯纤维掺量和引气减水剂掺量3个配合比因素对再生混凝土抗压强度、劈拉强度和抗压弹模的影响,用再生粗骨料掺量为70%、聚丙烯纤维掺量为O.7%和引气减水剂掺量为0.2%的参数进行配合比设计,可使设计强度为C30的再生混凝土获得良好的和易性和较高的强度.通过对混凝土拌合物含气量的测定,分析得出了随着引气减水剂掺量的增加,含气量增加1%时,再生混凝土的抗压强度降低4.1%,劈拉强度降低7.7%,抗压弹模降低3.9%.将再生粗骨料经机械强化后,可使再生混凝土的抗压强度提高约13%.结果表明:引气减水剂和再生粗骨料掺量是影响这3个力学性能的重要因素.     

Influence of parent concrete on the properties of recycled aggregate concrete

This paper discusses first the properties of recycled aggregates derived from parent concrete (PC) of three strengths, each of them made with three maximum sizes of aggregates. The relative physical and mechanical properties of fresh granite aggregate are discussed. Using these nine recycled aggregates, three strengths of recycled aggregate concrete (RAC) were made and studied. Typical relationship between water–cement ratio, compressive strength, aggregate-cement ratio and cement content have been formulated for RAC and compared with those of PC. RAC requires relatively lower water–cement ratio as compared to PC to achieve a particular compressive strength. The difference in strength between PC and RAC increases with strength of concrete. The relative evaluation of tensile and flexural strengths and modulus of elasticity has also been made.     

Mechanical properties of concrete with recycled coarse aggregate

This paper reports the results of an experimental study on some of the mechanical properties of recycled aggregate concrete (RAC) as compared to those of the conventional normal aggregate concrete (NAC). Ten mixes of concrete with target compressive cube strength ranging from 20 to 50 MPa were cast using normal or recycled coarse aggregates. The development of the cube compressive strength and the indirect shear strength at ages of 1, 3, 7, 14, 28 and 56 days, the compressive strength, the strains at maximum compressive stress and the modulus of elasticity tested by using concrete cylinders at 28 days are reported. The results show that the 28-day cube and cylinder compressive strength, and the indirect shear strength of recycled aggregate concrete were on the average 90% of those of natural aggregate concrete with the same mix proportions. For concrete with cylinder compressive strengths between 25 and 30 MPa, the modulus of elasticity of RAC was only 3% lower than that of NAC. The trends in the development of compressive and shear strength and the strain at peak stress in recycled aggregate concrete were similar to those in natural aggregate concrete.     

基于正交试验的再生骨料混凝土强度研究

研究不同影响因素对再生骨料混凝土强度的影响是再生骨料混凝土研究领域的主要方面之一,对实际工程应用有着重要的意义。采用三因素、三水平的正交试验设计方法对再生骨料混凝土的配合比进行了试验设计,分析了每个因素水平对再生骨料混凝土配合比的作用及各个水平之间的差异,探讨了水胶比、再生骨料掺量、超细粉煤灰掺量等试验因素对再生骨料混凝土强度的影响规律和机理,并与基准混凝土对比。试验结果表明:无论早期与后期,水胶比是影响再生骨料混凝土强度的最主要因素,也是最显著因素;掺粉煤灰再生骨料混凝土的拉压比与同强度等级的高强混凝土相比有所提高,抗裂性能有所改善。采用多元回归分析的方法,建立了再生骨料混凝土强度与水胶比、再生骨料掺量、超细粉煤灰掺量的经验公式。     

再生粗骨料混凝土力学性能试验研究

以某10年龄期的既有建筑物废弃混凝土作为再生粗骨料原料,配制了坍落度达140 mm的C40泵送混凝土。以再生粗骨料取代率、粉煤灰取代率为主要研究参量,对配制的混凝土试块的立方体抗压、棱柱体抗压、劈裂抗拉和弹性模量等力学性能指标进行了系统的试验研究。结果表明,再生混凝土的抗压、劈裂抗拉破坏形态与普通混凝土基本一致。在满足坍落度一定的前提下,立方体抗压强度、棱柱体抗压强度和弹性模量随着再生骨料取代率的增加而降低,而随着粉煤灰取代率的增加而有所提升;劈裂抗拉强度离散性较大,无明显规律;各力学指标间关系受再生粗骨料和粉煤灰取代率的影响也不明显。研究结果可为再生粗骨料的应用提供参考。     

Influence of recycled concrete aggregates on strength properties of concrete

Many structures in the middle-east’s Gulf region are now either reaching the end of their design life or were not constructed according to the specifications. Demolition or maintenance work on such structures results in large amount of concrete rubbles. Recycling concrete wastes will lead to reduction in valuable landfill space and savings in natural resources. The objective of this study is to investigate the strength of concrete made with recycled concrete coarse aggregate. The variables that are considered in the study include the source of the recycled concrete and target concrete strength. The toughness and soundness test results on the recycled coarse aggregate showed higher percentage loss than natural aggregate, but remained within the acceptable limits. The compressive and splitting tensile strengths of concrete made with recycled coarse aggregate depend on the mix proportions. In general, the strength of recycled concrete can be 10–25% lower than that of conventional concrete made with natural coarse aggregate.     

不同取代率再生粗骨料混凝土的力学性能

系统研究了坍落度相同的情况下再生粗骨料取代率对混凝土基本性能的影响.试验中再生粗骨料的掺入量分别为0,30%,50%,70%和100%,通过调节用水量使各组混凝土达到相同的坍落度.主要研究了达到相同坍落度时混凝土的用水量以及再生粗骨料取代率对混凝土坍落度、立方体抗压强度、棱柱体抗压强度、峰值应变和泊松比、弹性模量、劈裂抗拉强度以及抗折强度的影响.试验结果表明,再生粗骨料取代率对上述各性能指标均有一定影响,但程度不同.同时发现,除劈裂抗拉强度和抗折强度外,普通混凝土各基本力学性能指标间的关系不适用各种再生骨料取代率的混凝土.     

再生骨料混凝土在某框架结构中的应用及长期应变监测

以再生骨料混凝土在框架结构中的应用为工程背景,将分布于框架结构对称位置的再生及普通混凝土构件进行长期监测,分析再生骨料混凝土应用于不同类型构件的可行性。在实验室测试原位浇筑的再生与普通骨料混凝土抗压强度,在现场对再生及普通骨料混凝土梁、板、柱构件进行混凝土应变的长期对比监测。分析结果表明：采用优化配合比设计的再生骨料混凝土,其强度略低于普通骨料混凝土;当再生骨料混凝土应用于各类实体构件时,其早龄期抵抗由于干缩效应引起的拉应变的能力优于普通骨料混凝土,但再生骨料混凝土抵抗由于荷载及温度变化引起变形的能力劣于普通骨料混凝土;再生骨料混凝土各类构件应变发展与普通构件相当,再生骨料混凝土可应用于框架结构的梁、板、柱等构件中。     

再生混凝土抗拉强度与抗压强度关系的试验研究

总结了国内外再生混凝土抗压强度和抗拉强度的研究现状,并通过27组再生混凝土立方体试块的抗压试验及劈裂试验,建立了再生混凝土劈裂抗拉强度与立方体抗压强度之间的关系.试验结果表明,在相同立方体抗压强度条件下,再生混凝土的劈裂抗拉强度比普通混凝土降低30%左右.