Structural changes and their effect on mechanical properties of silk fibroin/chitosan blends

Silk fibroin/chitosan blend films were prepared by the solvent casting method. Miscibility between silk fibroin and chitosan was examined by dynamic mechanical thermal analysis. Structural changes of silk fibroin by the addition of chitosan were investigated by IR spectroscopy. The conformational transition of silk fibroin from random coil form to β‐sheet structure induced by blending with chitosan resulted in the increase of crystallinity and density of the blend films. The blend film containing 30 wt % chitosan exhibited a maximum increase in crystallinity and density. It was found that the tensile strength and initial tensile modulus of blend films were greatly enhanced with increasing the chitosan content and showed a maximum value at the composition of 30 wt % chitosan. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 74: 2571–2575, 1999     

丝素/羧甲基壳聚糖共混膜的结构性能探讨

将含有甘油和戊二醛的丝素与羧甲基壳聚糖按一定比例混合,制得丝素/羧甲基壳聚糖共混膜,对共混膜的结构与性能进行了探讨。结果表明:随着羧甲基壳聚糖含量的增加,共混膜的透气率增大,加入交联剂戊二醛有效地改善了共混膜的力学性能,但其透气率有所降低;当丝素与羧甲基壳聚糖的质量比为4/1时,共混膜的断裂强度最大,力学性能较好,共混膜相容性较好,其断面光滑、致密。制备丝素/羧甲基壳聚糖共混膜的较佳条件为:丝素中的甘油质量分数为15%,戊二醛质量分数为0.075%,丝素与羧甲基壳聚糖质量比为4/1。     

Structural and physical properties of silk fibroin/alginate blend sponges

Silk fibroin/alginate blend sponges were examined through IR spectroscopy, X‐ray diffractometry, and differential scanning calorimetry to determine the structural changes of silk fibroin. The effects of fibroin/alginate blend ratios on the physical and mechanical properties were investigated to discover the feasibility of using these blend sponges as biomedical materials such as wound dressings. The compressive modulus of silk fibroin was increased up to 30 kPa, from 7.1 kPa, by blending with alginate. Thermal crystallization behavior of fibroin induced by heat treatment was restricted by blending with alginate. In spite of that, the structural characteristics of fibroin were not changed by incorporation with alginate. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 2174–2179, 2004     

The Fabrication and Characterization of Cellulose/Mesoporous Silica Composites Packaging Films with Adjustable Permeability by NMMO Technology

Cellulose-based composites containing various amounts of SBA-15 mesoporous silica were prepared by NMMO-technology, and their morphologies, mechanical properties, permeability for oxygen and water vapor were studied. The investigation suggested that both the modified and unmodified mesoporous silica materials can improve the elongation at break of the cellulose films. However, the incorporation of the mesoporous silica materials can reduce the tensile strength of the films, and the modified one has less effect on that than the unmodified one. The composites films with rational mechanical properties have adjustable oxygen permeability (7.90 × 10^?15–94.6 × 10^?15 cm³ · cm/cm² · s · Pa) and water vapor permeability (7.12 × 10^?13–4.10 × 10^?13 g · cm/cm² · s · Pa).     

Oxygen barrier properties of polyketone/EVOH blend films and their resistance to moisture

Polyketone (PK) has excellent chemical and mechanical properties, but its use in food packaging is limited due to its oxygen barrier properties being insufficient for high-barrier film applications. To improve its oxygen barrier properties, PK has been blended with ethylene vinyl alcohol copolymer (EVOH), which is one of the highest oxygen barrier polymers in use today. The oxygen barrier properties under both dry and humid conditions, as well as the mechanical properties of PK/EVOH blend films were investigated in this study. These novel PK/EVOH blend films exhibited unusually low oxygen permeability values from 0.3 to 0.16 cc 20 μm m⁻² day⁻¹ atm⁻¹ with increasing EVOH content from 30 to 70 wt%, which are even lower than those of the ideal laminar model that expresses the theoretical minimum permeability values attainable for blended barrier films. These high oxygen barrier properties of PK/EVOH blend films can conceivably be attributed to the combination of two dominant effects: a tortuous diffusion path through the EVOH domains in the PK matrix and hydrogen bonding interactions between PK and EVOH. Furthermore, in high-humidity environments with retorting, the PK/EVOH blend films exhibited superior resistance to moisture over EVOH. Immediately after the retorting test, the oxygen permeability of the high-barrier PK/EVOH blend films with an EVOH content of 30–40 wt% increased by less than 3× the pre-retorting value, as opposed to 74× for EVOH. In addition, PK/EVOH blend films displayed superior stretching characteristics, with a breaking strain of over 300%, which are valuable for flexible packaging applications.     

Mechanical properties of silk fibroin–microcrystalline cellulose composite films

Silk fibroin–microcrystalline cellulose (cellulose whisker) composite films with varied compositions were prepared by casting mixed aqueous solution/suspensions of the two components. Silk fibroin was dissolved in 10M LiSCN followed by dialysis; a cellulose whisker suspension was prepared by sulfuric acid hydrolysis of tunicate cellulose. Macroscopically homogeneous films were obtained at all mixing ratios. While the Young's modulus of the composite films showed a linear, additive dependence on the mixing ratio, the tensile strength and ultimate strain showed a maximum at a 70–80% cellulose content, reaching five times those of fibroin‐alone or cellulose‐alone films. At the same mixing ratio, infrared spectra of the composite films showed a shift of the amide I peak from 1654 to 1625 cm^?1, indicating the conformational change of fibroin from a random coil to a β structure (silk II) at the whisker–matrix interface. This change seems to be induced by contact of fibroin molecules with a highly ordered surface of cellulose whisker. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 3425–3429, 2002     

Chitosan‐finished Antheraea mylitta silk fibroin nonwoven composite films for wound dressing

In this study, we aimed to produce nonwoven wound‐dressing films made of Antheraea mylitta (tasar) silk fibroin by a solution‐casting method. These nonwoven films were finished with chitosan solutions of different concentrations ranging from 0.75 to 2% w/v with a pad–dry method to fabricate nonwoven composite films. Chitosan‐finished tasar fibroin nonwoven composite films (CMTFFs) showed higher mechanical and dynamic mechanical properties as compared to nonwoven tasar fibroin. The physical, structural, and thermal properties of the films were investigated. The hemocompatibility, cytocompatibility, and biodegradation tests showed that the CMTFF was a promising material for use as a wound dressing. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 44341.     

Development of a novel glucosamine/silk fibroin–chitosan blend porous scaffold for cartilage tissue engineering applications

Silk fibroin–chitosan blend is reported to be an attractive scaffold material for tissue engineering applications. In our earlier study, we developed a scaffold having an optimal silk fibroin–chitosan blend ratio of 80:20 and proved its potentiality for cartilage tissue engineering applications. Glucosamine is one of the major structural components of cartilage tissue. The present work investigates the effect of glucosamine components on the physicochemical and biocompatibility properties of this scaffold. To this end, varied amounts of glucosamine were added to silk fibroin–chitosan blend with the aim of improving various scaffold properties. The addition of glucosamine components did not show any significant change in physicochemical properties of silk fibroin–chitosan blend scaffolds. The composite scaffold showed an open pore structure with desired pore size and porosity. However, cell culture study using human mesenchymal stem cells derived from umbilical cord blood revealed an overall increase in cell supportive properties of glucosamine-added scaffolds. Cell viability, cell proliferation and glycosaminoglycan assays confirmed enhanced cell viability and proliferation of mesenchymal stem cells. Thus, this study demonstrated the beneficial effect of glucosamine on improving the cell supportive property of silk fibroin–chitosan blend scaffolds making it more potential for cartilage tissue regeneration. To the best of our knowledge, this is the first report on the study of glucosamine-added silk fibroin–chitosan blend porous scaffolds seeded with mesenchymal stem cells derived from umbilical cord blood.     

Preparation and characterization of soy protein isolate–carboxymethylated konjac glucomannan blend films

To improve the mechanical and water vapor barrier properties of soy protein films, the transparent films were prepared by blending 5 wt % soy protein isolate (SPI) alkaline water solution with 2 wt % carboxymethylated konjac glucomannan (CMKGM) aqueous solution and drying at 30 °C. The structure and properties of the blend films were studied by infrared spectroscopy, wide‐angle X‐ray diffraction spectroscopy, scanning electron microscopy, thermogravimetric analysis, differential thermal analysis, and measurements of mechanical properties and water vapor transmission. The results demonstrated a strong interaction and good miscibility between SPI and CMKGM due to intermolecular hydrogen bonding. The thermostability and mechanical and water vapor barrier properties of blend films were greatly enhanced due to the strong intermolecular hydrogen bonding between SPI and CMKGM. The tensile strength and breaking elongation of blend films increased with the increase of CMKGM content: the maximum values achieved were 54.6 MPa and 37%, respectively, when the CMKGM content was 70 wt %. The water vapor transmission of blend films decreased with the increase of CMKGM content: the lowest value achieved was 74.8 mg · cm^?2 · d^?1 when the CMKGM content was 70 wt %. The SPI–CMKGM blend films provide promising applications to fresh food packaging. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 1095–1099, 2003     

Metal ion permeation properties of silk fibroin/chitosan blend membranes

Silk fibroin/chitosan (SF/CS) blend membranes were prepared and characterized by infrared spectroscopy (FTIR), thermogravimetric analysis (TGA) and scanning electron microscopy. It was found that SF and CS were compatible in the blend membranes and that the membranes were dense without microscopic phase separation. Swelling experiments showed that the swelling ratio of the blend membranes increased with CS content and reached the highest value when CS content was 70 wt%. Experiments indicated that the permeability coefficient of K⁺ through the blend membrane was 2–4 times higher than that of pure CS membrane, and 10 times higher than that of pure SF membrane. The permeation rate of K⁺ increased linearly with CS content in the blend membrane for the lower concentration feeding solution. For different metal ions, the permeability through SF/CS blend membranes was in the sequence K⁺ > Ca²⁺ > Cd²⁺ > Pb²⁺ > Cu²⁺ > Ni²⁺. Copyright © 2006 Society of Chemical Industry     

Characterization of minocycline loaded chitosan/polyethylene glycol/glycerol blend films as antibacterial wound dressings

Wound care has been a challenging subject for medical teams and researchers. Bacterial infections are one of the most serious complications in injured skins that often affect healing process. Antibacterial wound dressings can be used to facilitate wound healing process. The purpose of this study is to fabricate chitosan (Chito)/polyethylene glycol (PEG) antibacterial wound dressing doped with minocycline, and to evaluate the influence of composition ratio on the blending properties of the films. To improve the mechanical properties of these films, we examined various amounts of glycerol as a plasticizer. Moreover, we investigated morphological and mechanical aspects, water uptake, degradation, water vapor transmission and wettability properties of the films prepared with various ratios of Chito/PEG/Gly. Assessment of mechanical properties revealed that film containing 80:20 ratio Chito/PEG with 40 PHR Gly content exhibits the highest ultimate tensile strength and elongation at break (9.74 MPa and 45.73% respectively). Furthermore, results demonstrated that upon increasing PEG and Gly contents, degradability and hydrophilicity of the films increased whereas water uptake decreased. Water vapor transmission rate of the films was close to the range of 530–1200 g/m²d, indicating that the as formed films are possible candidates for dressing low exudate wounds or burns. Minocycline loaded films exhibited a biphasic drug release profile and it was more effective on gram-positive bacteria than on gram-negative bacteria. The polymeric film with the highest amount of loaded drug (2%) exhibited insignificant cytotoxicity (88%) against normal fibroblast cell line.     

葡甘聚糖-壳聚糖-聚乙烯醇共混膜的结构表征及性能研究

用溶液共混法制备了葡甘聚糖-壳聚糖-聚乙烯醇共混膜,并用红外光谱(FTIR)、X-射线衍射(XRD)、扫描电镜(SEM)及透光率表征了膜的结构,同时测定了共混膜的力学性能、吸水率、水蒸气透过率。结果表明:共混膜中葡甘聚糖、壳聚糖及聚乙烯醇之间存在着强烈的相互作用和良好的相容性,三者共混明显改善了纯聚合物和二元膜的性能。     

Preparation and characterization of LDPE/PVA blend films filled with glycerin‐plasticized polyvinyl alcohol

A series of LDPE/PVA blend films were prepared via a twin‐screw extruder, and their morphology, thermal property, oxygen and water vapor permeation, surface properties, and mechanical properties were investigated as a function of the PVA content. During the extrusion process of the blend films, glycerin improved the compatibility and processing conditions between LDPE and PVA. The melting temperature (T_m), melting enthalpy (ΔH_m), crystallinity (%), and thermal stability of the thermal decomposition temperature (T_5%) of the LDPE/PVA blend films decreased with increasing PVA content. The oxygen permeabilities of the blend films decreased from 24.0 to 11.4 cm³·cm (m²·day·atm)^?1 at 23°C. The WVTR increased from 7.8 to 15.0 g(m² day)^?1 and the water uptake increased from 0.13 to 9.31%, respectively. The mechanical properties of blend films were slightly enhanced up to 2% PVA and then decreased. The physical properties of the blend films strongly varied with the chemical structure and morphology depending on the PVA and glycerin. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41985.     

Study on the preparation of PU/HBP‐NH2 blend film and its properties

The blend films of polyurethane (PU) and amino‐terminal hyperbranched polymers (HBP‐NH₂) were prepared successfully by mixing HBP‐NH₂ solution and PU. The rate of moisture absorption and mechanical properties were determined. The results showed that the rates of moisture absorption and vapor permeability were improved from 0.34% to 7.51% and from 161 gm^?2 d^?1 to 879 gm^?2 d^?1, respectively. The addition of HBP‐NH₂ is helpful to improve the hygiene properties of PU films. Then, the structures of the blend films were characterized by IR, XRD, TG, and SEM at the same time. The results indicated that HBP‐NH₂ and PU had hydrogen‐bond interaction and a certain phase separation. The blend films had good heat stability. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41383.     

Preparation of insoluble fibroin films without methanol treatment

Insoluble fibroin films were prepared without methanol treatment. A 15 wt % fibroin solution was obtained through concentration, and then, the insoluble film was achieved by the adjustment of the drying temperature and rate. These films were examined through Fourier transform infrared–attenuated total reflection, X‐ray diffraction, and scanning electron microscopy to determine the structure of the silk fibroin. The physical and mechanical properties were investigated to discover the feasibility of using these films as biomedical materials. When fibroin films were dried above 60°C, abundant β‐sheet crystals existed in the fibroin films, and many globule‐containing micelles aggregated and interacted with each other, which resulted in excellent mechanical properties of the regenerated fibroin films in the wet state. Interestingly, the amide III band of the random coil structure in the fibroin films dried at 70 and 80°C was shifted to a lower frequency, 1228 cm^?1, which meant that a partly orientated structure formed. This may have also affected the mechanical properties of the fibroin films. The tensile strength and breaking elongation of the films dried at 70°C were 29.8 MPa and 59.6%, which is distinctly superior to fibroin films treated with methanol. If the drying temperature was raised to 60°C, the stability of the films in water was also excellent. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 96: 2168–2173, 2005     

Packaging‐related properties of alkyd‐coated,wax‐coated,and buffered chitosan and whey protein films

Packaging‐related properties of coated films of chitosan–acetic acid salt and whey protein concentrate (WPC) were studied. Chitosan (84.7% degree of deacetylation) and WPC (65–67% protein) were solution cast to films. These films are potential oxygen barriers for use in packaging. Coatings of wax or alkyds were used to enhance the water‐barrier properties. The packaging‐related properties of chitosan films treated in a buffering solution, with a pH of 7.8, were also investigated. The coated films were characterized with respect to Cobb absorbency, overall migration to water, water vapor transmission rate, and oxygen permeability. The creasability and bending toughness were determined. The wax was a more efficient barrier to liquid water and 90–95% relative humidity than the alkyd. However, the alkyd‐coated material had superior packaging‐converting properties. The alkyd‐coated WPC and chitosan–salt films were readily folded through 180° without any visible cracks or delamination. The overall migration from the alkyd‐coated materials was below the safety limit, provided the coat weight was higher than 7.5 mg/cm² on WPC and 2.1 mg/cm² on chitosan–salt. The barrier properties of chitosan film under moist conditions were improved by the buffer treatment. However, the buffering also resulted in shrinkage of the film. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 60–67, 2004     

Separation of alcohol–water mixture by pervaporation through a novel natural polymer blend membrane–chitosan/silk fibroin blend membrane

A novel natural polymer blend membrane, namely chitosan/silk fibroin blend membrane, was prepared. The selective solubility and the pervaporation properties of alcohol–water mixture were studied. The results showed that the membrane was water selective and the separation factor of ethanol–water mixture could be improved compared to pure chitosan membrane, when silk fibroin content in blend membrane was no more than 40 wt %. The blend membrane exhibited a best performance, (i.e., the water in permeate was large than 99 wt % when silk content was 20 wt % and the crosslinking agent–glutaraldehyde content was 0.5 mol %). The mechanism of improvement on pervaporation properties was explained by reducing the free volume and freeing hydrophilic groups of chitosan because of the strong intermolecular hydrogen bond forming between chitosan and silk fibroin in blend membrane. In addition, the influence of operation temperature and feed concentration as well as the pervaporation properties of isopropanol–water mixture were also studied. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 73: 975–980, 1999     

Mechanical properties and water vapor permeability of thin film from corn hull arabinoxylan

Isolated corn hull arabinoxylan was dissolved in water and provided a clear solution. Plasticizer (glycerol, propylene glycol, or sorbitol) was added to the arabinoxylan solution at 0–20 wt % (film dry weight), which was cast into stable films. Film thickness ranged from 22 to 32 μm. Mechanical properties, moisture content, and water vapor permeability (WVP) were studied for the arabinoxylan‐based films as a function of plasticizer concentration. Measured data for the corn hull arabinoxylan–based films were 13–18 wt % moisture content, 10–61 MPa tensile strength, 365–1320 MPa modulus, 6–12% elongation, and 0.23–0.43 × 10^?10 g m^?1 Pa^?1 s^?1 water vapor permeability. Plasticized arabinoxylan films produced in this study had lower WVPs than those of unplasticized films, which is likely attributable to the phenomenon known as antiplasticization. Scanning electron micrographs showed a homogeneous structure on film surfaces. Films containing sorbitol had the best moisture barrier properties. When grapes were coated with arabinoxylan and arabinoxylan/sorbitol films, weight loss rates of the fruit decreased by 18 and 41%, respectively, after 7 days. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 93: 2896–2902, 2004     

Effects of addition of condensed tannin on the structure and properties of silk fibroin film

Condensed tannin is a polymeric polyphenol compound, which has considerable protein‐binding ability and a variety of bioactivities, such as anti‐inflammatory, antithrombotic and antimicrobial activities. In this study, silk fibroin film was modified by adding condensed tannin. It was found that strong intermolecular interactions occurred between silk fibroin and tannin, and incorporation of 1–10% (w/w) tannin in the blend films resulted in more compact, stiffer but less elastic films. Swelling and dissolution trials showed that the addition of tannin significantly reduced the swelling and solubility of the films. The mechanical properties, swelling and solubility of the blend films varied as a function of tannin concentration, showing optimum values when containing 10% (w/w) tannin. The silk fibroin–tannin films all showed significant antioxidant activity and antibacterial activity against Gram‐positive bacteria, and the activities were positively related to the concentration of tannin. The results emphasized that the addition of condensed tannin could simultaneously improve the structural stability of silk fibroin film and impart functional properties. © 2016 Society of Chemical Industry     

Fabrication of Chitosan/Silk Fibroin Composite Nanofibers for Wound-dressing Applications

Chitosan, a naturally occurring polysaccharide with abundant resources, has been extensively exploited for various biomedical applications, typically as wound dressings owing to its unique biocompatibility, good biodegradability and excellent antibacterial properties. In this work, composite nanofibrous membranes of chitosan (CS) and silk fibroin (SF) were successfully fabricated by electrospinning. The morphology of electrospun blend nanofibers was observed by scanning electron microscopy (SEM) and the fiber diameters decreased with the increasing percentage of chitosan. Further, the mechanical test illustrated that the addition of silk fibroin enhanced the mechanical properties of CS/SF nanofibers. The antibacterial activities against Escherichia coli (Gram negative) and Staphylococcus aureus (Gram positive) were evaluated by the turbidity measurement method; and results suggest that the antibacterial effect of composite nanofibers varied on the type of bacteria. Furthermore, the biocompatibility of murine fibroblast on as-prepared nanofibrous membranes was investigated by hematoxylin and eosin (H&E) staining and MTT assays in vitro, and the membranes were found to promote the cell attachment and proliferation. These results suggest that as-prepared chitosan/silk fibroin (CS/SF) composite nanofibrous membranes could be a promising candidate for wound healing applications.