本文在苯乙烯-丁二烯-苯乙烯嵌段共聚物（Styrene—Butadiene—Styrene triblock copolymer,SBS）辐射接枝马来酸酐（Maleicanhydride,MAH）的基础上,进行MAH／苯乙烯（Styrene,St）二元单体辐射接枝研究,讨论了MAH／St比例和总浓度及吸收剂量对接枝率的影响。就MAH接枝产物SBS-g-MAH和MAH／St二元接枝产物SBS-g-MAH／St进行了傅立叶红外光谱（Fouriertransforminfraredspectroscopy,FFIR）、热重（Thernlalgravimetric,TG）分析与差示扫描量热（Differentialscanningcalorimetry,DSC）分析等表征与分析。结果表明：MAH／St二元接枝可明显提高MAIl接枝率。     

SBS辐射接枝共聚研究(Ⅱ):线型SBS液固相辐射接枝MAA

利用γ射线辐射接枝法制备苯乙烯-丁二烯-苯乙烯(Styrene—Butadiene—Styrene,SBS)粉体接枝甲基丙烯酸(MAA)聚合物,讨论了单体浓度、辐照剂量、气氛及辐照状态等因素对接枝率的影响,并采用傅立叶红外光谱(FT-IR)、差示扫描量热分析(DSC)、凝胶渗透色谱(GPC)、扫描电镜(SEM)、动态剪切流变(DSR)等分析手段对接枝聚合物进行了表征。研究结果表明,平均粒径为0．2mm的线型SBS粉体在辐照剂量为12kGy、剂量率为0．75kGy／h、MAA／SBS的质量比为0．6时,可获得最大接枝率。FTIR谱出现1705cm^-1。处羰基的吸收峰证实了接枝聚合物的存在,分子量分布测定表明SBS-g-MAA聚合物的分子量分布变宽,动态剪切流变中接枝聚合物的粘度增大,表明单体在SBS链上有接枝链的增长;热分析曲线中聚苯乙烯嵌段的玻璃化转变温度升高,损耗因子转折温度升高,都说明单体MAA对PS嵌段的影响较大。     

辐照交联SBS／LDPE共混物的形状记忆效应研究

以苯乙烯-丁二烯嵌段共聚物（SBS）热塑性弹性体和低密度聚乙烯（LDPE）为主要原料,使用混炼机将SBS与LDPE按80：20的比例共混并在硫化机上模压制成SBS／LDPE共混物,利用γ射线辐照上述共混物使之交联。通过DSC分析、力学性能和形状记忆性能测试,研究了辐照交联SBS／LDPE共混物材料的结构对形状记忆性能的影响。结果表明,SBS／LDPE共混物随吸收剂量的增加,交联度增大,拉伸强度与断裂伸长率均逐渐降低;此外,适度交联的SBS／LDPE共混物呈现良好的形状记忆效应,形变回复率高于95％。     

SBS的辐照效应研究

研究了室温下苯乙烯-丁二烯-苯乙烯（Styrene-Butadiene-Styrene.SBS）在^60Coγ射线下的辐照效应。采用傅立叶红外光谱（Fourier-transform infrared spectroscopy,FT-IR）、差示扫描分析（Differential scanning calorimetry,DSC）、热重分析（Thermal gravimetric analysis,TG）、扫描电镜（Scaning electron microscopy,SEM）、动态剪切流变（Dynamic shear rheology,DSR）等分析方法对辐照产物进行了表征。辐照产物经红外光谱分析,未发现有氧化物生成;SBS辐照后发生交联反应,随着吸收剂量的升高,不溶于甲苯的交联SBS量增加;DSC和TG表明辐照后材料的柔性聚丁二烯嵌段和刚性聚苯乙烯嵌段的玻璃化温度向高温方向移动,同时有更高的玻璃化温度点形成,耐高温物质量增加;动态剪切流变分析表明辐照后出现新的网络松弛行为,吸收剂量越高,材料的损耗因子峰越明显;辐照后SBS剪切粘度变大,储能模量增加,损耗模量下降,材料的温度敏感性下降;扫描电镜分析表明SBS辐照后抗氧化性能也得到了提高。     

SBS辐射接枝共聚研究(Ⅰ):SBS/MMA液相辐射接枝

利用^60Coγ射线对苯乙烯-丁二烯-苯乙烯(Styrene-Butadiene-Styrene,SBS)嵌段共聚物进行辐射接枝改性。研究了SBS／甲基丙烯酸甲酯(Methyl methacrylate,MMA)溶液体系的辐射接枝共聚反应,探讨了辐照剂量、单体浓度、SBS型号对接枝率的影响。并用红外光谱(FT-IR)对接枝共聚物进行了表征,用差示扫描量热仪(DSC)测量了接枝共聚物SBS-g-MMA的热性能。     

SBS辐射接枝共聚研究Ⅲ:星型SBS接枝改性

利用γ射线辐射接枝法分别制备甲基丙烯酸（Methacrylic acid,MAA）和甲基丙烯酸酯（Methyl methacrylate,MMA）两种单体接枝星型SBS聚合物,采用傅立叶红外光谱（Fourier transform infrared,FT-IR）、差示扫描热分析（Difierentail scanning calorimetry,DSC）、热重分析（Thermogravimetric analysis,TGA）、核磁共振谱（^13C{^1H}Nuclear magnetic resonance,NMR）等手段对接枝聚合物进行了表征,确定了单体成功地引入SBS链上,同时发现SBS接枝聚合物具有较好的高温稳定性。着重对敏化剂提高接枝率的原因进行了探讨,认为在液固相接枝体系中,溶剂水的辐解产物＊OH自由基对接枝率的提高起了非常重要的作用。     

SBS辐射接枝共聚研究(II):线型SBS液固相辐射接枝MAA

利用γ射线辐射接枝法制备苯乙烯-丁二烯-苯乙烯(Styrene-Butadiene-Styrene,SBS)粉体接枝甲基丙烯酸(MAA)聚合物,讨论了单体浓度、辐照剂量、气氛及辐照状态等因素对接枝率的影响,并采用傅立叶红外光谱(FT-IR)、差示扫描量热分析(DSC)、凝胶渗透色谱(GPC)、扫描电镜(SEM)、动态剪切流变(DSR)等分析手段对接枝聚合物进行了表征。研究结果表明,平均粒径为0.2mm的线型SBS粉体在辐照剂量为12kGy、剂量率为0.75kGy/h、MAA/SBS的质量比为0.6时,可获得最大接枝率。FTIR谱出现1705cm-1处羰基的吸收峰证实了接枝聚合物的存在,分子量分布测定表明SBS?g?MAA聚合物的分子量分布变宽,动态剪切流变中接枝聚合物的粘度增大,表明单体在SBS链上有接枝链的增长;热分析曲线中聚苯乙烯嵌段的玻璃化转变温度升高,损耗因子转折温度升高,都说明单体MAA对PS嵌段的影响较大。     

乙烯-乙烯醇基大分子型强化交联剂的合成与应用

通过熔融酯化反应制备了乙烯-乙烯醇-g-丙烯酸(EVOH-g-AA)共聚物,用红外光谱对接枝产物进行了表征.凝胶抽提结果显示,由于乙烯基双键的引入,难于辐射交联的EVOH在较低的吸收剂量下就可以辐射交联.改性EVOH与聚乳酸共混物的辐射效应研究结果表明,聚乳酸进入交联网格,说明改性EVOH具有一定的强化辐射交联剂的作用.     

高剂量γ辐照对SEBS／PS共混物性能的影响

研究了高剂量(0～2.0 MGy)γ辐照对不同配比苯乙烯一-乙烯-丁烯-苯乙烯嵌段共聚物/聚苯乙烯(SEBS/PS)共混物(100/0～50/50)力学性能、电性能以及热稳定性能的影响.结果表明,PS的加入,可以有效改善SEBS的辐照稳定性.PS的含量越高,辐照后SEBS/PS共混物的拉伸强度、体积电阻率的下降幅度越小,介电损耗因子的上升幅度越小,热稳定性能越好.但PS的加入减少了共混物中聚烯烃相的含量,使得共混物的断裂伸长率受辐照的影响较大,特别在高剂量辐照后,PS的含量越高的共混物断裂伸长率下降越明显.     

苯乙烯—丁二烯共聚物和顺—1,4—聚异戊二烯的辐…

研究了１２种多官能团不饱和单体对ＳＢＲ（苯乙烯－丁二烯共聚物）和ＩＲ（顺－１，４－聚异戊二烯）辐射交联的敏化效应，发现Ａ－ＴＭＭＴ（四丙烯酸四羟甲基甲烷酯）和２Ｇ（二甘醇二甲基丙烯酸酯）是ＳＢＲ和ＩＲ的有效敏化剂。对辐照交联ＳＢＲ和ＩＲ的应力－应变、动态力学以及其它性能进行了考察与分析，并与传统硫磺交联法所得产品性能进行了比较，获得了与硫磺交联产物性能相当的辐射交联ＳＢＲ和ＩＲ。     

γ辐射对PP/SBS的流变性能和内耗的影响

研究了一系列不同含量的ＳＢＳ与聚丙烯的共混物的辆射硫化效应。辐照一定剂量后,由于辐射交联和裂解的进行,使ＰＰ／ＳＢＳ的流变性能和结构及内耗行为发生大的变化,ＰＰ与ＳＢＳ两者玻璃化转变温度距离变小,从而改善了ＰＰ／ＳＢＳ的相容性。ＰＰ和ＳＢＳ在辐射引发自由基的情况下,分散相ＳＢＳ形成交联结构,连续相ＰＰ发生裂解,体系的表观粘度下降,但ＰＰ的玻璃化转变激活能仍然提高了。     

Studies on mechanical, thermal and morphological properties of irradiated recycled polyamide and waste rubber powder blends

The aim of this article was to show the effect of gamma irradiation on mechanical and thermal properties of recycled polyamide (rPA) copolymer blended with different content of waste rubber powder (WRP). In order to study the structural modifications of prepared blends have been subjected to irradiation doses up to 200 kGy were applied to all samples. Non-irradiated blends were used as control samples. Mechanical properties, namely, tensile strength (TS), elastic modulus, elongation at break and hardness have been followed up as a function of irradiation dose and degree of loading with rubber content. Furthermore, the influence of radiation dose in the thermal parameters, melting temperature, heat of fusion, ΔH_f of the recycled PA and its blend with waste rubber powder (WRP) was also investigated.     

SBS及~(60)Co辐照SBS改性沥青的制备

通过苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)含量、助溶剂类型及用量、加工温度、加工时间、辐照剂量率和辐照剂量条件优化实验,对SBS改性沥青制备方法、60 Co辐照SBS制备方法及辐照SBS改性沥青制备方法进行研究;通过对改性沥青结合料制品各项性能指标测试,对制备方法进行评价。实验结果表明,质量分数为15%~20%的SBS,质量分数为15%~30%的助溶剂,混匀后在100~165℃下,100~200r/min机械搅拌20~30min,升温至180~210℃,100~200r/min机械搅拌90~140min,或120~160℃下,100~200r/min机械搅拌80~100min,制得的SBS改性沥青结合料性能较好;60 Co 0.75kGy/h剂量率、30kGy剂量、真空辐照的辐照SBS改性沥青结合料性能较好。     

尼龙66/紫外辐照线性低密度聚乙烯共混物的力学性能

通过紫外辐照实现了高密度聚乙烯(HDPE)的官能化，改善了HDPE复合材料的性能。本工作采用傅立叶红外(FT-IR)、X射线光电子能谱(XPS)、凝胶、熔融指数和水接触角测试等研究了紫外辐照对线性低密度聚乙烯(LLDPE)化学结构和性能的影响。紫外辐照后，在LLDPE的分子链上引入了C=O、C-O和C(=O)O等含氧基团，其含量随辐照时间延长而增加。凝胶分析结果表明，紫外辐照过程中，LLDPE产生凝胶，     

60Co辐射交联乙烯-醋酸乙烯酯共聚物/氢氧化镁复合材料的热、力学及阻燃性能研究

以三羟甲基丙烷三丙烯酸酯为交联助剂,以60Co为辐射源,对三种不同醋酸乙烯酯(Vinyl-acetate,VA)含量的乙烯-醋酸乙烯酯共聚物(Ethylene vinyl-acetate copolymer,EVA)/氢氧化镁混合材料进行了辐照交联.通过对凝胶含量、维卡软化点、氧指数、UL-94垂直燃烧和拉伸性能的测试及热重分析,研究了辐照剂量对EVA/氢氧化镁交联体的交联度、热性能、力学性能和阻燃性能的影响.研究结果表明:VA含量高的EVA/氢氧化镁交联体更容易产生辐射交联;辐照交联后的EVA/氢氧化镁复合材料的抗热变形能力、力学性能及阻燃性能都获得明显改善.热重分析结果表明,60Co辐射明显影响EVA/氢氧化镁的热氧稳定性.     

Radiation cross-linking of small electrical wire insulator fabricated from NR/LDPE blends

A low voltage, radiation-crosslinked wire insulator has been fabricated from blends of natural rubber block (STR-5L) and LDPE with phthalic anhydride (PA) as a compatibilizer. Physical properties of the NR/LDPE blend ratios of 50/50 and 60/40 with 0.5, 1.0, and 1.5 wt% PA were evaluated. The gel content increased as the radiation dose increased. Tensile at break exhibited a maximum value of 12 MPa at 120 kGy for 1.0 and 1.5 wt% PA of both blend ratios. A higher PA content yielded a higher modulus for the same blend ratio. Blends of 60/40 ratio with 1.0 wt% PA and 0.8 wt% antimony oxide flame retardant gave the highest limiting oxygen index (LOI) of >30% at above 150 kGy. Other electrical properties of the wire insulator were investigated. It was found that an insulator fabricated from a PA content of 1.0 wt% in the NR/LDPE blend ratio of 50/50, after gamma ray cross-linked at a dose of 180 kGy in low vacuum (1 mm Hg), met the Thai Industrial Standard 11-2531 for low voltage wire below 1.0 kV. To comply with the standard for vertical flame test, a more suitable flame retardant was needed for the insulator.     

Radiation effects on styrene-butadiene-styrene copolymer

Styrene-butadiene-styrene copolymer (SBS) of different configuration and block ratio were irradiated by ⁶⁰Co γ-rays at 20 °C and 120 °C. The gel fraction and thermal properties before and after irradiation were discussed. The gel fraction increased with both absorbed doses and temperature. This means higher crosslinking efficiency was obtained at higher temperature. The radiation chemical yields were calculated according to the Charlesby-Pinner equation. The DSC analysis indicated that the crosslinking had taken place in the polybutadiene (PB) block while the chain scission of polystyrene (PS) block was dominant when irradiated at elevated temperature.