世界印刷书写纸及其涂布和浆布加填用颜料市场发展趋势

涂布和末涂布纸激烈的国际竞争,使世界上一些大型造纸商除通过大规模的资产重组及兼并大幅度降低成本外,还大量使用涂布及加填颜料提高产品质量,降低生产成本,提高市场竞争力。 本文将对世界印刷书写纸及其涂布和加填用颜料市场发展趋势作简要说明。 本文所提颜料包括:高岭土、碳酸钙、滑石粉、二氧化硅和二氧化钛等。使用这些颜料的纸种有:含磨木浆涂布纸、不含磨木浆涂布纸、未涂布超级压光纸、软压光纸、新闻纸、不含磨木浆未涂布纸和涂布纸板。论述范围只限于颜料发展     

颜料涂布纸加工化学品

随着我国经济的快速发展及人民生活物质文化水平的不断提高，涂布纸的用量不断提高，其中以颜料涂布纸的用量最普遍。它所采用的涂布颜料、胶粘剂及化学添加剂对纸张质量影响很大。本文将对这些涂布化学品作一论述。     

滤纸的多孔性对涂布性能的影响

<正>颜料涂布纸在涂布加工纸中占有很大的比例,这类涂布纸是将以二氧化硅、高岭土、碳酸钙、硫酸钡和二氧化钛等白色颜料为主加上胶黏剂以及为改变某些性能而添加的助剂等而制成的涂料,按某一定量均匀地涂布在纸和纸板表面上,然后再通过整饰加工而成。简言之,颜料涂布纸是由原纸、     

涂料主要组分对涂布纸抗液体渗透性能的影响

采用静态渗透性能和动态渗透特性相结合的方法评价了涂布纸的抗液体渗透性能。探讨了颜料中高岭土和碳酸钙的配比、胶黏剂和抗水剂的种类和用量对涂布纸抗渗透性能的影响。研究表明,随着PCC在颜料中比例的增加,润湿性Max值和特征值西5呈相近的变化规律。颜料中高岭土和PCC的比例为60：40时,涂布纸的静滴接触角为62.2&;#176;,动态渗透性能参数Max值和t95均最大,此时,涂布纸具有较好的抗水性能和最封闭的表面结构。无论是静态渗透性能还是动态渗透性能,就涂布淀粉、聚乙烯醇（部分醇解型）、羧基丁苯胶乳、丙烯酸胶乳及乙烯．醋酸乙烯共聚物胶乳5种胶黏剂而占,其涂布纸的抗液体渗透性能由强到弱的顺序是：羧基丁苯胶乳〉丙烯酸胶乳〉乙烯-醋酸乙烯共聚物胶乳〉聚乙烯醇（部分醇解型）〉涂布淀粉;涂布纸的抗渗透性能受胶乳用量的影响最大。在一定用量范围内,抗水剂可以较大程度地改善涂布纸的抗液体渗透性能。     

部分国家造纸化学品生产商

澳大利亚AlliedFlour&Starch产品:造纸化学品和添加剂。BuckmanLaboratoriesPtyLtd产品:造纸化学品和添加剂,涂布化学品。Clariant(Australia)PtyLtd产品:造纸化学品和添加剂,涂布化学品,颜料。EkaChemicals(Australia)PtyLtd产品:合成胶料和松香胶,脱墨化学品,助留剂和控制系统。HenkelAustraliaPtyLtd产品:造纸化学品和添加剂,涂布化学品,消泡剂,控制沉积的产品,涂布添加剂,腐浆控制剂,表面活性剂,聚合电解质,石蜡胶,湿强度剂,亚硫酸氢盐漂白剂。HuntsmanChemicalCompanyAus-traliaLimited产品:SBR胶乳,涂布化学药品。KaolinA…     

改善薄膜压榨涂布的运行性能

薄膜压榨涂布的影响因素———从预计量到涂布及薄膜剥离。把薄膜压榨压区中涂料的脱水理论与在每面涂布量约１０ｇ／ｍ２、车速１０００ｍ／ｍｉｎ以上,含磨木浆和不含磨木浆条件下造纸的结果进行了比较。决定纸张运行性能和成纸表面质量的因素有：纸机参数、颜料和胶粘剂。造纸工作者的工作就是要在纸页的运行性能和表面质量之间这两个互相矛盾的要求中找到一个最佳方案。随着预计量薄膜施胶压榨用于表面施胶的巨大成功,使人们了解了使用颜料涂布纸机的潜能。市场上,机内整饰颜料化纸（ＭＦＰ）的质量优于薄膜涂布胶印纸（ＦＣＯ）和其…     

硫酸钙作为颜料改进涂布纸的功能性质

在过去的几年间,人们对于高亮度纸的关注和需求已经驱使造纸厂家探寻新的方法来提高涂布纸的亮度和白度。用以提高纸和纸板光学性能(如亮度、白度和光泽度)的颜料涂布得到广泛应用。这些光学性质对于最终使用者非常重要,同时也决定了涂布纸的最终成本。相比于其它的常规颜料,如重质碳酸钙、沉淀碳酸钙和高岭土,硫酸钙具有固有的更好的光学性能。本研究的目的是利用从磷酸厂购得的废弃物合成硫酸钙,并研究它对涂料的流变性以及对涂布纸光学性能的影响。加入硫酸钙可以提高涂层的保水性,这对于改善运行性能是很有帮助的。结果还表明,将硫酸钙用作颜料,可以生产出高亮度和高白度的涂布纸。在涂料配方里,用50份的硫酸钙代替高岭土,涂布纸的亮度和白度可以分别提高4%和15%。研究表明,使用硫酸钙作为颜料,涂布纸板IGT印刷粘着性能的表面强度很高,印刷光泽度与无光泽涂布纸相似。     

改性高岭土替代二氧化硅生产低光泽涂布喷墨打印纸

分别以改性高岭土和二氧化硅为颜料配制喷墨打印纸涂料,制备了低光泽涂布喷墨打印纸,评估了以改性高岭土替代二氧化硅对喷墨打印纸视觉效果、表面性能、印刷性能以及涂布操作的影响。实验结果表明,与以传统的二氧化硅为颜料相比,以改性高岭土为颜料能明显改善涂料制备、涂料流变性及涂布机运转性能,提高涂料固含量。如果含改性高岭土涂料中不使用添加剂(阳离子固定剂),则改性高岭土喷墨打印纸的打印质量不及传统的二氧化硅喷墨打印纸。若不考虑打印颜色和打印机类型,涂料中添加阳离子固定剂可大幅提高最终喷墨打印纸的色密度,且对含改性高岭土的涂料的流变性和涂布操作没有负面影响,涂布后喷墨打印纸质量与商品喷墨打印纸相当。     

使用塑料颜料提高涂布白板纸的光学性能

塑料颜料作为一种新型有机颜料已广泛用于造纸涂布加工纸生产中.涂布白板纸涂料通常使用传统的高岭土、碳酸钙等颜料.着重研究在涂布白板纸涂料中使用塑料颜料,探讨塑料颜料对纸张的光泽度、白度及表面遮盖性等光学特性的影响.结果表明,在面涂涂料中添加8～10份塑料颜料,能显著提高涂布白板纸的光学性能.     

窄粒径分布碳酸钙颜料的干湿涂料结构

近4年来,窄粒径分布的天然研磨碳酸钙颜料已成功地用作造纸涂料。它们的高白度、高不透明度以及良好的覆盖性能使得它们具有高平滑度和高光泽度。这些颜料的应用给厂家提供了开发涂布纸和涂布纸板的机会。粒径分布的变化使涂料具有不同的性能,如：快速脱水、高固着层比率和增大的剪切粘度,这些性能使涂布过程中刮刀的压力增大了。优化刮刀涂布机的运行性能要求降低固含量,这意味着必须要脱去大量的水,消耗更多的干燥能量,而这两项都是造纸生产厂家所不希望的。本文叙述了专门设计的胶乳分散剂怎样对涂料的流变性进行控制。专门设计的胶乳分散剂使窄粒径分布的研磨碳酸钙颜料在涂布机上的运行性能提高了,而对涂布纸的光学性能和物理性能没有影响。     

合成胶乳性能剖析及在纸张涂布时的黏结机理

胶乳胶黏剂是纸张涂料的重要组成部分。胶乳的物化性能对涂布纸的适印性和印刷质量影响很大。本文剖析了合成胶乳的主要性能特征,讨论了胶乳特性与涂布纸质量的相关性;阐述了胶乳胶黏剂在纸张颜料悬浮液中与颜料粒子的相互作用及黏结机理,并分析了在涂布的不同阶段,乳胶微粒移动的不同方式。     

涂布育果外袋纸涂料的研制和应用

针对苹果育果袋纸抄造过程中碳黑流失严重、污染大等问题,研究将碳黑涂料涂于外袋纸上的生产技术。结果表明:利用涂布法生产育果袋外纸,碳黑利用率高,可降低生产成本,用涂布法制造苹果育果袋外袋纸是可行的;涂料配方为:碳黑:瓷土=40:60,分散剂用量3%(对颜料总量),分散液固含量20%,SBR胶乳分散液量5%(体积比)。     

Preparation of Ultrafine Starch Particle and its Application in Paper Coating

Despite its biodegradability, adequate cohesive strength and comparatively low cost, the use of cooked starch as a paper coating binder is limited due to its high viscosity and serious negative impact on the gloss. Starch-based bio-latex with size in the nanometer or sub-micrometer range has been developed recently to overcome these shortcomings. In this study, ultrafine starch particle (UFSP) was prepared by mechanical milling using a DYNO mill in combination with light chemical pretreatment. Model coating colors containing different dosages of UFSP were applied to base paper and the properties of the coated papers were evaluated. The results showed that the UFSP was disc-shaped with a median particle diameter of 167 nm. Water retention capacity of the coating colors was improved considerably with the addition of UFSP, i.e., the water retention value decreased by nearly 40% when styrene-butadiene latex was replaced by UFSP at a dosage of 3 pph (per hundred parts of pigment). The high shear rate viscosities of the coating colors containing no more than 2 pph of USFP were similar to that of the control coating color at shear strain rate higher than 2000 s1. The properties and performances of the coated papers were comparable to the control coated paper with single synthesized latex binder. The gloss and the print gloss of paper samples with or without USFP were 59.7% and 58.2%, 79.0% and 78.8%, respectively. Surface strength of paper samples with or without USFP were 0.96 and 0.90 m/s, respectively, while the ink absorptivity values were 34% and 33%. This study demonstrates a promising approach to obtain sub-micrometer sized starch for paper coating.     

空心球塑料颜料对涂布纸物理性能和印刷适性的影响

研究了空心塑料颜料对涂布纸物理性能的影响，包括：光泽度、白度、不透明度、松厚度、平滑度，以及对印刷适性的影响。实验显示：用少量空心球塑料颜料代替基础配方中的瓷土可有效提高涂布纸的综合性能，由此可认为空心球塑料颜料是一种优良的涂布功能颜料。加入HP塑料颜料后的涂层在较低压光整饰条件下就能迟到全矿物颜料在高整饰条件下的光学性能，并且提高了涂层的松厚度和印刷性能。     

颜料特性对涂布纸表面摩擦性能影响的研究

探讨了涂料中颜料特性对涂布纸表面摩擦性能的影响，并观察了涂层表面磨损情况。结果表明：在沉淀碳酸钙和瓷土混合颜料配方中，沉淀碳酸钙含量较高时涂布纸表面的静态和动态摩擦系数较高，而采用压光可降低涂层表面粗糙度和摩擦系数；在瓷土、沉淀碳酸钙和重质碳酸钙混合颜料配方中，重质碳酸钙添加量从0～20％时，涂层表面的摩擦系数增大，但继续增大其含量摩擦系数有所降低。     

碳化钨涂布刮刀的研制

刮刀是涂布机的关键部件,传统的(无涂层)蓝钢刀片戓工具钢带制造的涂布刮刀由于其磨损快、寿命短,己经不能满足高速涂布机的生产要求,需要开发具有金属/陶瓷碳化钨(WC/Co) 涂层的高耐磨型涂布刮刀。业界曾采用等离子喷涂等方法在钢带上制备各种陶瓷材质的耐磨涂层以提高涂布刮刀的使用寿命。但现行的工艺方法获得的涂层存在着涂层不致密、孔隙率高、结合强度低等不足之处,本研究采用国产的HVAF超音速火焰喷涂系统成功研制具有WC10Co4Cr碳化钨耐磨涂层的涂布刮刀,各项质量指标均超过等离子喷涂等方法制备的陶瓷涂布刮刀,其平均使用寿命为陶瓷刮刀的2倍以上,涂层质量可以与国际同类产品相媲美。     

颜料涂布纸油墨吸收性能影响因素的讨论

探讨了颜料涂布纸油墨吸收性的影响因素,结果表明,在一定的范围内,随着GCC量的增加,瓷土片状结构的有序性被打乱了,涂层的孔隙率增加,利于油墨的吸收性的增强;在瓷土／重钙的比例一定的情况下,随轻钙份数的增加,油墨的吸收性增加;随着胶乳用量的增加,涂层表面成膜性增强,孔隙率减少,油墨吸收性降低;涂料中加入一定的淀粉后,油墨的吸收性明显提高;涂布量的增加会使涂层的结构更加紧密,油墨的吸收性会随着涂布量的增加而降低。但是涂布量的增加,条痕等纸病会带来油墨吸收性的升高。     

铜版纸全研磨碳酸钙面涂涂料配方的优化研究

通过在面涂涂料中采用小粒径丁苯胶乳,探讨了铜版纸全研磨碳酸钙(GCC)面涂涂料配方与车间含高岭土涂料配方对涂料性能及铜版纸物理性能与印刷适性的影响。结果表明,优化的全GCC面涂涂料配方在高固含量的情况下,维持了涂料较低的高剪切黏度,使铜版纸获得了理想的光泽度和印刷适性。     

水性聚氨酯-丙烯酸酯包覆颜料色浆在涂料染色中的应用

为提高涂料染色色浆分散稳定性,简化染色工艺流程,以颜料聚丙烯酸酯为核、聚氨酯为壳,采用无皂乳液聚合法制成了水性聚氨酯丙烯酸酯包覆颜料色浆,用于棉织物涂料轧染。借助纳米粒度仪与透射电子显微镜对有色乳液平均粒径及分布、颗粒形貌进行分析;通过调节浸轧工艺配方中海藻酸钠用量,改变浸轧次数与焙烘温度优化染色工艺条件。结果表明：水性聚氨酯丙烯酸酯包覆颜料乳胶粒具有明显的核壳结构,平均粒径为126 nm;染色配方中海藻酸钠质量分数为0.2%,二浸二轧,80 ℃烘干,140 ℃焙烘,染色织物得色量较高;经柔软整理,织物手感较好,干摩擦牢度达到4~5 级,湿摩擦牢度达到4级,皂洗褪色牢度达到4 级。     

可聚合乳化剂在涂料印花粘合剂制备中的应用

运用可聚合乳化剂制备涂料印花粘合剂,研究乳化剂及其质量分数对单体转化率、聚合凝聚率、胶膜溶失率、胶膜力学性能及涂料印花色牢度的影响。结果表明：可聚合乳化剂与传统乳化剂复合,可以改善其聚合稳定性。键合在胶粒表面的可聚合乳化剂,可以明显降低胶膜溶失率,提升胶膜力学性能,提高涂料印花色牢度。可聚合复合乳化剂质量分数为6%时,乳液聚合具有较高的单体转化率和较低的聚合凝聚率,胶膜具有较低的溶失率,较高的断裂功和良好的涂料印花色牢度。可聚合复合乳化剂可作为涂料印花黏合剂的理想无APEO乳化剂。