Microstructural Development of Calcium alpha-SiAlON Ceramics with Elongated Grains

Silicon nitride (Si₃N₄) and SiAlONs can be self-toughened through the growth of elongated β-Si₃N₄/β-SiAlON grains in sintering. α-SiAlONs usually retain an equiaxed grain morphology and have a higher hardness but lower toughness than β-SiAlONs. The present work has demonstrated that elongated alpha-SiAlON grains can also be developed through pressureless sintering. alpha-SiAlONs with high-aspect-ratio grains in the calcium SiAlON system have exhibited significant grain debonding and pull-out effects during fracture, which offers promise for in-situ -toughened α-SiAlON ceramics.     

Change of Crystal Phases and Microstructure of Amorphous Si-C-N Powder by Hot Pressing

An amorphous Si-C-N powder with Y₂O₃ and Al₂O₃ powder as sintering additives was hot-pressed at 1900°C for 120 min in a nitrogen atmosphere. Changes in the crystalline phases and microstructure of the amorphous Si-C-N powder during sintering were investigated by X-ray diffractometry (XRD) and transmission electron microscopy (TEM). The defects at the fracture origins of the sintered bodies after bending tests also were investigated by scanning electron microscopy (SEM) and electron probe microanalysis (EPMA). XRD showed that alpha-Si₃N₄ was formed initially from the amorphous Si-C-N by 1530°C, which then transformed to ß-Si₃N₄ at 1600°C. Also, a slight formation of crystalline SiC occurred during the transformation from alpha- to ß-Si₃N₄, and it increased after the transformation was completed at 1900°C. TEM revealed that many SiC nanoparticles were incorporated into ß-Si₃N₄ grains after the transformation from alpha- to ß-Si₃N₄ at 1600°C. They were located at the triple points of the grain boundaries of ß-Si₃N₄ after continued Si₃N₄ grain growth at 1900°C. Besides the SiC nanoparticles, large agglomerations of carbon or SiC particles of 20-60 µm size were observed by SEM and EPMA at the fracture origins of the sintered bodies after the bending tests.     

Direct Observations of Debonding of Reinforcing Grains in Silicon Nitride Ceramics Sintered with Yttria Plus Alumina Additives

As in fiber-reinforced composites, debonding, which allows the elongated reinforcing grains to at least partially separate from the rest of the matrix, is a critical part of the toughening mechanism in self-reinforced silicon nitrides. In situ high-resolution electron microscopy observations reveal that the debonding path can occur at the interface between the grains and continuous nanometer-thick intergranular film (IGF) or within the IGF depending on the film's composition, which varies with the yttria to alumina ratio in the fixed total amount of sintering additives. Theoretical calculations reveal that the bonding across the interface can be weakened by decreasing the Al and O content ( z ) of the epitaxial Si_{6– Z} Al _Z O _Z N_{8– Z} layer on the grains, which is consistent with the observations of interfacial debonding. However, evidence also indicates that weakening of the amorphous network of the IGF occurs with increase in yttrium levels that can be responsible for the observed mixture of debonding by crack propagation along the interface and within the IGF when the sintering additive contains the highest yttria:alumina ratio.     

Microstructure Control of In-Situ-Toughened α-SiAlON Ceramics

Single-phase α-SiAlON with elongated grains is obtained from α-Si₃N₄ powder for a broad range of compositions of practical interest. Following the concept of nucleation and growth, two-step firing is used for microstructure control. This method takes advantage of the slow transformation reaction from α-Si₃N₄ to α-SiAlON at low temperature when the composition is near the α-SiAlON phase boundary and, hence, is marginally stable. For more-stable compositions, the seeding of α-SiAlON crystals is more effective, because it allows elongated grains to grow onto the seed crystals. The fracture toughness is strongly correlated with the microstructure and is enhanced greatly in the optimized materials.     

Microstructure and Mechanical Properties of the in situβ-Si3N4/α'-SiAlON Composite

The in situ β-Si₃N₄/α'-SiAlON composite was studied along the Si₃N₄–Y₂O₃: 9 AlN composition line. This two phase composite was fully densified at 1780°C by hot pressing Densification curves and phase developments of the β-Si₃N₄/α'-SiAlON composite were found to vary with composition. Because of the cooperative formation of α'-Si AlON and β-Si₃N₄ during its phase development, this composite had equiaxed α'-SiAlON (∼0.2 μm) and elongated β-Si₃N₄ fine grains. The optimum mechanical properties of this two-phase composite were in the sample with 30–40%α', which had a flexural strength of 1100 MPa at 25°C 800 MPa at 1400°C in air, and a fracture toughness 6 Mpa·m^1/2. α'-SiAlON grains were equiaxed under a sintering condition at 1780°C or lower temperatures. Morphologies of the α°-SiAlON grains were affected by the sintering conditions.     

Effect of Sintering Additives on Microstructure and Mechanical Properties of Porous Silicon Nitride Ceramics

Porous silicon nitride (Si₃N₄) ceramics with about 50% porosity were fabricated by pressureless sintering of α-Si₃N₄ powder with 5 wt% sintering additive. Four types of sintering aids were chosen to study their effect on the microstructure and mechanical properties of porous Si₃N₄ ceramics. XRD analysis proved the complete formation of a single β-Si₃N₄ phase. Microstructural evolution and mechanical properties were dependent mostly on the type of sintering additive. SEM analysis revealed the resultant porous Si₃N₄ ceramics as having high aspect ratio, a rod-like microstructure, and a uniform pore structure. The sintered sample with Lu₂O₃ sintering additive, having a porosity of about 50%, showed a high flexural strength of 188 MPa, a high fracture toughness of 3.1 MPa·m^1/2, due to fine β-Si₃N₄ grains, and some large elongated grains.     

Fabrication and Mechanical Properties of Silicon Carbide-Silicon Nitride Composites with Oxynitride Glass

A microstructure that consisted of uniformly distributed, elongated β-Si₃N₄ grains, equiaxed β-SiC grains, and an amorphous grain-boundary phase was developed by using β-SiC and alpha-Si₃N₄ powders. By hot pressing, elongated β-Si₃N₄ grains were grown via alpha right arrow β phase transformation and equiaxed β-SiC grains were formed because of inhibited grain growth. The strength and fracture toughness of SiC have been improved by adding Si₃N₄ particles, because of the reduced defect size and the enhanced bridging and crack deflection by the elongated β-Si₃N₄ grains. Typical flexural-strength and fracture-toughness values of SiC-35-wt%-Si₃N₄ composites were 1020 MPa and 5.1 MPam^1/2, respectively.     

Relationship between Microstructure and Mechanical Performance of a 70% Silicon Nitride–30% Barium Aluminum Silicate Self-Reinforced Ceramic Composite

The abnormal grain growth of β-Si₃N₄ was observed in a 70% Si₃N₄–30% barium aluminum silicate (70%-Si₃N₄–30%-BAS) self-reinforced composite that was pressureless-sintered at 1930°C; Si₃N₄ starting powders with a wide particle-size distribution were used. The addition of coarse Si₃N₄ powder encouraged the abnormal growth of β-Si₃N₄ grains, which allowed microstructural modification through control of the content and size distribution of β-Si₃N₄ nuclei. The mechanical response of different microstructures was characterized in terms of flexural strength, as well as indentation fracture resistance, at room temperature. The presence of even a small amount of abnormally grown β-Si₃N₄ grains improved the fracture toughness and minimized the variability in flexural strength.     

Microstructure Characterization of Gas-Pressure-Sintered β-Silicon Nitride Containing Large β-Silicon Nitride Seeds

Fine β-Si₃N₄ powders with or without the addition of 5 wt% of large β-Si₃N₄ particles (seeds) were gas-pressure sintered at 1900°C for 4 h using Y₂O₃ and Al₂O₃ as sintering aids. The microstructures were examined on polished and plasmaetched surfaces. These materials had a microstructure of in situ composites with similar small matrix grains and different elongated grains. The elongated grains in the materials with seeds had a larger diameter and a smaller aspect ratio than those in the materials without seeds. A core/rim structure was observed in the elongated grains; the core was pure β-Si₃N₄ and the rim was β-SiAION. These results show that the large β-Si₃N₄ particles acted as seeds for abnormal grain growth and the rim was formed by precipitation from the liquid containing aluminum.     

Effect of Grain Growth of β-Silicon Nitride on Strength, Weibull Modulus, and Fracture Toughness

β-Si₃N₄ powder containing 1 mol% of equimolar Y₂O₃–Nd₂O₃ was gas-pressure sintered at 2000°C for 2 h (SN2), 4 h (SN4), and 8 h (SN8) in 30-MPa nitrogen gas. These materials had a microstructure of " in-situ composites" as a result of exaggerated grain growth of some β Si₃N₄ grains during firing. Growth of elongated grains was controlled by the sintering time, so that the desired microstructures were obtained. SN2 had a Weibull modulus as high as 53 because of the uniform size and spatial distribution of its large grains. SN4 had a fracture toughness of 10.3 MPa-m^1/2 because of toughening provided by the bridging of elongated grains, whereas SN8 showed a lower fracture toughness, possibly caused by extensive microcracking resulting from excessively large grains. Gas-pressure sintering of β-Si₃N₄ powder was shown to be effective in fostering selective grain growth for obtaining the desired composite microstructure.     

Self-Reinforced Nitrogen-Rich Calcium–α-SiAlON Ceramics

Nitrogen-rich Ca–α-SiAlON ceramics with nominal compositions Ca _x Si_{12−2 x} Al_{2 x} N₁₆ and 0.2≤ x ≤2.6, extending along the Si₃N₄–1/2Ca₃N₂:3AlN tie line, were prepared from Si₃N₄, AlN, and CaH₂ precursors by hot pressing at 1800°C. The x values attained were determined by energy-dispersive X-ray (EDX) microanalysis and X-ray powder diffraction (XRPD) data using the Rietveld method. The results show that Ca–α-SiAlONs form continuously within the compositional range x =0 to at least x =1.82. Phase assemblages, lattice parameters, Vickers hardness, and fracture toughness were determined and correlated to the calcium content, x . Owing to a high sintering temperature and the use of CaH₂ as a precursor, grain growth was kinetically enhanced, resulting in self-reinforced microstructures with elongated grains. The obtained Ca–α-SiAlON ceramics demonstrate a combination of both high hardness ∼21 GPa, and high fracture toughness ∼5.5 MPa·m^1/2.     

Densification of Si3N4 with LiYO2 Additive

This paper deals with the densification and phase transformation during pressureless sintering of Si₃N₄ with LiYO₂ as the sintering additive. The dilatometric shrinkage data show that the first Li₂O- rich liquid forms as low as 1250°C, resulting in a significant reduction of sintering temperature. On sintering at 1500°C the bulk density increases to more than 90% of the theoretical density with only minor phase transformation from α-Si₃N₄ to β-Si₃N₄ taking place. At 1600°C the secondary phase has been completely converted into a glassy phase and total conversion of α-Si₃N₄ to β-Si₃N₄ takes place. The grain growth is anisotropic, leading to a microstructure which has potential for enhanced fracture toughness. Li₂O evaporates during sintering. Thus, the liquid phase is transient and the final material might have promising mechanical properties as well as promising high-temperature properties despite the low sintering temperature. The results show that the Li₂O−Y₂O₃ system can provide very effective low-temperature sintering additives for silicon nitride.     

New Strategies for Preparing NanoSized Silicon Nitride Ceramics

We report the preparation of nanosized silicon nitride (Si₃N₄) ceramics via high-energy mechanical milling and subsequent spark plasma sintering. A starting powder mixture consisting of ultrafine β-Si₃N₄ and sintering additives of 5-mol% Y₂O₃ and 2-mol% Al₂O₃ was prepared by high-energy mechanical milling. After milling, the powder mixture was mostly transformed into a non-equilibrium amorphous phase containing a large quantity of well-dispersed nanocrystalline β-Si₃N₄ particles. This powder precursor was then consolidated by spark plasma sintering at a temperature as low as 1600°C for 5 min at a heating rate of 300°C/min. The fully densified sample consisted of homogeneous nano-Si₃N₄ grains with an average diameter of about 70 nm, which led to noticeable high-temperature ductility and elevated hardness.     

Microstructure of an Extruded β-Silicon Nitride Whisker-Reinforced Silicon Nitride Composite

β-Si₃N₄ whisker-reinforced β'SiAlON composites were fabricated by extrusion and densified, using pressureless sintering. Whisker alignment was observed in both the green and sintered microstructures. SEM analysis of polished, sintered samples showed a microstructure consisting of the original β-Si₃N₄ whiskers in a matrix of fine SiAlON grains. SEM of plasma-etched samples and TEM analysis showed that the whiskers, as a result of grain growth, consisted of two phases, a core and a sheath layer. X-ray mapping and EDS analysis revealed that the core material contained no trace of Al, confirming the presence of original β-Si₃N₄ whiskers. The composition of the sheath was qualitatively identical to that of the fine β' SiAlON grains in the matrix. The sheath was thus formed by the precipitation of the β'SiAlON during liquid-phase sintering and led to substantial growth of the whiskers. Microdiffraction showed that the β'SiAlON grew epitaxially on the β-Si₃N₄ whiskers, resulting in a heavily faulted SiAlON layer.     

Mechanical Property and Oxidation Behavior of Self-Reinforced Si3N4 Doped with Re2O3 (Re=Yb, Lu)

In this work, self-reinforced silicon nitrides with β-Si₃N₄ seeds doped with Re₂O₃ (Re=Yb, Lu) were investigated. Firstly, the two kinds of seeds were obtained by heating α-Si₃N₄ powder with Yb₂O₃ or Lu₂O₃, respectively. Then the self-reinforced silicon nitride ceramics were prepared by HP-sintering of α-Si₃N₄ powder, Re₂O₃ as additive, and the as-prepared seeds. Oxidation test was carried out at 1400°C in air for 100 h with thermogravimetry analysis (TGA) measurement. Mechanical properties, scanning electronic microscopy microstructures, and X-ray diffraction patterns were measured before and after oxidation. The results indicated that the introduction of the seeds doped with Re₂O₃ (Re=Yb, Lu) could obviously increase the toughness and keep the room temperature and high-temperature strength of the ceramics at high values. After oxidation, the crystalline phase in grain boundary changed and the mechanical properties decreased. TGA showed a parabolic weight gain and the oxidation mechanism was discussed.     

Fracture Energies of Tape-Cast Silicon Nitride with β-Si3N4 Seed Addition

The fracture energies of the tape-cast silicon nitride with and without 3 wt% rod-like β-Si₃N₄ seed addition were investigated by a chevron-notched-beam technique. The material was doped with Lu₂O₃–SiO₂ as sintering additives for giving rigid grain boundaries and good heat resistance. The seeded and tape-cast silicon nitride has anisotropic microstructure, where the fibrous grains grown from seeds were preferentially aligned parallel to the casting direction. When a stress was applied parallel to the fibrous grain alignment direction, the strength measured at 1500°C was 738 MPa, which was almost the same as room temperature strength 739 MPa. The fracture energy of the tape-cast Si₃N₄ without seed addition was 109 and 454 J/m² at room temperature and 1500°C, respectively. On the contrary, the fracture energy of the seeded and tape-cast Si₃N₄ was 301 and 781 J/m² at room temperature and 1500°C, respectively, when a stress was applied parallel to the fibrous gain alignment. The large fracture energies were attributable primarily to the unidirectional alignment fibrous Si₃N₄ grains.     

Processing, Microstructure, and Wear Behavior of Silicon Nitride Hot-Pressed with Alumina and Yttria

Commercial silicon nitride powder with A1₂O₃ and Y₂O₃ additives was hot-pressed to complete density. The resulting microstructure contained elongated grains with no trace of remaining α-Si₃N₄. The aspect ratio of the elongated grains increased with increasing soak time at a fixed hot-pressing temperature. X-ray diffraction analysis showed that the crystalline phase in the hot-pressed samples was β-sialon (Si_6−zAl_zO_zN_8−z) with z values that increased with soak time. The fracture strength and fracture toughness of the samples increased as the aspect ratio of the grains increased. The Vickers hardness decreased slightly as the soak time was increased, which was attributed to a grain size effect. Wear tests of silicon nitride against silicon nitride were conducted on a reciprocating pin-on-disk apparatus with paraffin oil as a lubricant. Correlation studies of wear with microstructure and mechanical properties were performed. The wear rate increased rapidly with increasing soak time in spite of the increased strength and toughness. This was attributed to increased third-body wear caused by pullout of pieces from the wear surface. The pullout mechanism was not conclusively identified. However, TEM examination showed clear evidence of dislocation motion under the wear scar. Grain boundary microstresses caused by the anisotropic thermal expansion and elastic properties of the elongated grains may have contributed to the observed pullout.     

Microstructural Development During Gas-Pressure Sintering of α-Silicon Nitride

Gas-pressure sintering of α-Si₃N₄ was carried out at 1850 ° to 2000°C in 980-kPa N₂. The diameters and aspect ratios of hexagonal grains in the sintered materials were measured on polished and etched surfaces. The materials have a bimodal distribution of grain diameters. The average aspect ratio in the materials from α-Si₃N₄ powder was similar to that in the materials from β-Si₃N₄ powder. The aspect ratio of large and elongated grains was larger than that of the average for all grains. The development of elongated grains was related to the formation of large nuclei during the α-to-β phase transformation. The fracture toughness of gaspressure-sintered materials was not related to the α content in the starting powder or the aspect ratio of the grains, but to the diameter of the large grains. Crack bridging was the main toughening mechanism in gas-pressure-sintered Si₃N₄ ceramics.     

Kinetics of β-Si3N4 Grain Growth in Si3N4 Ceramics Sintered under High Nitrogen Pressure

The kinetics of anisotropic β-Si₃N₄ grain growth in silicon nitride ceramics were studied. Specimens were sintered at temperatures ranging from 1600° to 1900°C under 10 atm of nitrogen pressure for various lengths of time. The results demonstrate that the grain growth behavior of β-Si₃N₄ grains follows the empirical growth law Dⁿ– D₀ⁿ = kt , with the exponents equaling 3 and 5 for length [001] and width [210] directions, respectively. Activation energies for grain growth were 686 kJ/mol for length and 772 kJ/mol for width. These differences in growth rate constants and exponents for length and width directions are responsible for the anisotropy of β-Si₃N₄ growth during isothermal grain growth. The resultant aspect ratio of these elongated grains increases with sintering temperature and time.     

Spark Plasma Sintered Silicon Nitride Ceramics with High Thermal Conductivity Using MgSiN2 as Additives

Silicon nitride ceramics were prepared by spark plasma sintering (SPS) at temperatures of 1450°–1600°C for 3–12 min, using α-Si₃N₄ powders as raw materials and MgSiN₂ as sintering additives. Almost full density of the sample was achieved after sintering at 1450°C for 6 min, while there was about 80 wt%α-Si₃N₄ phase left in the sintered material. α-Si₃N₄ was completely transformed to β-Si₃N₄ after sintering at 1500°C for 12 min. The thermal conductivity of sintered materials increased with increasing sintering temperature or holding time. Thermal conductivity of 100 W·(m·K)⁻¹ was achieved after sintering at 1600°C for 12 min. The results imply that SPS is an effective and fast method to fabricate β-Si₃N₄ ceramics with high thermal conductivity when appropriate additives are used.